Precise Control of Green to Blue Emission of Halide Perovskite Nanocrystals Using Terbium Chloride as Chlorine Source.

ABSTRACT: CsPbClxBr3-x nanocrystals were prepared by ligand-assisted deposition at room temperature, and their wavelength was accurately adjusted by doping TbCl3. The synthesized nanocrystals were monoclinic and the morphology was almost unchanged after doping. The fluorescence emission of CsPbClxBr3-x nanocrystals was easily controlled from green to blue by adjusting the amount of TbCl3, which realizes the continuous and accurate spectral regulation in the range of green to blue. This method provides a new scheme for fast anion exchange of all-inorganic perovskite nanocrystals in an open environment at room temperature.

SUBMITTER: Deng W

PROVIDER: S-EPMC8470515 | biostudies-literature | 2021 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Precise Control of Green to Blue Emission of Halide Perovskite Nanocrystals Using Terbium Chloride as Chlorine Source.

Deng Wenqiang W Fan Ting T Lü Jiantao J Li Jingling J Deng Tingting T Liu Mingqi M

Nanomaterials (Basel, Switzerland) 20210914 9

CsPbClxBr3-x nanocrystals were prepared by ligand-assisted deposition at room temperature, and their wavelength was accurately adjusted by doping TbCl3. The synthesized nanocrystals were monoclinic and the morphology was almost unchanged after doping. The fluorescence emission of CsPbClxBr3-x nanocrystals was easily controlled from green to blue by adjusting the amount of TbCl3, which realizes the continuous and accurate spectral ...[more]

PMID: 34578706

Similar Datasets

Inhibiting the Appearance of Green Emission in Mixed Lead Halide Perovskite Nanocrystals for Pure Red Emission.

Project description:Mixed halide perovskites exhibit promising optoelectronic properties for next-generation light-emitting diodes due to their tunable emission wavelength that covers the entire visible light spectrum. However, these materials suffer from severe phase segregation under continuous illumination, making long-term stability for pure red emission a significant challenge. In this study, we present a comprehensive analysis of the role of halide oxidation in unbalanced ion migration (I/Br) within CsPbI2Br nanocrystals and thin films. We also introduce a new approach using cyclic olefin copolymer (COC) to encapsulate CsPbI2Br perovskite nanocrystals (PNCs), effectively suppressing ion migration by increasing the corresponding activation energy. Compared with that of unencapsulated samples, we observe a substantial reduction in phase separation under intense illumination in PNCs with a COC coating. Our findings show that COC enhances phase stability by passivating uncoordinated surface defects (Pb2+ and I-), increasing the formation energy of halide vacancies, improving the charge carrier lifetime, and reducing the nonradiative recombination density.

| S-EPMC11450971 | biostudies-literature

Hollow metal halide perovskite nanocrystals with efficient blue emissions.

Project description:Metal halide perovskite nanocrystals (NCs) have emerged as new-generation light-emitting materials with narrow emissions and high photoluminescence quantum efficiencies (PLQEs). Various types of perovskite NCs, e.g., platelets, wires, and cubes, have been discovered to exhibit tunable emissions across the whole visible spectrum. Despite remarkable advances in the field of perovskite NCs, many nanostructures in inorganic NCs have not yet been realized in metal halide perovskites, and producing highly efficient blue-emitting perovskite NCs remains challenging and of great interest. Here, we report the discovery of highly efficient blue-emitting cesium lead bromide (CsPbBr3) perovskite hollow NCs. By facile solution processing of CsPbBr3 precursor solution containing ethylenediammonium bromide and sodium bromide, in situ formation of hollow CsPbBr3 NCs with controlled particle and pore sizes is realized. Synthetic control of hollow nanostructures with quantum confinement effect results in color tuning of CsPbBr3 NCs from green to blue, with high PLQEs of up to 81%.

| S-EPMC7182421 | biostudies-literature

Pressure-induced emission of cesium lead halide perovskite nanocrystals.

