Lignin Resists High-Intensity Electron Beam Irradiation.

ABSTRACT: The electron beam irradiation (EBI) of native lignin has received little attention. Thus, its potential use in lignin-based biorefineries is not fully understood. EBI was applied to selected lignin samples and the structural and chemical changes were analyzed, revealing the suitability, limitations, and potential purpose of EBI in wood biorefineries. Isolated milled wood, kraft, and sulfite lignin from beech and eucalyptus were subjected to up to 200 kGy of irradiation. The analysis included gel permeation chromatography for molar masses, heteronuclear single quantum coherence (HSQC)- and ³¹P NMR and headspace gas chromatography-mass spectrometry for functional groups, and thermogravimetric analysis for thermal stability. Most samples resisted irradiation. Subtle changes occurred in the molecular weight distribution and thermal stability of milled wood lignin. EBI was found to be a suitable pretreatment method for woody biomass if the avoidance of lignin condensation and chemical modification is a high priority.

SUBMITTER: Sarosi O

PROVIDER: S-EPMC8512668 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Trehalose glycopolymer resists allow direct writing of protein patterns by electron-beam lithography.

Project description:Direct-write patterning of multiple proteins on surfaces is of tremendous interest for a myriad of applications. Precise arrangement of different proteins at increasingly smaller dimensions is a fundamental challenge to apply the materials in tissue engineering, diagnostics, proteomics and biosensors. Herein, we present a new resist that protects proteins during electron-beam exposure and its application in direct-write patterning of multiple proteins. Polymers with pendant trehalose units are shown to effectively crosslink to surfaces as negative resists, while at the same time providing stabilization to proteins during the vacuum and electron-beam irradiation steps. In this manner, arbitrary patterns of several different classes of proteins such as enzymes, growth factors and immunoglobulins are realized. Utilizing the high-precision alignment capability of electron-beam lithography, surfaces with complex patterns of multiple proteins are successfully generated at the micrometre and nanometre scale without requiring cleanroom conditions.

| S-EPMC4412366 | biostudies-literature

Grafting Polytetrafluoroethylene Micropowder via in Situ Electron Beam Irradiation-Induced Polymerization.

Project description:Decreasing the surface energy of polyacrylate-based materials is important especially in embossed holography, but current solutions typically involve high-cost synthesis or encounter compatibility problems. Herein, we utilize the grafting of polytetrafluoroethylene (PTFE) micropowder with poly (methyl methacrylate) (PMMA). The grafting reaction is implemented via in situ electron beam irradiation-induced polymerization in the presence of fluorinated surfactants, generating PMMA grafted PTFE micropowder (PMMA⁻g⁻PTFE). The optimal degree of grafting (DG) is 17.8%. With the incorporation of PMMA⁻g⁻PTFE, the interfacial interaction between polyacrylate and PTFE is greatly improved, giving rise to uniform polyacrylate/PMMA⁻g⁻PTFE composites with a low surface energy. For instance, the loading content of PMMA⁻g⁻PTFE in polyacrylate is up to 16 wt %, leading to an increase of more than 20 degrees in the water contact angle compared to the pristine sample. This research paves a way to generate new polyacrylate-based films for embossed holography.

| S-EPMC6415420 | biostudies-literature

Silicon nanocrystal growth under irradiation of electron beam.

Project description:In our experiment, it was observed that silicon nanocrystal rapidly grows with irradiation of electron beam on amorphous silicon film prepared by pulsed laser deposition, and shape of silicon nanocrystal is usually sphere in smaller nanoscale with less exposure time under electron beam, in which the quantum dots are prepared in nanoscale near 3 nm. In the electron interaction process, it was investigated that the various crystals structures in different orientations occur in the same time and the condensed structures of silicon nanocrystal are changed with different impurity atoms in silicon film.

| S-EPMC4660392 | biostudies-other

Electron beam irradiation on novel coronavirus (COVID-19): A Monte-Carlo simulation.

