Lanthanum Oxide Nickel Hydroxide Composite Triangle Nanosheets for Energy Density Asymmetric Supercapacitors.

ABSTRACT: Transition metal hydroxides are a kind of promising electrode material in electrochemical energy storage, but the poor conductivity limits their application. Lanthanides are good proton conductors and can usually improve the intrinsic conductivity of other materials. By integrating the merits of lanthanide elements and transition metal hydroxide, we designed lanthanum oxide nickel hydroxide composites (LONH) with unique ultrathin triangle nanosheet morphology via a controllable synthetic strategy for high-performance supercapacitors. When the LONH is used as positive electrode material in aqueous asymmetric supercapacitor, it reveals an energy density (107.8 W h kg^-1 at 800 W kg^-1), rate performance (86.9% retention at 4 kW kg^-1) and outstanding cycle stability (more than 90% retention after 3,000 cycles). This work confirms that compositing La₂O₃ and Ni(OH)₂ can significantly improve the supercapacitor performance of both pristine La₂O₃ and transition metal hydroxide composites. We hope this work would offer a good prospect for developing other lanthanide-transition metal hydroxide composites as an attractive class of electrode materials in electrochemical energy storage.

SUBMITTER: Duan H

PROVIDER: S-EPMC8632525 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Ultrathin nickel hydroxide and oxide nanosheets: synthesis, characterizations and excellent supercapacitor performances.

Project description:High-quality ultrathin two-dimensional nanosheets of ?-Ni(OH)2 are synthesized at large scale via microwave-assisted liquid-phase growth under low-temperature atmospheric conditions. After heat treatment, non-layered NiO nanosheets are obtained while maintaining their original frame structure. The well-defined and freestanding nanosheets exhibit a micron-sized planar area and ultrathin thickness (<2 nm), suggesting an ultrahigh surface atom ratio with unique surface and electronic structure. The ultrathin 2D nanostructure can make most atoms exposed outside with high activity thus facilitate the surface-dependent electrochemical reaction processes. The ultrathin ?-Ni(OH)2 and NiO nanosheets exhibit enhanced supercapacitor performances. Particularly, the ?-Ni(OH)2 nanosheets exhibit a maximum specific capacitance of 4172.5 F g(-1) at a current density of 1 A g(-1). Even at higher rate of 16 A g(-1), the specific capacitance is still maintained at 2680 F g(-1) with 98.5% retention after 2000 cycles. Even more important, we develop a facile and scalable method to produce high-quality ultrathin transition metal hydroxide and oxide nanosheets and make a possibility in commercial applications.

| S-EPMC4148663 | biostudies-literature

Lanthanum Hydroxide Nanorod-Templated Graphitic Hollow Carbon Nanorods for Supercapacitors.

Project description:Lanthanum hydroxide nanorods were employed as both a template and catalyst for carbon synthesis by chemical vapor deposition. The resulting carbon possesses hollow nanorod shapes with graphitic walls. The hollow carbon nanorods were interconnected at some junctions forming a mazelike network, and the broken ends of the tubular carbon provide accessibility to the inner surface of the carbon, resulting in a surface area of 771 m2/g. The hollow carbon was tested as an electrode material for supercapacitors. A specific capacitance of 128 F/g, an energy density of 55 Wh/kg, and a power density of 1700 W/kg at 1 A/g were obtained using the ionic liquid, 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide, as the electrolyte.

| S-EPMC6644425 | biostudies-literature

Charge storage mechanisms of manganese oxide nanosheets and N-doped reduced graphene oxide aerogel for high-performance asymmetric supercapacitors.

