Propolis in Oral Healthcare: Antibacterial Activity of a Composite Resin Enriched With Brazilian Red Propolis.

ABSTRACT: The aim of this study was to obtain a Brazilian red propolis (BRP) enriched composite resin and to perform the characterization of its antibacterial activity, mechanical, and physical-chemical properties. Brazilian red propolis ethyl acetate extract (EABRP) was characterized by LC-ESI-Orbitrap-FTMS, UPLC-DAD, antibacterial activity, total flavonoids content, and radical scavenging capacity. BRP was incorporated to a commercial composite resin (RC) to obtain BRP enriched composite at 0.1, 0.15 and 0.25% (RP10, RP15 and RP25, respectively). The antibacterial activity RPs was evaluated against Streptococcus mutans by contact direct test and expressed by antibacterial ratio. The RPs were characterized as its cytotoxicity against 3T3 fibroblasts, flexural strength (FS), Knoop microhardness (KHN), post-cure depth (CD), degree of conversion (DC%), water sorption (Wsp), water solubility (Wsl), average roughness (Ra), and thermal analysis. Were identified 50 chemical compounds from BRP extract by LC-ESI-Orbitrap-FTMS. EABRP was bacteriostatic and bactericide at 125 and 500 μg/ml, respectively. The RP25 exhibited antibacterial ratio of 90.76% after 1 h of direct contact with S. mutans (p < 0.0001) while RC no showed significative antibacterial activity (p = 0.1865), both compared with cell control group. RPs and RC no showed cytotoxicity. RPs exhibited CD from 2.74 to 4.48 mm, DC% from 80.70 to 83.96%, Wsp from 17.15 to 21.67 μg/mm3, Wsl from 3.66 to 4.20 μg/mm3, Ra from 14.48 to 20.76 nm. RPs showed thermal resistance between 448-455°C. The results support that propolis can be used on development of modified composite resins that show antibacterial activity and that have compatible mechanical and physical-chemical properties to the indicate for composite resins.

SUBMITTER: Oliveira JMDS

PROVIDER: S-EPMC8667603 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:BackgroundPropolis (bee glue) is a resinous honeybee product having a long history of application in many countries as a traditional remedy for treating wounds, burns, soar throat, stomach disorders, etc. It has been proved to possess beneficial biological effects, including antimicrobial, antioxidant, anti-inflammatory, cytotoxic, antiulcer, and many others. Bees gather propolis from diverse resinous plant parts and in different phytogeographic regions its chemical composition might vary significantly. In this article we report the results of the first study on the chemical profiles of propolis from Oman, its plant origin and antibacterial activity.ResultsThe chemical profiles of Omani propolis extracts were obtained by GC-MS analysis after silylation. Over 50 individual compounds were identified in the samples, belonging to different compound types: sugars, polyols, hydroxy acids, fatty acids, cardanols and cardols, anacardic acids, flavan derivatives, triterpenes, prenylated flavanones and chalcones. The profiles were dissimilar from other known propolis types. They demonstrate that although Oman is not a large country, the plant sources of propolis vary significantly, even in the same apiary and the same season. Based on chemical profiles, and isolation and identification of major marker compounds (new propolis constituents), new plant sources of propolis were found: Azadiracta indica (neem tree) and Acacia spp. (most probably A. nilotica). The ethanol extracts of the studied propolis samples demonstrated activity against S. aureus (MIC?<?100 ?g. mL-1) and E. coli (MIC?<?380 ?g. mL-1).ConclusionOmani propolis is different form the known propolis types and demonstrates significant chemical diversity. Its most important plant source is the resin of Azadirachta indica, and as a result its typical components are ?5-prenyl flavanones. Other plant sources have been identified, too, playing some role in resin collection by bees in Oman: Acacia spp. (most probably A. nilotica) and Mangifera indica. The results demonstrate also the potential of Omani propolis as antimicrobial.

Project description:BackgroundWhite Portland cement is a calcium silicate material. It exhibits antibacterial properties and is biocompatible. In addition, calcium silicate-based materials are known to release calcium ions and form apatite. The purpose of this study was to develop a novel bioactive restorative resin composite with antibacterial and apatite forming properties to prevent tooth caries at the interface of teeth and restorative materials, by incorporation of hydrated calcium silicate (hCS) derived from white Portland cement.MethodsTo prepare the experimental composite resins, a 30 wt% light-curable resin matrix and 70 wt% filler, which was mixed with hCS and silanized glass powder were prepared in following concentrations: 0, 17.5, 35.0, and 52.5 wt% hCS filler. The depth of cure, flexural strength, water sorption, solubility, and antibacterial effect were tested. After immersion in artificial saliva solution for 15, 30, 60, and 90 days, ion concentration by ICP-MS and apatite formation using SEM-EDS, Raman spectroscopy and XRD from experimental specimens were analyzed.ResultsAll experimental groups showed clinically acceptable depths of cure and flexural strength for the use as the restorative composite resin. Water sorption, solubility, released Ca and Si ions increased with the addition of hCS to the experimental composite resin. Experimental groups containing hCS showed greater antibacterial effects compared with the 0 wt% hCS filler group (p < 0.05). The 52.5 wt% hCS filler group produced precipitates mainly composed of Ca and P detected as hydroxyapatite after immersion in artificial saliva solution for 30, 60, and 90 days.ConclusionsThis results show that composite resins containing hCS filler is effective in antibacterial effects. hCS has also apatite formation ability for reducing gap size of microleakage by accumulating hydroxyapatite precipitates at the restoration-tooth interface. Therefore, novel composite resin containing hCS is promising bioactive resin because of its clinically acceptable physiochemical properties, antibacterial properties, and self-sealing potential for prevention of microleakage for longer usage of restorations.

Dataset Information

Propolis in Oral Healthcare: Antibacterial Activity of a Composite Resin Enriched With Brazilian Red Propolis.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets