Nanostructure of PMMA/MAM Blends Prepared by Out-of-Equilibrium (Extrusion) and Near-Equilibrium (Casting) Self-Assembly and Their Nanocellular or Microcellular Structure Obtained from CO₂ Foaming.

ABSTRACT: Blends of poly(methyl methacrylate) (PMMA) and a triblock copolymer poly(methyl methacrylate)-b-poly(butyl acrylate)-b-poly(methyl methacrylate) (MAM) have been obtained following both out-of-equilibrium (extrusion) and near-equilibrium (solvent casting) production routes. The self-assembly capability and the achievable nanostructures of these blends are analyzed by transmission electron microscopy (TEM) regarding their production route and potential for the achievement of nanocellular foams by CO₂ gas dissolution foaming. The influence of the initial nanostructure of the solids on the obtained cellular structure of bulk and film samples is determined by high-resolution scanning electron microscopy (HRSEM) for diverse foaming conditions (saturation pressure, saturation temperature, and post-foaming stage), taking into account the required use of a foaming mold to achieve foams from films. Moreover, the influence of the nanostructuration on the presence of solid outer layers, typical of the selected foaming process, is addressed. Finally, consideration of a qualitative model and the obtained results in terms of nanostructuration, cellular structure, and foaming behavior, allow proposing a detailed cell nucleation, growth, and stabilization scheme for these materials, providing the first direct evidence of the cell nucleation happening inside the poly(butyl acrylate) phase in the PMMA/MAM blends.

SUBMITTER: Barroso-Solares S

PROVIDER: S-EPMC8620990 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Improving the Continuous Microcellular Extrusion Foaming Ability with Supercritical CO2 of Thermoplastic Polyether Ester Elastomer through In-Situ Fibrillation of Polytetrafluoroethylene.

Project description:In-situ fibrillated polytetrafluoroethylene (PTFE) enhanced nanocomposites were successfully prepared by mixing thermoplastic polyether ester elastomer (TPEE) and PTFE using a twin-screw extruder. Well-dispersed, long aspect ratio PTFE nanofibrils with a diameter of less than 200 nm were generated and interwoven into networks. Differential scanning calorimetry and in-situ polarized optical microscopy showed that the PTFE nanofibrils can greatly accelerate and promote crystallization of the TPEE matrix and the crystallization temperature can be increased by 6 °C. Both shearing and elongational rheometry results confirmed that the introduction of PTFE nanofibrils can significantly improve the rheological properties. The remarkable changes in the strain-hardening effect and the melt viscoelastic response, as well as the promoted crystallization, led to substantially improved foaming behavior in the continuous extrusion process using supercritical CO2 as the blowing agent. The existing PTFE nanofibrils dramatically decreased the cell diameter and increased cell density, together with a higher expansion ratio and more uniform cell structure. The sample with 5% PTFE fibrils showed the best foaming ability, with an average diameter of 10.4-14.7 μm, an expansion ratio of 9.5-12.3 and a cell density of 6.6 × 107-8.6 × 107 cells/cm3.

| S-EPMC6960977 | biostudies-literature

Fabrication of Highly Interconnected Poly(ε-caprolactone)/cellulose Nanofiber Composite Foams by Microcellular Foaming and Leaching Processes.

Project description:In this study, microcellular polycaprolactone (PCL)/sodium bicarbonate (NaHCO3)/cellulose nanofiber (CNF) composite foams with highly interconnected porous structures were successfully fabricated by microcellular foaming and particle leaching processes. Supercritical CO2 (scCO2) served as a physical foaming agent, NaHCO3 was chosen as a chemical foaming agent and porogen, and CNF acted as a heterogeneous nucleating agent. The effect of scCO2, NaHCO3, and CNF on pore structures and the cofoaming mechanism were investigated. The results indicated that the addition of NaHCO3 and CNF increased the melt strength of the PCL matrix significantly. During the foaming process, the presence of CNF can form a rigid network due to the hydrogen bonding or mechanical entanglement between individual nanofibers, improving the nucleating efficiency but slowing down the cell growth rate. Additionally, due to the interaction of "soft" PCL matrix and "hard" domains in a PCL-based composite during the foaming process, together with the NaHCO3 leaching process, highly interconnected cell structures appeared. The obtained PCL/NaHCO3/CNF composite foams had a cell size of 15.8 μm and cell density of 6.3 × 107 cells/cm3, as well as an open-cell content of 82%. The reported strategy in this paper may provide the guidelines and data supports for the fabrication of a PCL-based porous scaffold.

| S-EPMC8427651 | biostudies-literature

Supertough and Transparent Poly(lactic acid) Nanostructure Blends with Minimal Stiffness Loss.

