Electrochemical Performance of Na₃V₂(PO₄)₂F₃ Electrode Material in a Symmetric Cell.

ABSTRACT: A NASICON-based Na₃V₂(PO₄)₂F₃ (NVPF) cathode material is reported herein as a potential symmetric cell electrode material. The symmetric cell was active from 0 to 3.5 V and showed a capacity of 85 mAh/g at 0.1 C. With cycling, the NVPF symmetric cell showed a very long and stable cycle life, having a capacity retention of 61% after 1000 cycles at 1 C. The diffusion coefficient calculated from cyclic voltammetry (CV) and the galvanostatic intermittent titration technique (GITT) was found to be ~10^-9-10^-11, suggesting a smooth diffusion of Na⁺ in the NVPF symmetric cell. The electrochemical impedance spectroscopy (EIS) carried out during cycling showed increases in bulk resistance, solid electrolyte interphase (SEI) resistance, and charge transfer resistance with the number of cycles, explaining the origin of capacity fade in the NVPF symmetric cell. Finally, the postmortem analysis of the symmetric cell after 1000 cycles at a 1 C rate indicated that the intercalation/de-intercalation of sodium into/from the host structure occurred without any major structural destabilization in both the cathode and anode. However, there was slight distortion in the cathode structure observed, which resulted in capacity loss of the symmetric cell. The promising electrochemical performance of NVPF in the symmetric cell makes it attractive for developing long-life and cost-effective batteries.

SUBMITTER: James Abraham J

PROVIDER: S-EPMC8584735 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Enhancing Electrochemical Performance with g-C3N4/CeO2 Binary Electrode Material.

Project description:An innovative form of 2D/0D g-C3N4/CeO2 nanostructure was synthesized using a simple precursor decomposition process. The 2D g-C3N4 directs the growth of 0D CeO2 quantum dots, while also promoting good dispersion of CeO2QDs. This 2D/0D nanostructure shows a capacitance of 202.5 F/g and notable rate capability and stability, outperforming the g-C3N4 electrode, reflecting the state-of-the-art g-C3N4 binary electrodes. The binary combination of materials also enables an asymmetric device (g-C3N4/CeO2QDs//AC) to deliver the highest energy density (9.25 Wh/kg) and power density (900 W/kg). The superior rate capacity and stability endorsed the quantum structural merits of CeO2QDs and layered g-C3N4, which offer more accessible sites for ion transport. These results suggest that the g-C3N4/CeO2QDs nanostructure is a promising electrode material for energy storage devices.

| S-EPMC10059818 | biostudies-literature

High power Na3V2(PO4)3 symmetric full cell for sodium-ion batteries.

Project description:Sodium-ion batteries (SIBs) are a viable substitute for lithium-ion batteries due to the low cost and wide availability of sodium. However, practical applications require the development of fast charging sodium-ion-based full-cells with high power densities. Na3V2(PO4)3 (NVP) is a bipolar material with excellent characteristics as both a cathode and an anode material in SIBs. Designing symmetric cells with NVP results in a single voltage plateau with significant specific capacity which is ideal for a full cell. Here we demonstrate for the first time a tremendous improvement in the performance of NVP symmetric full cells by introducing an ether-based electrolyte which favors fast reaction kinetics. In a symmetric full cell configuration, 75.5% of the initial capacity was retained even after 4000 cycles at 2 A g-1, revealing ultra-long cyclability. Excellent rate performances were obtained at current densities as high as 1000C, based on the cathode mass, revealing ultrafast Na+ transfer. The power density obtained for this NVP symmetric cell (48 250 W kg-1) is the best among those of all the sodium-ion-based full cells reported to date.

| S-EPMC9419746 | biostudies-literature

Na3V2(PO4)3-decorated Na3V2(PO4)2F3 as a high-rate and cycle-stable cathode material for sodium ion batteries.

Project description:Since Na3V2(PO4)3 (NVP) possesses modest volume deformation and three-dimensional ion diffusion channels, it is a potential sodium-ion battery cathode material that has been extensively researched. Nonetheless, NVP still endures the consequences of poor electronic conductivity and low voltage platforms, which need to be further improved. On this basis, a high voltage platform Na3V2(PO4)2F3 was introduced to form a composite with NVP to increase the energy density. In this study, the sol-gel technique was successfully used to synthesize a Na3V2(PO4)2.75F0.75/C (NVPF·3NVP/C) composite cathode material. The citric acid-derived carbon layer was utilized to construct three-dimensional conducting networks to effectively promote ion and electron diffusion. Furthermore, the composites' synergistic effect accelerates the quick ionic migration and improves the kinetic reaction. In particular, NVP as the dominant phase enhanced the structural stability and significantly increased the capacitive contribution. Therefore, at 0.1C, the discharge capacity of the modified NVPF·3NVP/C composite is 120.7 mA h g-1, which is greater than the theoretical discharge capacity of pure NVP (118 mA h g-1). It discharged 110.9 mA h g-1 of reversible capacity even at an elevated multiplicity of 10C, and after 200 cycles, it retained 64.1% of its capacity. Thus, the effort produced an optimized NVPF·3NVP/C composite cathode material that may be used in the sodium ion cathode.

| S-EPMC11017267 | biostudies-literature

New Microfluidic System for Electrochemical Impedance Spectroscopy Assessment of Cell Culture Performance: Design and Development of New Electrode Material.

