Hierarchically Porous Microspheres by Thiol-ene Photopolymerization of High Internal Phase Emulsions-in-Water Colloidal Systems.

ABSTRACT: A facile method for the preparation of hierarchically porous spherical particles using high internal phase water-in-oil-in-water (w/o/w) double emulsions via the photopolymerization of the water-in-oil high internal phase emulsion (w/o HIPE) was developed. Visible-light photopolymerization was used for the synthesis of microspherical particles. The HIP emulsion had an internal phase volume of 80% and an oil phase containing either thiol pentaerythritol tetrakis(3-mercaptopropionate) (PETMP) or trimethylolpropane tris(3-mercaptopropionate) (TMPTMP) and acrylate trimethylolpropane triacrylate (TMPTA). This enabled the preparation of microspheres with an open porous morphology, on both the surface and within the microsphere, with high yields in a batch manner. The effect of the thiol-to-acrylate ratio on the microsphere diameter, pore and window diameter, and degradation was investigated. It is shown that thiol has a minor effect on the microsphere and pore diameter, while the acrylate ratio affects the degradation speed, which decreases with increasing acrylate content. The possibility of free thiol group functionalization was demonstrated by a reaction with allylamine, while the microsphere adsorption capabilities were tested by the adsorption of methylene blue.

SUBMITTER: Kramer S

PROVIDER: S-EPMC8512400 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Thiol-Ene Cross-linking of Poly(ethylene glycol) within High Internal Phase Emulsions: Degradable Hydrophilic PolyHIPEs for Controlled Drug Release.

Project description:Macroporous polymer monoliths prepared from high internal phase emulsions (HIPEs) can be found in various biomedical applications. While typically water-in-oil HIPEs are applied for polyHIPE preparation, they are not suitable for hydrophilic polyHIPE preparation. Herein, direct oil-in-water emulsions based on water-soluble poly(ethylene glycol)diacrylate or poly(ethylene glycol)dimethacrylate were developed. Furthermore, the incorporation of a hydrophilic water-miscible thiol, ethoxylated trimethylolpropane tris(3-mercaptopropionate) (ETTMP) was reported for the first time within thiol-ene polyHIPEs. Due to the transparency of the emulsions, rapid curing via photopolymerization was feasible. The average pore diameters of the resulting polyHIPEs ranged between 1.2 and 3.6 μm, and porosity of up to 90% was achieved. The water uptake of the materials reached up to 1000% by weight. Drug loading and release were demonstrated, employing salicylic acid as a model drug. Porous profile and biodegradability add to the usefulness of the material for biomedical applications.

| S-EPMC8619294 | biostudies-literature

Ionogels Obtained by Thiol-ene Photopolymerization-Physicochemical Characterization and Application in Electrochemical Capacitors.

Project description:Flexible ionogels with good mechanical properties were obtained in situ by thiol-ene photopolymerization of trimethylolpropane tris(3-mercaptopropionate) (TMPTP) and 1,3,5-triallyl-1,3,5-triazine-2,4,6(1H,3H,5H)-trione (TATT) (with C=C: SH ratio 1:1) in four imidazolium ionic liquids (1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide-EMImNTf2, 1-ethyl-3-methylimidazolium trifluoromethanesulfonate-EMImOTf, 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide-BMImNTf2, and 1-butyl-3-methylimidazolium trifluoromethanesulfonate-BMImOTf) used in the range 50 to 70 wt.%. The mechanical and electrochemical properties of obtained ionogels were examined. Ionogels with ionic liquids (ILs) with NTf2- anion are more puncture resistant than with OTf⁻ anion. Moreover, ionogels with the NTF2- anion have better electrochemical properties than those with the OTf⁻ anion. Although it should be noted that ionogels with the EMIm+ cation have a higher conductivity than the BMIm+. This is connected with intermolecular interactions between polymer matrix and IL related to the polarity of IL described by the Kamlet-Taft parameters. These parameters influence the morphology of the polymer matrix (as shown by the SEM micrograph), which is formed by interconnected polymer spheres.

| S-EPMC7867143 | biostudies-literature

Synthesis of Spherical Nanoparticle Hybrids via Aerosol Thiol-Ene Photopolymerization and Their Bioconjugation.