Project description:This contribution is an attempt to explore the effectiveness of a series of newly obtained thermoplastic elastomers (TPEs) as a toughening agent for modifying poly(lactic acid) (PLA). The TPEs, including ionically modified isotactic polypropylene-graft-PLA (iPP-g-PLA) copolymers with explicit graft length, graft density, and ionic group content, and an iPP-g-PLA copolymer with a very high molecular weight and explicit graft density, were elaborately designed and synthesized. The semicrystal or rubbery copolymer backbone originated from iPP was designed to improve the toughness and maintain a relatively high strength, while the grafted PLA side chain was to ensure a high level of compatibility with the PLA matrix. To obtain further enhancement in interfacial reinforcement, the imidazolium-based ionic group was also added during graft onto reaction. All of these graft copolymers were identified with randomly distributed PLA branches, bearing a very high molecular weight ((33-398) × 104) and very high PLA content (57.3-89.3 wt %). Unprecedentedly, with a very small amount of newly designed TPE, the modified PLA blends exhibited a significantly increased elongation at break (up to about 190%) and simultaneously retained the very high stiffness and excellent transparency. The nanometer-scale phase-separated particles with good compatibility and refractive index matching to the PLA matrix were demonstrated to play a crucial role in the excellent performance. The findings suggested that the newly designed iPP-g-PLA copolymers are very economic, promising, and effective modifying agents for developing highly transparent and tough PLA-based sustainable materials.

| S-EPMC7288571 | biostudies-literature

Gradient 2D/3D Perovskite Films Prepared by Hot-Casting for Sensitive Photodetectors.

Project description:2D Ruddlesden-Popper perovskites have attracted wide attention recently because of tunable optoelectronic properties and have been used as alternatives to their 3D counterparts in various optoelectronic devices. Here, a series of (PEA)2(MA) n -1Pb n I3 n +1 perovskite thin films is designed and fabricated by a convenient hot-casting method to obtain gradient n in the films, which leads to the formation of vertical heterojunctions that can enhance charge separation in the films under light illumination. Based on a single gradient perovskite film, a highly sensitive and stable photodetector with a responsivity up to 149 AW-1 and a specific detectivity of 2 × 1012 Jones is obtained. This work paves a way to realizing high-performance optoelectronic devices with enhanced charge separation by introducing compositional gradient in a perovskite film.

| S-EPMC7375231 | biostudies-literature

Sorption Properties of PET Copolyesters and New Approach for Foaming with Filament Extrusion Additive Manufacturing.

Project description:The mass transfer process of binary esters of acetic acid in polyethylene terephthalate (PET), polyethylene terephthalate with a high degree of glycol modification (PETG), and glycol-modified polycyclohexanedimethylene terephthalate (PCTG) was studied. It was found that the desorption rate of the complex ether at the equilibrium point is significantly lower than the sorption rate. The difference between these rates depends on the type of polyester and temperature and allows the accumulation of ester in the volume of the polyester. For example, the stable content of acetic ester in PETG at 20 °C is 5 wt.%. The remaining ester, which has the properties of a physical blowing agent, was used in the filament extrusion additive manufacturing (AM) process. By varying the technological parameters of the AM process, foams of PETG with densities ranging from 150 to 1000 g/cm3 were produced. Unlike conventional polyester foams, the resulting foams are not brittle.

| S-EPMC10006899 | biostudies-literature

Extrusion Foaming of Lightweight Polystyrene Composite Foams with Controllable Cellular Structure for Sound Absorption Application.

Project description:Polymer foams are promising for sound absorption applications. In order to process an industrial product, a series of polystyrene (PS) composite foams were prepared by continuous extrusion foaming assisted by supercritical CO₂. Because the cell size and cell density were the key to determine the sound absorption coefficient at normal incidence, the bio-resource lignin was employed for the first time to control the cellular structure on basis of hetero-nucleation effect. The sound absorption range of the PS/lignin composite foams was corresponding to the cellular structure and lignin content. As a result, the maximum sound absorption coefficient at normal incidence was higher than 0.90. For a comparison, multiwall carbon nanotube (MWCNT) and micro graphite (mGr) particles were also used as the nucleation agent during the foaming process, respectively, which were more effective on the hetero-nucleation effect. The mechanical property and thermal stability of various foams were measured as well. Lignin showed a fire retardant effect in PS composite foam.

| S-EPMC6401839 | biostudies-literature

Role of Plasticizers on PHB/bio-TPE Blends Compatibilized by Reactive Extrusion.

