Electrospun Ultrafine Cationic Cellulose Fibers Produced from Sugarcane Bagasse for Potential Textile Applications.

ABSTRACT: Sugarcane bagasse (SCB) is an abundant by-product of sugar refining that can be utilized as a raw material for cellulose isolation for several industrial applications. Electrospinning has garnered attention in recent years because it allows the preparation of cellulosic materials with unique properties. In this study, cellulose was isolated from sugarcane bagasse and acetylated to fabricate fine acetate cellulose fibers through electrospinning. Subsequently, the electrospun fibers were deacetylated and cationized in order to produce functionalized materials with potential textile applications. The functional fibers were colored with an anionic dye (vinyl sulfone) with and without the presence of salt and were evaluated according to dye fixation, color attributes, morphological characteristics, and thermal stability. Cationic cellulose fibers that were dyed without added salt were found to be brighter and demonstrated better color fixation than those with added salt. In addition, morphological analysis performed using scanning electron microscopy demonstrated that cationized fibers dyed without added salt were better preserved at this stage. The cationic fiber also evidenced a high-temperature resistance, exhibiting a degradation temperature above 236 °C. The results suggest that cellulose fibers dyed in this manner can potentially be considered for use in textile applications due to their suitable dye fixation and tunable porosity (i.e., breathability).

SUBMITTER: Ochica Larrota AF

PROVIDER: S-EPMC8621662 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Electrospun Polymer Fibers for Electronic Applications.

Project description:Nano- and micro- fibers of conjugated polymer semiconductors are particularly interesting both for applications and for fundamental research. They allow an investigation into how electronic properties are influenced by size confinement and chain orientation within microstructures that are not readily accessible within thin films. Moreover, they open the way to many applications in organic electronics, optoelectronics and sensing. Electro-spinning, the technique subject of this review, is a simple method to effectively form and control conjugated polymer fibers. We provide the basics of the technique and its recent advancements for the formation of highly conducting and high mobility polymer fibers towards their adoption in electronic applications.

| S-EPMC5453086 | biostudies-other

Tensan Silk-Inspired Hierarchical Fibers for Smart Textile Applications.

Project description:Tensan silk, a natural fiber produced by the Japanese oak silk moth ( Antherea yamamai, abbreviated to A. yamamai), features superior characteristics, such as compressive elasticity and chemical resistance, when compared to the more common silk produced from the domesticated silkworm, Bombyx mori ( B. mori). In this study, the "structure-property" relationships within A. yamamai silk are disclosed from the different structural hierarchies, confirming the outstanding toughness as dominated by the distinct mesoscale fibrillar architectures. Inspired by this hierarchical construction, we fabricated A. yamamai silk-like regenerated B. mori silk fibers (RBSFs) with mechanical properties (extensibility and modulus) comparable to natural A. yamamai silk. These RBSFs were further functionalized to form conductive RBSFs that were sensitive to force and temperature stimuli for applications in smart textiles. This study provides a blueprint in exploiting rational designs from A. yamanmai, which is rare and expensive in comparison to the common and cost-effective B. mori silk to empower enhanced material properties.

| S-EPMC6501189 | biostudies-literature

Data supporting the production of dietary fibers from sugarcane bagasse and sugarcane tops using microwave - assisted alkaline treatments.

Project description:The treatment of agroindustrial residues is an alternative to waste management and obtain products with added value. In this article, we describe the confocal microscopy images, the microbiological data, policosanol content and color measurement linked to the paper "production of dietary fibers from sugarcane bagasse and sugarcane tops using microwave - assisted alkaline treatments". The data contain photographs after elaboration of noodles-type pasta and chapatti-type fermented bread; the confocal laser scanning micrographs, before and after including sugarcane bagasse and sugarcane tops fibers in foods. Microbiological analyses of total coliforms, molds and yeasts, and aerobic mesophiles were also presented according to Mexican Standard NOM- 247-SSA1-2008 which confirmed that the food is safe for human consumption. The data provided in this article have not been previously published and are available to enable critical or extended analyses.

| S-EPMC6545404 | biostudies-literature

Robust Silica-Bacterial Cellulose Composite Aerogel Fibers for Thermal Insulation Textile.

