Development of Amino Acids Functionalized SBA-15 for the Improvement of Protein Adsorption.

ABSTRACT: Ordered mesoporous materials and their modification with multiple functional groups are of wide scientific interest for many applications involving interaction with biological systems and biomolecules (e.g., catalysis, separation, sensor design, nano-science or drug delivery). In particular, the immobilization of enzymes onto solid supports is highly attractive for industry and synthetic chemistry, as it allows the development of stable and cheap biocatalysts. In this context, we developed novel silylated amino acid derivatives (Si-AA-NH₂) that have been immobilized onto SBA-15 materials in biocompatible conditions avoiding the use of toxic catalyst, solvents or reagents. The resulting amino acid-functionalized materials (SBA-15@AA) were characterized by XRD, TGA, EA, Zeta potential, nitrogen sorption and FT-IR. Differences of the physical properties (e.g., charges) were observed while the structural ones remained unchanged. The adsorption of the enzyme lysozyme (Lyz) onto the resulting functionalized SBA-15@AA materials was evaluated at different pHs. The presence of different functional groups compared with bare SBA-15 showed better adsorption results, for example, 79.6 nmol of Lyz adsorbed per m² of SBA-15@Tyr compared with the 44.9 nmol/m² of the bare SBA-15.

SUBMITTER: Gutierrez-Climente R

PROVIDER: S-EPMC8512485 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Novel Magnetic Nanocomposites Based on Carboxyl-Functionalized SBA-15 Silica for Effective Dye Adsorption from Aqueous Solutions.

Project description:In this study, three novel magnetic nanocomposites based on carboxyl-functionalized SBA-15 silica and magnetite nanoparticles were prepared through an effective and simple procedure and applied for methylene blue (MB) and malachite green G (MG) adsorption from single and binary solutions. Structure, composition, morphology, magnetic, and textural properties of the composites were thoroughly investigated. The influence of the amount of carboxyl functional groups on the physicochemical and adsorptive properties of the final materials was investigated. The capacity of the synthesized composites to adsorb MB and MG from single and binary solutions and the factors affecting the adsorption process, such as contact time, solution pH, and dye concentration, were assessed. Kinetic modelling showed that the dye adsorption mechanism followed the pseudo-second-order kinetic model, indicating that adsorption was a chemically controlled multilayer process. The adsorption rate was simultaneously controlled by external film diffusion and intraparticle diffusion. It was evidenced that the molecular geometry of the dye molecule plays a major role in the adsorption process, with the planar geometry of the MB molecule favoring adsorption. The analysis of equilibrium data revealed the best description of MB adsorption behavior by the Langmuir isotherm model, whereas the Freundlich model described better the MG adsorption.

| S-EPMC9268668 | biostudies-literature

Grafting of Amines on Ethanol-Extracted SBA-15 for CO2 Adsorption.

Project description:SBA-15 prepared via ethanol extraction for template removing was grafted with three kinds of amine precursors (mono-, di-, tri-aminosilanes) to synthesis new CO₂ adsorbents. The SBA-15 support and the obtained adsorbents were characterized by X-ray diffraction (XRD), small-angle X-ray scattering (SAXS), N₂ adsorption/desorption, thermogravimetry (TG), elemental analysis, Fourier transform infrared (FTIR) spectrometry, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was found that, except higher silanol density, the ethanol-extracted SBA-15 support possessed a more regular mesophase and thicker walls than traditionally calcined samples, leading to a good stability of the adsorbent under steam treatment. The adsorption capacity of different amine-grafted samples was found to be influenced by not only the surface amine density, but also their physiochemical properties. These observations provide important support for further studies of applying amine-grafted adsorbents in practical CO₂ capture process.

| S-EPMC5512959 | biostudies-other

H3PMo12O40 Immobilized on Amine Functionalized SBA-15 as a Catalyst for Aldose Epimerization.

