Electrochemical Performance of Orthorhombic CsPbI₃ Perovskite in Li-Ion Batteries.

ABSTRACT: A facile solution process was employed to prepare CsPbI₃ as an anode material for Li-ion batteries. Rietveld refinement of the X-ray data confirms the orthorhombic phase of CsPbI₃ at room temperature. As obtained from bond valence calculations, strained bonds between Pb and I are identified within PbI₆ octahedral units. Morphological study shows that the as-prepared δ-CsPbI₃ forms a nanorod-like structure. The XPS analysis confirm the presence of Cs (3d, 4d), Pb (4d, 4f, 5d) and I (3p, 3d, 4d). The lithiation process involves both intercalation and conversion reactions, as confirmed by cyclic voltammetry (CV) and first-principles calculations. Impedance spectroscopy coupled with the distribution function of relaxation times identifies charge transfer processes due to Li metal foil and anode/electrolyte interfaces. An initial discharge capacity of 151 mAhg^-1 is found to continuously increase to reach a maximum of ~275 mAhg^-1 at 65 cycles, while it drops to ~240 mAhg^-1 at 75 cycles and then slowly decreases to 235 mAhg^-1 at 100 cycles. Considering the performance and structural integrity during electrochemical performance, δ-CsPbI₃ is a promising material for future Li-ion battery (LIB) application.

SUBMITTER: Kaisar N

PROVIDER: S-EPMC8510073 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Electrochemical Li Topotactic Reaction in Layered SnP3 for Superior Li-Ion Batteries.

Project description:The development of new anode materials having high electrochemical performances and interesting reaction mechanisms is highly required to satisfy the need for long-lasting mobile electronic devices and electric vehicles. Here, we report a layer crystalline structured SnP3 and its unique electrochemical behaviors with Li. The SnP3 was simply synthesized through modification of Sn crystallography by combination with P and its potential as an anode material for LIBs was investigated. During Li insertion reaction, the SnP3 anode showed an interesting two-step electrochemical reaction mechanism comprised of a topotactic transition (0.7-2.0?V) and a conversion (0.0-2.0?V) reaction. When the SnP3-based composite electrode was tested within the topotactic reaction region (0.7-2.0?V) between SnP3 and LixSnP3 (x???4), it showed excellent electrochemical properties, such as a high volumetric capacity (1st discharge/charge capacity was 840/663?mA h cm(-3)) with a high initial coulombic efficiency, stable cycle behavior (636?mA h cm(-3) over 100 cycles), and fast rate capability (550?mA h cm(-3) at 3C). This layered SnP3 anode will be applicable to a new anode material for rechargeable LIBs.

| S-EPMC5075908 | biostudies-other

Electrochemical Oscillation during Galvanostatic Charging of LiCrTiO4 in Li-Ion Batteries.

Project description:In the late 1960s, the establishment of Prigogine's dissipative structure theory laid the foundation for the (electro)chemical oscillation phenomenon, which has been widely investigated in some electrochemical reactions, such as electro-catalysis and electro-deposition, while the electrochemical oscillation of Li-ion batteries has just been discovered in spinel Li4Ti5O12 a few years before. In this work, spinel LiCrTiO4 samples were synthesized by using a high-temperature solid-state method, characterized with SEM (Scanning electron microscope), XRD (X-ray diffraction), Raman and XPS (X-ray photoelectron spectroscopy) measurements, and electrochemically tested in Li-ion batteries to study the electrochemical oscillation. When sintering in a powder form at a temperature between 800 and 900 °C, we achieved the electrochemical oscillation of spinel LiCrTiO4 during charging, and it is suppressed in the non-stoichiometric LiCrTiO4 samples, especially for reducing the Li content or increasing the Cr content. Therefore, this work developed another two-phase material as the powder-sintered LiCrTiO4 exhibiting the electrochemical oscillation in Li-ion batteries, which would inspire us to explore more two-phase electrode materials in Li-ion batteries, Na-ion batteries, etc.

| S-EPMC8269718 | biostudies-literature

Superior Electrochemical Performance of Thin-Film Thermoplastic Elastomer-Coated SnSb as an Anode for Li-ion Batteries.