Project description:Metal halide perovskites (MHPs) are of great interest for optoelectronics because of their high quantum efficiency in solar cells and light-emitting devices. However, exploring an effective strategy to further improve their optical activities remains a considerable challenge. Here, we report that nanocrystals (NCs) of the initially nonfluorescent zero-dimensional (0D) cesium lead halide perovskite Cs4PbBr6 exhibit a distinct emission under a high pressure of 3.01 GPa. Subsequently, the emission intensity of Cs4PbBr6 NCs experiences a significant increase upon further compression. Joint experimental and theoretical analyses indicate that such pressure-induced emission (PIE) may be ascribed to the enhanced optical activity and the increased binding energy of self-trapped excitons upon compression. This phenomenon is a result of the large distortion of [PbBr6]4- octahedral motifs resulting from a structural phase transition. Our findings demonstrate that high pressure can be a robust tool to boost the photoluminescence efficiency and provide insights into the relationship between the structure and optical properties of 0D MHPs under extreme conditions.

| S-EPMC6206024 | biostudies-literature

CsPb(Br/Cl)3 Perovskite Nanocrystals with Bright Blue Emission Synergistically Modified by Calcium Halide and Ammonium Ion.

Project description:Colloidal cesium lead halide (CsPbX3, X = Cl, Br, and I) perovskite nanocrystals (NCs) demonstrate supreme optical properties in the spectra region of infrared, red, and green. High-performance blue-emitting counterparts are still eagerly required for next-generation full-color displays. However, it is challenging to obtain efficient blue perovskite NCs, especially in a deep blue region with an emission wavelength of around 460 nm or shorter. Herein, calcium halide and ammonium ions are applied simultaneously to modify the CsPb(Br/Cl)3 NCs in situ to reduce surface defects, finally remarkably enhancing the photoluminescence quantum yield (PLQY) from 13% to 93% with an emission peak at 455 nm and the Commission Internationale de l'Eclairage (CIE) coordinates at (0.147, 0.030), which is close to the requirement of the Rec.2020 standard and also meets the requirement of blue emission in DCI-P3. Bright white emission and a wide color gamut are also achieved by combining the commercial red-emitting and green-emitting phosphors. The combination of time-resolved PL spectra and femtosecond transient absorption results discloses the reason for PLQY improvement as suppressing the nonradiative recombination.

| S-EPMC9231175 | biostudies-literature

Size-Dependent Photon Emission from Organometal Halide Perovskite Nanocrystals Embedded in an Organic Matrix.

Project description:In recent years, organometal halide perovskite materials have attracted significant research interest in the field of optoelectronics. Here, we introduce a simple and low-temperature route for the formation of self-assembled perovskite nanocrystals in a solid organic matrix. We demonstrate that the size and photoluminescence peak of the perovskite nanocrystals can be tuned by varying the concentration of perovskite in the matrix material. The physical origin of the blue shift of the perovskite nanocrystals’ emission compared to its bulk phase is also discussed.

| S-EPMC4415888 | biostudies-other

Free-Standing Metal Halide Perovskite Nanowire Arrays with Blue-Green Heterostructures.

Project description:Vertically aligned metal halide perovskite (MHP) nanowires are promising for various optoelectronic applications, which can be further enhanced by heterostructures. However, present methods to obtain free-standing vertically aligned MHP nanowire arrays and heterostructures lack the scalability needed for applications. We use a low-temperature solution process to prepare free-standing vertically aligned green-emitting CsPbBr3 nanowires from anodized aluminum oxide templates. The length is controlled from 1 to 20 μm by the precursor amount. The nanowires are single-crystalline and exhibit excellent photoluminescence, clear light guiding and high photoconductivity with a responsivity of 1.9 A/W. We demonstrate blue-green heterostructured nanowire arrays by converting the free-standing part of the nanowires to CsPbCl1.1Br1.9 in an anion exchange process. Our results demonstrate a scalable, self-aligned, and lithography-free approach to achieve high quality free-standing MHP nanowires arrays and heterostructures, offering new possibilities for optoelectronic applications.

| S-EPMC9011394 | biostudies-literature

Cesium Lead Halide Perovskite Nanocrystals Assembled in Metal-Organic Frameworks for Stable Blue Light Emitting Diodes.

