Understanding the physicochemical properties of Zn-Fe LDH nanostructure as sorbent material for removing of anionic and cationic dyes mixture.

ABSTRACT: In our work, the removal of cationic and anionic dyes from water was estimated both experimentally and computationally. We check the selectivity of the adsorbent, Zn-Fe layered double hydroxide (LDH) toward three dyes. The physical and chemical properties of the synthesis adsorbent before and after the adsorption process were investigated using X-ray photoelectron spectroscopy, energy dispersive X-ray, X-ray diffraction, FT-IR, HRTEM, and FESEM analysis, particle size, zeta potential, optical and electric properties were estimated. The effect of pH on the adsorption process was estimated. The chemical stability was investigated at pH 4. Monte Carlo simulations were achieved to understand the mechanism of the adsorption process and calculate the adsorption energies. Single dye adsorption tests revealed that Zn-Fe LDH effectively takes up anionic methyl orange (MO) more than the cationic dyes methylene blue (MB) and malachite green (MG). From MO/MB/MG mixture experiments, LDH selectively adsorbed in the following order: MO > MB > MG. The adsorption capacity of a single dye solution was 230.68, 133.29, and 57.34 mg/g for MO, MB, and MG, respectively; for the ternary solution, the adsorption capacity was 217.97, 93.122, and 49.57 mg/g for MO, MB, and MG, respectively. Zn-Fe LDH was also used as a photocatalyst, giving 92.2% and 84.7% degradation at concentrations of 10 and 20 mg/L, respectively. For visible radiation, the Zn-Fe LDH showed no activity.

SUBMITTER: Mahmoud RK

PROVIDER: S-EPMC8560778 | biostudies-literature | 2021 Nov

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Understanding the physicochemical properties of Zn-Fe LDH nanostructure as sorbent material for removing of anionic and cationic dyes mixture.

Mahmoud Rehab K RK Taha Mohamed M Zaher Amal A Amin Rafat M RM

Scientific reports 20211101 1

In our work, the removal of cationic and anionic dyes from water was estimated both experimentally and computationally. We check the selectivity of the adsorbent, Zn-Fe layered double hydroxide (LDH) toward three dyes. The physical and chemical properties of the synthesis adsorbent before and after the adsorption process were investigated using X-ray photoelectron spectroscopy, energy dispersive X-ray, X-ray diffraction, FT-IR, HRTEM, and FESEM analysis, particle size, zeta potential, optical an ...[more]

PMID: 34725383

Similar Datasets

Project description:Silica-supported hierarchical graphitic carbon sheltering cobalt nanoparticles Co-HGC@SiO2 (1) were prepared by pyrolysis at 850 °C of [Co(phen)(H2O)4]SO4·2H2O complex with silica in the presence of pyrene as a carbon source under nitrogen atmosphere. Nanocomposites (2) and (3) were obtained by acid treatment of (1) with HCl and HF acid, respectively. The nanocomposites showed rough hierarchical carbon microstructures over silica support decorated with irregular cobalt nanospheres and nanorods 50 to 200 nm in diameter. The nanoparticles consist of graphitic shells and cobalt cores. SEM, EDAX and TEM elemental mapping indicate a noticeable loss of cobalt in the case of (2) and loss of cobalt and silica in the case of (3) with an increase in porosity. Nanocomposite (3) showed the highest BET surface area 217.5 m2g-1. Raman spectrum shows defect D-band and graphitic G-band as expected in carbon nanostructures. PXRD reveals the presence of cobalt(0) nanoparticles. XPS indicates the presence of Co(II) oxides and the successful doping of nitrogen in the nanocomposites. Moreover, TEM elemental mapping provides information about the abundance of Si, Co, C, N and S elements in zones. Nanocomposite (1) showed maximum uptake capacity of 192.3 and 224.5 mg/g for crystal violet CV and methyl orange MO dyes, respectively. Nanocomposite (2) showed a capacity of 94.1 and 225.5 mg/g for CV and MO dyes, respectively. Nanocomposite (4) obtained after treatment of (1) with crystal violet proved successful adsorption of CV. Co-HGC (5) prepared without addition of silica has a capacity for CV equal to 192 mg/g, while it is 769.2 mg/g with MO. Electrostatics and π-π interactions of graphite and cobalt species in the nanocomposites with aromatic rings of cationic and anionic dyes are responsible for the adsorption. Yan et al. was the best model to describe column kinetics. The thomas column adsorption model showed that the maximum uptake capacity of (1) was 44.42 mg/g for CV and 32.62 mg/g for MO. for a column packed with 0.5 gm of (1) and dye concentration of 100 mg/L at a flow rate of 1 mL/min. The column was recycled three times with no noticeable clogging or degradation of nanocomposites. Thus, Co-HGC@SiO2 adsorbents can be used efficiently to treat water contaminated with cationic and anionic dyes.

Dataset Information

Understanding the physicochemical properties of Zn-Fe LDH nanostructure as sorbent material for removing of anionic and cationic dyes mixture.

Publications

Understanding the physicochemical properties of Zn-Fe LDH nanostructure as sorbent material for removing of anionic and cationic dyes mixture.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets