Facile and Quantitative Method for Estimating the Isolation Degree of Cellulose Nanocrystals (CNCs) Suspensions.

ABSTRACT: The isolation degree of cellulose nanocrystals (CNCs) suspensions calculated from the amount of sediments obtained with the centrifugation method can be estimated with turbidimetry, surface charge and dispersion analysis of the CNCs suspension. Three different types of raw cellulosic materials were used and carried out with an acid hydrolysis and mechanical disintegration. As the number of high-pressure homogenizer treatments increased, the isolation degree of CNCs from microcrystalline cellulose (MCC) increased from 2.3 to 99.6%, while the absorbencies from turbidimetric measurement of the CNCs suspension decreased, from 2.6 to 0.1 Abs units. Furthermore, the surface charges based on zeta potential measurements of the CNCs suspensions increased from -34.6 to -98.7 mV, but the heights of sediments from the CNCs suspensions were reduced, from 4.01 to 0.07 mm. Similar results were obtained for CNCs from softwood pulp (SWP) and cotton pulp (CP). These results show a direct correlation between yield, turbidity, surface charge and sedimentation of CNCs suspensions. Their correlation indices (0.9) were close to a maximal value of 1. This approach can be suggested as a facile and rapid estimation method for CNCs manufacturing process.

SUBMITTER: Lee M

PROVIDER: S-EPMC8585153 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Cellulose Nanocrystals (CNCs) from Corn Stalk: Activation Energy Analysis.

Project description:Cellulose nanocrystals (CNCs) were isolated from corn stalk using sulfuric acid hydrolysis, and their morphology, chemical structure, and thermal stability properties were characterized. The CNCs had an average length of 120.2 ± 61.3 nm and diameter of 6.4 ± 3.1 nm (L/D = 18.7). The degree of crystallinity of the CNCs increased to 69.20% from the 33.20% crystallinity of raw corn stalk fiber, while the chemical structure was well kept after sulfuric acid hydrolysis. Thermal stability analysis showed that the degradation temperature of the CNCs reached 239.5 °C, which was higher than that of the raw fiber but lower than that of the extracted cellulose. The average activation energy values for the CNCs, evaluated using the Friedman, Flynn-Wall-Ozawa (F-W-O) and Coats-Redfern methods, were 312.6, 302.8, and 309 kJ·mol-1 in the conversion range of 0.1 to 0.8. The isolated CNCs had higher values of activation energy than did the purified cellulose, which was attributed to the stronger hydrogen bonds present in the crystalline domains of CNCs than in those of cellulose. These findings can help better understand the thermal properties of polymer/CNC composites.

| S-EPMC5344553 | biostudies-other

Screen-Printed Glucose Sensors Modified with Cellulose Nanocrystals (CNCs) for Cell Culture Monitoring.

Project description:Glucose sensors are potentially useful tools for monitoring the glucose concentration in cell culture medium. Here, we present a new, low-cost, and reproducible sensor based on a cellulose-based material, 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO) oxidized-cellulose nanocrystals (CNCs). This novel biocompatible and inert nanomaterial is employed as a polymeric matrix to immobilize and stabilize glucose oxidase in the fabrication of a reproducible, operationally stable, highly selective, cost-effective, screen-printed glucose sensor. The sensors have a linear range of 0.1-2 mM (R2 = 0.999) and a sensitivity of 5.7 ± 0.3 µA cm-2?mM-1. The limit of detection is 0.004 mM, and the limit of quantification is 0.015 mM. The sensor maintains 92.3 % of the initial current response after 30 consecutive measurements in a 1 mM standard glucose solution, and has a shelf life of 1 month while maintaining high selectivity. We demonstrate the practical application of the sensor by monitoring the glucose consumption of a fibroblast cell culture over the course of several days.

| S-EPMC7557574 | biostudies-literature

Structure Selectivity of Alkaline Periodate Oxidation on Lignocellulose for Facile Isolation of Cellulose Nanocrystals.

Project description:Reported here for the first time is the alkaline periodate oxidation of lignocelluloses for the selective isolation of cellulose nanocrystals (CNCs). With the high concentrations as a potassium salt at pH?10, periodate ions predominantly exist as dimeric orthoperiodate ions (H2 I2 O10 4- ). With reduced oxidizing activity in alkaline solutions, dimeric orthoperiodate ions preferentially oxidized non-ordered cellulose regions. The alkaline surroundings promoted the degradation of these oxidized cellulose chains by ?-alkoxy fragmentation and generated CNCs. The obtained CNCs were uniform in size and generally contained carboxy groups. Furthermore, the reaction solution could be reused after regeneration of the periodate with ozone gas. This method allows direct production of CNCs from diverse sources, in particular lignocellulosic raw materials including sawdust (European beech and Scots pine), flax, and kenaf, in addition to microcrystalline cellulose and pulp.

| S-EPMC7027850 | biostudies-literature

Twist-Bend Stage in the Relaxation of Sheared Chiral Nematic Suspensions of Cellulose Nanocrystals.

