3D Printing of Thermal Insulating Polyimide/Cellulose Nanocrystal Composite Aerogels with Low Dimensional Shrinkage

ABSTRACT: Polyimide (PI)-based aerogels have been widely applied to aviation, automobiles, and thermal insulation because of their high porosity, low density, and excellent thermal insulating ability. However, the fabrication of PI aerogels is still restricted to the traditional molding process, and it is often challenging to prepare high-performance PI aerogels with complex 3D structures. Interestingly, renewable nanomaterials such as cellulose nanocrystals (CNCs) may provide a unique approach for 3D printing, mechanical reinforcement, and shape fidelity of the PI aerogels. Herein, we proposed a facile water-based 3D printable ink with sustainable nanofillers, cellulose nanocrystals (CNCs). Polyamic acid was first mixed with triethylamine to form an aqueous solution of polyamic acid ammonium salts (PAAS). CNCs were then dispersed in the aqueous PAAS solution to form a reversible physical network for direct ink writing (DIW). Further freeze-drying and thermal imidization produced porous PI/CNC composite aerogels with increased mechanical strength. The concentration of CNCs needed for DIW was reduced in the presence of PAAS, potentially because of the depletion effect of the polymer solution. Further analysis suggested that the physical network of CNCs lowered the shrinkage of aerogels during preparation and improved the shape-fidelity of the PI/CNC composite aerogels. In addition, the composite aerogels retained low thermal conductivity and may be used as heat management materials. Overall, our approach successfully utilized CNCs as rheological modifiers and reinforcement to 3D print strong PI/CNC composite aerogels for advanced thermal regulation.

SUBMITTER: Feng C

PROVIDER: S-EPMC8588507 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Cellulose Diacetate Aerogels with Low Drying Shrinkage, High-Efficient Thermal Insulation, and Superior Mechanical Strength.

Project description:The inherent characteristics of cellulose-derived aerogels, such as their natural abundance and environmental friendliness, make them highly interesting. However, its significant shrinkage before and after the supercritical drying procedure and low mechanical strength limit its potential application. Here, we propose a strategy to prepare cellulose diacetate aerogels (CDAAs) with low drying shrinkage, exceptional thermal insulation, and superior mechanical strength. The low drying shrinkage (radial drying shrinkage of 1.4%) of CDAAs is attributed to their relative strong networking skeletons, which are greatly formed by tert-butanol solvent exchange in exerting the interaction of reducing the surface tension force. In this case, CDAAs are eventually endowed with the low bulk density of 0.069 g cm-3 as well. Additionally, as-prepared CDAAs possess an abundant three-dimensional networking structure whose pore size is concentrated in the diameter range of ~50 nm, and the result above is beneficial for improving the thermal insulation performance (thermal conductivity of 0.021 W m-1 K-1 at ambient environmental and pressure conditions). On the other hand, the optimal compressive stresses of CDAAs at 3% and 5% strain are 0.22 and 0.27 MPa respectively, indicating a mechanically well robustness. The above evidence demonstrates indeed the exceptional thermal insulation and superior compressive properties of CDAAs. This work may provide a new solution for developing a kind of high-performance cellulose-derived aerogel in the future.

| S-EPMC10970052 | biostudies-literature

Cellulose Nanofiber Biotemplated Palladium Composite Aerogels.

Project description:Noble metal aerogels offer a wide range of catalytic applications due to their high surface area and tunable porosity. Control over monolith shape, pore size, and nanofiber diameter is desired in order to optimize electronic conductivity and mechanical integrity for device applications. However, common aerogel synthesis techniques such as solvent mediated aggregation, linker molecules, sol⁻gel, hydrothermal, and carbothermal reduction are limited when using noble metal salts. Here, we present the synthesis of palladium aerogels using carboxymethyl cellulose nanofiber (CNF) biotemplates that provide control over aerogel shape, pore size, and conductivity. Biotemplate hydrogels were formed via covalent cross linking using 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide hydrochloride (EDC) with a diamine linker between carboxymethylated cellulose nanofibers. Biotemplate CNF hydrogels were equilibrated in precursor palladium salt solutions, reduced with sodium borohydride, and rinsed with water followed by ethanol dehydration, and supercritical drying to produce freestanding aerogels. Scanning electron microscopy indicated three-dimensional nanowire structures, and X-ray diffractometry confirmed palladium and palladium hydride phases. Gas adsorption, impedance spectroscopy, and cyclic voltammetry were correlated to determine aerogel surface area. These self-supporting CNF-palladium aerogels demonstrate a simple synthesis scheme to control porosity, electrical conductivity, and mechanical robustness for catalytic, sensing, and energy applications.

| S-EPMC6100374 | biostudies-literature

Facile synthesis of super-thermal insulating polyimide aerogel-like films.

