Physical and Mechanical Characterization of Titica Vine (Heteropsis flexuosa) Incorporated Epoxy Matrix Composites.

ABSTRACT: Titica vine (Heteropsis flexuosa) is a typical plant of the Amazon region commonly used for making baskets, bags, brooms and furniture, owing to its stiff fibers. In spite of its interesting properties, there is so far no reported information regarding the use of titica vine fibers (TVFs) in engineering composite materials. In this work, the TVF and its epoxy composites were for the first time physically, thermally and mechanically characterized. Additionally, the effect of two kinds of chemical treatments, one with sodium carbonate and one with calcium lignosulfonate, as well as different volume fractions, 10, 20, 30 and 40 vol%, of TVF-reinforced composites were assessed for corresponding basic properties. The thermogravimetric results of the composites reveal enhanced thermal stability for higher TVF content. In addition, the composite incorporated with 40 vol% of TVFs treated with sodium carbonate absorbed 19% more water than the composites with untreated fibers. By contrast, the calcium lignosulfonate treatment decreased water absorption by 8%. The Charpy and Izod impact tests showed that the composites, incorporated with the highest investigated volume fraction (40 vol%) of TVF, significantly increased the absorbed energy by 18% and 28%, respectively, compared to neat epoxy. ANOVA and Tukey statistical analyses displayed no direct influence of the chemical treatments on the energy absorption of the composites for either impact tests. SEM images revealed the main fracture mechanisms responsible for the performance of TVF composites.

SUBMITTER: da Cunha JDSC

PROVIDER: S-EPMC8659021 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Evaluation of Mechanical, Physical, and Morphological Properties of Epoxy Composites Reinforced with Different Date Palm Fillers.

Project description:The present study deals with the fabrication of epoxy composites reinforced with 50 wt% of date palm leaf sheath (G), palm tree trunk (L), fruit bunch stalk (AA), and leaf stalk (A) as filler by the hand lay-up technique. The developed composites were characterized and compared in terms of mechanical, physical and morphological properties. Mechanical tests revealed that the addition of AA improves tensile (20.60-40.12 MPa), impact strength (45.71-99.45 J/m), flexural strength (32.11-110.16 MPa) and density (1.13-1.90 g/cm3). The water absorption and thickness swelling values observed in this study were higher for AA/epoxy composite, revealing its higher cellulosic content, compared to the other composite materials. The examination of fiber pull-out, matrix cracks, and fiber dislocations in the microstructure and fractured surface morphology of the developed materials confirmed the trends for mechanical properties. Overall, from results analysis it can be concluded that reinforcing epoxy matrix with AA filler effectively improves the properties of the developed composite materials. Thus, date palm fruit bunch stalk filler might be considered as a sustainable and green promising reinforcing material similarly to other natural fibers and can be used for diverse commercial, structural, and nonstructural applications requiring high mechanical resistance.

| S-EPMC6651275 | biostudies-literature

Preparation, Thermal Analysis, and Mechanical Properties of Basalt Fiber/Epoxy Composites.

Project description:In this study, basalt fiber-reinforced polymer (BFRP) composites with epoxy matrix, 20 layers, and volume fraction of fibers Vf = 53.66%, were prepared by a hand lay-up compression molding combined method. The fabric of the basalt fibers is in twill 2/2 weave. Through dynamic mechanical analysis (DMA), their viscoelastic behavior at elevated temperatures and in various frequencies was explored, whereas thermomechanical analysis (TMA) took part in terms of creep recovery and stress-relaxation tests. Moreover, the glass transition temperature (Tg) of the BFRP composites was determined through the peak of the tan? curves while the decomposition of the BFRP composites and basalt fibers, in air or nitrogen atmosphere, was explored through thermogravimetric analysis (TGA). The mechanical behavior of the BFRP composites was investigated by tensile and three-point bending experiments. The results showed that as the frequency is raised, the BFRP composites can achieve slightly higher Tg while, under the same circumstances, the storage modulus curve obtains a less steep decrease in the middle transition region. Moreover, the hand lay-up compression molding hybrid technique can be characterized as efficient for the preparation of polymer matrix composites with a relatively high Vf of over 50%. Remarkably, through the TGA experiments, the excellent thermal resistance of the basalt fibers, in the temperature range 30-900 °C, was revealed.

| S-EPMC7465910 | biostudies-literature

Variation of mechanical and thermal properties in sustainable graphene oxide/epoxy composites.

