Low-Mass Liquid Crystalline Materials Blended in Recycled Thermoplastic Polyester Elastomer for Corrosion Inhibitor Application.

ABSTRACT: In this work, the development and application of multicomponents obtained from recycled polyethylene terephthalate (r-PET) waste and monotropic liquid crystals as anticorrosion coatings are reported. The r-PET raw material was alcoholyzed and reproduced as a thermoplastic polyester elastomer (TPEE) with different amounts (n%, n = 0, 1, 3, and 5) of 1,6-hexanediamine (HDA). Then, a fluorine-containing liquid crystal (4-cyano-3-fluorophenyl 4-ethylbenzoate (4CFE)) was incorporated into the TPEE mixture via solvent blending to modify and enhance the water resistance. The adhesion behavior of the coating on glass and iron substrates was evaluated by cross-cut tests and immersion tests in aqueous NaCl. In the corrosion resistance measurements, all of the coating samples fabricated with 10 ± 1 mm thickness were less active toward electrochemical corrosion (PEF% > 99%) than the bare iron plate, indicating that our work provided better protection against corrosion of the iron plate.

SUBMITTER: Chen CJ

PROVIDER: S-EPMC8472966 | biostudies-literature | 2021 Sep

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Low-Mass Liquid Crystalline Materials Blended in Recycled Thermoplastic Polyester Elastomer for Corrosion Inhibitor Application.

Chen Chun-Jui CJ Huang Bo-Wei BW Tseng Po-Jung PJ Yang Zhi-Yu ZY Huang Xiang X Rwei Syang-Peng SP Chen Hsiu-Hui HH

Polymers 20210920 18

In this work, the development and application of multicomponents obtained from recycled polyethylene terephthalate (<i>r</i>-PET) waste and monotropic liquid crystals as anticorrosion coatings are reported. The <i>r</i>-PET raw material was alcoholyzed and reproduced as a thermoplastic polyester elastomer (TPEE) with different amounts (n%, n = 0, 1, 3, and 5) of 1,6-hexanediamine (HDA). Then, a fluorine-containing liquid crystal (4-cyano-3-fluorophenyl 4-ethylbenzoate (4CFE)) was incorporated in ...[more]

PMID: 34578089

Similar Datasets

Project description:Preparation of inherently bioactive scaffolds has become a challenging issue owing to their complicated synthesis and nonrobust modified cell-actuating property. Liquid crystalline elastomers (LCEs), due to their combined specialties of liquid crystals and elastomers as well as their ability to respond to various kinds of stimuli, have reversibly led to the design of a new class of stimuli-responsive tissue-engineered scaffolds. In this line, in the first stage of this research work, synthesis and evaluation of acrylate-based LCE films (LCEfilm) encompassing mesogenic monomers are carried out. In the second step, the design of an affordable electrospinning technique for preparing LCE nanofibers (LCEfiber) as a problematic topic, thanks to the low molecular weight of the mesogenic chains of LCEs, is investigated. For this purpose, two approaches are considered, including (1) photo-cross-linking of electrospun LCEfiber and (2) blending LCE with poly(ε-caprolactone) (PCL) to produce morphologically stable nanofibers (PCL-LCEfiber). In the following, thermal, mechanical, and morphological evaluations show the optimized crosslinker (mol)/aliphatic spacer (mol) molar ratio of 50:50 for LCEfilm samples. On the other hand, for LCEfiber samples, the appropriate amounts of excessive mesogenic monomer and PCL/LCE (v/v) to fabricate the uniform nanofibers are determined to be 20% and 1:2, respectively. Eventually, PC12 cell compatibility and the impact of the liquid crystalline phase on the PC12 cell dynamic behavior of the samples are examined. The obtained results reveal that PC12 cells cultured on electrospun PCL-LCEfiber nanofibers with an average diameter of ∼659 nm per sample are alive and the scaffold has susceptibility for cell proliferation and actuation because of the rapid increase in cell density and number of singularity points formed in time-lapse cell imaging. Moreover, the PCL-LCEfiber nanofibrous scaffold exhibits a high performance for cell differentiation according to detailed biological evaluations such as gene expression level measurements. The time-lapse evaluation of PC12 cell flow fields confirms the significant influence of the reprogrammable liquid crystalline phase in the PCL-LCEfiber nanofibrous scaffold on topographical cue induction compared to the biodegradable PCL nanofibers.

Dataset Information

Low-Mass Liquid Crystalline Materials Blended in Recycled Thermoplastic Polyester Elastomer for Corrosion Inhibitor Application.

Publications

Low-Mass Liquid Crystalline Materials Blended in Recycled Thermoplastic Polyester Elastomer for Corrosion Inhibitor Application.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets