A novel insertion design of fiber materials for the adhesive reattachment in vertically fractured teeth.

ABSTRACT:

Objective

This ex vivo study aimed to evaluate the strengthening effect of different ferrule and reattachment designs with fiber and adhesive materials on vertically fractured teeth.

Methods

Ninety extracted single-root premolars were instrumented and divided into nine groups (two control groups and seven experimental groups; n = 10). The negative control (NC) group comprised of intact teeth, while the positive control (PC) group comprised of root canal-treated teeth. The roots of the teeth in the experimental groups were vertically fractured into two equal fragments. The fragments were reattached with one of the followings: 4-methacryloxyethyl trimellitate anhydride/methacrylate-tri-n-butyl borane (4-META/MMA-TBB) resin, 4-META/MMA-TBB + quartz fiber post, 4-META/MMA-TBB + glass fiber bundles, 4-META/MMA-TBB + quartz fiber post + 1 mm ferrule, 4-META/MMA-TBB + glass fiber bundles + 1 mm ferrule, 4-META/MMA-TBB + quartz fiber post + 2 mm ferrule, and 4-META/MMA-TBB + glass fiber bundles + 2 mm ferrule. The core build-ups were made with composite resin. The specimens were subjected to compressive loading until failure occurred. Mean load necessary to fracture each sample and the fracture types of these samples were recorded.

Results

The highest mean fracture load was recorded in the NC group (1,036.7 N), which was not significantly higher than the PC group (989.66 N) (p > 0.05). The roots reattached with quartz fiber post demonstrated significantly less fracture strength (871.9 N) as compared to the other test and control groups (p < 0.05). There was no significant difference between the PC group and reattached fragments with different ferrule designs in terms of fracture resistance (p > 0.05).

Conclusions

The customized fiber bundles may be more suitable for reattachment of vertically fractured teeth than the rigid fiber posts. For reattachment procedures, the ferrule design may be preferred to increase the fracture strength of vertically fractured teeth.

SUBMITTER: Kurnaz S

PROVIDER: S-EPMC8513869 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Recent and potential applications of electrochromic materials include smart windows, optoelectronic devices, and energy conversion. In this study, we have incorporated bis(terpyridine) iron (II) complexes into vertically-oriented silica thin films deposited on indium-tin oxide (ITO) and their electrochromic behavior has been investigated. If 2,2':6',2″-terpyridine is commonly used as a ligand for forming metallo-supramolecular assemblies, with the objective to get metal-terpyridine complexes with multiple stable redox states, their simple and reliable arrangement into linear structures enabling effective electronic communication is however more challenging. We propose to overcome this difficulty by generating such complexes within vertical nanochannels on electrode. Terpyridine ligands were firstly immobilized by combining a click chemistry azide/alkyne approach with an electrochemically-assisted self-assembly (EASA) method used to grow an oriented mesoporous silica membrane bearing azide groups which were further derivatized with 4'-ethynyl-terpyridine ligands. The resulting terpyridine-functionalized films were consecutively dipped in an aqueous solution of Fe(BF4)2 and then in a solution of terpyridine in acetonitrile to form the bis(terpyridine) iron (II) complexes in situ. The electrochromic properties of the films functionalized at various levels were examined by monitoring the changes in their UV/Vis spectra upon electrochemical oxidation at controlled potential of +1.2 V vs. Ag/AgCl. Due to facile charge delocalization during the Fe2+ to Fe3+ redox process, the bis(terpyridine) iron (II) functionalized silica films exhibited electrochromic properties by changing from violet to non-colored using TBABF4 in acetonitrile as an electrolyte. The bis(terpyridine) iron(II) film experienced reversible electrochromic switching by applying +0.5 V in a reverse reduction electrochemical process. The Fe(tpy)2-functionalized silica thin films displayed a good contrast ratio (ΔT%) of 47% and relatively high coloration efficiency (CE) of about 245 cm2/C with a response time of coloring and bleaching of a few seconds (< 4 s).