A Systematic Study on Bio-Based Hybrid Aerogels Made of Tannin and Silica.

ABSTRACT: Tannin-silica hybrid materials are expected to feature excellent mechanic-chemical stability, large surface areas, high porosity and possess, after carbothermal reduction, high thermal stability as well as high thermal conductivity. Typically, a commercially available tetraethoxysilane is used, but in this study, a more sustainable route was developed by using a glycol-based silica precursor, tetrakis(2-hydroxyethyl)orthosilicate (EGMS), which is highly water-soluble. In order to produce highly porous, homogeneous hybrid tannin-silica aerogels in a one-pot approach, a suitable crosslinker has to be used. It was found that an aldehyde-functionalized silane (triethoxysilylbutyraldehyde) enables the covalent bonding of tannin and silica. Solely by altering the processing parameters, distinctly different tannin-silica hybrid material properties could be achieved. In particular, the amount of crosslinker is a significant factor with respect to altering the materials' properties, e.g., the specific surface area. Notably, 5 wt% of crosslinker presents an optimal percentage to obtain a sustainable tannin-silica hybrid system with high specific surface areas of roughly 800-900 m² g^-1 as well as a high mesopore volume. The synthesized tannin-silica hybrid aerogels permit the usage as green precursor for silicon carbide materials.

SUBMITTER: Koopmann AK

PROVIDER: S-EPMC8468457 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Chitosan-GPTMS-Silica Hybrid Mesoporous Aerogels for Bone Tissue Engineering.

Project description:This study introduces a new synthesis route for obtaining homogeneous chitosan (CS)-silica hybrid aerogels with CS contents up to 10 wt%, using 3-glycidoxypropyl trimethoxysilane (GPTMS) as coupling agent, for tissue engineering applications. Aerogels were obtained using the sol-gel process followed by CO2 supercritical drying, resulting in samples with bulk densities ranging from 0.17 g/cm3 to 0.38 g/cm3. The textural analysis by N2-physisorption revealed an interconnected mesopore network with decreasing specific surface areas (1230-700 m2/g) and pore sizes (11.1-8.7 nm) by increasing GPTMS content (2-4 molar ratio GPTMS:CS monomer). In addition, samples exhibited extremely fast swelling by spontaneous capillary imbibition in PBS solution, presenting swelling capacities from 1.75 to 3.75. The formation of a covalent crosslinked hybrid structure was suggested by FTIR and confirmed by an increase of four hundred fold or more in the compressive strength up to 96 MPa. Instead, samples synthesized without GPTMS fractured at only 0.10-0.26 MPa, revealing a week structure consisted in interpenetrated polymer networks. The aerogels presented bioactivity in simulated body fluid (SBF), as confirmed by the in vitro formation of hydroxyapatite (HAp) layer with crystal size of approximately 2 µm size in diameter. In vitro studies revealed also non cytotoxic effect on HOB® osteoblasts and also a mechanosensitive response. Additionally, control cells grown on glass developed scarce or no stress fibers, while cells grown on hybrid samples showed a significant (p < 0.05) increase in well-developed stress fibers and mature focal adhesion complexes.

| S-EPMC7698430 | biostudies-literature

Cellulose Nanofibrils/Xyloglucan Bio-Based Aerogels with Shape Recovery.

Project description:Bio-based aerogels containing cellulose nanofibrils (CNFs) are promising materials due to the inherent physical properties of CNF. The high affinity of cellulose to plant hemicelluloses (xyloglucan, xylan, pectin) is also an opportunity to develop biomaterials with new properties. Here, we prepared aerogels from gelled dispersions of CNFs and xyloglucan (XG) at different ratios by using a freeze-casting procedure in unidirectional (UD) and non-directional (ND) manners. As showed by rheology analysis, CNF and CNF/XG dispersions behave as true gels. We investigated the impact of the freezing procedure and the gel's composition on the microstructure and the water absorption properties. The introduction of XG greatly affects the microstructure of the aerogel from lamellar to cellular morphology. Bio-based aerogels showed high water absorption capacity with shape recovery after compression. The relation between morphology and aerogel compositions is discussed.

| S-EPMC7839008 | biostudies-literature

Ambient Pressure Hybrid Silica Monoliths with Hexamethyldisilazane: From Vitreous Hydrophilic Xerogels to Superhydrophobic Aerogels.

