Unusually thick shear-softening surface of micrometer-size metallic glasses.

ABSTRACT: The surface of glass is crucial for understanding many fundamental processes in glassy solids. A common notion is that a glass surface is a thin layer with liquid-like atomic dynamics and a thickness of a few tens of nanometers. Here, we measured the shear modulus at the surface of both millimeter-size and micrometer-size metallic glasses (MGs) through high-sensitivity torsion techniques. We found a pronounced shear-modulus softening at the surface of MGs. Compared with the bulk, the maximum decrease in the surface shear modulus (G) for the micro-scale MGs reaches ~27%, which is close to the decrease in the G upon glass transition, yet it still behaves solid-like. Strikingly, the surface thickness estimated from the shear-modulus softening is at least 400 nm, which is approximately one order of magnitude larger than that revealed from the glass dynamics. The unusually thick surface is also confirmed by measurements using X-ray nano-computed tomography, and this may account for the brittle-to-ductile transition of the MGs with size reductions. The unique and unusual properties at the surface of the micrometer-size MGs are physically related to the negative pressure effect during the thermoplastic formation process, which can dramatically reduce the density of the proximate surface region in the supercooled liquid state.

SUBMITTER: Dong J

PROVIDER: S-EPMC8454631 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Shear-banding Induced Indentation Size Effect in Metallic Glasses.

Project description:Shear-banding is commonly regarded as the "plasticity carrier" of metallic glasses (MGs), which usually causes severe strain localization and catastrophic failure if unhindered. However, through the use of the high-throughput dynamic nanoindentation technique, here we reveal that nano-scale shear-banding in different MGs evolves from a "distributed" fashion to a "localized" mode when the resultant plastic flow extends over a critical length scale. Consequently, a pronounced indentation size effect arises from the distributed shear-banding but vanishes when shear-banding becomes localized. Based on the critical length scales obtained for a variety of MGs, we unveil an intrinsic interplay between elasticity and fragility that governs the nanoscale plasticity transition in MGs. Our current findings provide a quantitative insight into the indentation size effect and transition mechanisms of nano-scale plasticity in MGs.

| S-EPMC4914989 | biostudies-literature

The Critical Criterion on Runaway Shear Banding in Metallic Glasses.

Project description:The plastic flow of metallic glasses (MGs) in bulk is mediated by nanoscale shear bands, which is known to proceed in a stick-slip manner until reaching a transition state causing catastrophic failures. Such a slip-to-failure transition controls the plasticity of MGs and resembles many important phenomena in natural science and engineering, such as friction, lubrication and earthquake, therefore has attracted tremendous research interest over past decades. However, despite the fundamental and practical importance, the physical origin of this slip-to-failure transition is still poorly understood. By tracking the behavior of a single shear band, here we discover that the final fracture of various MGs during compression is triggered as the velocity of the dominant shear band rises to a critical value, the magnitude of which is independent of alloy composition, sample size, strain rate and testing frame stiffness. The critical shear band velocity is rationalized with the continuum theory of liquid instability, physically originating from a shear-induced cavitation process inside the shear band. Our current finding sheds a quantitative insight into deformation and fracture in disordered solids and, more importantly, is useful to the design of plastic/tough MG-based materials and structures.

| S-EPMC4759565 | biostudies-literature

Extra plasticity governed by shear band deflection in gradient metallic glasses.

Project description:Inspired by gradient materials in nature, advanced engineering components with controlled structural gradients have attracted substantial research interests due to their exceptional combinations of properties. However, it remains challenging to generate structural gradients that penetrate through bulk materials, which is essential for achieving enhanced mechanical properties in metallic materials. Here, we report practical strategies to design controllable structural gradients in bulk metallic glasses (BMGs). By adjusting processing conditions, including holding time and/or controlling temperatures, of cryogenic thermal cycling and fast cooling, two different types of gradient metallic glasses (GMGs) with spatially gradient-distributed free volume contents can be synthesized. Both mechanical testing and atomistic simulations demonstrate that the spatial gradient can endow GMGs with extra plasticity. Such an enhanced mechanical property is governed by the gradient-induced deflection of shear deformation that fundamentally suppresses the unlimited shear localization on a straight plane that would be expected in BMGs without such a gradient.

| S-EPMC9018681 | biostudies-literature

Experimental evidence that shear bands in metallic glasses nucleate like cracks

Project description:Highly time-resolved mechanical measurements, modeling, and simulations show that large shear bands in bulk metallic glasses nucleate in a manner similar to cracks. When small slips reach a nucleation size, the dynamics changes and the shear band rapidly grows to span the entire sample. Smaller nucleation sizes imply lower ductility. Ductility can be increased by increasing the nucleation size relative to the maximum (“cutoff”) shear band size at the upper edge of the power law scaling range of their size distribution. This can be achieved in three ways: (1) by increasing the nucleation size beyond this cutoff size of the shear bands, (2) by keeping all shear bands smaller than the nucleation size, or (3) by choosing a sample size smaller than the nucleation size. The discussed methods can also be used to rapidly order metallic glasses according to ductility.

| S-EPMC9630419 | biostudies-literature

Fast surface dynamics enabled cold joining of metallic glasses.