Project description:Hybrid nanomaterials possess the properties of both organic and inorganic components and find applications in various fields of research and technology. In this study, aerosol photopolymerization is used in combination with thiol-ene chemistry to produce silver poly(thio-ether) hybrid nanospheres. In aerosol photopolymerization, a spray solution of monomers is atomized, forming a droplet aerosol, which then polymerizes, producing spherical polymer nanoparticles. To produce silver poly(thio-ether) hybrids, silver nanoparticles were introduced to the spray solution. Diverse methods of stabilization were used to produce stable dispersions of silver nanoparticles to prevent their agglomeration before the photopolymerization process. Successfully stabilized silver nanoparticle dispersion in the spray solution subsequently formed nanocomposites with non-agglomerated silver nanoparticles inside the polymer matrix. Nanocomposite particles were analyzed via scanning and transmission electron microscopy to study the degree of agglomeration of silver nanoparticles and their location inside the polymer spheres. The nanoparticle hybrids were then introduced onto various biofunctionalization reactions. A two-step bioconjugation process was developed involving the hybrid nanoparticles: (1) conjugation of (biotin)-maleimide to thiol-groups on the polymer network of the hybrids, and (2) biotin-streptavidin binding. The biofunctionalization with gold-nanoparticle-conjugates was carried out to confirm the reactivity of -SH groups on each conjugation step. Fluorescence-labeled biomolecules were conjugated to the spherical nanoparticle hybrids (applying the two-step bioconjugation process) verified by Fluorescence Spectroscopy and Fluorescence Microscopy. The presented research offers an effective method of synthesis of smart systems that can further be used in biosensors and various other biomedical applications.

| S-EPMC8838805 | biostudies-literature

Poly(ethylene glycol) hydrogels formed by thiol-ene photopolymerization for enzyme-responsive protein delivery.

Project description:Degradable hydrogels have been extensively used in biomedical applications such as drug delivery, and recent interest has grown in hydrogels that degrade in recognition of a cellular response. This contribution describes a poly(ethylene glycol) (PEG) hydrogel platform with human neutrophil elastase (HNE) sensitive peptide cross-links formed using thiol-ene photopolymerization rendering the gel degradable at sites of inflammation. Further, protein therapeutics can be physically entrapped within the network and selectively released upon exposure to HNE. HNE-responsive hydrogels exhibited surface erosion where the degradation kinetics was influenced by changes in peptide k(cat), concentration of HNE, and concentration of peptide within the gel. Using this platform, we were able to achieve controlled, zero-order release of bovine serum albumin (BSA) in the presence of HNE, and release was arrested in the absence of HNE. To further exploit the advantages of surface eroding delivery systems, a smaller protein (carbonic anhydrase) was delivered at the same rate as BSA and only dependent on gel formulation and environmental conditions. Also, protein release was predicted from a 3-layered hydrogel device using mass loss data. Lastly, the bioactivity of lysozyme was maintained above 90% following the exposure to thiol-ene photopolymerization conditions.

| S-EPMC2761537 | biostudies-literature

Fabrication of Woven Jute Fiber Epoxy Bio-Composites through the Epoxy/Thiol-Ene Photopolymerization Technique.

Project description:An eco-friendly epoxy/thiol-ene photopolymerization (ETEP) process was employed to prepare epoxy bio-composites using a commercial biobased epoxy resin and a woven jute fabric as reinforcement. In this process the components of the thiol-ene system, an allyl-functionalized ditertiary amine curing agent, a multifunctional thiol and a radical photoinitiator, were added to the epoxy resin to produce a polyether-polythioether crosslinked co-network. Moreover, the jute fibers were functionalized with thiol groups using the 3-mercaptopropyl (trimethoxysilane) with the purpose of creating a chemically bonded polymeric matrix/fiber system. The obtained bio-composites prepared with the thiol-functionalized cellulose fibers exhibited an increase up to 52% and 40% in flexural modulus and strength with respect to the non-functionalized counterparts. Under the three-point bending loadings, the composites displayed higher deformation at break and toughness due to the presence of polythioethers in the co-network. The prepared bio-composites developed in this work are excellent candidates to extend the use of cellulose fibers for structural applications.

| S-EPMC9824046 | biostudies-literature

Thiol-ene click chemistry: a biocompatible way for orthogonal bioconjugation of colloidal nanoparticles.

Project description:Bioconjugation based on crosslinking primary amines to carboxylic acid groups has found broad applications in protein modification, drug development, and nanomaterial functionalization. However, proteins, which are made up of amino acids, typically give nonselective bioconjugation when using primary amine-based crosslinking. In order to control protein orientation and activity after conjugation, selective bioconjugation is desirable. We herein report an efficient and cysteine-selective thiol-ene click reaction-based bioconjugation strategy using colloidal nanoparticles. The resulting thiol-ene based aptamer and enzyme nanoconjugates demonstrated excellent target binding ability and enzymatic activity, respectively. Thus, thiol-ene click chemistry can provide a stable and robust crosslinker in a biocompatible manner for bioconjugation of any thiol-containing biomolecule with nanomaterials. This will open more opportunities for applications of thiol-ene reactions and functional colloidal nanoparticles in chemical biology.

| S-EPMC5628335 | biostudies-literature

Enhanced mechanical properties of photo-clickable thiol-ene PEG hydrogels through repeated photopolymerization of in-swollen macromer.