Project description:Hybrid silica-based monoliths were synthesized at ambient pressure, using minimum amounts of the silylating agent hexamethyldisilazane (HMDZ). Depending on the synthesis approach, the materials ranged from dense and vitreous xerogels to transparent and superhydrophobic aerogels. Emphasis was given to understanding the role of the silylating agent, its content and incorporation process on the final morphology, and properties of the xerogels/aerogels. It is proven that as a coprecursor, increasing HMDZ content contributes to increase the lipophilic/hydrophilic balance, induce high surface areas, and decrease densities, but there is a maximum usable content for producing monoliths. Conversely, as a postsynthesis modifier, there is an optimum HMDZ content that maximizes hydrophobicity (water contact angle of ∼144°) and induces high surface area (∼700 m2·g-1), keeping the density low (∼300 kg·m-3). It is proven that the aging period in the hydrophobizing solution is a crucial parameter. The most superhydrophobic xerogels were obtained using HMDZ as a postsynthesis modifier, achieving values of water contact angles as high as ∼173°, at the cost of density increase to ∼600 kg·m-3 and decrease of the surface area to ∼300 m2·g-1. The best compromise between low density, high surface area, and superhydrophobicity is obtained using HMDZ both as a coprecursor and as a postsynthesis modifier, in a low HMDZ/tetraethoxysilane total molar ratio (<0.2), with an aging period of 16-24 h. The use of subcritical drying, along with the minimization of the expensive organic modifier quantities, allows envisaging a safe and low-cost large-scale production of a variety of materials, including superhydrophobic aerogels with potential distinctive applications.

| S-EPMC6641688 | biostudies-literature

Polymer/Carbon-Based Hybrid Aerogels: Preparation, Properties and Applications.

Project description:Aerogels are synthetic porous materials derived from sol-gel materials in which the liquid component has been replaced with gas to leave intact solid nanostructures without pore collapse. Recently, aerogels based on natural or synthetic polymers, called polymer or organic aerogels, have been widely explored due to their porous structures and unique properties, such as high specific surface area, low density, low thermal conductivity and dielectric constant. This paper gives a comprehensive review about the most recent progresses in preparation, structures and properties of polymer and their derived carbon-based aerogels, as well as their potential applications in various fields including energy storage, adsorption, thermal insulation and flame retardancy. To facilitate further research and development, the technical challenges are discussed, and several future research directions are also suggested in this review.

| S-EPMC5455374 | biostudies-other

Eco-Friendly Synthesis of Water-Glass-Based Silica Aerogels via Catechol-Based Modifier.

Project description:Silica aerogels have attracted much attention owing to their excellent thermal insulation properties. However, the conventional synthesis of silica aerogels involves the use of expensive and toxic alkoxide precursors and surface modifiers such as trimethylchlorosilane. In this study, cost-effective water-glass silica aerogels were synthesized using an eco-friendly catechol derivative surface modifier instead of trimethylchlorosilane. Polydopamine was introduced to increase adhesion to the SiO2 surface. The addition of 4-tert-butyl catechol and hexylamine imparted hydrophobicity to the surface and suppressed the polymerization of the polydopamine. After an ambient pressure drying process, catechol-modified aerogel exhibited a specific surface area of 377 m2/g and an average pore diameter of approximately 21 nm. To investigate their thermal conductivities, glass wool sheets were impregnated with catechol-modified aerogel. The thermal conductivity was 40.4 mWm-1K-1, which is lower than that of xerogel at 48.7 mWm-1K-1. Thus, by precisely controlling the catechol coating in the mesoporous framework, an eco-friendly synthetic method for aerogel preparation is proposed.

| S-EPMC7761200 | biostudies-literature

Bio-inspired synthesis of hybrid silica nanoparticles templated from elastin-like polypeptide micelles.

Project description:The programmed self-assembly of block copolymers into higher order nanoscale structures offers many attractive attributes for the development of new nanomaterials for numerous applications including drug delivery and biosensing. The incorporation of biomimetic silaffin peptides in these block copolymers enables the formation of hybrid organic-inorganic materials, which can potentially enhance the utility and stability of self-assembled nanostructures. We demonstrate the design, synthesis and characterization of amphiphilic elastin-like polypeptide (ELP) diblock copolymers that undergo temperature-triggered self-assembly into well-defined spherical micelles. Genetically encoded incorporation of the silaffin R5 peptide at the hydrophilic terminus of the diblock ELP leads to presentation of the silaffin R5 peptide on the coronae of the micelles, which results in localized condensation of silica and the formation of near-monodisperse, discrete, sub-100 nm diameter hybrid ELP-silica particles. This synthesis method, can be carried out under mild reaction conditions suitable for bioactive materials, and will serve as the basis for the development and application of functional nanomaterials. Beyond silicification, the general strategies described herein may also be adapted for the synthesis of other biohybrid nanomaterials as well.

| S-EPMC4499310 | biostudies-literature

3D Hybrid Nanofiber Aerogels Combining with Nanoparticles Made of a Biocleavable and Targeting Polycation and MiR-26a for Bone Repair.

