Easy Preparation of Liposome@PDA Microspheres for Fast and Highly Efficient Removal of Methylene Blue from Water.

ABSTRACT: Mussel-inspired chemistry was usefully exploited here with the aim of developing a high-efficiency, environmentally friendly material for water remediation. A micro-structured material based on polydopamine (PDA) was obtained by using liposomes as templating agents and was used for the first time as an adsorbent material for the removal of methylene blue (MB) dye from aqueous solutions. Phospholipid liposomes were made by extrusion and coated with PDA by self-polymerization of dopamine under simple and mild conditions. The obtained Liposome@PDA microspheres were characterized by DLS and Zeta potential analysis, TEM microscopy, and FTIR spectroscopy. The effects of pH, temperature, MB concentration, amount of Liposome@PDA, and contact time on the adsorption process were investigated. Results showed that the highest adsorption capacity was obtained in weakly alkaline conditions (pH = 8.0) and that it could reach up to 395.4 mg g^-1 at 298 K. In addition, adsorption kinetics showed that the adsorption behavior fits a pseudo-second-order kinetic model well. The equilibrium adsorption data, instead, were well described by Langmuir isotherm. Thermodynamic analysis demonstrated that the adsorption process was endothermic and spontaneous (ΔG⁰ = -12.55 kJ mol^-1, ΔH⁰ = 13.37 kJ mol^-1) in the investigated experimental conditions. Finally, the applicability of Liposome@PDA microspheres to model wastewater and the excellent reusability after regeneration by removing MB were demonstrated.

SUBMITTER: De Leo V

PROVIDER: S-EPMC8584841 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Novel Superadsorbent Highly Porous Hydrogel Based on Arabic Gum and Acrylamide Grafts for Fast and Efficient Methylene Blue Removal.

Project description:Environmental pollution with dyes released from industrial effluent is one of the major and most critical problems in the world. To alleviate this issue, advanced and safe materials with fast and highly efficient dye removal should be designed. Great attention has been paid recently to hydrogels based on polysaccharides such as Arabic Gum (AG) grafted with polyacrylamide (PAM) and polyacrylic acid (PAA). These materials combine the merits of natural polymers such as biodegradability and non-toxicity with the high adsorption ability of PAM and PAA towards cationic dyes such as methylene blue (MB). Many previous works have been done to enhance three-dimensional (3D) structure and swelling ability of the graft copolymers by using a crosslinking agent or even adding nanomaterials as a filler inside the hydrogel matrix. However, these additives may negatively affect the adsorption ability, and few previous studies could reach 2000 mg/g of maximum MB capacity removal within a good period of time. In our work, we synthesized partially hydrolyzed polyacrylamide grafted Arabic gum (AG-g-PAM/PAA) to have both amide and carboxylate groups. The modified water dissolved graft product undergoes water in oil (W/O) emulsion using paraffin oil as the continuous phase and Triton X-100 as a stabilizing agent; then, the system was inversed to oil in water (O/W) emulsion by increasing the shear mixing rate and cross-linked using Epichlorohydrin (ECH). The precipitated graft product showed hierarchically interconnected micro and macropores' sponge like shape with fast water swelling and high MB adsorption capacity (2300 mg g-1) after 45 min at near neutral pH conditions.

| S-EPMC7077498 | biostudies-literature

Lignin Nanoparticles and Alginate Gel Beads: Preparation, Characterization and Removal of Methylene Blue.

Project description:A novel and effective green system consisting of deep eutectic solvent (DES) was proposed to prepare lignin nanoparticles (LNPs) without any lignin modification. The LNPs are obtained through the dialysis of the kraft lignin-DES solution. The particle size distribution, Zeta potential and morphology of the LNPs are characterized by using dynamic light scattering (DLS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The average diameter of LNPs is in the range 123.6 to 140.7 nm, and the LNPs show good stability and dispersibility in water. The composite beads composed of LNPs and sodium alginate (SA) are highly efficient (97.1%) at removing methylene blue (MB) from the aqueous solution compared to 82.9% and 77.4% by the SA/bulk kraft lignin composite and pure SA, respectively. Overall, the LNPs-SA bio-nanocomposite with high adsorption capacity (258.5 mg/g) could be useful in improving water quality and other related applications.

| S-EPMC8746983 | biostudies-literature

Synthesis of Magnetic Microspheres with Sodium Alginate and Activated Carbon for Removal of Methylene Blue.

