Hot Oscillatory Pressing of Carbon Nanotube-Reinforced Copper Matrix Nanocomposite.
Ontology highlight
ABSTRACT:
SUBMITTER: Han M
PROVIDER: S-EPMC8471937 | biostudies-literature |
REPOSITORIES: biostudies-literature
Similar Datasets
Project description:This research is motivated by the desire to restore the quality of life to amputees. The study uses multi-walled carbon nanotube (WMCNT) reinforced natural rubber (NR) polymer nanocomposite (PNC) for prosthetic foot application. The compound formulation was carried out in accordance to a modified procedure described by Hemkaew et al. Mixing of the ingredients during vulcanisation was performed according to ASTM D-3182 standard on an open two-roll mill. The various compositions of the nanocomposites (NCs) were cured at a temperature of 150 ± 2 °C and a pressure of 0.2 MPa for 10 minutes in an electrically heated hydraulic press. Mechanical investigation revealed that NR/MWCNT-3 exhibited the highest capacity to withstand tensile and dynamic loading (449.79 MPa). It also showed superior filler distribution and hence improved crystallinity and cross-link. Water absorption test indicated that NR/MWCNT-3 offers optimum dimensional stability at ambient conditions. Moreover, thermogravimetric analysis/differential thermogravimetry (TGA/DTG) showed degradation peaks at 305 °C and 290 °C respectively with temperature range within which the NCs degraded lying between 250 °C and 600 °C. Dynamic mechanical analysis (DMA) revealed that filler incorporation results in higher storage and loss moduli (2000-7500 MPa and 500-1413 MPa respectively). Tan δ curves proved that NR/MWCNT-3 has the highest capacity to dissipate energy through segmental motion. Furthermore, microstructure examination confirmed good filler/matrix adhesion as NR/MWCNT-3 indicated improved interaction; hence higher strength (6.02 MPa) of the NC. Better wear resistance ability can also be reported of the newly developed than existing prosthetic material. It can be deduced that the formulated nanocomposite from MWCNTs for reinforced natural rubber is suitable for the development of the anthropomorphic prosthetic foot.
| S-EPMC6934845 | biostudies-literature
Project description:Carbon nanotubes exhibit mechanical properties ideally suited for reinforced structural composites and surface area and conductivity attractive for electrochemical capacitors. Here we demonstrate the multifunctional synergy between these properties in a composite material exhibiting simultaneous mechanical and energy storage properties. This involves a reinforcing electrode developed using dense, aligned carbon nanotubes grown on stainless steel mesh that is layered in an ion conducting epoxy electrolyte matrix with Kevlar or fiberglass mats. The resulting energy storage composites exhibit elastic modulus over 5?GPa, mechanical strength greater than 85?MPa, and energy density up to 3?mWh/kg for the total combined system including electrodes, current collector, Kevlar or fiberglass, and electrolyte matrix. Furthermore, findings from in-situ mechano-electro-chemical tests indicate simultaneous mechanical and electrochemical functionality with invariant and stable supercapacitor performance maintained throughout the elastic regime.
| S-EPMC6281659 | biostudies-literature
Project description:With the rapid development of electronics and portable devices, polymer nanocomposites with high through-plane thermal conductivity (TC) are urgently needed. In this work, we fabricated graphene nanosheets-perfluoroalkoxy (GNs-PFA) composite sheets with high through-plane TCs via hot-pressing followed by mechanical machining. When the GNs content exceeded 10 wt%, GNs were vertically aligned in the PFA matrix, and the through-plane TCs of nanocomposites were 10-15 times higher than their in-plane TCs. In particular, the composite with 30 wt% GNs exhibited a through-plane TC of 25.57 W/(m·K), which was 9700% higher than that of pure PFA. The composite with 30 wt% GNs was attached to the surface of a high-power light-emitting diode (LED) to assess its heat-dissipation capability. The composite with vertically aligned GNs lowered the LED surface temperature by approximately 16 °C compared with pure PFA. Our facile, low-cost method allows for the large-scale production of GNs-PFA nanocomposites with high through-plane TCs, which can be used in various thermal-management applications.
| S-EPMC6781095 | biostudies-literature
Project description:This paper presents the electromagnetic interference properties of multi-walled carbon nanotubes (MWCNTs) as a novel nano-reinforcement filler in poly (lactic acid) (PLA)/poly (ethylene glycol) (PEG) polymer matrix that was prepared via melt blending mode. Plasticization of PLA was first carried out by PEG, which overcomes its brittleness problem, in order to enhance its flexibility. A waveguide adapter technique was used to measure the dielectric properties ?r, and S-parameters reflection (S11) and transmission (S21) coefficients. The dielectric properties, microwave attenuation performances, and electromagnetic interference shielding effectiveness (EMISE) for all the material under test have been calculated over the full X-Band (8-12 GHz) due to its importance for military and commercial applications. The prepared samples were studied while using X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Fourier transforms infrared spectroscopy (FTIR), mechanical properties measurements, as well as thermogravimetric analysis (TGA). The results showed that the dielectric properties increased with increased multi-walled carbon nanotubes (MWCNTs) filler, as well as the shielding effectiveness of the MWCNT/PLA/PEG nanocomposites increased with the increasing of MWCNTs. The highest SE total value was found to be 42.07 dB at 12 GHz for 4 wt% filler content. It is also observed that the attenuation values of the nanocomposites increased with an increase in MWCNTs loading, as well as the power loss values for all of the samples increased with the increase in MWCNTs loading, except the amount of the transmitted wave through the nanocomposites.
| S-EPMC7077650 | biostudies-literature
Project description:Multiwalled carbon nanotube (MWNT)/cellulose composite nanofibers have been prepared by electrospinning a MWNT/cellulose acetate blend solution followed by deacetylation. These composite nanofibers were then used as precursors for carbon nanofibers (CNFs). The effect of nanotubes on the stabilization of the precursor and microstructure of the resultant CNFs were investigated using thermogravimetric analysis, transmission electron microscopy and Raman spectroscopy. It is demonstrated that the incorporated MWNTs reduce the activation energy of the oxidative stabilization of cellulose nanofibers from ?230 to ?180 kJ mol(-1). They also increase the crystallite size, structural order, and electrical conductivity of the activated CNFs (ACNFs). The surface area of the ACNFs increased upon addition of nanotubes which protrude from the fiber leading to a rougher surface. The ACNFs were used as the electrodes of a supercapacitor. The electrochemical capacitance of the ACNF derived from pure cellulose nanofibers is demonstrated to be 105 F g(-1) at a current density of 10 A g(-1), which increases to 145 F g(-1) upon the addition of 6% of MWNTs.
| S-EPMC3807724 | biostudies-literature
Project description:The degradation of polypropylene (PP) and PP-multiwalled carbon nanotube (PP-MWCNT) panels during environmental weathering resulted in an increased degree of crystallinity, making them brittle, and creating surface cracks. The degradation led to a breakdown of the panels and increased the potential for nanorelease. Thermal analysis revealed that the thickness of the test panels and reinforcement with MWCNTs had a significant influence on the stability of PP-MWCNT composites. Differential scanning calorimetry indicated that the MWCNTs acted as nucleation points, increasing the crystallization temperatures of PP-MWCNT, which reduced the extent of aging. Weathering decreased both the melting and crystallization temperatures of PP by as much as 20 o C. The reduction in the temperatures was inversely proportional to the thickness of the panels. The activation energy (E a ) obtained using isoconversional kinetics of the TGA analysis showed that the effective thermo-oxidative degradations of PP changed during aging. The E a for the initial stages of thermal degradation decreased from ~330 kJ/mol to ~100 kJ/mol for aged PP. During the late degradation stages, the E a values increased to ~300 kJ/mol. These results suggest that early degradation were altered because of the changes in the molecular structure of the aged P and a shift in the degradation rate-limiting steps.
| S-EPMC7433849 | biostudies-literature
Project description:In this article, different concentrations of multiwalled carbon nanotube (MWCNT) were homogeneously dispersed throughout the chitosan (CS) matrix. A simple solvent-cast method was used to fabricate chitosan films with 0.1, 0.5, and 1% of MWCNT with the average diameter around 30 nm. The CS/MWCNT films were characterized for structural, viscous and mechanical properties with optical microscopy, wide-angle X-ray diffraction, Raman spectroscopy, tensile test machine, and microindentation testing machine. Murine osteoblasts were used to examine the cell viability and attachment of the nanocomposite films at two time points. In comparison to the pure chitosan film, the mechanical properties, including the tensile modulus and strength of the films, were greatly improved by increasing the percentage of MWCNT. Furthermore, adding MWCNT up to 1% increased the viscosity of the chitosan solution by 15%. However, adding MWCNT decreased the samples ductility and transparency. In biological point of view, no toxic effect on osteoblasts was observed in the presence of different percentages of MWCNT at day 3 and day 7. This investigation suggested MWCNT could be a promising candidate for improving chitosan mechanical properties without inducing remarkable cytotoxicity on bone cells.
| S-EPMC4443444 | biostudies-literature
Project description:Multiwall carbon nanotube (CNT)-filled high density polyethylene (HDPE) nanocomposites were prepared by extrusion and considered for their suitability in the offshore sheathing applications. Transmission electron microscopy was conducted to analyse dispersion after bulk extrusion. Monolithic and nanocomposite samples were subjected to accelerated weathering and photodegradation (carbonyl and vinyl indices) characterisations, which consisted of heat, moisture (seawater) and UV light, intended to imitate the offshore conditions. The effects of accelerated weathering on mechanical properties (tensile strength and elastic modulus) of the nanocomposites were analysed. CNT addition in HDPE produced environmentally resilient nanocomposites with improved mechanical properties. The energy utilised to extrude nanocomposites was also less than the energy used to extrude monolithic HDPE samples. The results support the mass substitution of CNT-filled HDPE nanocomposites in high-end offshore applications.
| S-EPMC7412307 | biostudies-literature
Project description:To increase the strength of carbon nanotube (CNT) fibers (CNTFs), the mean size of voids between bundles of CNTs was reduced by wet-pressing, and the CNTs were cross-linked. Separate and simultaneous physical (roller pressing) and chemical methods (cross-linking) were tested to confirm each method's effects on the CNTF strength. By reducing the fraction of pores, roller pressing decreased the cross-sectional area from 160 ?m² to 66 ?m² and increased the average load-at-break from 2.83 ± 0.25 cN to 4.41 ± 0.16 cN. Simultaneous injection of crosslinker and roller pressing augmented the cross-linking effect by increasing the infiltration of the crosslinker solution into the CNTF, so the specific strength increased from 0.40 ± 0.05 N/tex to 0.67 ± 0.04 N/tex. To increase the strength by cross-linking, it was necessary that the size of the pores inside the CNTF were reduced, and the infiltration of the solution was increased. These results suggest that combined physical and chemical treatment is effective to increase the strength of CNTFs.
| S-EPMC6266003 | biostudies-literature
Project description:We present research progress made in developing copper/carbon nanotube composites (Cu/CNT) to fulfil a growing demand for lighter copper substitutes with superior electrical, thermal and mechanical performances. Lighter alternatives to heavy copper electrical and data wiring are needed in automobiles and aircrafts to enhance fuel efficiencies. In electronics, better interconnects and thermal management components than copper with higher current- and heat-stabilities are required to enable device miniaturization with increased functionality. Our literature survey encouragingly indicates that Cu/CNT performances (electrical, thermal and mechanical) reported so far rival that of Cu, proving the material's viability as a Cu alternative. We identify two grand challenges to be solved for Cu/CNT to replace copper in real-life applications. The first grand challenge is to fabricate Cu/CNT with overall performances exceeding that of copper. To address this challenge, we propose research directions to fabricate Cu/CNT closer to ideal composites theoretically predicted to surpass Cu performances (i.e. those containing uniformly distributed Cu and individually aligned CNTs with beneficial CNT-Cu interactions). The second grand challenge is to industrialize and transfer Cu/CNT from lab bench to real-life use. Toward this, we identify and propose strategies to address market-dependent issues for niche/mainstream applications. The current best Cu/CNT performances already qualify for application in niche electronic device markets as high-end interconnects. However, mainstream Cu/CNT application as copper replacements in conventional electronics and in electrical/data wires are long-term goals, needing inexpensive mass-production by methods aligned with existing industrial practices. Mainstream electronics require cheap CNT template-making and electrodeposition procedures, while data/electrical cables require manufacture protocols based on co-electrodeposition or melt-processing. We note (with examples) that initiatives devoted to Cu/CNT manufacturing for both types of mainstream applications are underway. With sustained research on Cu/CNT and accelerating its real-life application, we expect the successful evolution of highly functional, efficient, and sustainable next-generation electrical and electronics systems.
| S-EPMC6281931 | biostudies-literature