Mechanically Robust Flexible Multilayer Aramid Nanofibers and MXene Film for High-Performance Electromagnetic Interference Shielding and Thermal Insulation.

ABSTRACT: In order to overcome the various defects caused by the limitations of solid metal as a shielding material, the development of electromagnetic shielding materials with flexibility and excellent mechanical properties is of great significance for the next generation of intelligent electronic devices. Here, the aramid nanofiber/Ti₃C₂T_x MXene (ANF/MXene) composite films with multilayer structure were successfully prepared through a simple alternate vacuum-assisted filtration (AVAF) process. With the intervention of the ANF layer, the multilayer-structure film exhibits excellent mechanical properties. The ANF2/MXene1 composite film exhibits a tensile strength of 177.7 MPa and a breaking strain of 12.6%. In addition, the ANF5/MXene4 composite film with a thickness of only 30 μm exhibits an electromagnetic interference (EMI) shielding efficiency of 37.5 dB and a high EMI-specific shielding effectiveness value accounting for thickness (SSE/t) of 4718 dB·cm² g^-1. Moreover, the composite film was excellent in heat-insulation performance and in avoiding light-to-heat conversion. No burning sensation was produced on the surface of the film with a thickness of only 100 μm at a high temperature of 130 °C. Furthermore, the surface of the film was only mild when touched under simulated sunlight. Therefore, our multilayer-structure film has potential significance in practical applications such as next-generation smart electronic equipment, communications, and military applications.

SUBMITTER: Zhou J

PROVIDER: S-EPMC8620062 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Super-Tough and Environmentally Stable Aramid. Nanofiber@MXene Coaxial Fibers with Outstanding Electromagnetic Interference Shielding Efficiency.

Project description:Although electrically conductive and hydrophilic MXene sheets are promising for multifunctional fibers and electronic textiles, it is still a challenge to simultaneously enhance both conductivity and mechanical properties of MXene fibers because of the high rigidity of MXene sheets and insufficient inter-sheet interactions. Herein, we demonstrate a core-shell wet-spinning methodology for fabricating highly conductive, super-tough, ultra-strong, and environmentally stable Ti3C2Tx MXene-based core-shell fibers with conductive MXene cores and tough aramid nanofiber (ANF) shells. The highly orientated and low-defect structure endows the ANF@MXene core-shell fiber with super-toughness of ~ 48.1 MJ m-3, high strength of ~ 502.9 MPa, and high conductivity of ~ 3.0 × 105 S m-1. The super-tough and conductive ANF@MXene fibers can be woven into textiles, exhibiting an excellent electromagnetic interference (EMI) shielding efficiency of 83.4 dB at a small thickness of 213 μm. Importantly, the protection of the ANF shells provides the fibers with satisfactory cyclic stability under dynamic stretching and bending, and excellent resistance to acid, alkali, seawater, cryogenic and high temperatures, and fire. The oxidation resistance of the fibers is demonstrated by their well-maintained EMI shielding performances. The multifunctional core-shell fibers would be highly promising in the fields of EMI shielding textiles, wearable electronics and aerospace.

| S-EPMC9035413 | biostudies-literature

Multifunctional MXene/Aramid Nanofiber Composite Films for Efficient Electromagnetic Interference Shielding and Repeatable Early Fire Detection.

Project description:Rapid development of highly integrated electronic and telecommunication devices has led to urgent demands for electromagnetic interference (EMI) shielding materials that incorporate flame retardancy, and more desirably the early fire detection ability, due to the potential fire hazards caused by heat propagation and thermal failure of the devices during operation. Here, multifunctional flexible films having the main dual functions of high EMI shielding performance and repeatable fire detection ability are fabricated by vacuum filtration of the mixture of MXene and aramid nanofiber (ANF) suspensions. ANFs serve to reinforce MXene films via the formation of hydrogen bonding between the carbonyl groups of ANFs and the hydroxyl groups of MXene. When the ANF content is 20 wt %, the tensile strength of the film is increased from 24.6 MPa for a pure MXene film to 79.5 MPa, and such a composite film (9 μm thickness) exhibits a high EMI shielding effectiveness (SE) value of ∼40 dB and a specific SE (SSE) value of 4361.1 dB/mm. Upon fire exposure, the composite films can trigger the fire detection system within 10 s owing to the thermoelectric property of MXene. The self-extinguishing feature of ANFs ensures the structural integrity of the films during burning, thus allowing for continuous alarm signals. Moreover, the films also exhibit excellent Joule heating and photothermal conversion performances with rapid response and sufficient heating reliability.