Project description:Design of bulk metallic glasses (BMGs) with excellent properties has been a long-sought goal in materials science and engineering. The grand challenge has been scaling up the size and improving the properties of metallic glasses of technological importance. In this work, we demonstrate a facile, flexible route to synthesize BMGs and metallic glass-glass composites out of metallic-glass ribbons. By fully activating atomic-scale stress relaxation within an ultrathin surface layer under ultrasonic vibrations, we accelerate the formation of atomic bonding between ribbons at a temperature far below the glass transition point. In principle, our approach overcomes the size and compositional limitations facing traditional methods, leading to the rapid bonding of metallic glasses of distinct physical properties without causing crystallization. The outcome of our current research opens up a window not only to synthesize BMGs of extended compositions, but also toward the discovery of multifunctional glass-glass composites, which have never been reported before.

| S-EPMC6874482 | biostudies-literature

Experimental characterization of shear transformation zones for plastic flow of bulk metallic glasses.

Project description:We report experimental characterization of shear transformation zones (STZs) for plastic flow of bulk metallic glasses (BMGs) based on a newly developed cooperative shearing model [Johnson WL, Samwer K (2005) A universal criterion for plastic yielding of metallic glasses with a (T/T(g))(2/3) temperature dependence. Phys Rev Lett 95: 195501]. The good agreement between experimental measurements and theoretical predictions in the STZ volumes provides compelling evidence that the plastic flow of metallic glasses occurs through cooperative shearing of unstable STZs activated by shear stresses. Moreover, the ductility of BMGs was found to intrinsically correlate with their STZ volumes. The experiments presented herein pave a way to gain a quantitative insight into the atomic-scale mechanisms of BMG mechanical behavior.

| S-EPMC2567442 | biostudies-literature

Local microstructure evolution at shear bands in metallic glasses with nanoscale phase separation.

Project description:At room temperature, plastic flow of metallic glasses (MGs) is sharply localized in shear bands, which are a key feature of the plastic deformation in MGs. Despite their clear importance and decades of study, the conditions for formation of shear bands, their structural evolution and multiplication mechanism are still under debate. In this work, we investigate the local conditions at shear bands in new phase-separated bulk MGs containing glassy nanospheres and exhibiting exceptional plasticity under compression. It is found that the glassy nanospheres within the shear band dissolve through mechanical mixing driven by the sharp strain localization there, while those nearby in the matrix coarsen by Ostwald ripening due to the increased atomic mobility. The experimental evidence demonstrates that there exists an affected zone around the shear band. This zone may arise from low-strain plastic deformation in the matrix between the bands. These results suggest that measured property changes originate not only from the shear bands themselves, but also from the affected zones in the adjacent matrix. This work sheds light on direct visualization of deformation-related effects, in particular increased atomic mobility, in the region around shear bands.

| S-EPMC4867588 | biostudies-literature

Origin of Shear Stability and Compressive Ductility Enhancement of Metallic Glasses by Metal Coating.

Project description:Metallic glasses (MGs) are notorious for the poor macroscopic ductility and to overcome the weakness various intrinsic and extrinsic strategies have been proposed in past decades. Among them, the metal coating is regarded as a flexible and facile approach, yet the physical origin is poorly understood due to the complex nature of shear banding process. Here, we studied the origin of ductile enhancement in the Cu-coating both experimentally and theoretically. By examining serrated shear events and their stability of MGs, we revealed that the thin coating layer plays a key role in stopping the final catastrophic failure of MGs by slowing down shear band dynamics and thus retarding its attainment to a critical instable state. The mechanical analysis on interplay between the coating layer and shear banding process showed the enhanced shear stability mainly comes from the lateral tension of coating layer induced by the surface shear step and the bonding between the coating layer and MGs rather than the layer thickness is found to play a key role in contributing to the shear stability.

| S-EPMC4897694 | biostudies-literature

Atomistic processes of surface-diffusion-induced abnormal softening in nanoscale metallic crystals.

Project description:Ultrahigh surface-to-volume ratio in nanoscale materials, could dramatically facilitate mass transport, leading to surface-mediated diffusion similar to Coble-type creep in polycrystalline materials. Unfortunately, the Coble creep is just a conceptual model, and the associated physical mechanisms of mass transport have never been revealed at atomic scale. Akin to the ambiguities in Coble creep, atomic surface diffusion in nanoscale crystals remains largely unclear, especially when mediating yielding and plastic flow. Here, by using in situ nanomechanical testing under high-resolution transmission electron microscope, we find that the diffusion-assisted dislocation nucleation induces the transition from a normal to an inverse Hall-Petch-like relation of the strength-size dependence and the surface-creep leads to the abnormal softening in flow stress with the reduction in size of nanoscale silver, contrary to the classical "alternating dislocation starvation" behavior in nanoscale platinum. This work provides insights into the atomic-scale mechanisms of diffusion-mediated deformation in nanoscale materials, and impact on the design for ultrasmall-sized nanomechanical devices.

| S-EPMC8413310 | biostudies-literature

Localized shear deformation and softening of bulk metallic glass: stress or temperature driven?

Project description:Metallic glasses due to their unique combination of physical and chemical properties have a great potential in various applications: materials for construction, medical, MEMs devices and so on. The deformation mechanism in metallic glasses is very much different from that in conventional crystalline materials and not yet fully understood. Here we are trying to find out what drives shear deformation in metallic glasses. The compression experiments of the bulk metallic glassy (BMG) samples coated with tin, Rose metal and indium were performed. There were no melting sites of the coating observed near individual shear bands. Melting occurred only near fracture surface, near microcracks and in the places of shear band concentrations. The results indicate that shear banding is rather a stress driven process while the temperature rise that was observed takes place due to friction forces in the viscous supercooled liquid thin layer in the shear bands.

| S-EPMC3792420 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data