Project description:Aerogels are nanoporous materials with excellent properties, especially super thermal insulation. However, owing to their serious high brittleness, the macroscopic forms of aerogels are not sufficiently rich for the application in some fields, such as thermal insulation clothing fabric. Recently, freeze spinning and wet spinning have been attempted for the synthesis of aerogel fibers. In this study, robust fibrous silica-bacterial cellulose (BC) composite aerogels with high performance were synthesized in a novel way. Silica sol was diffused into a fiber-like matrix, which was obtained by cutting the BC hydrogel and followed by secondary shaping to form a composite wet gel fiber with a nanoscale interpenetrating network structure. The tensile strength of the resulting aerogel fibers reached up to 5.4 MPa because the quantity of BC nanofibers in the unit volume of the matrix was improved significantly by the secondary shaping process. In addition, the composite aerogel fibers had a high specific area (up to 606.9 m2/g), low density (less than 0.164 g/cm3), and outstanding hydrophobicity. Most notably, they exhibited excellent thermal insulation performance in high-temperature (210 °C) or low-temperature (-72 °C) environments. Moreover, the thermal stability of CAFs (decomposition temperature was about 330 °C) was higher than that of natural polymer fiber. A novel method was proposed herein to prepare aerogel fibers with excellent performance to meet the requirements of wearable applications.

| S-EPMC8482140 | biostudies-literature

Photo-Patternable, High-Speed Electrospun Ultrafine Fibers Fabricated by Intrinsically Negative Photosensitive Polyimide.

Project description:This work describes polyimide (PI) ultrafine fibrous membranes (UFMs) with aligned fibrous structures, fabricated via the high-speed electrospinning procedure. Organo-soluble intrinsically photosensitive PI is utilized as the fiber-forming agent. The effects of different rotating speeds on the fiber morphology and properties are studied. The aligned UFMs possess hydrophobicity, favorable optical properties, and improved deformation durability. The extension strength of the UFMs reinforces obviously with the increased rotating speed and reaches the maximum of 9.18 MPa at 2500 rpm. In addition, due to the photo-cross-link nature of the PI resin, the UFMs present lithography capability, which can obtain micro-sized patterns on aluminum substrates, and even part of the fibrous structure was retained after development. This work shows promise in manufacturing fiber-based photolithographic hierarchical structures on flexible substrates, which exhibit potential in achieving multiple functions on fiber-based electronic devices.

| S-EPMC8296557 | biostudies-literature

Co-Carbonized Waste Polythene/Sugarcane Bagasse Nanocomposite for Aqueous Environmental Remediation Applications

Project description:The conversion of worthless municipal solid wastes to valuables is a major step towards environmental conservation and sustainability. This work successfully proposed a technique to utilize the two most commonly available municipal solid wastes viz polythene (PE) and sugarcane bagasse (SB) for water decolorization application. An SBPE composite material was developed and co-pyrolyzed under an inert atmosphere to develop the activated SBPEAC composite. Both SBPE and SBPEAC composites were characterized to analyze their morphological characteristics, specific surface area, chemical functional groups, and elemental composition. The adsorption efficacies of the composites were comparatively tested in the removal of malachite green (MG) from water. The SBPEAC composite had a specific surface area of 284.5 m2/g and a pore size of ~1.33 nm. Batch-scale experiments revealed that the SBPEAC composite performed better toward MG adsorption compared to the SBPE composite. The maximum MG uptakes at 318 K on SBPEAC and SBPE were 926.6 and 375.6 mg/g, respectively. The adsorption of MG on both composites was endothermic. The isotherm and kinetic modeling data for MG adsorption on SBPEAC was fitted to pseudo-second-order kinetic and Langmuir isotherm models, while Elovich kinetic and D-R isotherm models were better fitted for MG adsorption on SBPE. Mechanistically, the MG adsorption on both SBPE and SBPEAC composites involved electrostatic interaction, H-bonding, and π-π/n-π interactions.

| S-EPMC10097173 | biostudies-literature

Pretreatment of Cellulose from Sugarcane Bagasse with Xylanase for Improving Dyeability with Natural Dyes.

