Roll-To-Roll Friendly Solution-Processing of Ultrathin, Sintered CdTe Nanocrystal Photovoltaics.

ABSTRACT: Roll-to-roll (R2R) device fabrication using solution-processed materials is a cheap and versatile approach that has attracted widespread interest over the past 2 decades. Here, we systematically introduce and investigate R2R-friendly modifications in the fabrication of ultrathin, sintered CdTe nanocrystal (NC) solar cells. These include (1) scalable deposition techniques such as spray-coating and doctor-blading, (2) a bath-free, controllable sintering of CdTe NCs by quantitative addition of a sintering agent, and (3) radiative heating with an infrared lamp. The impact of each modification on the CdTe nanostructure and solar cell performance was first independently studied and compared to the standard, non-R2R-friendly procedure involving spin-coating the NCs, soaking in a CdCl₂ bath, and annealing on a hot plate. The R2R-friendly techniques were then combined into a single, integrated process, yielding devices that reach 10.4% power conversion efficiency with a V_oc, J_sc, and FF of 697 mV, 22.2 mA/cm², and 67%, respectively, after current/light soaking. These advances reduce the barrier for large-scale manufacturing of solution-processed, ultralow-cost solar cells on flexible or curved substrates.

SUBMITTER: Kurley JM

PROVIDER: S-EPMC8461606 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Hole Transfer Layer Engineering for CdTe Nanocrystal Photovoltaics with Improved Efficiency.

Project description:Interface engineering has led to significant progress in solution-processed CdTe nanocrystal (NC) solar cells in recent years. High performance solar cells can be fabricated by introducing a hole transfer layer (HTL) between CdTe and a back contact electrode to reduce carrier recombination by forming interfacial dipole effect at the interface. Here, we report the usage of a commercial product 2,2',7,7'-tetrakis[N,N-di(4-methoxyphenyl)amino]-9,9'-spirobifluorene (Spiro) as a hole transfer layer to facilitate the hole collecting for CdTe nanocrystal solar cells. It is found that heat treatment on the hole transfer layer has significant influence on the NC solar cells performance. The Jsc, Voc, and power conversion efficiency (PCE) of NC solar cells are simultaneously increased due to the decreased contact resistance and enhanced built-in electric field. We demonstrate solar cells that achieve a high PCE of 8.34% for solution-processed CdTe NC solar cells with an inverted structure by further optimizing the HTL annealing temperature, which is among the highest value in CdTe NC solar cells with the inverted structure.

| S-EPMC7407640 | biostudies-literature

Roll-to-roll gravure-printed flexible perovskite solar cells using eco-friendly antisolvent bathing with wide processing window.

Project description:Driven by recent improvements in efficiency and stability of perovskite solar cells (PSCs), upscaling of PSCs has come to be regarded as the next step. Specifically, a high-throughput, low-cost roll-to-roll (R2R) processes would be a breakthrough to realize the commercialization of PSCs, with uniform formation of precursor wet film and complete conversion to perovskite phase via R2R-compatible processes necessary to accomplish this goal. Herein, we demonstrate the pilot-scale, fully R2R manufacturing of all the layers except for electrodes in PSCs. Tert-butyl alcohol (tBuOH) is introduced as an eco-friendly antisolvent with a wide processing window. Highly crystalline, uniform formamidinium (FA)-based perovskite formation via tBuOH:EA bathing was confirmed by achieving high power conversion efficiencies (PCEs) of 23.5% for glass-based spin-coated PSCs, and 19.1% for gravure-printed flexible PSCs. As an extended work, R2R gravure-printing and tBuOH:EA bathing resulted in the highest PCE reported for R2R-processed PSCs, 16.7% for PSCs with R2R-processed SnO2/FA-perovskite, and 13.8% for fully R2R-produced PSCs.

| S-EPMC7555830 | biostudies-literature

Metastable CdTe@HgTe Core@Shell Nanostructures Obtained by Partial Cation Exchange Evolve into Sintered CdTe Films Upon Annealing.

Project description:Partial Hg2+ → Cd2+ cation exchange (CE) reactions were exploited to transform colloidal CdTe nanocrystals (NCs, 4-6 nm in size) into CdTe@HgTe core@shell nanostructures. This was achieved by working under a slow CE rate, which limited the exchange to the surface of the CdTe NCs. In such nanostructures, when annealed at mild temperatures (as low as 200 °C), the HgTe shell sublimated or melted and the NCs sintered together, with the concomitant desorption of their surface ligands. At the end of this process, the annealed samples consisted of ligand-free CdTe sintered films containing an amount of Hg2+ that was much lower than that of the starting CdTe@HgTe NCs. For example, the CdTe@HgTe NCs that initially contained 10% of Hg2+, after being annealed at 200 °C were transformed to CdTe sintered films containing only traces of Hg2+ (less than 1%). This procedure was then used to fabricate a proof-of-concept CdTe-based photodetector exhibiting a photoresponse of up to 0.5 A/W and a detectivity of ca. 9 × 104 Jones under blue light illumination. Our strategy suggests that CE protocols might be exploited to lower the overall costs of production of CdTe thin films employed in photovoltaic technology, which are currently fabricated at high temperatures (above 350 °C), using post-process ligand-stripping steps.

| S-EPMC8016170 | biostudies-literature

Efficient Nanocrystal Photovoltaics via Blade Coating Active Layer.