Project description:Based on the adsorption performance of composite microspheres with activated carbon (AC) and sodium alginate (SA), as well as the magnetic property of Fe₃O₄, we designed and explored an efficient strategy to prepare a unique, multifunctional Fe₃O₄/AC/SA composite absorbent (MSA-AC) that extracted dye from aqueous solution. The composite exhibited the following advantages: rapid and simple to prepare, environmentally friendly process, low-cost, recyclability, and multi-functionality. The physicochemical properties of the prepared magnetic microspheres were measured, and methylene blue (MB) was selected to investigate the performance of the magnetic absorbent. The results showed a maximum adsorption capacity of 222.3 mg/g for MB. Adsorption studies revealed that the data of adsorption isotherms and kinetics fit the pseudo-second-order kinetic model and Langmuir isotherm model.

| S-EPMC5344609 | biostudies-other

Preparation and Characterization of Sludge-Based Magnetic Biochar by Pyrolysis for Methylene Blue Removal.

Project description:The development of low-cost adsorbent is an urgent need in the field of wastewater treatment. In this study, sludge-based magnetic biochar (SMB) was prepared by pyrolysis of sewage sludge and backwashing iron mud without any chemical agents. The samples were characterized by TGA, XRD, ICP, Organic element analysis, SEM, TEM, VSM and BET. Characterization analysis indicated that the magnetic substance in SMB was Fe3O4, and the saturation magnetization was 25.60 emu·g-1, after the adsorption experiment, SMB could be separated from the solution by a magnet. The batch adsorption experiment of methylene blue (MB) adsorption showed that the adsorption capacities of SMB at 298 K, 308 K and 318 K were 47.44 mg·L-1, 39.35 mg·L-1, and 25.85 mg·L-1, respectively. After one regeneration with hydrochloric acid, the maximum adsorption capacity of the product reached 296.52 mg·g-1. Besides, the adsorption kinetic described well by the pseudo-second order model revealed that the intraparticle diffusion was not just the only rate controlling step in adsorption process. This study gives a reasonable reference for the treatment of sewage sludge and backwashing iron mud. The product could be used as a low-cost adsorbent for MB removal.

| S-EPMC8539958 | biostudies-literature

One-Pot Synthesis of Cellulose/MXene/PVA Foam for Efficient Methylene Blue Removal.

Project description:Ti3C2Tx MXene has attracted considerable interest as a new emerging two-dimensional material for environmental remediation due to its high adsorption capacity. However, its use is greatly limited by its poor mechanical properties, low processability and recyclability, and the low dispersity of such powder materials. In this work, a porous adsorbent (C-CMP) containing cellulose nanocrystals (CNC), Ti3C2Tx MXene and polyvinyl alcohol (PVA) was prepared by a simple and environmentally-friendly foaming method. Glutaraldehyde was used as crosslinker to improve the mechanical properties and boost the adsorption efficiency of methylene blue (MB) molecules. Fourier transform infrared (FT-IR), elemental analysis (EDX) and thermogravimetric analysis (TGA) further confirmed that the preparation of the C-CMP foam and cross-linking reaction were successful. Scanning electron microscope (SEM) indicated that the macropores were distributed homogeneously. The adsorption experiment showed that maximum adsorption capacity of MB can reach 239.92 mg·g-1 which was much higher than anionic dye (methyl orange, 45.25 mg·g-1). The adsorption behavior fitted well with the Langmuir isotherm and pseudo-second-order kinetic models. Thermodynamic analysis indicated that the adsorption process was spontaneous and endothermic. Based on FT-IR, EDX and X-ray photoelectron spectroscopy (XPS) analysis, the adsorption mechanism between C-CMP and MB molecules was attributed to electrostatic interaction.

| S-EPMC9268378 | biostudies-literature

Ultra-Highly Efficient Removal of Methylene Blue Based on Graphene Oxide/TiO2/Bentonite Sponge.

Project description:An ultra-highly efficient Graphene Oxide/TiO2/Bentonite (GO/TiO2/Bent) sponge was synthesized using an in situ hydrothermal method. GO/TiO2/Bent sponge with a GO mass concentration of 10% exhibited the highest treatment efficiency of methylene blue (MB), combining adsorption and photocatalytic degradation, and achieved a maximum removal efficiency of 100% within about 70 min. To further prove the ultra-high removal capacity of the sponge, the concentration of MB in water increased to ten times the original concentration. At so high a MB concentration, the removal rate was still as high as 80% in 90 min. The photocatalytic mechanism of GO/TiO2/Bent sponge was discussed through XPS, PL and radicals quenching experiments. Here Bent can immobilize TiO2 and react with a photo-generated hole to increase the amount of hydroxyl radical; effectively enhancing the degradation of MB.GO sponge enlarges the sensitivity range of TiO2 to visible light by increasing the charge separation of TiO2 and reducing the recombination of photo-generated electron-hole pairs. Additionally, GO sponge with an interconnected porous structure provides an effective platform to immobilize TiO2/bent and makes them be easily recovered. The as-prepared sponge develops a simple and cost-effective strategy to realize the ultra-highly efficient treatment of dyes in wastewater.

| S-EPMC7078707 | biostudies-literature

Preparation and characterization of biopolymer-based adsorbents and their application for methylene blue removal from wastewater.