Project description:In this work, the functional graphene oxide (bGO) was facilely synthesized through a grafted reaction between graphene oxide (GO) and bio-based bis-furan di-epoxide (BFDE). The structure of bGO was confirmed by FTIR spectra and Raman spectra. The properties of polymer composite materials depend on the distribution of the nanofiller in the matrix and due to the presence of polymer chains our bGO sheets exhibit a better dispersibility in solvents and polymer matrix, which provides a potential opportunity for the preparation of BFDE composites with excellent performance. Bio-based BFDE composites containing 0.05-0.5 wt.% of bGO exhibit superior mechanical and thermal properties. The addition of just 0.5?wt% such bGO to an BFDE causes 80%, 49%, 21%, 69% and 97% enhancement in tensile strength, flexural strength, flexural modulus, critical stress intensity factor and critical strain energy release rate, respectively. The thermal decomposition temperature Td of bGO/BFDE composites was increased about ~17?°C compared to blank BFDE sample. In addition, we found that introducing unmodified GO to epoxy matrix lead to an insignificant increase of the thermal property of the resulting GO/BFDE composites. The enhanced mechanical properties and thermal properties of bGO/BFDE composites could be attributed to strong interfacial interactions and high affinity between bGO and epoxy matrix.

| S-EPMC6224379 | biostudies-literature

Enhancing the Mechanical Toughness of Epoxy-Resin Composites Using Natural Silk Reinforcements.

Project description:Strong and tough epoxy composites are developed using a less-studied fibre reinforcement, that of natural silk. Two common but structurally distinct silks from the domestic B. mori/Bm and the wild A. pernyi/Ap silkworms are selected in fabric forms. We show that the toughening effects on silk-epoxy composites or SFRPs are dependent on the silk species and the volume fraction of silk. Both silks enhance the room-temperature tensile and flexural mechanical properties of the composite, whereas the more resilient Ap silk shows a more pronounced toughening effect and a lower critical reinforcement volume for the brittle-ductile transition. Specifically, our 60 vol.% Ap-SFRP displays a three-fold elevation in tensile and flexural strength, as compared to pure epoxy resin, with an order of magnitude higher breaking energy via a distinct, ductile failure mode. Importantly, the 60 vol.% Ap-SFRP remains ductile with 7% flexural elongation at lower temperatures (-50?°C). Under impact, these SFRPs show significantly improved energy absorption, and the 60 vol.% Ap-SFRP has an impact strength some eight times that of pure epoxy resin. The findings demonstrate both marked toughening and strengthening effects for epoxy composites from natural silk reinforcements, which presents opportunities for mechanically superior and "green" structural composites.

| S-EPMC5607334 | biostudies-literature

Mechanical and Tribological Behavior of Functionally Graded Unidirectional Glass Fiber-Reinforced Epoxy Composites.

Project description:This paper aims to assess experimentally the mechanical and tribological behavior of conventional and functionally graded (FG) polymeric matrix composites reinforced with continuous glass fibers. The small punch test (SPT) and a pin-on-disc device were used in the present work to examine the mechanical and wear behavior, respectively. The hand lay-up technique was used in the present investigation to manufacture the conventional and FG composites. Various wooden looms with different nailed spacing were employed to manufacture the FG composites. According to test type, the FG composite is composed of four and ten layers, with a different glass fiber volume of fraction (Vf%) for each layer. In addition, the finite element simulation based on Hashin's failure criterion and cohesive zone modeling was used to show the progressive failure and give more explanation regarding the flexural behavior of such composites. The present results indicate that the wear rate of an FG composite could be affected by many factors, including the disk speed, applied load, the composite layers number, and average glass fiber volume fraction. On the other hand, the arrangement of layers in the composite materials by variation of Vf% for each layer can improve the wear rate and value of the ultimate load before the fracture of the composite material when subjected to SPT. The experimental and numerical results for all SPT specimens showed that the fracture of the SPT specimens began beneath the punch tip and grew along the fiber direction. The ultimate flexural capacity of FG composites increased by 30% compared with the conventional composites.

| S-EPMC9147567 | biostudies-literature

High Mechanical and Thermal Properties of Epoxy Composites with Liquid Crystalline Polyurethane Modified Graphene.