Project description:Electrochemical impedance spectroscopy (EIS) is widely accepted as an effective and non-destructive method to assess cell health during cell-culture. However, there is a lack of compact devices compatible with microfluidic integration and microscopy that could provide the real-time and non-invasive monitoring of cell-cultures using EIS. In this paper, we reported the design and characterization of a modular EIS testing system based on a patented technology. This device was fabricated using easily processable methodologies including screen-printing of the impedance electrodes and molding or micromachining of the cell culture chamber with an easy assembly procedure. Accordingly, to obtain processable, biocompatible and sterilizable electrode materials that lower the impact of interfacial impedance on TEER (Transepithelial electrical resistance) measurements, and to enable concomitant microscopy observations, we optimized the formulation of the electrode inks and the design of the EIS electrodes, respectively. First, electrode materials were based on carbon biocompatible inks enriched with IrOx particles to obtain low interfacial impedance electrodes approaching the performances of classical non-biocompatible Ag/AgCl second-species electrodes. Secondly, we proposed three original electrode designs, which were compared to classical disk electrodes that were optically compatible with microscopy. We assessed the impact of the electrode design on the response of the impedance sensor using COMSOL Multiphysics. Finally, the performance of the impedance spectroscopy devices was assessed in vitro using human airway epithelial cell cultures.

| S-EPMC9313146 | biostudies-literature

Carbonization and H3PO4 activation of fern Dicranopteris linearis and electrochemical properties for electric double layer capacitor electrode.

Project description:Today, the world's climate change is a growing problem, plant carbon sequestration is one of the effective ways to mitigate climate change by reducing greenhouse gases, mostly carbon gases. Dicranopteris linearis (D. linearis), a common fern species in the tropic or subtropic ecoregions, has been recently recognized as a potential feedstock to produce highly porous biochar. This study aims to enhance the specific surface area (SSA) and pore volumes of biochars derived from the D. linearis by H3PO4 activation and examine electrical properties of the activated biochars and their possible usage for the electric double-layer capacitor (EDLC) electrode. The treated raw fern was activated with H3PO4 85% by the three different mixing ratios 1:0, 1:1, and 1:3 (w/w) and then pyrolysis under N2 flow maintained at 500 °C for 1 h. The performance as the electrode for an EDLC was evaluated in 1 mol L-1 H2SO4 solution for the H3PO4-activated samples. The SSA and pore volumes were drastically increased after activation. The maximum SSA and pore volume were 1212 m2 g-1 and 1.43 cm3 g-1, respectively for the biochar activated at 400 °C with a weight mixing ratio 1:3 (w/w) between the fern and H3PO4 acid while these values of the biochar at 400 °C were 12 m2 g-1 and 0.02 cm3 g-1, respectively. The biochar activated at 600 °C with the mixing ratio 1:1 (w/w) showed the maximum capacitance value, ca. 108 F g-1 at 1 mV s-1. The activation using H3PO4 showed a positive tendency to enhance electrochemical properties and it could be a premise toward a higher performance of EDLC from the D. linearis derived activated biochar.

| S-EPMC7672103 | biostudies-literature

In situ anchor of Na2Ti3O7 in nitrogen-rich carbon hollow red blood cell-like structure as a 0D-3D hierarchical electrode material for efficient electrochemical desalination.

Project description:Reasonable design of the structure and complementary compounding of electrode materials is helpful to enhance capacitive deionization (CDI) performance. Herein, a novel 0D-3D hierarchical electrode material containing Na2Ti3O7 nanoparticles anchored at hollow red blood cell (HRBC)-like nitrogen-rich carbon (HRBC-NTO/N-C-60) was prepared via selective protection, pyrolysis, and alkalization. Specifically, a HRBC-like NH2-MIL-125-based material (HRBC-MOF-60) was first constructed by a selective protection approach of tannic acid (TN), which addresses the shortcomings of using sacrificial templates or corrosive agents. Afterwards, HRBC-NTO/N-C-60 was obtained in situ by annealing and alkalization of HRBC-MOF-60. The nitrogen-rich carbon with a HRBC-like structure has the ability to rapidly transport electrons, and its porous structure enables remarkable charge transfer. Benefiting from the grafted 3D N-doped porous carbon with a HRBC-like structure, well-dispersed 0D Na2Ti3O7 nanoparticles, and satisfactory bonding effects, HRBC-NTO/N-C-60 exhibited high specific capacitance and fast ionic and electronic diffusion kinetics. Moreover, HRBC-NTO/N-C-60 was well-suited for desalination by functioning as a cathode material for capacitive deionization (CDI), and delivering a high desalination capacity of 66.8 mg g-1 in 200 mg L-1 NaCl solution at 1.4 V. This work introduces an excellent high-performance candidate for electrochemical deionization as well as affording afflatus for accurately inventing OD-3D hierarchical materials with hollow structures.

| S-EPMC9019914 | biostudies-literature

Na3 Zr2 Si2 PO12 Solid Electrolyte Membrane for High-Performance Seawater Battery.