| S-EPMC9404508 | biostudies-literature

Nanocellulose-MXene Biomimetic Aerogels with Orientation-Tunable Electromagnetic Interference Shielding Performance.

Project description:Designing lightweight nanostructured aerogels for high-performance electromagnetic interference (EMI) shielding is crucial yet challenging. Ultrathin cellulose nanofibrils (CNFs) are employed for assisting in building ultralow-density, robust, and highly flexible transition metal carbides and nitrides (MXenes) aerogels with oriented biomimetic cell walls. A significant influence of the angles between oriented cell walls and the incident EM wave electric field direction on the EMI shielding performance is revealed, providing an intriguing microstructure design strategy. MXene "bricks" bonded by CNF "mortars" of the nacre-like cell walls induce high mechanical strength, electrical conductivity, and interfacial polarization, yielding the resultant MXene/CNF aerogels an ultrahigh EMI shielding performance. The EMI shielding effectiveness (SE) of the aerogels reaches 74.6 or 35.5 dB at a density of merely 8.0 or 1.5 mg cm-3, respectively. The normalized surface specific SE is up to 189 400 dB cm2 g-1, significantly exceeding that of other EMI shielding materials reported so far.

| S-EPMC7404164 | biostudies-literature

Graphene fibre film/polydimethylsiloxane nanocomposites for high-performance electromagnetic interference shielding.

Project description:Exploration of high-performance electromagnetic interference (EMI) shielding materials has become a trend to address the increasing electromagnetic (EM) wave pollution environment. In this paper, oriented graphene fibre film (GFF)/polydimethylsiloxane (PDMS) nanocomposites with one-ply unidirectional, two-ply cross-ply, and two-ply unidirectional configurations were prepared using wet-spinning and hot-pressing techniques in a two-step process. Due to the anisotropic electrical performance of GFF, the one-ply laminate exhibits EMI shielding anisotropy that is affected by fibre orientation relative to the electric field component in EM waves. The maximum shielding difference at 8.8 GHz is up to 32.0 dB between the fibre orientation parallel to and perpendicular to the electric field component. In addition, we found that adding a layer of GFF is an intuitive method to enhance the shielding efficiency (SE) of GFF/PDMS nanocomposites by providing more interfaces to enhance absorption losses. An optimal EMI shielding performance of a two-ply unidirectional laminate is observed with an SE value of 50.6 dB, which shields 99.999% of EM waves. The shielding mechanisms are also discussed and clarified from the results of both experimental and theoretical analyses by adjusting the GFF structural parameters, such as the fibre orientation, areal density, number of plies and stacking sequence.

| S-EPMC9470028 | biostudies-literature

Environmentally Tough and Stretchable MXene Organohydrogel with Exceptionally Enhanced Electromagnetic Interference Shielding Performances.

Project description:Conductive hydrogels have potential applications in shielding electromagnetic (EM) radiation interference in deformable and wearable electronic devices, but usually suffer from poor environmental stability and stretching-induced shielding performance degradation. Although organohydrogels can improve the environmental stability of materials, their development is at the expense of reducing electrical conductivity and thus weakening EM interference shielding ability. Here, a MXene organohydrogel is prepared which is composed of MXene network for electron conduction, binary solvent channels for ion conduction, and abundant solvent-polymer-MXene interfaces for EM wave scattering. This organohydrogel possesses excellent anti-drying ability, low-temperature tolerance, stretchability, shape adaptability, adhesion and rapid self-healing ability. Two effective strategies have been proposed to solve the problems of current organohydrogel shielding materials. By reasonably controlling the MXene content and the glycerol-water ratio in the gel, MXene organohydrogel can exhibit exceptionally enhanced EM interference shielding performances compared to MXene hydrogel due to the increased physical cross-linking density of the gel. Moreover, MXene organohydrogel shows attractive stretching-enhanced interference effectiveness, caused by the connection and parallel arrangement of MXene nanosheets. This well-designed MXene organohydrogel has potential applications in shielding EM interference in deformable and wearable electronic devices.

