Nanocellulose Xerogel as Template for Transparent, Thick, Flame-Retardant Polymer Nanocomposites.

ABSTRACT: Cellulose nanofibers (CNFs) have excellent properties, such as high strength, high specific surface areas (SSA), and low coefficients of thermal expansion (CTE), making them a promising candidate for bio-based reinforcing fillers of polymers. A challenge in the field of CNF-reinforced composite research is to produce strong and transparent CNF/polymer composites that are sufficiently thick for use as load-bearing structural materials. In this study, we successfully prepared millimeter-thick, transparent CNF/polymer composites using CNF xerogels, with high porosity (~70%) and high SSA (~350 m² g^-1), as a template for monomer impregnation. A methacrylate was used as the monomer and was cured by UV irradiation after impregnation into the CNF xerogels. The CNF xerogels effectively reinforced the methacrylate polymer matrix, resulting in an improvement in the flexural modulus (up to 546%) and a reduction in the CTE value (up to 78%) while maintaining the optical transparency of the matrix polymer. Interestingly, the composites exhibited flame retardancy at high CNF loading. These unique features highlight the applicability of CNF xerogels as a reinforcing template for producing multifunctional and load-bearing polymer composites.

SUBMITTER: Sakuma W

PROVIDER: S-EPMC8619435 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

A Novel Flame-Retardant, Smoke-Suppressing, and Superhydrophobic Transparent Bamboo.

Project description:Silica glass, known for its brittleness, weight, and non-biodegradable nature, faces challenges in finding suitable alternatives. Transparent wood, made by infusing polymers into wood, shows promise but is hindered by limited availability of wood in China and fire risks associated with its use. This study explores the potential of utilizing bamboo, which has a shorter growth cycle, as a valuable resource for developing flame-retardant, smoke-suppressing, and superhydrophobic transparent bamboo. A 3-layered flame-retardant barrier, composed of a top silane layer, an intermediate layer of SiO2 formed through hydrolysis-condensation of Na2SiO3 on the surface, and an inner layer of Na2SiO3, has been confirmed to be effective in reducing heat release, slowing flame spread, and inhibiting the release of combustible volatiles, toxic smoke, and CO. Compared to natural bamboo and other congeneric transparent products, the transparent bamboo displays remarkable superiority, with the majority of parameters being notably lower by an entire order of magnitude. It achieves a long ignition time of 116 s, low total heat release (0.7 MJ/m2), low total smoke production (0.063 m2), and low peak CO concentration (0.008 kg/kg). Moreover, when used as a substrate for perovskite solar cells, the transparent bamboo displays the potential to act as a light management layer, leading to a marked efficiency enhancement of 15.29%. The excellent features of transparent bamboo make it an enticing choice for future advancements in flame-retardant glasses and optical devices.

| S-EPMC10865110 | biostudies-literature

Thermal and Flame Retardant Properties of Phosphate-Functionalized Silica/Epoxy Nanocomposites.

Project description:We report a flame retardant epoxy nanocomposite reinforced with 9,10-dihydro-9-oxa-10-phosphaphenantrene-10-oxide (DOPO)-tethered SiO2 (DOPO-t-SiO2) hybrid nanoparticles (NPs). The DOPO-t-SiO2 NPs were successfully synthesized through surface treatment of SiO2 NPs with (3-glycidyloxypropyl)trimethoxysilane (GPTMS), followed by a click reaction between GPTMS on SiO2 and DOPO. The epoxy nanocomposites with DOPO-t-SiO2 NPs as multifunctional additive exhibited not only high flexural strength and fracture toughness but also excellent flame retardant properties and thermal stability, compared to those of pristine epoxy and epoxy nanocomposites with a single additive of SiO2 or DOPO, respectively. Our approach allows a facile, yet effective strategy to synthesize a functional hybrid additive for developing flame retardant nanocomposites.

| S-EPMC7730795 | biostudies-literature

Synergistic Combination of Dual Clays in Multilayered Nanocomposites for Enhanced Flame Retardant Properties

Project description: Not available

| S-EPMC10870267 | biostudies-literature

Acetylation of Nanocellulose: Miscibility and Reinforcement Mechanisms in Polymer Nanocomposites.