Project description:Aqueous suspensions of cellulose nanocrystals (CNCs), prepared from natural cellulose by sulfuric acid hydrolysis, form stable chiral nematic suspensions above a critical CNC concentration. The chiral nematic organization may be preserved in films prepared from the suspensions by evaporation. However, shrinkage, gelation, and shear during film formation impair the optical properties of the dry film. In this article, we report an unusual behavior for a sample in which gelation occurred before the sample reached iridescent pitch values. In attempting to decouple changes in texture due to evaporation from those due to shear relaxation effects for this sample, we observed a transitory nematic-like texture that was induced by shear during the preparation of the sample for polarized light microscopy. We propose that the transition between chiral nematic and nematic structures involves a twist-bend-like intermediate and not an untwisting of the chiral nematic phase.

| S-EPMC6641273 | biostudies-literature

Towards the scalable isolation of cellulose nanocrystals from tunicates.

Project description:In order for sustainable nanomaterials such as cellulose nanocrystals (CNCs) to be utilized in industrial applications, a large-scale production capacity for CNCs must exist. Currently the only CNCs available commercially in kilogram scale are obtained from wood pulp (W-CNCs). Scaling the production capacity of W-CNCs isolation has led to their use in broader applications and captured the interest of researchers, industries and governments alike. Another source of CNCs with potential for commercial scale production are tunicates, a species of marine animal. Tunicate derived CNCs (T-CNCs) are a high aspect ratio CNC, which can complement commercially available W-CNCs in the growing global CNC market. Herein we report the isolation and characterization of T-CNCs from the tunicate Styela clava, an invasive species currently causing significant harm to local aquaculture communities. The reported procedure utilizes scalable CNC processing techniques and is based on our experiences from laboratory scale T-CNC isolation and pilot scale W-CNC isolation. To our best knowledge, this study represents the largest scale where T-CNCs have been isolated from any tunicate species, under any reaction conditions. Demonstrating a significant step towards commercial scale isolation of T-CNCs, and offering a potential solution to the numerous challenges which invasive tunicates pose to global aquaculture communities.

| S-EPMC7645590 | biostudies-literature

Isolation and Characterization of Cellulose Nanocrystals from Date Palm Waste.

Project description:This study presents the isolation, characterization, and kinetic analyses of cellulose nanocrystals (CNCs) from date palm waste in the United Arab Emirates. After bleaching date palm stem waste with acidified NaClO2 and delignification via NaOH treatments, cellulose was extracted. Mineral acid hydrolysis (62 wt % H2SO4) was performed at 45 °C for 45 min to produce crystalline nanocellulose. Fourier transform infrared (FTIR) and chemical composition analysis confirmed the removal of noncellulosic constituents. The crystallinity index increased gradually with chemical treatments, according to the obtained X-ray diffraction (XRD) results. Thermogravimetric analysis and differential scanning calorimetry results revealed that the CNC has high thermal stability. The Coats-Redfern method was used to determine the kinetic parameters. The kinetic analysis confirmed that CNC has more activation energy than cellulose and thus confirms its compact and resistive crystalline structure. This has been attributable to the stronger hydrogen bonding in CNC crystalline domains than that in cellulose crystalline domains. Scanning electron microscopy revealed that lignin and hemicellulose were eliminated after chemical pretreatments, and CNC with a rodlike shape was obtained after hydrolysis. Moreover, transmission electron microscopy confirmed the nanoscale of crystalline cellulose. ζ potential analysis indicated that the CNC afforded a stable suspension (-29.27 mV), which is less prone to flocculation. Kinetic analyses of cellulose and cellulose nanocrystals isolated from date palm waste are useful for making composites and designing selective pyrolysis reactors.

| S-EPMC9330260 | biostudies-literature

Effect of Process Conditions and Colloidal Properties of Cellulose Nanocrystals Suspensions on the Production of Hydrogel Beads.

Project description:The influence of the physical, rheological, and process parameters on the cellulose nanocrystal (CNC) drops before and after external gelation in a CaCl2 solution was investigated. The dominant role of the CNC's colloidal suspension properties, such as the viscous force, inertial, and surface tension forces in the fluid dynamics was quantitatively evaluated in the formation of drops and jellified beads. The similarity and difference between the behavior of carbohydrate polymers and rod-like crystallites such as CNC were enlightened. Pump-driven and centrifugally-driven external gelation approaches were followed to obtain CNC hydrogel beads with tunable size and regular shape. A superior morphological control-that is, a more regular shape and smaller dimension of the beads-were obtained by centrifugal force-driven gelation. These results suggest that even by using a simple set-up and a low-speed centrifuge device, the extrusion of a colloidal solution through a small nozzle under a centrifugal field is an efficient approach for the production of CNC hydrogel beads with good reproducibility, control over the bead morphology and size monodispersion.

| S-EPMC8125024 | biostudies-literature

Influence of Epoxidized Canola Oil (eCO) and Cellulose Nanocrystals (CNCs) on the Mechanical and Thermal Properties of Polyhydroxybutyrate (PHB)-Poly(lactic acid) (PLA) Blends.