Project description:Although manganese oxide- and graphene-based supercapacitors have been widely studied, their charge storage mechanisms are not yet fully investigated. In this work, we have studied the charge storage mechanisms of K-birnassite MnO2 nanosheets and N-doped reduced graphene oxide aerogel (N-rGOae) using an in situ X-ray absorption spectroscopy (XAS) and an electrochemical quart crystal microbalance (EQCM). The oxidation number of Mn at the MnO2 electrode is +3.01 at 0?V vs. SCE for the charging process and gets oxidized to +3.12 at +0.8?V vs. SCE and then reduced back to +3.01 at 0?V vs. SCE for the discharging process. The mass change of solvated ions, inserted to the layers of MnO2 during the charging process is 7.4??g?cm-2. Whilst, the mass change of the solvated ions at the N-rGOae electrode is 8.4??g?cm-2. An asymmetric supercapacitor of MnO2//N-rGOae (CR2016) provides a maximum specific capacitance of ca. 467?F?g-1 at 1?A?g-1, a maximum specific power of 39?kW?kg-1 and a specific energy of 40?Wh?kg-1 with a wide working potential of 1.6?V and 93.2% capacity retention after 7,500 cycles. The MnO2//N-rGOae supercapacitor may be practically used in high power and energy applications.

| S-EPMC5114613 | biostudies-literature

3D Hierarchically Mesoporous Zinc-Nickel-Cobalt Ternary Oxide (Zn0.6Ni0.8Co1.6O4) Nanowires for High-Performance Asymmetric Supercapacitors.

Project description:Increased efforts have been devoted recently to develop high-energy-density supercapacitors (SC) without renouncing their power efficiency. Herein, a hierarchically mesoporous nanostructure of zinc-nickel-cobalt oxide (ZNCO) nanowires (NWs) is constructed by hierarchical aggregation of ZNCO nanoparticles. It is worth noting that cobalt and nickel rich lattice imparts higher charge storage capability by enhanced reversible Faradaic reaction while zinc provides structural stability and higher conductivity. Moreover, particulate nature of ZNCO NWs allows deep diffusion of electrolyte thus enabling reversible charge storage under higher current densities. The as-prepared ZNCO NWs exhibited excellent specific capacitance of 2082.21 F g-1 at the current density of 1 A g-1 with high stability up to 5,000 charge-discharge cycles. Further, the asymmetric SC device was assembled using ZNCO NWs (ZNCO NWs//MWCNTs) which exhibited high energy density of 37.89 Wh kg-1 and excellent capacitance retention up to 88.5% over 1,000 cycles. This work presents ways to construct multi-component high-energy-density materials for next-generation energy storage devices.

| S-EPMC7307270 | biostudies-literature

In Situ Growth of Nickel–Cobalt Metal Organic Frameworks Guided by a Nickel–Molybdenum Layered Double Hydroxide with Two-Dimensional Nanosheets Forming Flower-Like Struc-Tures for High-Performance Supercapacitors

Project description:Metal organic frameworks (MOFs) are a kind of porous coordination polymer supported by organic ligands with metal ions as connection points. They have a controlled structure and porosity and a significant specific surface area, and can be used as functional linkers or sacrificial templates. However, long diffusion pathways, low conductivity, low cycling stability, and the presence of few exposed active sites limit the direct application of MOFs in energy storage applications. The targeted design of MOFs has the potential to overcome these limitations. This study proposes a facile method to grow and immobilize MOFs on layered double hydroxides through an in situ design. The proposed method imparts not only enhanced conductivity and cycling stability, but also provides additional active sites with excellent specific capacitance properties due to the interconnectivity of MOF nanoparticles and layered double hydroxide (LDH) nanosheets. Due to this favorable heterojunction hook, the NiMo-LDH@NiCo-MOF composite exhibits a large specific capacitance of 1536 F·g−1 at 1 A·g−1. In addition, the assembled NiMo-LDH@NiCo-MOF//AC asymmetric supercapacitor can achieve a high-energy density value of 60.2 Wh·kg−1 at a power density of 797 W·kg−1, indicating promising applications.

| S-EPMC9919709 | biostudies-literature

Low-crystalline iron oxide hydroxide nanoparticle anode for high-performance supercapacitors.