Project description:In this study, cellulose was obtained from sugarcane bagasse (SCB) and treated with xylanase to remove residual noncellulosic polymers (hemicellulose and lignin) to improve its dyeability. The cellulose fibers were dyed with natural dye solutions extracted from the heart wood of Ceasalpinia sappan Linn. and Artocarpus heterophyllus Lam. Fourier-transform infrared (FTIR) spectroscopy, Raman analysis, and whiteness index (WI) indicated successful extraction of cellulose by eliminating hemicellulose and lignin. The FTIR analysis of the dyed fibers confirmed successful interaction between natural dyes and cellulose fibers. The absorption (K) and scattering (S) coefficient (K/S) values of the dyed fibers increased in cellulose treated with xylanase before dyeing. Scanning electron microscopy (SEM) analysis showed that the surface of alkaline-bleached fibers (AB-fibers) was smoother than alkaline-bleached xylanase fibers (ABX-fibers), and the presence of dye particles on the surface of dyed fibers was confirmed by energy-dispersive spectrometry (EDS) analysis. The X-ray diffraction (XRD) revealed a higher crystallinity index (CrI), and thermal gravimetric analysis (TGA) also presented higher thermal stability in the dyed fibers with good colorfastness to light. Therefore, xylanase treatment and natural dyes can enhance dyeability and improve the properties of cellulose for various industrial applications.

| S-EPMC7643204 | biostudies-literature

Coloration and Chromatic Sensing Behavior of Electrospun Cellulose Fibers with Curcumin.

Project description:The effective approach for coloration and chromatic sensing of electrospun cellulose fabrics with a natural colorant, curcumin, is demonstrated. To achieve high surface area, the morphology of fiber was controlled to have rough and porous surface through an electrospinning of a cellulose acetate (CA) solution under optimized electrospinning parameters and solvent system. The resulting CA fibers were treated with a curcumin dye/NaOH ethanol solution, in which deacetylation of the CA fiber and high-quality coloration with curcumin were simultaneously achieved. As a control, a cotton fiber with similar diameter and smooth surface morphology was treated by the same method, resulting in poor coloration quality. The difference can be attributed to high surface area as well as trapping of dye molecules inside of cellulose fiber during deacetylation. Both fibers were further utilized for a chromatic sensing application for specific toxic gases. The incorporated curcumin dye responded to hydrogen chloride and ammonia gases reversibly via keto-enol tautomerism, and, as a consequence, the color was reversibly changed between reddish-brown and yellow colors. The cellulose fiber fabricated by the electrospinning showed ten times higher and two times quicker responsiveness compared to curcumin-colored cotton fiber sample prepared with the same immersion method.

| S-EPMC7830206 | biostudies-literature

Cotton-quality fibers from complexation between anionic and cationic cellulose nanoparticles.

Project description:Natural polymers are attractive sustainable materials for production of fibers and composite materials. Cotton and flux are traditional plants used to produce textiles with comforting properties while technologies like Viscose, Lyocell and Ioncell-F allowed to extent fiber use into regenerated cellulose from wood. Neither natural nor man-made fibers completely satisfy the needs for cellulose based fabrics boosting development of new approaches to bring more sustainability into the fashion. Technologies like Spinnova are arising based on the spinning of mechanically pretreated cellulose materials with a lower environmental impact though challenged by the fiber quality and strength related to the inconsistency of the mechanical fibers. Nanoscaled cellulose is an excellent solution to improve the consistency of spin fibers, but charges introduced by traditional chemical treatments prevent rebuilding native hydrogen bonding and compromise the mechanical properties especially in wet conditions. We used nanocellulose with low surface charge isolated using reactive eutectic media to spin fibers able to restore the native hydrogen bonding and enable constitutional mechanical strength of cellulose. We performed un-optimized spinning to reveal the intrinsic properties of the fibers and confirmed the preserved strength of wet fibers compliant with the low surface charge enabling further engineering towards cotton-like fabric from wood.

| S-EPMC11310312 | biostudies-literature

Mullite-Fibers-Reinforced Bagasse Cellulose Aerogels with Excellent Mechanical, Flame Retardant, and Thermal Insulation Properties.

Project description:Cellulose aerogels are considered as ideal thermal insulation materials owing to their excellent properties such as a low density, high porosity, and low thermal conductivity. However, they still suffer from poor mechanical properties and low flame retardancy. In this study, mullite-fibers-reinforced bagasse cellulose (Mubce) aerogels are designed using bagasse cellulose as the raw material, mullite fibers as the reinforcing agent, glutaraldehyde as the cross-linking agent, and chitosan as the additive. The resulted Mubce aerogels exhibit a low density of 0.085 g/cm3, a high porosity of 93.2%, a low thermal conductivity of 0.0276 W/(m∙K), superior mechanical performances, and an enhanced flame retardancy. The present work offers a novel and straightforward strategy for creating high-performance aerogels, aiming to broaden the application of cellulose aerogels in thermal insulation.

| S-EPMC11312846 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data