Project description:Graphene nanosheets (GNs) often result in incompatibility with the hydrophobic polymer matrix, and the tendency to form aggregates during processing. Herein, liquid crystalline polyurethane modified GNs (GPLP) were obtained by ??? stacking interactions between GNs and perylene bisimide derivatives, and then in-situ polymerization of liquid-crystalline polyurethane. Spectroscopic studies, elemental analysis, and thermal properties confirmed the successful ??? stacking and the integrated structure of GPLP. The good dispersion state of GPLP in the epoxy matrix (EP), and the strong interactions between GPLP and EP, lead to the significant improvement of the thermal and mechanical performance of the GPLP/EP composites. The impact strength, Young's modulus, tensile strength, and toughness of the GPLP/EP composites with 1.47 wt % GNs reached the highest values of 54.31 kJ/m², 530.8 MPa, 112.33 MPa and 863 J/m³, which significantly increased by 210%, 57%, 143%, and 122% compared to that of neat epoxy, respectively. As well, the glass transition temperature increased by a notable 33 °C. It is hoped that this work can be used to exploit more efficient methods to overcome the poor adhesion between GNs and polymers.

| S-EPMC6415506 | biostudies-literature

Enhancing Thermo-Mechanical Properties of Epoxy Composites Using Fumed Silica with Different Surface Treatment.

Project description:The objectives of this study are to improve the thermal and mechanical properties of epoxy/fumed silica composite with different surface treatments of fumed silica. The addition of silica nanoparticles improved the thermal stability of the composite and slowed down the pyrolysis process. The crosslinking density and Tg of the epoxy/fumed silica composites increased because of the interfacial interaction between the PDMS-treated fumed silica particles and the epoxy matrix. The flexural strength of the epoxy nanocomposite was very high even at a low silica content because of the strong interactions between the PDMS-treated fillers and the epoxy matrix. These strong interfacial interactions originate from the attractive forces between the polymer and the filler. Therefore, the polymer nanocomposite containing the PDMS-treated fumed silica is shown to be sufficiently commercially promising.

| S-EPMC8400810 | biostudies-literature

Innovative Fly Ash Geopolymer-Epoxy Composites: Preparation, Microstructure and Mechanical Properties.

Project description:The preparation and characterization of composite materials based on geopolymers obtained from fly ash and epoxy resins are reported for the first time. These materials have been prepared through a synthetic method based on the concurrent reticulation of the organic and inorganic components that allows the formation of hydrogen bonding between the phases, ensuring a very high compatibility between them. These new composites show significantly improved mechanical properties if compared to neat geopolymers with the same composition and comparable performances in respect to analogous geopolymer-based composites obtained starting from more expensive raw material such as metakaolin. The positive combination of an easy synthetic approach with the use of industrial by-products has allowed producing novel low cost aluminosilicate binders that, thanks to their thixotropicity and good adhesion against materials commonly used in building constructions, could be used within the field of sustainable building.

| S-EPMC5456760 | biostudies-other

A Comprehensive Study on the Mechanical Properties of Different 3D Woven Carbon Fiber-Epoxy Composites.

Project description:In this work, the tensile, compressive, and flexural properties of three types of 3D woven composites were studied in three directions. To make an accurate comparison, three 3D woven composites are made to have the same fiber volume content by controlling the weaving parameters of 3D fabric. The results show that the 3D orthogonal woven composite (3DOWC) has better overall mechanical properties than those of the 3D shallow straight-joint woven composite (3DSSWC) and 3D shallow bend-joint woven composite (3DSBWC) in the warp direction, including tension, compression, and flexural strength. Interestingly their mechanical properties in the weft direction are about the same. In the through-thickness direction, however, the tensile and flexural strength of 3DOWC is about the same as 3DSBW, both higher than that of 3DSSWC. The compressive strength, on the other hand, is mainly dependent on the number of weft yarns in the through-thickness direction.

| S-EPMC7344398 | biostudies-literature

Enhancement of mechanical and electrical properties of continuous-fiber-reinforced epoxy composites with stacked graphene.

Project description:Impregnation of expandable graphite (EG) after thermal treatment with an epoxy resin containing surface-active agents (SAAs) enhanced the intercalation of epoxy monomer between EG layers and led to further exfoliation of the graphite, resulting in stacks of few graphene layers, so-called "stacked" graphene (SG). This process enabled electrical conductivity of cured epoxy/SG composites at lower percolation thresholds, and improved thermo-mechanical properties were measured with either Kevlar, carbon or glass-fiber-reinforced composites. Several compositions with SAA-modified SG led to higher dynamic moduli especially at high temperatures, reflecting the better wetting ability of the modified nanoparticles. The hydrophilic/hydrophobic nature of the SAA dictates the surface energy balance. More hydrophilic SAAs promoted localization of the SG at the Kevlar/epoxy interface, and morphology seems to be driven by thermodynamics, rather than the kinetic effect of viscosity. This effect was less obvious with carbon or glass fibers, due to the lower surface energy of the carbon fibers or some incompatibility with the glass-fiber sizing. Proper choice of the surfactant and fine-tuning of the crosslink density at the interphase may provide further enhancements in thermo-mechanical behavior.

| S-EPMC5629411 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data