Project description:The novel coronavirus pneumonia triggered by COVID-19 is now raging the whole world. As a rapid and reliable killing COVID-19 method in industry, electron beam irradiation can interact with virus molecules and destroy their activity. With the unexpected appearance and quickly spreading of the virus, it is urgently necessary to figure out the mechanism of electron beam irradiation on COVID-19. In this study, we establish a virus structure and molecule model based on the detected gene sequence of Wuhan patient, and calculate irradiated electron interaction with virus atoms via a Monte Carlo simulation that track each elastic and inelastic collision of all electrons. The characteristics of irradiation damage on COVID-19, atoms' ionizations and electron energy losses are calculated and analyzed with regions. We simulate the different situations of incident electron energy for evaluating the influence of incident energy on virus damage. It is found that under the major protecting of an envelope protein layer, the inner RNA suffers the minimal damage. The damage for a ∼100-nm-diameter virus molecule is not always enhanced by irradiation energy monotonicity, for COVID-19, the irradiation electron energy of the strongest energy loss damage is 2 keV.

| S-EPMC7351116 | biostudies-literature

Response of Microcystis aeruginosa and Microcystin-LR to electron beam irradiation doses.

Project description:Harmful cyanobacterial blooms (cyanoHABs) pose threats to human and animal health due to the production of harmful cyanotoxins. Microcystis aeruginosa is a common cyanobacterium associated with these blooms and is responsible for producing the potent cyclic hepatotoxin microcystin-LR (MC-LR). Concerns over the public health implications of these toxins in water supplies have increased due to rising occurrence of these blooms. High energy electron beam (eBeam) irradiation technology presents a promising strategy for the mitigation of both cyanobacterial cells and cyanotoxins within the water treatment process. However, it is imperative that both cellular and chemical responses to eBeam irradiation are understood to ensure efficient treatment. We sought to investigate the effect of eBeam irradiation on M. aeruginosa cells and MC-LR degradation. Results indicate that doses as low as 2 kGy are lethal to M. aeruginosa cells and induce cell lysis. Even lower doses are required for degradation of the parent MC-LR toxin. However, it was observed that there is a delay in cell lysis after irradiation where M. aeruginosa cells may still be metabolically active and able to synthesize microcystin. These results suggest that eBeam may be suitable for cyanoHAB mitigation in water treatment if employed following cell lysis.

| S-EPMC8143040 | biostudies-literature

Process evaluation of electron beam irradiation-based biodegradation relevant to lignocellulose bioconversion.

Project description:In order to solve the inefficient problem of long-term biodegradation by wood-decaying fungus, rice straw (RS) was depolymerized using electron beam irradiation-based biodegradation (EBIBB). This environment-friendly program without the use of inhibitory byproducts significantly increased the digestibility and fermentability of RS. Specifically, when irradiated RS was simultaneously biodegraded by Phanerochaete chrysosporium for 10 days, the sugar yield was 65.5% of the theoretical maximum. This value was on the same level as the 64.8% (for 15 days) measured from unirradiated RS. In case of fermentability, similarly, EBIBB program had an effect on time/energy saving. Furthermore, the transcriptomic profiles under different biosystem were analyzed in order to verify possible substrate-specific regulation based on change of lignocellulosic components. Interestingly, the overall correlation based on the bias (upregulation or downregulation) was reasonably analogous, especially lignocellulolysis-related genes.

| S-EPMC4164673 | biostudies-literature

Effects of electron-beam irradiation on buccal-cell DNA.