Project description:Current hydrogels used for tissue engineering are limited to a single range of mechanical properties within the replicated tissue construct. We show that repeated in-swelling by a single hydrogel pre-cursor solution into an existing polymerized hydrogel followed by photo-exposure increases hydrogel mechanical properties. The process is demonstrated with a photo-clickable thiol-ene hydrogel using a biocompatible precursor solution of poly(ethylene glycol) dithiol and 8-arm poly(ethylene glycol) functionalized with norbornene. The polymer fraction in the precursor solution was varied by 5, 10, and 20 percent by weight and an off-stoichiometric ratio of thiol : ene was used, leaving free enes available for subsequent reaction. Multiple swelling and exposure cycles for the same precursor solution were performed. The compressive modulus increased by a factor between three and ten (formulation dependent), while volume swelling ratio decreased by a factor of two, consistent with increased crosslink density. The modified hydrogels also demonstrate increased toughness by fracturing at compressive forces five times greater than the initial hydrogel. We attribute the increased toughness to subsequent increases in crosslink density created by the repeated photopolymerization of in-swollen macromer. This technique demonstrates the ability to significantly modify hydrogel network properties by exploiting swelling and polymerization processes that can be applied to traditional three-dimensional printing systems to spatially control local mechanical properties.

| S-EPMC5341082 | biostudies-literature

New, highly versatile bimolecular photoinitiating systems for free-radical, cationic and thiol-ene photopolymerization processes under low light intensity UV and visible LEDs for 3D printing application.

Project description:1-Amino-4-methyl-naphthalene-2-carbonitrile derivatives are proposed for the role of photosensitizers of iodonium salt during the photopolymerization processes upon near UV-A and visible ranges. Remarkably, 1-amino-4-methyl-naphthalene-2-carbonitrile derivatives are highly versatile allowing access to photoinitiating systems for (i) the cationic photopolymerization of epoxide monomers with a ring opening mechanism and vinyl ether monomers with chain growth mechanisms (ii) the free-radical photopolymerization of acrylate monomers, (iii) the photopolymerization of interpenetrated polymer networks (IPNs) based on epoxide and acrylate monomers under air and under laminate in an oxygen-free atmosphere (iv) the thiol-ene photopolymerization processes. Excellent polymerization profiles are obtained during all types of photopolymerization processes. The initiation mechanisms are analyzed through steady state photolysis, cyclic voltammetry and fluorescence experiments. Moreover, the newly developed bimolecular photoinitiating systems were investigated by applying an additive manufacturing process under visible light sources. Furthermore, vat photopolymerization processes using IPN compositions, which are polymerizable by using new photoinitiating systems, provide high resolution and speeds. For these reasons, new bimolecular photoinitiating systems are promising initiators for photopolymerization-based 3D printing process to fabricate 3D structures.

| S-EPMC9049847 | biostudies-literature

Preparation of uniform magnetic recoverable catalyst microspheres with hierarchically mesoporous structure by using porous polymer microsphere template.

Project description:Merging nanoparticles with different functions into a single microsphere can exhibit profound impact on various applications. However, retaining the unique properties of each component after integration has proven to be a significant challenge. Our previous research demonstrated a facile method to incorporate magnetic nanoparticles into porous silica microspheres. Here, we report the fabrication of porous silica microspheres embedded with magnetic and gold nanoparticles as magnetic recoverable catalysts. The as-prepared multifunctional composite microspheres exhibit excellent magnetic and catalytic properties and a well-defined structure such as uniform size, high surface area, and large pore volume. As a result, the very little composite microspheres show high performance in catalytic reduction of 4-nitrophenol, special convenient magnetic separability, long life, and good reusability. The unique nanostructure makes the microspheres a novel stable and highly efficient catalyst system for various catalytic industry processes.

| S-EPMC4113952 | biostudies-literature

Hierarchically porous SiO<sub>2</sub>/C hollow microspheres: a highly efficient adsorbent for Congo Red removal.

Project description:Hierarchically porous SiO2/C hollow microspheres (HPSCHMs) were synthesized by a hydrothermal and NaOH-etching combined route. The adsorption performance of the prepared HPSCHMs was investigated to remove Congo Red (CR) in aqueous solution. The results show that the synthesized composite possesses a hollow microspherical structure with hierarchical pores and a diameter of about 100-200 nm, and its surface area is up to 1154 m2 g-1. This material exhibits a remarkable adsorption performance for CR in solution, and its maximum adsorption amount for CR can reach up to 2512 mg g-1. It shows faster adsorption and much higher adsorption capacity than the commercial AC and γ-Al2O3 samples under the same conditions. The studies of the kinetics and thermodynamics indicate that the adsorption of CR on the PHSCHM sample obeys the pseudo-second order model well and belongs to physisorption. The adsorption activation energy is about 7.72 kJ mol-1. In view of the hierarchically meso-macroporous structure, large surface area and pore volume, the HPSCHM material could be a promising adsorbent for removal of pollutants, and it could also be used as a catalyst support.

| S-EPMC9080780 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data