Project description:Two major obstacles to utilizing polyhydroxybutyrate (PHB)-a biodegradable and biocompatible polymer-in commercial applications are its low tensile yield strength (<10 MPa) and elongation at break (~5%). In this work, we investigated the modification of the mechanical properties of PHB through the use of a variety of bio-derived additives. Poly(lactic acid) (PLA) and sugarcane-sourced cellulose nanocrystals (CNCs) were proposed as mechanical reinforcing elements, and epoxidized canola oil (eCO) was utilized as a green plasticizer. Zinc acetate was added to PHB and PLA blends in order to improve blending. Composites were mixed in a micro-extruder, and the resulting filaments were molded into 2-mm sheets utilizing a hot-press prior to characterization. The inclusion of the various additives was found to influence the crystallization process of PHB without affecting thermal stability. In general, the addition of PLA and, to a lesser degree, CNCs, resulted in an increase in the Young's modulus of the material, while the addition of eCO improved the strain at break. Overall, samples containing eCO and PLA (at concentrations of 10 wt %, and 25 wt %, respectively) demonstrated the best mechanical properties in terms of Young's modulus, tensile strength and strain at break.

| S-EPMC6631437 | biostudies-literature

Recycling Waste Cotton Cloths for the Isolation of Cellulose Nanocrystals: A Sustainable Approach.

Project description:There is an interest in the sustainable utilization of waste cotton cloths because of their enormous volume of generation and high cellulose content. Waste cotton cloths generated are disposed of in a landfill, which causes environmental pollution and leads to the waste of useful resources. In the present study, cellulose nanocrystals (CNCs) were isolated from waste cotton cloths collected from a landfill. The waste cotton cloths collected from the landfill were sterilized and cleaned using supercritical CO2 (scCO2) technology. The cellulose was extracted from scCO2-treated waste cotton cloths using alkaline pulping and bleaching processes. Subsequently, the CNCs were isolated using the H2SO4 hydrolysis of cellulose. The isolated CNCs were analyzed to determine the morphological, chemical, thermal, and physical properties with various analytical methods, including attenuated total reflection-Fourier transform-infrared spectroscopy (ATR-FTIR), field-emission scanning electron microscopy (FE-SEM), energy-filtered transmission electron microscopy (EF-TEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). The results showed that the isolated CNCs had a needle-like structure with a length and diameter of 10-30 and 2-6 nm, respectively, and an aspect ratio of 5-15, respectively. Additionally, the isolated CNCs had a high crystallinity index with a good thermal stability. The findings of the present study revealed the potential of recycling waste cotton cloths to produce a value-added product.

| S-EPMC7922772 | biostudies-literature

Isolation of Cellulose Nanocrystals from Banana Peel Using One-Pot Microwave and Mild Oxidative Hydrolysis System.

Project description:The current investigation deals with the application of a one-pot system to facilitate the production of cellulose nanocrystals (CNCs) from banana peel by a combination of microwave pre-treatment and mild oxidative hydrolysis with hydrogen peroxide (H2O2, 0-30 wt%) and sulfuric acid (H2SO4, 0-10%). H2O2 causes decolorization of the banana peel suspension from dark brown to light yellow, while further treatment with H2SO4 produces a white suspension, indicating successful removal of the non-cellulosic components from the banana peel. This finding was further supported by Fourier Transform Infrared (FTIR) spectroscopic analysis, which showed the gradual disappearance of lignin and hemicellulose peaks with increasing H2O2 and H2SO4 concentrations. The CNCs has considerably high crystallinity, with the highest crystallinity (~85%) being obtained at 6% H2SO4. Therefore, CNCs obtained at 6% H2SO4 were selected for further characterization. Scanning Electron Microscope (SEM) analysis confirmed the disintegration of the cellulose fibres into small fragments after hydrolysis. Transmission Electron Microscope (TEM) and Atomic Force Microscope (AFM) analyses revealed the spherical shape of the CNCs with an average size of approximately 20 nm. The CNCs have good stability with zeta potential of -42.9 mV. Findings from this study suggest that the combination of microwave pre-treatment and oxidative hydrolysis with 30 wt% H2O2 and 6% H2SO4, which is about 11 times lower than the commonly used H2SO4 concentration, is proven effective for the isolation of CNCs from banana peel. These observations are expected to provide insight into a facile and environmentally benign alternative to the conventional CNCs isolation method, using abundant and underutilized agricultural waste as feedstock.

| S-EPMC9565709 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data