Project description:The improvement of properties in nanocomposites obtained by topochemical surface modification, e.g., acetylation, of the nanoparticles is often ascribed to improved compatibility between the nanoparticle and the matrix. It is not always clear however what is intended: specific interactions at the interface leading to increased adhesion or the miscibility between the nanoparticle and the polymer. In this work, it is demonstrated that acetylation of cellulose nanocrystals greatly improves mechanical properties of their nanocomposites with polycaprolactone. In addition, molecular dynamics simulations with a combination of potential of mean force calculations and computational alchemy are employed to analyze the surface energies between the two components. The work of adhesion between the two phases decreases with acetylation. It is discussed how acetylation can still contribute to the miscibility, which leads to a stricter use of the concept of compatibility. The integrated experimental-modeling toolbox used has wide applicability for assessing changes in the miscibility of polymer nanocomposites.

| S-EPMC10811682 | biostudies-literature

Development of a Flame Retardant and an Organohalogen Flame Retardant Chemical Inventory

Project description:There have been many attempts to compile comprehensive lists of flame retardants. However, this goal has proven challenging due to the heterogeneity of compounds that can be used as flame retardants coupled with changes in formulation chemistry over time. Flame retardants have been the focus of many recent existing hazard, exposure, and risk assessments. These assessments have been class-based or for individual chemical substances. Here, diverse sets of publicly available data sources from governmental organizations and the open literature were compiled to develop an inventory of chemicals used as flame retardants and organohalogen flame retardants. The chemical substances from these data sources were mapped to appropriate chemical identifiers via manual curation and deduplicated. Despite different data sources containing a large number of overlapping chemical substances, compiling information from multiple data sources was found to increase the breadth of potential flame retardant chemistries. The flame retardant and organohalogen flame retardant inventories were developed as a resource for scientists interested in better understanding properties of flame retardant and organohalogen flame retardant classes. Measurement(s)chemical use informationTechnology Type(s)manual and automated literature collection

| S-EPMC9192637 | biostudies-literature

Influence of Zinc Oxide Nanoparticles and Char Forming Agent Polymer on Flame Retardancy of Intumescent Flame Retardant Coatings.

Project description:Zinc oxide nanoparticles (ZnO NPs) were synthesized by a precipitation method, and a new charring-foaming agent (CFA) N-ethanolamine triazine-piperazine, melamine polymer (ETPMP) was synthesized via nucleophilic substitution reaction by using cyanuric chloride, ethanolamine, piperazine, and melamine as precursor molecules. FTIR and energy-dispersive X-ray spectroscopy (EDS) studies were employed to characterize and confirm the synthesized ETPMP structure. New intumescent flame retardant epoxy coating compositions were prepared by adding ammonium polyphosphate (APP), ETPMP, and ZnO NPs into an epoxy resin. APP and ETPMP were fixed in a 2:1 w/w ratio and used as an intumescent flame-retardant (IFR) system. ZnO NPs were loaded as a synergistic agent in different amounts into the IFR coating system. The synergistic effects of ZnO NPs on IFR coatings were systematically evaluated by limited oxygen index (LOI) tests, vertical burning tests (UL-94 V), TGA, cone calorimeter tests, and SEM. The obtained results revealed that a small amount of ZnO NPs significantly increased the LOI values of the IFR coating and these coatings had a V-0 ratings in UL-94 V tests. From the TGA data, it is clear that the addition of ZnO NPs could change the thermal degradation behaviors of coatings with increasing char residue percentage at high temperatures. Cone calorimeter data reported that ZnO NPs could decrease the combustion parameters including peak heat release rates (PHRRs), and total heat release (THR) rates. The SEM results showed that ZnO NPs could enhance the strength and the compactness of the intumescent char, which restricted the flow of heat and oxygen.

| S-EPMC7022803 | biostudies-literature

Controlling Miscibility of the Interphase in Polymer-Grafted Nanocellulose/Cellulose Triacetate Nanocomposites.

Project description:The miscibility at the interphase of polymer-grafted nanocellulose/cellulose triacetate (CTA) composite films was tailored using different casting solvents. The polymer-grafted cellulose nanofibrils were prepared by modifying surfaces of 2,2,6,6-tetramethylpiperidine-1-oxyl-oxidized nanocellulose with amine-terminated poly(ethylene glycol) (PEG). The PEG-grafted nanocelluloses were individually dispersed in dichloromethane, 1,4-dioxane, and N,N-dimethylacetamide. The PEG-grafted nanocellulose/CTA composite films were prepared by mixing the nanocellulose dispersion and CTA solution and subsequent casting-drying. The miscibility of PEG and CTA at the interphase of the composite was controlled by controlling the solvent, which was confirmed by dynamic mechanical analysis. All the composite films showed high optical transparency. However, the mechanical properties of the composites differed because of the difference in the PEG/CTA interfacial miscibility. The composite films with better PEG/CTA interfacial miscibility showed higher Young's modulus, strength, and toughness. This interfacial design technique paves the way to exploiting the reinforcing potential of highly transparent and hydrophobic surface-grafted nanocellulose/polymer composite materials.

| S-EPMC7513333 | biostudies-literature

Synergistic Flame Retardant Effect of an Intumescent Flame Retardant Containing Boron and Magnesium Hydroxide.