Project description:Seawater batteries (SWBs) have gained tremendous interest in the electrochemical energy storage research field because of their low cost, natural abundance, and potential use for long-duration energy storage. Advancing a SWB to demonstration projects is plagued by the poor electrochemical performance stemming from the poor interfaces of the solid electrolyte (SE), as well as the structural and chemical instabilities and sluggish ionic transport properties. In this study, the anode compartment of a surrogate SWB is constructed with a Na | SE | hard carbon configuration, and tailored dopants are introduced into the Nasicon-type Na3 Zr2 Si2 PO12 (NZSP) SE membrane. After doping with TiO2 , a much more densely packed pellet with uniformly distributed porous structure is obtained. Changes in surface chemistry and local structure in the bulk are observed, which are believed to contribute to the improved ionic conductivity and higher critical current density of the TiO2 -doped NZSP. Stable cycling performance with reversible capacities based on different Na storage mechanisms are also demonstrated.

| S-EPMC10265043 | biostudies-literature

Understanding the redox process upon electrochemical cycling of the P2-Na0.78Co1/2Mn1/3Ni1/6O2 electrode material for sodium-ion batteries.

Project description:Rechargeable sodium-ion batteries have recently attracted renewed interest as an alternative to Li-ion batteries for electric energy storage applications, because of the low cost and wide availability of sodium resources. Thus, the electrochemical energy storage community has been devoting increased attention to designing new cathode materials for sodium-ion batteries. Here we investigate P2- Na0.78Co1/2Mn1/3Ni1/6O2 as a cathode material for sodium ion batteries. The main focus is to understand the mechanism of the electrochemical performance of this material, especially differences observed in redox reactions at high potentials. Between 4.2 V and 4.5 V, the material delivers a reversible capacity which is studied in detail using advanced analytical techniques. In situ X-ray diffraction reveals the reversibility of the P2-type structure of the material. Combined soft X-ray absorption spectroscopy and resonant inelastic X-ray scattering demonstrates that Na deintercalation at high voltages is charge compensated by formation of localized electron holes on oxygen atoms.

| S-EPMC9814369 | biostudies-literature

Enhancing electrochemical performance of carbon fiber with lignin for flexible supercapacitors in PVA/H3PO4 matrix.

Project description:Lignin is an unlimited resource of an aromatic natural polymer useful for multiple applications, though its use remains limited due to the lack of technology developments. The introduction of lignin as coating of fibers and textile for composites is being recently studied with very promising results. Here, commercial woven carbon fibers (WCFs) have been superficially modified following an easy approach to introduce lignin and carbonize it to enhance the electrochemical performance of the fibers. The modified carbon fibers containing lignin were tested as electrodes using KCl 3 M as electrolyte, reaching 5 F/g at 10 mVs-1. A symmetric supercapacitor was fabricated using these electrodes, and a proof of concept based on a red and yellow light-emitting diode (LED) powered on and a bending test were done. The supercapacitor was able to recover 99% of its capacitance when returned to its original unbent position.

| S-EPMC11301100 | biostudies-literature

Niobium Nitride Nb4N5 as a New High-Performance Electrode Material for Supercapacitors.

Project description:Supercapacitors suffer either from low capacitance for carbon or derivate electrodes or from poor electrical conductivity and electrochemical stability for metal oxide or conducting polymer electrodes. Transition metal nitrides possess fair electrical conductivity but superior chemical stability, which may be desirable candidates for supercapacitors. Herein, niobium nitride, Nb4N5, is explored to be an excellent capacitive material for the first time. An areal capacitance of 225.8 mF cm-2, with a reasonable rate capability (60.8% retention from 0.5 to 10 mA cm-2) and cycling stability (70.9% retention after 2000 cycles), is achieved in Nb4N5 nanochannels electrode with prominent electrical conductivity and electrochemical activity. Faradaic pseudocapacitance is confirmed by the mechanistic studies, deriving from the proton incorporation/chemisorption reaction owing to the copious +5 valence Nb ions in Nb4N5. Moreover, this Nb4N5 nanochannels electrode with an ultrathin carbon coating exhibits nearly 100% capacitance retention after 2000 CV cycles, which is an excellent cycling stability for metal nitride materials. Thus, the Nb4N5 nanochannels are qualified for a candidate for supercapacitors and other energy storage applications.

| S-EPMC5115299 | biostudies-literature