Project description:The electrochemical reduction of CO2 offers an elegant solution to the current energy crisis and carbon emission issues, but the catalytic efficiency for CO2 reduction is seriously restricted by the inherent scaling relations between the adsorption energies of intermediates. Herein, by combining the concept of single-atom catalysts and multiple active sites, we design heteronuclear dual-atom catalysts to break through the stubborn restriction of scaling relations on catalytic activity. Twenty-one kinds of heteronuclear transition-metal dimers are embedded in monolayer C2N as potential dual-atom catalysts. First-principles calculations reveal that by adjusting the components of dimers, the two metal atoms play the role of carbon adsorption sites and oxygen adsorption sites respectively, which results in the decoupling of adsorption energies of key intermediates. Free energy profiles demonstrate that CO2 can be efficiently reduced to CH4 on CuCr/C2N and CuMn/C2N with low limiting potentials of -0.37 V and -0.32 V, respectively. This study suggests that the introduction of multiple active sites into porous two-dimensional materials would provide a great possibility for breaking scaling relations to achieve efficient multi-intermediate electrocatalytic reactions.
Project description:Electrocatalytic CO2 reduction to generate multicarbon products is of interest for applications in artificial photosynthetic schemes. This is a particularly attractive goal for CO2 reduction by copper electrodes, where a broad range of hydrocarbon products can be generated but where selectivity for C-C coupled products relative to CH4 and H2 remains an impediment. Herein we report a simple yet highly selective catalytic system for CO2 reduction to C?2 hydrocarbons on a polycrystalline Cu electrode in bicarbonate aqueous solution that uses N-substituted pyridinium additives. Selectivities of 70-80% for C2 and C3 products with a hydrocarbon ratio of C?2/CH4 significantly greater than 100 have been observed with several additives. 13C-labeling studies verify CO2 to be the sole carbon source in the C?2 hydrocarbons produced. Upon electroreduction, the N-substituted pyridinium additives lead to film deposition on the Cu electrode, identified in one case as the reductive coupling product of N-arylpyridinium. Product selectivity can also be tuned from C?2 species to H2 (?90%) while suppressing methane with certain N-heterocyclic additives.
Project description:The sources and nature of organic carbon on Mars have been a subject of intense research. Steele et al. (2012) showed that 10 martian meteorites contain macromolecular carbon phases contained within pyroxene- and olivine-hosted melt inclusions. Here, we show that martian meteorites Tissint, Nakhla, and NWA 1950 have an inventory of organic carbon species associated with fluid-mineral reactions that are remarkably consistent with those detected by the Mars Science Laboratory (MSL) mission. We advance the hypothesis that interactions among spinel-group minerals, sulfides, and a brine enable the electrochemical reduction of aqueous CO2 to organic molecules. Although documented here in martian samples, a similar process likely occurs wherever igneous rocks containing spinel-group minerals and/or sulfides encounter brines.
Project description:Electrochemical reduction of CO2 into carbon-based products using excess clean electricity is a compelling method for producing sustainable fuels while lowering CO2 emissions. Previous electrolytic CO2 reduction studies all involve dioxygen production at the anode, yet this anodic reaction requires a large overpotential and yields a product bearing no economic value. We report here that the cathodic reduction of CO2 to CO can occur in tandem with the anodic oxidation of organic substrates that bear higher economic value than dioxygen. This claim is demonstrated by 3 h of sustained electrolytic conversion of CO2 into CO at a copper-indium cathode with a current density of 3.7 mA cm-2 and Faradaic efficiency of >70%, and the concomitant oxidation of an alcohol at a platinum anode with >75% yield. These results were tested for four alcohols representing different classes of alcohols and demonstrate electrolytic reduction and oxidative chemistry that form higher-valued carbon-based products at both electrodes.
Project description:CO2 reduction through artificial photosynthesis represents a prominent strategy toward the conversion of solar energy into fuels or useful chemical feedstocks. In such configuration, designing highly efficient chromophores comprising earth-abundant elements is essential for both light harvesting and electron transfer. Herein, we report that a copper purpurin complex bearing an additional redox-active center in natural organic chromophores is capable to shift the reduction potential 540 mV more negative than its organic dye component. When this copper photosensitizer is employed with an iron porphyrin as the catalyst and 1,3-dimethyl-2-phenyl-2,3-dihydro-1H-benzo[d]imidazole as the sacrificial reductant, the system achieves over 16100 turnover number of CO from CO2 with a 95% selectivity (CO vs H2) under visible-light irradiation, which is among the highest reported for a homogeneous noble metal-free system. This work may open up an effective approach for the rational design of highly efficient chromophores in artificial photosynthesis.