Project description:Poly(hydroxybutyrate) (PHB) is a biopolymer biologically synthesized by controlled bacterial fermentation from a wide variety of microorganisms. PHB is proposed as a potential green alternative to commonly used plastics in packaging, due to its biodegradability and biocompatibility. However, if PHB is to replace commodities, it has some limitations regarding its thermo-mechanical performance to overcome. Among them are its critically the low toughness values at room temperature and poor thermoforming ability. With the aim of overcoming these weaknesses, in this work, blends of PHB with the addition of a biodegradable thermoplastic elastomer (bio-TPE) were prepared and evaluated. Films of such compounds were made by cast extrusion. In order to enhance the compatibility of both polymers during the extrusion process, three different reactive agents (poly-hexametylene diisocianate, triglycidyl isocyanurate, and Joncryl® ADR-4368) were assessed. The morphology and mechanical- and thermal properties of the films obtained were analyzed. In addition, the thermoforming ability of the produced films was evaluated. The results show that the plasticizers present in the bio-TPE interacted with the reactive agents, making them chemical competitors and altering the outcome of the blends.

| S-EPMC8840646 | biostudies-literature

Open-Celled Foams from Polyethersulfone/Poly(Ethylene Glycol) Blends Using Foam Extrusion.

Project description:Polyethersulfone (PESU), as both a pristine polymer and a component of a blend, can be used to obtain highly porous foams through batch foaming. However, batch foaming is limited to a small scale and is a slow process. In our study, we used foam extrusion due to its capacity for large-scale continuous production and deployed carbon dioxide (CO2) and water as physical foaming agents. PESU is a high-temperature thermoplastic polymer that requires processing temperatures of at least 320 °C. To lower the processing temperature and obtain foams with higher porosity, we produced PESU/poly(ethylene glycol) (PEG) blends using material penetration. In this way, without the use of organic solvents or a compounding extruder, a partially miscible PESU/PEG blend was prepared. The thermal and rheological properties of homopolymers and blends were characterized and the CO2 sorption performance of selected blends was evaluated. By using these blends, we were able to significantly reduce the processing temperature required for the extrusion foaming process by approximately 100 °C without changing the duration of processing. This is a significant advancement that makes this process more energy-efficient and sustainable. Additionally, the effects of blend composition, nozzle temperature and foaming agent type were investigated, and we found that higher concentrations of PEG, lower nozzle temperatures, and a combination of CO2 and water as the foaming agent delivered high porosity. The optimum blend process settings provided foams with a porosity of approximately 51% and an average foam cell diameter of 5 µm, which is the lowest yet reported for extruded polymer foams according to the literature.

| S-EPMC9824152 | biostudies-literature

Reliable Fabrication of Graphene Nanostructure Based on e-Beam Irradiation of PMMA/Copper Composite Structure.

Project description:Graphene nanostructures are widely perceived as a promising material for fundamental components; their high-performance electronic properties offer the potential for the construction of graphene nanoelectronics. Numerous researchers have paid attention to the fabrication of graphene nanostructures, based on both top-down and bottom-up approaches. However, there are still some unavoidable challenges, such as smooth edges, uniform films without folds, and accurate dimension and location control. In this work, a direct writing method was reported for the in-situ preparation of a high-resolution graphene nanostructure of controllable size (the minimum feature size is about 15 nm), which combines the advantages of e-beam lithography and copper-catalyzed growth. By using the Fourier infrared absorption test, we found that the hydrogen and oxygen elements were disappearing due to knock-on displacement and the radiolysis effect. The graphene crystal is also formed via diffusion and the local heating effect between the e-beam and copper substrate, based on the Raman spectra test. This simple process for the in-situ synthesis of graphene nanostructures has many promising potential applications, including offering a way to make nanoelectrodes, NEMS cantilever resonant structures, nanophotonic devices and so on.

| S-EPMC8401420 | biostudies-literature

Supercritical Fluid Microcellular Foaming of High-Hardness TPU via a Pressure-Quenching Process: Restricted Foam Expansion Controlled by Matrix Modulus and Thermal Degradation.

Project description:High-hardness thermoplastic polyurethane (HD-TPU) presents a high matrix modulus, low-temperature durability, and remarkable abrasion resistance, and has been used in many advanced applications. However, the fabrication of microcellular HD-TPU foam is rarely reported in the literature. In this study, the foaming behavior of HD-TPU with a hardness of 75D was investigated via a pressure-quenching foaming process using CO2 as a blowing agent. Microcellular HD-TPU foam with a maximum expansion ratio of 3.9-fold, a cell size of 25.9 μm, and cell density of 7.8 × 108 cells/cm3 was prepared, where a high optimum foaming temperature of about 170 °C had to be applied with the aim of softening the polymer's matrix modulus. However, the foaming behavior of HD-TPU deteriorated when the foaming temperature further increased to 180 °C, characterized by the presence of coalesced cells, microcracks, and a high foam density of 1.0 g/cm3 even though the crystal domains still existed within the matrix. The cell morphology evolution of HD-TPU foam was investigated by adjusting the saturation time, and an obvious degradation occurred during the high-temperature saturation process. A cell growth mechanism of HD-TPU foams in degradation environments was proposed to explain this phenomenon based on the gas escape through the defective matrix.

| S-EPMC9783504 | biostudies-literature