Project description:CdTe semiconductor nanocrystal (NC) solar cells have attracted much attention in recent year due to their low-cost solution fabrication process. However, there are still few reports about the fabrication of large area NC solar cells under ambient conditions. Aiming to push CdTe NC solar cells one step forward to the industry, this study used a novel blade coating technique to fabricate CdTe NC solar cells with different areas (0.16, 0.3, 0.5 cm2) under ambient conditions. By optimizing the deposition parameters of the CdTe NC's active layer, the power conversion efficiency (PCE) of NC solar cells showed a large improvement. Compared to the conventional spin-coated device, a lower post-treatment temperature is required by blade coated NC solar cells. Under the optimal deposition conditions, the NC solar cells with 0.16, 0.3, and 0.5 cm2 areas exhibited PCEs of 3.58, 2.82, and 1.93%, respectively. More importantly, the NC solar cells fabricated via the blading technique showed high stability where almost no efficiency degradation appeared after keeping the devices under ambient conditions for over 18 days. This is promising for low-cost, roll-by-roll, and large area industrial fabrication.

| S-EPMC8226763 | biostudies-literature

Efficient Nanocrystal Photovoltaics with PTAA as Hole Transport Layer.

Project description:The power conversion efficiency (PCE) of solution-processed CdTe nanocrystals (NCs) solar cells has been significantly promoted in recent years due to the optimization of device design by advanced interface engineering techniques. However, further development of CdTe NC solar cells is still limited by the low open-circuit voltage (Voc) (mostly in range of 0.5-0.7 V), which is mainly attributed to the charge recombination at the CdTe/electrode interface. Herein, we demonstrate a high-efficiency CdTe NCs solar cell by using organic polymer poly[bis(4-phenyl)(2,4,6-trimethylphenyl)amine] (PTAA) as the hole transport layer (HTL) to decrease the interface recombination and enhance the Voc. The solar cell with the architecture of ITO/ZnO/CdS/CdSe/CdTe/PTAA/Au was fabricated via a layer-by-layer solution process. Experimental results show that PTAA offers better back contact for reducing interface resistance than the device without HTL. It is found that a dipole layer is produced between the CdTe NC thin film and the back contact electrode; thus the built-in electric field (Vbi) is reinforced, allowing more efficient carrier separation. By introducing the PTAA HTL in the device, the open-circuit voltage, short-circuit current density and the fill factor are simultaneously improved, leading to a high PCE of 6.95%, which is increased by 30% compared to that of the control device without HTL (5.3%). This work suggests that the widely used PTAA is preferred as the excellent HTL for achieving highly efficient CdTe NC solar cells.

| S-EPMC9458081 | biostudies-literature

Roll-to-roll fabrication of large scale and regular arrays of three-dimensional nanospikes for high efficiency and flexible photovoltaics.

Project description:Three-dimensional (3-D) nanostructures have demonstrated enticing potency to boost performance of photovoltaic devices primarily owning to the improved photon capturing capability. Nevertheless, cost-effective and scalable fabrication of regular 3-D nanostructures with decent robustness and flexibility still remains as a challenging task. Meanwhile, establishing rational design guidelines for 3-D nanostructured solar cells with the balanced electrical and optical performance are of paramount importance and in urgent need. Herein, regular arrays of 3-D nanospikes (NSPs) were fabricated on flexible aluminum foil with a roll-to-roll compatible process. The NSPs have precisely controlled geometry and periodicity which allow systematic investigation on geometry dependent optical and electrical performance of the devices with experiments and modeling. Intriguingly, it has been discovered that the efficiency of an amorphous-Si (a-Si) photovoltaic device fabricated on NSPs can be improved by 43%, as compared to its planar counterpart, in an optimal case. Furthermore, large scale flexible NSP solar cell devices have been fabricated and demonstrated. These results not only have shed light on the design rules of high performance nanostructured solar cells, but also demonstrated a highly practical process to fabricate efficient solar panels with 3-D nanostructures, thus may have immediate impact on thin film photovoltaic industry.

| S-EPMC5394750 | biostudies-literature

Bioinspired superhydrophobic surfaces, fabricated through simple and scalable roll-to-roll processing.