| S-EPMC8938570 | biostudies-literature

Bridging sheet size controls densification of MXene films for robust electromagnetic interference shielding.

Project description:Numerous voids among the incompact layer-structure of MXene films result in their low ambient stability and poor innate conductivity for electromagnetic interference (EMI) shielding. Herein, we report a bridging-sheet-size-controlled densification process of MXene films by applying graphene oxide (GO) as a bridging agent. Specifically, the sheet size of GO is tailored to quantify a negative correlation of sheet size with densification for directing the preparation of most compact MXene-GO films. Benefiting from the shortest electron-transport-distance in the most compact structure, the conductivity of the MXene-GO film achieves 1.7 times (∼1.6 × 105 S/m) that of MXene film. The EMI shielding performance (5.2 × 106 dB/m) reaches the record-value among reported MXene films at 10 μm-scale thickness. Moreover, the compact structure boosts the ambient stability of MXene-GO films where the conductivity and EMI shielding performance remain 88.7% and 90.0% after 15 days, respectively. The findings rationale the structure-activity relationship of compact MXene films for flexible electronics.

| S-EPMC9464893 | biostudies-literature

Improved Mechanical Strength of Dicatechol Crosslinked MXene Films for Electromagnetic Interference Shielding Performance.

Project description:Pristine MXene films express outstanding excellent electromagnetic interference (EMI) shielding properties. Nevertheless, the poor mechanical properties (weak and brittle nature) and easy oxidation of MXene films hinder their practical applications. This study demonstrates a facile strategy for simultaneously improving the mechanical flexibility and the EMI shielding of MXene films. In this study, dicatechol-6 (DC), a mussel-inspired molecule, was successfully synthesized in which DC as mortars was crosslinked with MXene nanosheets (MX) as bricks to create the brick-mortar structure of the MX@DC film. The resulting MX@DC-2 film has a toughness of 40.02 kJ·m-3 and Young's modulus of 6.2 GPa, which are improvements of 513% and 849%, respectively, compared to those of the bare MXene films. The coating of electrically insulating DC significantly reduced the in-plane electrical conductivity from 6491 S·cm-1 for the bare MXene film to 2820 S·cm-1 for the MX@DC-5 film. However, the EMI shielding effectiveness (SE) of the MX@DC-5 film reached 66.2 dB, which is noticeably greater than that of the bare MX film (61.5 dB). The enhancement in EMI SE resulted from the highly ordered alignment of the MXene nanosheets. The synergistic concurrent enhancement in the strength and EMI SE of the DC-coated MXene film can facilitate the utilization of the MXene film in reliable, practical applications.

| S-EPMC10005341 | biostudies-literature

Ultrathin and Flexible CNTs/MXene/Cellulose Nanofibrils Composite Paper for Electromagnetic Interference Shielding.

Project description:As the rapid development of portable and wearable devices, different electromagnetic interference (EMI) shielding materials with high efficiency have been desired to eliminate the resulting radiation pollution. However, limited EMI shielding materials are successfully used in practical applications, due to the heavy thickness and absence of sufficient strength or flexibility. Herein, an ultrathin and flexible carbon nanotubes/MXene/cellulose nanofibrils composite paper with gradient and sandwich structure is constructed for EMI shielding application via a facile alternating vacuum-assisted filtration process. The composite paper exhibits outstanding mechanical properties with a tensile strength of 97.9 ± 5.0 MPa and a fracture strain of 4.6 ± 0.2%. Particularly, the paper shows a high electrical conductivity of 2506.6 S m-1 and EMI shielding effectiveness (EMI SE) of 38.4 dB due to the sandwich structure in improving EMI SE, and the gradient structure on regulating the contributions from reflection and absorption. This strategy is of great significance in fabricating ultrathin and flexible composite paper for highly efficient EMI shielding performance and in broadening the practical applications of MXene-based composite materials.