Project description:In this work various amount of phosphomolybdic acid (PMo) were immobilized on amine functionalized SBA-15 and used as heterogeneous catalysts in the epimerization of glucose in aqueous solution. 13.3PMo/NH2-SBA-15 exhibited the best catalytic performance with a glucose conversion of 34.8% and mannose selectivity of 85.6% within two hours at 120 °C. The activation energy of 80.1 ± 0.1 kJ·mol-1 was lower than that of 96 kJ·mol-1 over the homogeneous H3PMo12O40 catalyst. The catalytic activities of 13.3PMo/NH2-SBA-15 for the transformation of some other aldoses including mannose, arabinose and xylose were also investigated.

| S-EPMC7040683 | biostudies-literature

Development of Poly(2-Methacryloyloxyethyl Phosphorylcholine)-Functionalized Hydrogels for Reducing Protein and Bacterial Adsorption.

Project description:A series of hydrogels with intrinsic antifouling properties was prepared via surface-functionalization of poly(2-hydroxyethyl methacrylate) [p(HEMA)]-based hydrogels with the biomembrane-mimicking zwitterionic polymer, poly(2-methacryloyloxyethyl phosphorylcholine) [p(MPC)]. The p(MPC)-modified hydrogels have enhanced surface wettability, high water content retention (61.0%-68.3%), and good transmittance (>90%). Notably, the presence of zwitterionic MPC moieties at the hydrogel surfaces lowered the adsorption of proteins such as lysozyme and bovine serum albumin (BSA) by 73%-74% and 59%-66%, respectively, and reduced bacterial adsorption by approximately 10%-73% relative to the unmodified control. The anti-biofouling properties of the p(MPC)-functionalized hydrogels are largely attributed to the dense hydration layer formed at the hydrogel surfaces by the zwitterionic moieties. Overall, the results demonstrate that biocompatible and antifouling hydrogels based on p(HEMA)-p(MPC) structures have promising potential for application in biomedical materials.

| S-EPMC7079665 | biostudies-literature

Characteristics of Carbon Material Formation on SBA-15 and Ni-SBA-15 Templates by Acetylene Decomposition and Their Bioactivity Effects.

Project description:Carbon spheres and tubes were formed from acetylene decomposition on SBA-15 and Ni-SBA-15 at 650-850 °C. At 650 °C, the decomposed carbons covered the surface of the support, and no carbon spheres and filament materials were formed. Carbon sphere formation occurred at 750 °C-850 °C; with diameters ranging from 0.8 μm-1.1 μm. For Ni-SBA-15, the diameters of the spheres and filaments were 0.8 μm and 62 nm, respectively, at 650 °C. At 750 °C, the diameter of the ball carbon materials ranged from 0.7 μm-0.8 μm, the diameter of the carbon tubes formed was 120-130 nm, and their pore diameter was 8.0 nm-11 nm. At 850 °C, the diameters of ball carbon materials and carbon tubes were similar to those of the materials at the formation temperature, 750 °C. Si, O and C were the main constituents of SBA-15; Ni-SBA-15 and carbon material formation supports. High-ring PAHs (such as BaP (five rings); IND (six rings); DBA (five rings) and B[ghi]P (six rings)) exist in carbon materials. SBA-15 revealed insignificant cytotoxicity, but Ni-SBA-15 inhibited the proliferation of human lung cancer cells (A549). Less inhibition on cell viability and reactive oxidative species (ROS) generation on A549 were determined for carbon material formation on the Ni-SBA-15 compared to the Ni-SBA-15.

| S-EPMC5503084 | biostudies-literature

Surface Functionalization of SBA-15 for Immobilization of Myoglobin.

Project description:Mesoporous molecular sieve SBA-15 was successfully modified with 3-aminopropyltriethoxysilane (APTES) and 3-glycidyloxypropyltrimethoxysilane (GPTMS). The functionalized SBA-15 were characterized by small-angle X-ray (SAXRD), thermogravimetric analysis (TG), N2 adsorption, and Fourier transformed infrared spectrum (FT-IR). APTES functionalized SBA-15 (named SBA-15-A) and GPTMS functionalized SBA-15 (named SBA-15-G) were used to immobilize myoglobin (Mb). The loading amounts of Mb by SBA-15-A and SBA-15-G were 511.2 and 547.8 mg/g, respectively, whereas only 359.6 mg/g was achieved by SBA-15. Mb/SBA-15-G and Mb/SBA-15-A demonstrated better reusability than SBA-15, retaining 84.6% and 82.7% of the initial activity after repeated use seven times. The Mb/SBA-15-A and Mb/SBA-15-G also exhibited improved thermal stability and storage stability.

| S-EPMC9160787 | biostudies-literature

Synthesis of unnatural amino acids functionalized with sterically shielded pyrroline nitroxides.