Project description:Buccal cells were collected from 29 participants, by use of mouthwash rinses, and were split into equal aliquots, with one aliquot irradiated by electron-beam (E-beam) irradiation equivalent to the sterilizing dosage used by the U.S. Postal Service and the other left untreated. Aliquots were extracted and tested for DNA yields (e.g., TaqMan assay for quantifying human genomic DNA), genomic integrity, and amplification-based analysis of genetic variants (e.g., single-nucleotide polymorphisms [SNPs] and single tandem repeats [STRs]). Irradiated aliquots had lower median DNA yields (3.7 microg/aliquot) than untreated aliquots (7.6 microg/aliquot) (P<.0005) and were more likely to have smaller maximum DNA fragment size, on the basis of genomic integrity gels, than untreated aliquots (P<.0005). Irradiated aliquots showed poorer PCR amplification of a 989-bp beta-globin target (97% for weak amplification and 3% for no amplification) than untreated aliquots (7% for weak amplification and 0% for no amplification) (P<.0005), but 536-bp and 268-bp beta-globin targets were amplified from all aliquots. There was no detectable irradiation effect on SNP assays, but there was a significant trend for decreased detection of longer STRs (P=.01) in irradiated versus untreated aliquots. We conclude that E-beam irradiation reduced the yield and quality of buccal-cell specimens, and, although irradiated buccal-cell specimens may retain sufficient DNA integrity for some amplified analyses of many common genomic targets, assays that target longer DNA fragments (>989 bp) or require whole-genome amplification may be compromised.

| S-EPMC1180689 | biostudies-other

Electron Beam Irradiation of Cellulosic Materials-Opportunities and Limitations.

Project description:The irradiation of pulp is of interest from different perspectives. Mainly it is required when a modification of cellulose is needed. Irradiation could bring many advantages, such as chemical savings and, therefore, cost savings and a reduction in environmental pollutants. In this account, pulp and dissociated celluloses were analyzed before and after irradiation by electron beaming. The focus of the analysis was the oxidation of hydroxyl groups to carbonyl and carboxyl groups in pulp and the degradation of cellulose causing a decrease in molar mass. For that purpose, the samples were labeled with a selective fluorescence marker and analyzed by gel permeation chromatography (GPC) coupled with multi-angle laser light scattering (MALLS), refractive index (RI), and fluorescence detectors. Degradation of the analyzed substrates was the predominant result of the irradiation; however, in the microcrystalline samples, oxidized cellulose functionalities were introduced along the cellulose chain, making this substrate suitable for further chemical modification.

| S-EPMC5452524 | biostudies-other

In Situ Atomic-Scale Observation of Silver Oxidation Triggered by Electron Beam Irradiation.

Project description:Understanding the mechanism of metal oxidation processes is critical for maintaining the desired properties of metals and catalysts, as well as for designing advanced materials. In this work, we investigate the electron beam induced oxidation of silver using in situ transmission electron microscopy. The additions of Ag-O columns on {111} and {110} planes were captured with atomic resolution. Interestingly, oscillatory growth on {110} planes was observed, which resulted from the double effect of electron beam irradiation. It was found that not only thermodynamic factors but also kinetic factors played significant roles in morphology evolutions. These results can facilitate the fundamental understanding of the oxidation process of Ag and provide a promising approach for the fabrication of desired nanostructures.

| S-EPMC8073916 | biostudies-literature

Sapphire Wafer for 226 nm Far UVC Generation with Carbon Nanotube-Based Cold Cathode Electron Beam (C-Beam) Irradiation.

Project description:Far ultraviolet C (UVC) light sources have the potential for numerous applications ranging from sterilization, purification, sensing, deodorization, surface modification, and so on. In particular, a short wavelength of far UVC is effective at sterilizing viruses and bacteria by minimizing damage to mammalian skin. Recently, many researchers are devoting materials and alternative light sources to overcome low efficiency, small light-emitting area, UV absorption, and complicated manufacturing processes of far UVC generation. Here, the sapphire wafer is evaluated for far UVC light generation using electron beam irradiation with carbon nanotube (CNT) emitters. A CNT-based cold cathode electron beam (C-beam) that emits electrons and accelerated onto ?-Al2O3 of the sapphire wafer was used as an excitation source to demonstrate high-power far UVC light generation. High-efficiency 226 nm far UVC is made with a power conversion efficiency of 0.87% and a light-emitting area of 960 mm2. Far UVC generation depends on the input power and the crystallinity of sapphire wafers.

| S-EPMC7331211 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data