| S-EPMC7770921 | biostudies-literature

Direct Ink Writing of Highly Conductive MXene Frames for Tunable Electromagnetic Interference Shielding and Electromagnetic Wave-Induced Thermochromism.

Project description:Highlights3D printing of MXene frames with tunable electromagnetic interference shielding efficiency is demonstrated. Highly conductive MXene frames are reinforced by cross-linking with aluminum ions. Electromagnetic wave is visualized by electromagnetic-thermochromic MXene patterns. The highly integrated and miniaturized next-generation electronic products call for high-performance electromagnetic interference (EMI) shielding materials to assure the normal operation of their closely assembled components. However, the most current techniques are not adequate for the fabrication of shielding materials with programmable structure and controllable shielding efficiency. Herein, we demonstrate the direct ink writing of robust and highly conductive Ti3C2Tx MXene frames with customizable structures by using MXene/AlOOH inks for tunable EMI shielding and electromagnetic wave-induced thermochromism applications. The as-printed frames are reinforced by immersing in AlCl3/HCl solution to remove the electrically insulating AlOOH nanoparticles, as well as cross-link the MXene sheets and fuse the filament interfaces with aluminum ions. After freeze-drying, the resultant robust and porous MXene frames exhibit tunable EMI shielding efficiencies in the range of 25-80 dB with the highest electrical conductivity of 5323 S m-1. Furthermore, an electromagnetic wave-induced thermochromic MXene pattern is assembled by coating and curing with thermochromic polydimethylsiloxane on a printed MXene pattern, and its color can be changed from blue to red under the high-intensity electromagnetic irradiation. This work demonstrates a direct ink printing of customizable EMI frames and patterns for tuning EMI shielding efficiency and visualizing electromagnetic waves.

| S-EPMC8219826 | biostudies-literature

Highly Ordered Thermoplastic Polyurethane/Aramid Nanofiber Conductive Foams Modulated by Kevlar Polyanion for Piezoresistive Sensing and Electromagnetic Interference Shielding.

Project description:Highly ordered and uniformly porous structure of conductive foams is a vital issue for various functional purposes such as piezoresistive sensing and electromagnetic interference (EMI) shielding. With the aids of Kevlar polyanionic chains, thermoplastic polyurethane (TPU) foams reinforced by aramid nanofibers (ANF) with adjustable pore-size distribution were successfully obtained via a non-solvent-induced phase separation. In this regard, the most outstanding result is the in situ formation of ANF in TPU foams after protonation of Kevlar polyanion during the NIPS process. Furthermore, in situ growth of copper nanoparticles (Cu NPs) on TPU/ANF foams was performed according to the electroless deposition by using the tiny amount of pre-blended Ti3C2Tx MXene as reducing agents. Particularly, the existence of Cu NPs layers significantly promoted the storage modulus in 2,932% increments, and the well-designed TPU/ANF/Ti3C2Tx MXene (PAM-Cu) composite foams showed distinguished compressive cycle stability. Taking virtues of the highly ordered and elastic porous architectures, the PAM-Cu foams were utilized as piezoresistive sensor exhibiting board compressive interval of 0-344.5 kPa (50% strain) with good sensitivity at 0.46 kPa-1. Meanwhile, the PAM-Cu foams displayed remarkable EMI shielding effectiveness at 79.09 dB in X band. This work provides an ideal strategy to fabricate highly ordered TPU foams with outstanding elastic recovery and excellent EMI shielding performance, which can be used as a promising candidate in integration of satisfactory piezoresistive sensor and EMI shielding applications for human-machine interfaces.

| S-EPMC10082146 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data