Project description:Thermal superinsulation materials play a key role in reducing energy consumption. In this article, flexible polyimide aerogel-like films are developed by a facile non-solvent-induced phase separation combined with ambient drying method. The pore structure and insulation properties are well controlled by changing the compositions of the coagulation bath. Polyimide films with macro-nano hierarchical pore structure and uniform nanopores are prepared by adjusting the content of water and alcohol as the non-solvent. The relationship between the insulation performance and textured structure of polyimide was studied. After optimization, the produced film achieved a low thermal conductivity of 0.019 W⋅m-1·K-1 but good tensile strength of 89.6 MPa, compared favorably with literature results. Hence, this article demonstrates that application of the facile phase inversion method to prepare porous polymers can be expanded from desalination or gas separation fields to insulation for energy-saving purposes.

| S-EPMC9732405 | biostudies-literature

Lightweight, Anisotropic, Compressible, and Thermally-Insulating Wood Aerogels with Aligned Cellulose Fibers.

Project description:The growing demand for lightweight, renewable, and excellent thermal insulation materials has fueled a search for high performance biomass materials with good mechanical compressibility and ultralow thermal conductivity. We propose a fabrication method for making a lightweight, anisotropic, and compressible wood aerogel with aligned cellulose fibers by a simple chemical treatment. The wood aerogel was mainly composed of highly aligned cellulose fibers with a relative crystallinity of 77.1%. The aerogel exhibits a low density of 32.18 mg/cm3 and a high specific surface area of 31.68 m2/g due to the removal of lignin and hemicellulose from the wood. Moreover, the multilayer structure of the aerogel was formed under the restriction of wood rays. Combined with a nanoscale pore, the aerogel presents good compressibility and an ultralow thermal conductivity of 0.033 W/mK. These results show that the wood aerogel is a high quality biomass material with a potential function of thermal insulation through optimizing structures.

| S-EPMC7022930 | biostudies-literature

Thermal conductivity enhancement in electrospun poly(vinyl alcohol) and poly(vinyl alcohol)/cellulose nanocrystal composite nanofibers.

Project description:The thermal conductivity enhancement of neat poly(vinyl alcohol) and poly(vinyl alcohol) (PVA)/cellulose nanocrystal (CNC) composite was attempted via electrospinning. The suspended microdevice technique was applied to measure the thermal conductivity of electrospun nanofibers (NFs). Neat PVA NFs and PVA/CNC NFs with a diameter of approximately 200 nm showed thermal conductivities of 1.23 and 0.74 W/m-K, respectively, at room temperature, which are higher than that of bulk PVA by factors of 6 and 3.5, respectively. Material characterization by Fourier transform infrared spectroscopy, differential scanning calorimetry, and thermogravimetric analysis confirmed that the thermal conductivity of the PVA/CNC NFs was enhanced by the reinforcement of their backbone rigidity, while that of the neat PVA NFs was attributed to the increase in their crystallinity that occurred during the electrospinning.

| S-EPMC6395720 | biostudies-literature

Chemically Cross-Linked Cellulose Nanocrystal Aerogels for Effective Removal of Cation Dye.

Project description:In this study, porous aerogels were prepared by directional freeze-drying via cross-linking cellulose nanocrystals (CNCs) with poly(methyl vinyl ether-co-maleic acid) (PMVEMA) and poly(ethylene glycol) (PEG). The thermal properties and physical adsorption performance toward cation methylene blue dye of the obtained CNC aerogels were investigated. The maximum degradation temperature was increased from 324°C of CNCs to 355°C of cross-linked CNC aerogels. The dye adsorption isotherm results showed that the maximum methylene blue adsorption capacity of CNC aerogels was 116.2 mg g-1, according to the Langmuir model, which was mainly due to the electrostatic attractions between negatively charged carboxyl groups or sulfonate groups on the CNC aerogles and cation MB molecules. The reusability test showed that the CNC aerogels contained the same dye adsorption performance in five adsorption/desorption cycles. Overall, this study described an ideal alternative for water purification with high dye adsorption capacity and enhanced physical performance.

| S-EPMC7359072 | biostudies-literature

Super-Insulating Transparent Polyisocyanurate-Polyurethane Aerogels: Analysis of Thermal Conductivity and Mechanical Properties.