Project description:Carbon materials are generally preferred as anodes in supercapacitors; however, their low capacitance limits the attained energy density of supercapacitor devices with aqueous electrolytes. Here, we report a low-crystalline iron oxide hydroxide nanoparticle anode with comprehensive electrochemical performance at a wide potential window. The iron oxide hydroxide nanoparticles present capacitances of 1,066 and 716 F g-1 at mass loadings of 1.6 and 9.1 mg cm-2, respectively, a rate capability with 74.6% of capacitance retention at 30 A g-1, and cycling stability retaining 91% of capacitance after 10,000 cycles. The performance is attributed to a dominant capacitive charge-storage mechanism. An aqueous hybrid supercapacitor based on the iron oxide hydroxide anode shows stability during float voltage test for 450 h and an energy density of 104 Wh kg-1 at a power density of 1.27 kW kg-1. A packaged device delivers gravimetric and volumetric energy densities of 33.14 Wh kg-1 and 17.24 Wh l-1, respectively.

| S-EPMC5343484 | biostudies-literature

Hierarchical Cobalt Hydroxide and B/N Co-Doped Graphene Nanohybrids Derived from Metal-Organic Frameworks for High Energy Density Asymmetric Supercapacitors.

Project description:To cater for the demands of electrochemical energy storage system, the development of cost effective, durable and highly efficient electrode materials is desired. Here, a novel electrode material based on redox active β-Co(OH)2 and B, N co-doped graphene nanohybrid is presented for electrochemical supercapacitor by employing a facile metal-organic frameworks (MOFs) route through pyrolysis and hydrothermal treatment. The Co(OH)2 could be firmly stabilized by dual protection of N-doped carbon polyhedron (CP) and B/N co-doped graphene (BCN) nanosheets. Interestingly, the porous carbon and BCN nanosheets greatly improve the charge storage, wettability, and redox activity of electrodes. Thus the hybrid delivers specific capacitance of 1263 F g-1 at a current density of 1A g-1 with 90% capacitance retention over 5000 cycles. Furthermore, the new aqueous asymmetric supercapacitor (ASC) was also designed by using Co(OH)2@CP@BCN nanohybrid and BCN nanosheets as positive and negative electrodes respectively, which leads to high energy density of 20.25 Whkg-1. This device also exhibits excellent rate capability with energy density of 15.55 Whkg-1 at power density of 9331 Wkg-1 coupled long termed stability up to 6000 cycles.

| S-EPMC5327408 | biostudies-literature

Fabrication of 9.6?V High-performance Asymmetric Supercapacitors Stack Based on Nickel Hexacyanoferrate-derived Ni(OH)2 Nanosheets and Bio-derived Activated Carbon.

Project description:Hydrated Ni(OH)2 and activated carbon based electrodes are widely used in electrochemical applications. Here we report the fabrication of symmetric supercapacitors using Ni(OH)2 nanosheets and activated carbon as positive and negative electrodes in aqueous electrolyte, respectively. The asymmetric supercapacitors stack connected in series exhibited a stable device voltage of 9.6?V and delivered a stored high energy and power of 30 mWh and 1632 mW, respectively. The fabricated device shows an excellent electrochemical stability and high retention of 81% initial capacitance after 100,000 charge-discharges cycling at high charging current of 500?mA. The positive electrode material Ni(OH)2 nanosheets was prepared through chemical decomposition of nickel hexacyanoferrate complex. The XRD pattern revealed the high crystalline nature of Ni(OH)2 with an average crystallite size of ~10?nm. The nitrogen adsorption-desorption isotherms of Ni(OH)2 nanosheets indicate the formation of mesoporous Ni(OH)2 nanosheets. The chemical synthesis of Ni(OH)2 results the formation of hierarchical nanosheets that are randomly oriented which was confirmed by FE-SEM and HR-TEM analysis. The negative electrode, activated porous carbon (OPAA-700) was obtained from orange peel waste. The electrochemical properties of Ni(OH)2 nanosheets and OPAA-700 were studied and exhibit a high specific capacity of 1126?C/g and high specific capacitance of 311?F/g at current density of 2?A/g, respectively. Ni(OH)2 nanosheets delivered a good rate performance and remarkable capacitance retention of 96% at high current density of 32?A/g.