Project description:A simple, scalable, non-lithographic, technique for fabricating durable superhydrophobic (SH) surfaces, based on the fingering instabilities associated with non-Newtonian flow and shear tearing, has been developed. The high viscosity of the nanotube/elastomer paste has been exploited for the fabrication. The fabricated SH surfaces had the appearance of bristled shark skin and were robust with respect to mechanical forces. While flow instability is regarded as adverse to roll-coating processes for fabricating uniform films, we especially use the effect to create the SH surface. Along with their durability and self-cleaning capabilities, we have demonstrated drag reduction effects of the fabricated films through dynamic flow measurements.

| S-EPMC4651109 | biostudies-literature

Efficient CdTe Nanocrystal/TiO₂ Hetero-Junction Solar Cells with Open Circuit Voltage Breaking 0.8 V by Incorporating A Thin Layer of CdS Nanocrystal.

Project description:Nanocrystal solar cells (NCs) allow for large scale solution processing under ambient conditions, permitting a promising approach for low-cost photovoltaic products. Although an up to 10% power conversion efficiency (PCE) has been realized with the development of device fabrication technologies, the open circuit voltage (Voc) of CdTe NC solar cells has stagnated below 0.7 V, which is significantly lower than most CdTe thin film solar cells fabricated by vacuum technology (around 0.8 V~0.9 V). To further improve the NC solar cells' performance, an enhancement in the Voc towards 0.8⁻1.0 V is urgently required. Given the unique processing technologies and physical properties in CdTe NC, the design of an optimized band alignment and improved junction quality are important issues to obtain efficient solar cells coupled with high Voc. In this work, an efficient method was developed to improve the performance and Voc of solution-processed CdTe nanocrystal/TiO₂ hetero-junction solar cells. A thin layer of solution-processed CdS NC film (~5 nm) as introduced into CdTe NC/TiO₂ to construct hetero-junction solar cells with an optimized band alignment and p-n junction quality, which resulted in a low dark current density and reduced carrier recombination. As a result, devices with improved performance (5.16% compared to 2.63% for the control device) and a Voc as high as 0.83 V were obtained; this Voc value is a record for a solution-processed CdTe NC solar cell.

| S-EPMC6116231 | biostudies-literature

Room-Temperature Interconversion Between Ultrathin CdTe Magic-Size Nanowires Induced by Ligand Shell Dynamics.

Project description:The formation mechanisms of colloidal magic-size semiconductor nanostructures have remained obscure. Herein, we report the room temperature synthesis of three species of ultrathin CdTe magic-size nanowires (MSNWs) with diameters of 0.7 ± 0.1 nm, 0.9 ± 0.2 nm, and 1.1 ± 0.2 nm, and lowest energy exciton transitions at 373, 418, and 450 nm, respectively. The MSNWs are obtained from Cd(oleate)2 and TOP-Te, provided diphenylphosphine and a primary alkylamine (RNH2) are present at sufficiently high concentrations, and exhibit sequential, discontinuous growth. The population of each MSNW species is entirely determined by the RNH2 concentration [RNH2] so that single species are only obtained at specific concentrations, while mixtures are obtained at concentrations intermediate between the specific ones. Moreover, the MSNWs remain responsive to [RNH2], interconverting from thinner to thicker upon [RNH2] decrease and from thicker to thinner upon [RNH2] increase. Our results allow us to propose a mechanism for the formation and interconversion of CdTe MSNWs and demonstrate that primary alkylamines play crucial roles in all four elementary kinetic steps (viz., monomer formation, nucleation, growth in length, and interconversion between species), thus being the decisive element in the creation of a reaction pathway that leads exclusively to CdTe MSNWs. The insights provided by our work thus contribute toward unravelling the mechanisms behind the formation of shape-controlled and atomically precise magic-size semiconductor nanostructures.

| S-EPMC9483966 | biostudies-literature

Flexure-based Roll-to-roll Platform: A Practical Solution for Realizing Large-area Microcontact Printing.

Project description:A continuous roll-to-roll microcontact printing (MCP) platform promises large-area nanoscale patterning with significantly improved throughput and a great variety of applications, e.g. precision patterning of metals, bio-molecules, colloidal nanocrystals, etc. Compared with nanoimprint lithography, MCP does not require a thermal imprinting step (which limits the speed and material choices), but instead, extreme precision with multi-axis positioning and misalignment correction capabilities for large area adaptation. In this work, we exploit a flexure-based mechanism that enables continuous MCP with 500 nm precision and 0.05 N force control. The fully automated roll-to-roll platform is coupled with a new backfilling MCP chemistry optimized for high-speed patterning of gold and silver. Gratings of 300, 400, 600 nm line-width at various locations on a 4-inch plastic substrate are fabricated at a speed of 60 cm/min. Our work represents the first example of roll-to-roll MCP with high reproducibility, wafer scale production capability at nanometer resolution. The precision roll-to-roll platform can be readily applied to other material systems.

| S-EPMC4603702 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data