Project description:All inorganic cesium lead trihalide nanocrystals are promising light emitters for bright light emitting diodes (LEDs). Here, CsPb(BrCl)1.5 nanocrystals in metal-organic frameworks (MOF) thin films are demonstrated to achieve bright and stable blue LEDs. The lead metal nodes in the MOF thin film react with Cs-halide salts, resulting in 10-20 nm nanocrystals. This is revealed by X-ray scattering and transmission electron microscopy. Employing the CsPbX3 -MOF thin films as emission layers, bright deep blue and sky-blue LEDs are demonstrated that emit at 452 and 476 nm respectively. The maximum external quantum efficiencies of these devices are 0.72% for deep blue LEDs and 5.6% for sky blue LEDs. More importantly, the device can maintain 50% of its original electroluminescence (T50 ) for 2.23 h when driving at 4.2 V. Detailed optical spectroscopy and time-of-flight secondary ion mass spectroscopy suggest that the ion migration can be suppressed that maintains the emission brightness and spectra. The study provides a new route for fabricating stable blue light emitting diodes with all-inorganic perovskite nanocrystals.

| S-EPMC9108663 | biostudies-literature

Blue-Green Color Tunable Solution Processable Organolead Chloride-Bromide Mixed Halide Perovskites for Optoelectronic Applications.

Project description:Solution-processed organo-lead halide perovskites are produced with sharp, color-pure electroluminescence that can be tuned from blue to green region of visible spectrum (425-570 nm). This was accomplished by controlling the halide composition of CH3NH3Pb(BrxCl1-x)3 [0 ≤ x ≤ 1] perovskites. The bandgap and lattice parameters change monotonically with composition. The films possess remarkably sharp band edges and a clean bandgap, with a single optically active phase. These chloride-bromide perovskites can potentially be used in optoelectronic devices like solar cells and light emitting diodes (LEDs). Here we demonstrate high color-purity, tunable LEDs with narrow emission full width at half maxima (FWHM) and low turn on voltages using thin-films of these perovskite materials, including a blue CH3NH3PbCl3 perovskite LED with a narrow emission FWHM of 5 nm.

| S-EPMC4762541 | biostudies-literature

Stable green and red dual-color emission in all-inorganic halide-mixed perovskite single microsheets.

Project description:Recently, all-inorganic perovskites have attracted tremendous attention due to their excellent optoelectronic properties and extensive potential applications. However, these perovskites usually show a single emission wavelength because of the high ionic migration. Herein, we synthesized all-inorganic halide-mixed perovskite CsPbBr x I3-x microsheets with high crystal quality using the anti-solvent solution method and observed extraordinary green and red dual-color emission in single CsPbBr x I3-x microsheets. Power dependent PL spectra reveal excitonic and defect related recombination features of CsPbBr3 and CsPbI3 for the green and red emission. Temperature dependent PL spectra indicated a distinctive exciton-phonon coupling strength in CsPbBr x I3-x microsheets compared with pure CsPbBr3 and CsPbI3. The PL dynamics showing longer emission lifetime further confirmed this conclusion. Our work not only provides a novel strategy to produce stable dual-color emission integration, but also promotes the fundamental insight into the emission dynamics and exciton/free carrier related photophysics in all-inorganic halide-mixed perovskites.

| S-EPMC9053764 | biostudies-literature

Synergistic Halide- and Ligand-Exchanges of All-Inorganic Perovskite Nanocrystals for Near-Unity and Spectrally Stable Red Emission

Project description:All-inorganic perovskite nanocrystals (NCs) of CsPbX3 (X = Cl, Br, I) are promising for displays due to wide color gamut, narrow emission bandwidth, and high photoluminescence quantum yield (PLQY). However, pure red perovskite NCs prepared by mixing halide ions often result in defects and spectral instabilities. We demonstrate a method to prepare stable pure red emission and high-PLQY-mixed-halide perovskite NCs through simultaneous halide-exchange and ligand-exchange. CsPbBr3 NCs with surface organic ligands are first synthesized using the ligand-assisted reprecipitation (LARP) method, and then ZnI2 is introduced for anion exchange to transform CsPbBr3 to CsPbBrxI3−x NCs. ZnI2 not only provides iodine ions but also acts as an inorganic ligand to passivate surface defects and prevent ion migration, suppressing non-radiative losses and halide segregation. The luminescence properties of CsPbBrxI3−x NCs depend on the ZnI2 content. By regulating the ZnI2 exchange process, red CsPbBrxI3−x NCs with organic/inorganic hybrid ligands achieve near-unity PLQY with a stable emission peak at 640 nm. The CsPbBrxI3−x NCs can be combined with green CsPbBr3 NCs to construct white light-emitting diodes with high-color gamut. Our work presents a facile ion exchange strategy for preparing spectrally stable mixed-halide perovskite NCs with high PLQY, approaching the efficiency limit for display or lighting applications.

| S-EPMC10458086 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data