Project description:The healing of large bone defects represents a clinical challenge, often requiring some form of grafting. Three-dimensional (3D) nanofiber aerogels could be a promising bone graft due to their biomimetic morphology and controlled porous structures and composition. miR-26a has been reported to induce the differentiation of bone marrow-derived mesenchymal stem cells (BMSCs) and facilitate bone formation. Introducing miR-26a with a suitable polymeric vector targeting BMSCs could improve and enhance the functions of 3D nanofiber aerogels for bone regeneration. Herein, we first developed the comb-shaped polycation (HA-SS-PGEA) carrying a targeting component, biocleavable groups and short ethanolamine (EA)-decorated poly(glycidyl methacrylate) (PGMA) (abbreviated as PGEA) arms as miR-26a delivery vector. We then assessed the cytotoxicity and transfection efficiency of this polycation and cellular response to miR-26a-incorporated nanoparticles (NPs) in vitro. HA-SS-PGEA exhibited a stronger ability to transport miR-26a and exert its functions than the gold standard polyethyleneimine (PEI) and low-molecular-weight linear PGEA. We finally examined the efficacy of HA-SS-PGEA/miR-26a NPs loaded 3D hybrid nanofiber aerogels showing a positive effect on the cranial bone defect healing. Together, the combination of 3D nanofiber aerogels and functional NPs consisting of a biodegradable and targeting polycation and therapeutic miRNA could be a promising approach for bone regeneration.

| S-EPMC8315031 | biostudies-literature

Air-like plasmonics with ultralow-refractive-index silica aerogels.

Project description:The coupling of the surface plasmon near-field into the sensing medium is key to the sensitivity of surface plasmon-based sensing devices. A low-index dielectric is necessary for the sensing medium to support a highly-penetrating surface plasmon evanescent field that extends well into the dielectric medium. The air-like refractive index, n, of an aerogel substrate provides another dimension for ultralow-index plasmonic devices. In this paper, we experimentally observed an angular surface plasmon resonance dip at 74° with the ultralow-index aerogel substrate, as was expected from theory. We also demonstrated the comparatively high-sensitivity surface plasmon resonance wavelength, ?, while the change in ??/?n with different substrates was studied in detail. A 740 nm-period metal grating was imprinted on aerogel (n?=?1.08) and polydimethylsiloxane (PDMS; n?=?1.4) substrates. The ultraviolet-visible-near-infrared spectra were observed in the reflection mode on the grating, resulting in sensitivities of 740.2 and 655.9?nm/RIU for the aerogel and PDMS substrates, respectively. Numerical simulations were performed to understand the near-field of the surface plasmon, which demonstrated resonances well correlated with the experimentally observed results. The near-field due to excitation of the surface plasmon polaritons is observed to be more confined and to penetrate deeper into the sensing medium when a low-index substrate is used.

| S-EPMC6381121 | biostudies-literature

Preparation and Properties of Organic-Inorganic Hybrid Antireflection Films Made by a Low-Temperature Process Using Hollow Silica Nanoparticles.

Project description:Layers made of hollow silica nanoparticles have potential applications as antireflection films with lower refractive index values compared with existing materials such as silica glass (1.50) and magnesium fluoride (1.38). The advantages of such nanoparticles result from interactions between the solid shell, the cavity phase core, and the voids between particles. To obtain practical antireflection films, it is necessary to control the number of layers of these hollow silica nanoparticles and to fill the gaps between particles with a solid. In the present study, antireflection films were prepared by applying a coating of hollow silica nanoparticles dispersed in a UV-curable monomer solution onto plastic substrates. After film formation and exposure to UV light, the voids between the nanoparticles were completely filled with a polymer matrix. Tuning the particle concentration in the coating solution allowed the formation of antireflection films comprising one to three layers of the hollow silica nanoparticles. The reflectance of the films was dependent on the number of layers, and a 100 nm thick film in which two layers of hollow silica nanoparticles were precisely arranged showed the lowest reflectance of 0.92% at 550 nm wavelength, equivalent to a refractive index of 1.23. Because the voids between particles were filled with the polymer, these films resisted contamination during manual handling and so would be expected to maintain low reflectance during practical applications. This work demonstrates that nanosized inorganic-organic hybrid films composed of hollow silica nanoparticles and a UV-curable resin can exhibit optical properties and structural integrity that cannot be achieved by either substance alone.

| S-EPMC8015096 | biostudies-literature

Silica-Resorcinol-Melamine-Formaldehyde Composite Aerogels as High-Performance Thermal Insulators.

Project description:Here, we report the gelation and supercritical drying of ethanol-based silica-resorcinol-melamine-formaldehyde (RMF) composite aerogels with relative concentrations of initial reagents ranging from neat silica to neat RMF alcogels. The as-prepared materials are subsequently supercritically dried with carbon dioxide. Their properties include a thermal conductivity in the 15-20 mW·m-1·K-1 range even with a silica content as low as 20%wt. The possible reasons behind this interesting insulation performance and the mechanisms leading to the underlying gel structure are discussed in depth. A focus is made on the different gelation modes happening between the RMF and silica phases, from a coating of silica surfaces with RMF species to discontinuous RMF particles within a silica backbone and a continuous RMF backbone with isolated silica particles. The implications in terms of mechanical properties and thermal conductivity are elaborated upon. The initial ratio of silica-RMF species in this ethanol-based synthesis affects the micro- and macrostructure of the composites, resulting in materials with drastically different pore structures and thus an interesting array of possibilities for a new class of silica-organic composite aerogels, based on a sol-gel process.

| S-EPMC9088793 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data