Project description:In the present study, four biopolymer-based materials consisting of native corn starch (CS), phosphate corn starch (PS), starch nanocrystals (SNCs), and phosphate corn starch nanocrystals (PSNCs) were synthesized and used for methylene blue (MB) removal as a function of various parameters, including initial MB concentration (C0, 10-500 mg L-1), adsorbent dosage (Cs, 0.02-0.15 g), contact time (t, 5-15 min), solution pH (2-11), and temperature (25-45 °C). The removal percentage of MB increased dramatically upon increasing the biopolymer dosage, temperature, and pH; while it decreased upon increasing the initial MB concentration. The adsorption behavior of biopolymer-based materials towards MB was found to be accurately described by the pseudo-second-order kinetic and Langmuir isotherm models. According to the Langmuir model, the maximum adsorption capacities of the adsorbents were ordered as follows: PSNCs (88.53 mg g-1) > SNCs (79.55 mg g-1) > PS (73.17 mg g-1) > CS (63.02 mg g-1). PSNCs was able to remove 96.8% and 76.5% of 20 mg L-1 MB in greywater and petrochemical wastewater, respectively, at an optimum pH of 9 and retained 86.42% of its usability even after five adsorption-desorption cycles. The analysis of the surface charge of the adsorbents before and after MB adsorption, combined with the FTIR spectrum of MB-saturated biopolymer-based materials, provided evidence that electrostatic interactions was the primary mechanism involved in the adsorption of MB. Meanwhile, hydrogen bonding and π-π interactions were found to have a minor contribution to the adsorption process. Based on the results, it can be inferred that PSNCs has promising potential as an adsorbent for the treatment of MB-containing wastewater, owing to its exceptional properties, which include high adsorption capacity, low cost, and applicability for multiple reuses.

| S-EPMC10570327 | biostudies-literature

Facile Preparation of Porous Carbon Derived from Pomelo Peel for Efficient Adsorption of Methylene Blue.

Project description:Pomelo peel waste-derived porous carbon (PPPC) was prepared by a facile one-step ZnCl2 activation method. The preparation parameters of PPPC were the mass ratio of ZnCl2 to pomelo peel of 2:1, carbonization temperature of 500 °C, and carbonization time of 1 h. This obtained PPPC possessed abundant macro-,meso-, and micro-porous structures, and a large specific surface area of 939.4 m2 g-1. Surprisingly, it had excellent adsorption ability for methylene blue, including a high adsorption capacity of 602.4 mg g-1 and good reusability. The adsorption isotherm and kinetic fitted with Langmuir and pseudo-second order kinetic models. This work provides a novel strategy for pomelo peel waste utilization and a potential adsorbent for treating dye wastewater.

| S-EPMC9144290 | biostudies-literature

Removal of silver nanoparticles by mussel-inspired Fe<sub>3</sub>O<sub>4</sub>@ polydopamine core-shell microspheres and its use as efficient catalyst for methylene blue reduction.

Project description:The removal of silver nanoparticles (AgNPs) from water is highly needed because of their increasing use and potential risk to the environment due to their toxic effects. Catalysis over AgNPs has received significant attention because of their highly catalytic performance. However, their use in practical applications is limited due to high cost and limited resources. Here, we present for the first time that the mussel-inspired Fe3O4@polydopamine (Fe3O4@PDA) nanocomposite can be used for efficient removal and recovery of AgNPs. Adsorption of AgNPs over Fe3O4@PDA was confirmed by TEM, FT-IR, XRD, TGA and magnetic property. The adsorption efficiency of AgNPs by Fe3O4@PDA was investigated as a function of pH, contact time, ionic strength and concentration of AgNPs. The kinetic data were well fitted to a pseudo-second order kinetic model. The isotherm data were well described by Langmuir model with a maximum adsorption capacity of 169.5 mg/g, which was higher than those by other adsorbents. Notably, the obtained AgNPs-Fe3O4@PDA exhibited highly catalytic activity for methylene blue reduction by NaBH4 with a rate constant of 1.44 × 10-3/s, which was much higher than those by other AgNPs catalysts. The AgNPs-Fe3O4@PDA promised good recyclability for at least 8 cycles and acid resistant with good stability.

| S-EPMC5311861 | biostudies-literature

Citrus Pectin-Derived Carbon Microspheres with Superior Adsorption Ability for Methylene Blue.

Project description:In this study, citrus pectin-derived, green, and tunable carbon microspheres with superior adsorption capacity and high adsorption rate, as well as good reusability toward methylene blue adsorption, were prepared by a facile hydrothermal method without any hazardous chemicals. The materials hold great potential for the treatment of methylene blue wastewater.

| S-EPMC5535227 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data