Project description:A family of transparent polyisocyanurate-polyurethane (PUR-PIR) aerogels with an interesting combination of physical properties were synthesized. First, their textural properties were analyzed aiming to study catalyst influence on the final porous structures and densities. Their thermal conductivities were measured at different temperatures allowing observation of a clear trend relating the initial formulation with the porous structure and reaching values as low as 12 mW/mK, the lowest found in the literature for aerogels based on this polymer matrix. Contributions to thermal conductivity were calculated, improving the understanding of the porous structure-insulating performance relationship. Moreover, their mechanical properties were studied (elastic modulus, stress at different strains and elastic behavior). The aerogels showed tunable stiffness (elastic modulus from 6.32 to 0.13 MPa) by changing the catalyst concentration and significant elasticity. Thus, super-insulating transparent PUR-PIR aerogels with tailored mechanical properties were obtained opening a wide range of potential applications in the energy, building, automotive and aeronautical sectors, among others. The exceptional insulation of silica aerogels was reached at the same time that their general brittleness was improved while keeping good transparency to visible light (85%, 650 nm). Therefore, these aerogels may constitute an alternative to silica aerogels.

| S-EPMC9320143 | biostudies-literature

Effect of Acetylation of Two Cellulose Nanocrystal Polymorphs on Processibility and Physical Properties of Polylactide/Cellulose Nanocrystal Composite Film.

Project description:Polylactide (PLA) has become a popular alternative for petroleum-based plastics to reduce environmental pollution. The broader application of PLA is hampered by its brittle nature and incompatibility with the reinforcement phase. The aim of our work was to improve the ductility and compatibility of PLA composite film and investigate the mechanism by which nanocellulose enhances PLA polymer. Here, we present a robust PLA/nanocellulose hybrid film. Two different allomorphic cellulose nanocrystals (CNC-I and CNC-III) and their acetylated products (ACNC-I and ACNC-III) were used to realize better compatibility and mechanical performance in a hydrophobic PLA matrix. The tensile stress of the composite films with 3% ACNC-I and ACNC-III increased by 41.55% and 27.22% compared to pure PLA film, respectively. Compared to the CNC-I or CNC-III enhanced PLA composite films, the tensile stress of the films increased by 45.05% with 1% ACNC-I and 56.15% with 1% ACNC-III. In addition, PLA composite films with ACNCs showed better ductility and compatibility because the composite fracture gradually transitioned to a ductile fracture during the stretching process. As a result, ACNC-I and ACNC-III were found to be excellent reinforcing agents for the enhancement of the properties of polylactide composite film, and the replacement some petrochemical plastics with PLA composites would be very promising in actual life.

| S-EPMC10302014 | biostudies-literature

Cellulose Nanocrystal Aerogels as Electrolyte Scaffolds for Glass and Plastic Dye-Sensitized Solar Cells.

Project description:The fabrication, thickness, and structure of aerogel films composed of covalently cross-linked cellulose nanocrystals (CNCs) and poly(oligoethylene glycol methacrylate) (POEGMA) were optimized for use as electrolyte absorbers in dye-sensitized solar cells (DSSCs). The aerogel films were cast directly on transparent conducting counter electrode substrates (glass and flexible poly(ethylene terephthalate) plastic) and then used to absorb drop-cast liquid electrolyte, thus providing an alternative method of filling electrolyte in DSSCs. This approach eliminates the use of electrolyte-filling holes, which are a typical pathway of electrolyte leakage, and furthermore enables a homogeneous distribution of electrolyte components within the photoelectrode. Unlike typical in situ electrolyte gelation approaches, the phase inversion method used here results in a highly porous (>99%) electrolyte scaffold with excellent ionic conductivity and interfacial properties. DSSCs prepared with CNC-POEGMA aerogels reached similar power conversion efficiencies as compared to liquid electrolyte devices, indicating that the aerogel does not interfere with the operation of the device. These aerogels retain their structural integrity upon bending, which is critical for their application in flexible devices. Furthermore, the aerogels demonstrate impressive chemical and mechanical stability in typical electrolyte solvents because of their stable covalent cross-linking. Overall, this work demonstrates that the DSSC fabrication process can be simplified and made more easily upscalable by taking advantage of CNCs, being an abundant and sustainable bio-based material.

| S-EPMC6752057 | biostudies-literature

Hierarchically Multifunctional Polyimide Composite Films with Strongly Enhanced Thermal Conductivity.

Project description:The development of lightweight and integration for electronics requires flexible films with high thermal conductivity and electromagnetic interference (EMI) shielding to overcome heat accumulation and electromagnetic radiation pollution. Herein, the hierarchical design and assembly strategy was adopted to fabricate hierarchically multifunctional polyimide composite films, with graphene oxide/expanded graphite (GO/EG) as the top thermally conductive and EMI shielding layer, Fe3O4/polyimide (Fe3O4/PI) as the middle EMI shielding enhancement layer and electrospun PI fibers as the substrate layer for mechanical improvement. PI composite films with 61.0 wt% of GO/EG and 23.8 wt% of Fe3O4/PI exhibits high in-plane thermal conductivity coefficient (95.40 W (m K)-1), excellent EMI shielding effectiveness (34.0 dB), good tensile strength (93.6 MPa) and fast electric-heating response (5 s). The test in the central processing unit verifies PI composite films present broad application prospects in electronics fields.

| S-EPMC8664909 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data