Project description:The electrocatalytic carbon dioxide (CO2 ) reduction reaction (CO2 RR) into hydrocarbons is a promising approach for greenhouse gas mitigation, but many details of this dynamic reaction remain elusive. Here, time-resolved surface-enhanced Raman spectroscopy (TR-SERS) is employed to successfully monitor the dynamics of CO2 RR intermediates and Cu surfaces with sub-second time resolution. Anodic treatment at 1.55 V vs. RHE and subsequent surface oxide reduction (below -0.4 V vs. RHE) induced roughening of the Cu electrode surface, which resulted in hotspots for TR-SERS, enhanced time resolution (down to ≈0.7 s) and fourfold improved CO2 RR efficiency toward ethylene. With TR-SERS, the initial restructuring of the Cu surface was followed (<7 s), after which a stable surface surrounded by increased local alkalinity was formed. Our measurements revealed that a highly dynamic CO intermediate, with a characteristic vibration below 2060 cm-1 , is related to C-C coupling and ethylene production (-0.9 V vs. RHE), whereas lower cathodic bias (-0.7 V vs. RHE) resulted in gaseous CO production from isolated and static CO surface species with a distinct vibration at 2092 cm-1 .
Project description:Biomimetic catalysts inspired by the active site of the [FeFe] hydrogenase enzyme can convert protons into molecular hydrogen. Minimizing the overpotential of the electrocatalytic process remains a major challenge for practical application of the catalyst. The catalytic cycle of the hydrogen production follows an ECEC mechanism (E represents an electron transfer step, and C refers to a chemical step), in which the electron and proton transfer steps can be either sequential or coupled (PCET). In this study, we have calculated the pKa's and the reduction potentials for a series of commonly used ligands (80 different complexes) using density functional theory. We establish that the required acid strength for protonation at the Fe-Fe site correlates with the standard reduction potential of the di-iron complexes with a linear energy relationship. These linear relationships allow for fast screening of ligands and tuning of the properties of the catalyst. Our study also suggests that bridgehead ligand properties, such as bulkiness and aromaticity, can be exploited to alter or even break the linear scaling relationships.
Project description:We present a microkinetic model for CO(2) reduction (CO(2)R) on Cu(211) towards C2 products, based on energetics estimated from an explicit solvent model. We show that the differences in both Tafel slopes and pH dependence for C1 vs C2 activity arise from differences in their multi-step mechanisms. We find the depletion in C2 products observed at high overpotential and high pH to arise from the 2nd order dependence of C-C coupling on CO coverage, which decreases due to competition from the C1 pathway. We further demonstrate that CO(2) reduction at a fixed pH yield similar activities, due to the facile kinetics for CO2 reduction to CO on Cu, which suggests C2 products to be favored for CO2R under alkaline conditions. The mechanistic insights of this work elucidate how reaction conditions can lead to significant enhancements in selectivity and activity towards higher value C2 products.
Project description:2D metal-organic-framework (MOF) based composites have emerged as promising candidates for electrocatalysis due to their high structural flexibility and fully exposed active sites. Herein, a freestanding metal-organic layer (MOL) with a 2D kgd (kagome dual) lattice was constructed with abundant surface oxygenate groups serving as anchoring sites to immobilize diverse guests. Taking Bi as an example, tetragonal Bi2 O3 nanowires can be uniformly grown on MOLs after solvothermal treatment, the structural evolution of which was followed by ex situ electron microscopy. The as-prepared Bi2 O3 /MOL exhibits excellent CO2 electroreduction activity towards formate reaching a specific current of 2.3 A mgBi -1 and Faradaic efficiencies of over 85 % with a wide potential range from -0.87 to -1.17 V, far surpassing Bi2 O3 /UiO (a 3D Zr6 -oxo based MOF) and Bi2 O3 /AB (Acetylene Black). Such a post-synthetic modification strategy can be flexibly extended to develop versatile MOL composites, highlighting the superiority of optimizing MOL-based composites for electrocatalysis.
Project description:Noble-metal alloys are widely used as heterogeneous catalysts. However, due to the existence of scaling properties of adsorption energies on transition metal surfaces, the enhancement of catalytic activity is frequently accompanied by side reactions leading to a reduction in selectivity for the target product. Herein, we describe an approach to breaking the scaling relationship for propane dehydrogenation, an industrially important reaction, by assembling single atom alloys (SAAs), to achieve simultaneous enhancement of propylene selectivity and propane conversion. We synthesize ?-alumina-supported platinum/copper SAA catalysts by incipient wetness co-impregnation method with a high copper to platinum ratio. Single platinum atoms dispersed on copper nanoparticles dramatically enhance the desorption of surface-bounded propylene and prohibit its further dehydrogenation, resulting in high propylene selectivity (~90%). Unlike previous reported SAA applications at low temperatures (<400?°C), Pt/Cu SAA shows excellent stability of more than 120?h of operation under atmospheric pressure at 520?°C.