Project description:A series of unnatural amino acids functionalized with sterically shielded pyrroline nitroxides were synthesized. Their reduction by ascorbate/glutathione indicates that L-cysteine functionalized with gem-diethylpyrroline nitroxide is reduced at the slowest rate and is comparable to that measured for the most resistant to reduction pyrroline and pyrrolidine nitroxides.

| S-EPMC4201325 | biostudies-literature

Synthesis of Amino-Functionalized Waste Wood Flour Adsorbent for High-Capacity Pb(II) Adsorption.

Project description:An innovative wood flour-based adsorbent for Pb(II) removal was synthesized via a cost-effective and environment-friendly method, which could be high on the priority list owing to its high absorption capacity. By increasing the specific surface and introducing functional groups through delignification and amination, the experimental adsorption capacity of the prepared adsorbent could reach 189.9 mg/g in 180 min (pH = 4, T = 293 K, dosage = 1 g/L, and ion concentration = 300 mg/L). This value is higher than most of those achieved in previous studies on wood-based adsorbents. Pseudo-second-order and Langmuir models were utilized to describe the adsorption kinetics and isotherms, respectively. The effects of solution pH, adsorbent dosage, and temperature on the adsorption efficiency were also evaluated. With a low decrease rate of 20.2% in five cycles, the adsorbent possessed reusability. The adsorbents exhibited high selectivity in the Pb(II), Cu(II), and Zn(II) mixed solution, and the selectivity coefficient k of adsorbents to Pb(II) could reach approximately 2.74 in triad. The method could prompt the development of cost-effective methods for the removal of heavy metals from wastewater.

| S-EPMC6648050 | biostudies-literature

Transient colloidal stability controls the particle formation of SBA-15.

Project description:A hypothesis about (transient) colloidal stability as a controlling mechanism for particle formation in SBA-15 is presented. The hypothesis is based on results from both in situ and ex situ investigations, including cryogenic transmission electron microscopy (cryo-TEM), UV-vis spectroscopy, and dynamic light scattering (DLS). Cryo-TEM images show that particles grow via the formation of silica-Pluronic-water "flocs", which coalesce in a seemingly arbitrary manner. Despite this, the final material consists of well-defined particles with a small size distribution. We argue that the interface between the flocs and surrounding media is covered by Pluronic molecules, which provide steric stabilization. As the flocs grow, the coverage of polymers at the interface is increased until a stable size is reached, and that regulates the particle size. By targeting the characteristics of the Pluronic molecules, during the on-going synthesis, the hypothesis is tested. The results are consistent with the concept of (transient) colloidal stability.

| S-EPMC3836357 | biostudies-literature

Preparation of highly selective magnetic cobalt ion-imprinted polymer based on functionalized SBA-15 for removal Co<sup>2+</sup> from aqueous solutions.

Project description:In this research, a novel magnetic cobalt ion imprinted adsorbent (Co(II)-MIIP) was synthesized by use of magnetic SBA-15 core-shell. It was functionalized by dithizone, and after identification by various techniques was used for removal of cobalt from aquatic systems. The uptake of cobalt proceeded very fast and achieved to equilibration within 5 min at which 74 mg g-1 of cobalt was adsorbed at pH?=?8 with adsorbent dose of 0.15 g. The ion imprinted sorbent exhibited good selectivity towards cobalt ions. Separation and recovery of the used sorbent was carried out respectively by use of magnetic field and by use of HNO3 (0.1 M), and 85% of the initial capacity was obtained after seven 7 regeneration cycles. Different isotherm models, and error analysis were used to evaluate the experimental data. Thermodynamic, and kinetic evaluations showed that sorption process was endothermic, and described by second order kinetic model (R2?>?0.99). The equilibrium was established within five min.

| S-EPMC6985317 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data