| S-EPMC6355786 | biostudies-literature

Hierarchical Nanosheets/Walls Structured Carbon-Coated Porous Vanadium Nitride Anodes Enable Wide-Voltage-Window Aqueous Asymmetric Supercapacitors with High Energy Density.

Project description:The energy density of aqueous asymmetric supercapacitors (ASCs) is usually limited by low potential windows and capacitances of both anode and cathode. Herein, a facile strategy to fabricate hierarchical carbon-coated porous vanadium nitride nanosheet arrays on vertically aligned carbon walls (CC/CW/p-VN@C) as anode for aqueous ASCs is reported. The potential window of CC/CW/p-VN@C electrode can be stably extended to -1.3 to 0 V (vs Ag/AgCl) with greatly improved specific capacitance (604.8 F g-1 at 1 A g-1), excellent rate capability (368 F g-1 at 60 A g-1), and remarkable electrochemical stability. To construct ASCs, a Birnessite Na0.5MnO2 nanosheet arrays (CC/CW/Na0.5MnO2) cathode is similarly built. Benefiting from the matchable potential windows and high specific capacitances of the rationally designed anode and cathode, aqueous CC/CW/p-VN@C||CC/CW/Na0.5MnO2 ASCs with a wide voltage window of 2.6 V are fabricated. Moreover, the ASCs showcase an ultrahigh energy density up to 96.7 W h kg-1 at a high power density of 1294 W kg-1, and excellent cycling stability (92.5% retention after 10 000 cycles), outperforming most of previously reported ASCs and even comparable to that of organic electrolyte supercapacitors (SCs). This efficient strategy for fabricating 2.6 V aqueous ASCs suggests a promising research system for high energy density SCs.

| S-EPMC6702630 | biostudies-literature

Lavender-like cobalt hydroxide nanoflakes deposited on nickel nanowire arrays for high-performance supercapacitors.

Project description:Hierarchical nanostructured electrodes with excellent electronic properties and high specific surface areas have promising applications in high-performance supercapacitors. However, high active mass loading and uniform structure are still crucial in fabricating such architectures. Herein, Co(OH)2 nanoflakes were homogeneously deposited on nickel nanowire arrays (NNA) through a hydrothermal approach to form an NNA@Co(OH)2 (NNACOH) composite electrode. The as-synthesized one dimensional (1D) system had a lavender-like structure with a high mass loading of 5.42 mg cm-2 and a high specific surface area of 74.5 m2 g-1. Due to the unique electrode structure characteristics, the electrode could deliver a high specific capacitance of 891.2 F g-1 at the current density of 1 A g-1 (corresponding to an areal capacitance of 4.83 F cm-2 at 5.42 mA cm-2). The capacitance could still maintain a high value of 721 F g-1 when the current density is increased to 50 A g-1. In addition, the electrode showed superior cycle stability with a capacitance retention of 89.3% after charging/discharging at the current density of 10 A g-1 for 20 000 cycles. A flexible asymmetric supercapacitor (ASC) was assembled by employing NNACOH as the positive electrode and activated carbon (AC) as the negative electrode. It delivered a maximum energy density of 23.1 W h kg-1 at the power density of 712 W kg-1 and an energy density of 13.5 W h kg-1 at the maximum power density of 14.7 kW kg-1 (based on the total mass of the electrodes), showing the state-of-the-art energy storage ability of the Co(OH)2 cathode material at device level.

| S-EPMC9080414 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data