Project description:The high failure strain of thermoplastic elastomers (TPEs) is a very desirable feature for rechargeable Li-ion batteries by improving the lifetime of high specific capacity anode materials that undergo mechanical fractures induced by large volume variations. In this work, poly(styrene-b-2-hydroxyethyl acrylate) called PS-b-PHEA was synthesized by a nitroxide meditated polymerization method. Owing to the use of a specific polystyrene macroinitiator (SG1), a suitable TPE copolymer with long hydroxyethyl acrylate blocks to ensure good mechanical properties is obtained for the first time. We show that the electrochemical properties of the PS-b-PHEA-coated SnSb anode are drastically improved by suppressing the crack formation at the surface of the electrode. Indeed, electrochemical characterization revealed that a high and stable gravimetric capacity over 100 cycles could be achieved. Moreover, excellent capacity reversibility was achieved when cycled at multiple C-rates and fast kinetics confirming the strong protection role of the polymer. The advanced chemical and mechanical properties of PS-b-PHEA open up promising perspectives to significantly improve the electrochemical performance of all electrodes that are known to suffer from large volume variations.

| S-EPMC6416307 | biostudies-literature

Orthorhombic Nb<sub>2</sub>O<sub>5-x</sub> for Durable High-Rate Anode of Li-Ion Batteries.

Project description:Li4Ti5O12 anode can operate at extraordinarily high rates and for a very long time, but it suffers from a relatively low capacity. This has motivated much research on Nb2O5 as an alternative. In this work, we present a scalable chemical processing strategy that maintains the size and morphology of nano-crystal precursor but systematically reconstitutes the unit cell composition, to build defect-rich porous orthorhombic Nb2O5-x with a high-rate capacity many times those of commercial anodes. The procedure includes etching, proton ion exchange, calcination, and reduction, and the resulting Nb2O5-x has a capacity of 253 mA h g-1 at 0.5C, 187 mA h g-1 at 25C, and 130 mA h g-1 at 100C, with 93.3% of the 25C capacity remaining after cycling for 4,000 times. These values are much higher than those reported for Nb2O5 and Li4Ti5O12, thanks to more available surface/sub-surface reaction sites and significantly improved fast ion and electron conductivity.

| S-EPMC6941880 | biostudies-literature

Hierarchically ordered mesoporous Co3O4 materials for high performance Li-ion batteries.

Project description:Highly ordered mesoporous Co3O4 materials have been prepared via a nanocasting route with three-dimensional KIT-6 and two-dimensional SBA-15 ordered mesoporous silicas as templates and Co(NO3)2 · 6H2O as precursor. Through changing the hydrothermal treating temperature of the silica template, ordered mesoporous Co3O4 materials with hierarchical structures have been developed. The larger pores around 10 nm provide an efficient transport for Li ions, while the smaller pores between 3-5 nm offer large electrochemically active areas. Electrochemical impedance analysis proves that the hierarchical structure contributes to a lower charge transfer resistance in the mesoporous Co3O4 electrode than the mono-sized structure. High reversible capacities around 1141 mAh g(-1) of the hierarchically mesoporous Co3O4 materials are obtained, implying their potential applications for high performance Li-ion batteries.

| S-EPMC4726024 | biostudies-other

Electrochemical properties of cobalt hydroxychloride microspheres as a new anode material for Li-ion batteries.

Project description:The use of cobalt hydroxychloride [Co2(OH)3Cl] as an anode material for lithium ion batteries (LIBs) is investigated using spherical shape and ultrafine nanocrystals directly formed by spray pyrolysis from spray solution of cobalt chloride salt. Dot-mapping images of the resulting powders reveal a uniform distribution of Co, O, and Cl throughout the powder. The Co2(OH)3Cl powder prepared directly by spray pyrolysis exhibits a high thermal stability at temperatures below 220 °C, as well as having superior electrochemical properties compared with those of the CoCl2(H2O)2 and CoO powders prepared by the same process. The initial discharge capacities of the Co2(OH)3Cl and CoO powders at a constant current density of 1000 mA g(-1) are found to be 1570 and 1142 mA h g(-1), respectively, and their initial Coulombic efficiencies are 72 and 70%. The discharge capacities of the Co2(OH)3Cl and CoO powders after 100 cycles are 955 and 632 mA h g(-1), respectively. The Co2(OH)3Cl powders have a high discharge capacity of 609 mA h g(-1) even after 1000 cycles at a high current density of 5000 mA g(-1).

| S-EPMC4148658 | biostudies-literature

Operando Raman Shift Replaces Current in Electrochemical Analysis of Li-ion Batteries: A Comparative Study.