Project description:In this study, to develop an organic/inorganic synergistic flame retardant and to reduce the dosage and cost of flame retardants, organic/inorganic synergistic flame retardants, hexakis(4-boronic acid-phenoxy)-cyclophosphazene (CP-6B), and magnesium hydroxide (MH) were chosen. The flame retardant properties of CP-6B/MH in epoxy resin (EP) were discussed. EP/CP-6B/MH had better flame retardancy and heat resistance compared with EP/CP-6B and EP/MH. A limiting oxygen index of EP/3.0%CP-6B/0.5%MH of 31.9% was achieved, and vertical burning V-0 rating was achieved. Compared with EP, the cone calorimeter dates of EP/CP-6B/MH decreased. CP-6B/MH inhibited combustion and did little to damage mechanical properties. Besides, the flame retardant mechanism was studied by scanning electron microscopy, energy-dispersive X-ray spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and pyrolysis-gas chromatography-mass spectrometry. CP-6B/MH exerted good synergistic effects.

| S-EPMC6648587 | biostudies-literature

Suppression of Smoldering of Calcium Alginate Flame-Retardant Paper by Flame-Retardant Polyamide-66.

Project description:Calcium alginate (Ca-Alg) fibers are renewable fibers obtained from the ocean with essential flame retardancy, which have recently been applied as components of flame-retardant paper. However, the application of Ca-Alg fibers is limited because of their tendency to smolder. Therefore, composites papers were fabricated by blending using flame-retardant polyamide-66 (FR-PA), with a 5 wt% content of phosphorous flame retardant, which will form molten carbon during combustion. When the FR-PA content is 30% of the composite paper, FR-PA forms a compact carbon layer on the surface of the Ca-Alg fibers during combustion, which isolates the mass/heat transfer and effectively suppresses the smoldering of Ca-Alg. This consists of a condensed flame retardant mechanism. Furthermore, the combustion and thermal degradation behavior of paper were analyzed by cone calorimetry (CONE), TG and TG-IR. Ca-Alg in the composite paper decomposed and released CO2 before ignition, which delayed the ignition time. Simultaneously, the FR-PA contained in the composite paper effectively inhibited the combustion of volatile combustibles in the gas phase. Overall, FR-PA and Ca-Alg improve the thermal stability of the composite paper in different temperature regions under air atmosphere. Ca-Alg reduces the formation of aromatic products and NH3 in the composite paper under N2 atmosphere. Ca-Alg-based paper with excellent flame retardancy was successfully prepared.

| S-EPMC7866267 | biostudies-literature

Silicon/nitrogen synergistically reinforced flame-retardant PA6 nanocomposites with simultaneously improved anti-dripping and mechanical properties.

Project description:A facile route of 'copolymerization/blending' was proposed to fabricate silicon/nitrogen synergistically reinforced flame-retardant PA6 nanocomposites with simultaneously improved anti-dripping and mechanical properties. Firstly, a persistently inherent flame-retardant PA6 (FR-PA6), with 1,3-bis(3-aminopropyl)tetramethyl disiloxane (MSDS), was synthesized via controllable amidation and a polycondensation reaction. Melamine cyanurate (MCA) nanoparticles as a 'gas phase' synergistic agent were then added into FR-PA6 to further improve its flame retardancy. The primarily obtained FR-PA6 could be extinguished after a few melt droplets dropped as ignited, and passed the V-2 rating with enhanced mechanical properties, while PA6 had no rating (NR). The prepared FR-PA6/MCA nanocomposites could attain a limiting oxygen index (LOI) value of 32.7%, and passed the V-0 level with only 1 melting droplet with similar mechanical properties to PA6. Accordingly, the special 'condensed-gas phase' synergistic flame-retardant mechanism of FR-PA6/MCA nanocomposites was proposed through studying the residues and pyrolysis volatiles. This work provided a facile route as a model for developing functional PA6 for diverse engineering applications.

| S-EPMC9061166 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data