Project description:Li-rich and catalytically active γ-LixV2O5 (x = 1.48) was investigated as a cathode for its heterogeneous charge transfer kinetics. Using a specially designed two-electrode system lithium half cell, Butler-Volmer analysis was performed, and Raman spectra were acquired in 18 mV intervals. A direct correlation was observed between the Raman shift of the active modes Ag,Bg, Au, and Bu, and the development of the Faraday current at the working electrode. The Raman intensity and the Raman shift were implemented to replace the current in a Tafel plot used for the analysis of Butler-Volmer kinetics. Striking similarities in the charge transfer proportionality constants α were found for current and Raman-based analysis. The potential of this new method of Raman-aided electrochemical detection at the diffraction limit is discussed.

| S-EPMC8439359 | biostudies-literature

Colloidal Antimony Sulfide Nanoparticles as a High-Performance Anode Material for Li-ion and Na-ion Batteries.

Project description:To maximize the anodic charge storage capacity of Li-ion and Na-ion batteries (LIBs and SIBs, respectively), the conversion-alloying-type Sb2S3 anode has attracted considerable interest because of its merits of a high theoretical capacity of 946 mAh g-1 and a suitable anodic lithiation/delithiation voltage window of 0.1-2 V vs. Li+/Li. Recent advances in nanostructuring of the Sb2S3 anode provide an effective way of mitigating the challenges of structure conversion and volume expansion upon lithiation/sodiation that severely hinder the Sb2S3 cycling stability. In this context, we report uniformly sized colloidal Sb2S3 nanoparticles (NPs) as a model Sb2S3 anode material for LIBs and SIBs to investigate the effect of the primary particle size on the electrochemical performance of the Sb2S3 anode. We found that compared with microcrystalline Sb2S3, smaller ca. 20-25 nm and ca. 180-200 nm Sb2S3 NPs exhibit enhanced cycling stability as anode materials in both rechargeable LIBs and SIBs. Importantly, for the ca. 20-25 nm Sb2S3 NPs, a high initial Li-ion storage capacity of 742 mAh g-1 was achieved at a current density of 2.4 A g-1. At least 55% of this capacity was retained after 1200 cycles, which is among the most stable performance Sb2S3 anodes for LIBs.

| S-EPMC7018818 | biostudies-literature

One-Pot Synthesis of High-Performance Tin Chalcogenides/C Anodes for Li-Ion Batteries.

Project description:Tin chalcogenides are considered as promising anode materials for lithium-ion batteries (LIBs) due to their high theoretical lithium-storage capacity. Herein, we have successfully synthesized the composites of tin chalcogenides and graphite, that is, SnS/C, SnSe/C, and SnS0.5Se0.5/C, via a simple one-pot solid-state method. During the electrochemical test, they exhibit excellent lithium-storage ability and cyclic performance as the anode electrodes of LIBs due to the introduction of carbon. In particular, (i) SnS/C displayed a high specific capacity of 875 mAh g-1 at 0.2 A g-1 over 200 cycles; (ii) SnSe/C presents 734 mAh g-1 at 0.2 A g-1 after 100 cycles, and it delivers 690 mAh g-1 at 1.0 A g-1 over 300 cycles; and (iii) the SnS0.5Se0.5/C composite electrode delivers a specific capacity of 643 mAh g-1 at 0.5 A g-1 over 150 cycles. Furthermore, another series of tin-based composites have also been successfully fabricated (i.e., Sn/C, SnS2/C, SnSe2/C, and SnTe/C), showing the general applicability of the synthetic route applied here. Our synthetic approach demonstrates a promising route for the large-scale production of high-performance tin chalcogenides/C anode materials for LIBs and other battery systems (e.g., Na-ion and K-ion batteries).

| S-EPMC8280710 | biostudies-literature

TiO2 modified FeS nanostructures with enhanced electrochemical performance for lithium-ion batteries.

Project description:Anatase TiO2 modified FeS nanowires assembled by numerous nanosheets were synthesized by using a typical hydrothermal method. The carbon-free nanocoated composite electrodes exhibit improved reversible capacity of 510 mAh g(-1) after 100 discharge/charge cycles at 200 mA g(-1), much higher than that of the pristine FeS nanostructures, and long-term cycling stability with little performance degradation even after 500 discharge/charge cycles at current density of 400 mA g(-1). Full batteries fabricated using the FeS@TiO2 nanostructures anode and the LiMn2O4 nanowires cathode with excellent stability, and good rate capacities could also be achieved. The enhanced electrochemical performance of the composite electrodes can be attributed to the improved conductively of the integrated electrodes and the enhanced kinetics of lithium insertion/extraction at the electrode/electrolyte interface because of the incorporation of anatase TiO2 phase.

| S-EPMC3684812 | biostudies-other