Temperature-adjustable F-carbon nanofiber/carbon fiber nanocomposite fibrous masks with excellent comfortability and anti-pathogen functionality.

ABSTRACT: Wearing surgical masks remains the most effective protective measure against COVID-19 before mass vaccination, but insufficient comfortability and low antibacterial/antiviral activities accelerate the replacement frequency of surgical masks, resulting in large amounts of medical waste. To solve this problem, we report new nanofiber membrane masks with outstanding comfortability and anti-pathogen functionality prepared using fluorinated carbon nanofibers/carbon fiber (F-CNFs/CF). This was used to replace commercial polypropylene (PP) nonwovens as the core layer of face masks. The through-plane and in-plane thermal conductivity of commercial PP nonwovens were only 0.12 and 0.20 W/m K, but the F-CNFs/CF nanofiber membranes reached 0.62 and 5.23 W/m K, which represent enhancements of 380% and 2523%, respectively. The surface temperature of the PP surgical masks was 23.9 ℃ when the wearing time was 15 min, while the F-CNFs/CF nanocomposite fibrous masks reached 27.3 ℃, displaying stronger heat dissipation. Moreover, the F-CNFs/CF nanofiber membranes displayed excellent electrical conductivity and produced a high-temperature layer that killed viruses and bacteria in the masks. The surface temperature of the F-CNFs/CF nanocomposite fibrous masks reached 69.2 ℃ after being connected to a portable power source for 60 s. Their antibacterial rates were 97.9% and 98.6% against E. coli and S. aureus, respectively, after being connected to a portable power source for 30 min.

SUBMITTER: Xiong SW

PROVIDER: S-EPMC8673729 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Environment-friendly, high-performance cellulose nanofiber-vanillin epoxy nanocomposite with excellent mechanical, thermal insulation and UV shielding properties.

Project description:With the increased demand for biobased epoxy thermosets as an alternative to petroleum-based materials in various fields, developing environment-friendly and high-performance natural fiber-biobased epoxy nanocomposites is crucial for industrial applications. Herein, an environment-friendly nanocomposite is reported by introducing cellulose nanofiber (CNF) in situ interaction with lignin-derived vanillin epoxy (VE) monomer and 4, 4´-diaminodiphenyl methane (DDM) hardener that serves as a multifunctional platform. The CNF-VE nanocomposite is fabricated by simply dispersing the CNF suspension to the VE and DDM hardener solution through the in-situ reaction, and its mechanical properties and thermal insulation behavior, wettability, chemical resistance, and optical properties are evaluated with the CNF weight percent variation. The well-dispersed CNF-VE nanocomposite exhibited high tensile strength (∼127.78 ± 3.99 MPa) and strain-at-break (∼16.49 ± 0.61 %), haziness (∼50 %) and UV-shielding properties. The in situ loading of CNF forms covalent crosslinking with the VE and favors improving the mechanical properties along with the homogeneous dispersion of CNF. The CNF-VE nanocomposite also shows lower thermal conductivity (0.26 Wm-1K-1) than glass. The environment-friendly and high-performance nanocomposite provides multiple platforms and can be used for building materials.

| S-EPMC10847658 | biostudies-literature

Highly Sensitive Ultrathin Flexible Thermoplastic Polyurethane/Carbon Black Fibrous Film Strain Sensor with Adjustable Scaffold Networks.

Project description:In recently years, high-performance wearable strain sensors have attracted great attention in academic and industrial. Herein, a conductive polymer composite of electrospun thermoplastic polyurethane (TPU) fibrous film matrix-embedded carbon black (CB) particles with adjustable scaffold network was fabricated for high-sensitive strain sensor. This work indicated the influence of stereoscopic scaffold network structure built under various rotating speeds of collection device in electrospinning process on the electrical response of TPU/CB strain sensor. This structure makes the sensor exhibit combined characters of high sensitivity under stretching strain (gauge factor of 8962.7 at 155% strain), fast response time (60 ms), outstanding stability and durability (> 10,000 cycles) and a widely workable stretching range (0-160%). This high-performance, wearable, flexible strain sensor has a broad vision of application such as intelligent terminals, electrical skins, voice measurement and human motion monitoring. Moreover, a theoretical approach was used to analyze mechanical property and a model based on tunneling theory was modified to describe the relative change of resistance upon the applied strain. Meanwhile, two equations based from this model were first proposed and offered an effective but simple approach to analyze the change of number of conductive paths and distance of adjacent conductive particles.

| S-EPMC8187661 | biostudies-literature

Silk Fiber Multiwalled Carbon Nanotube-Based Micro-/Nanofiber Composite as a Conductive Fiber and a Force Sensor.

Project description:Silk cocoon fibers (SFs) are natural polymers that are made up of fibroin protein. These natural fibers have higher mechanical stability and good elasticity properties. In this work, we coated multiwalled carbon nanotubes (MWCNTs) on the surface of SFs using a simple stirring technique with vinegar as the medium. This SF-MWCNT micro-/nanofiber composite was prepared without any adhesives. The characterization results revealed that the SF-MWCNT micro-/nanofiber composite exhibited excellent electrical conductivity (995 Ω cm-1), tensile strength (up to 200% greater elongation), and durability characteristics. In addition, this micro-/nanofiber composite shows a change in resistance from 1450 to 960 Ω cm-1 for an applied mechanical force of 0.3-1 N kg-1. Based on our findings, SF-MWCNT micro-/nanofiber composite-based conductive fibers (CFs) and force sensors (FSs) were developed.

| S-EPMC9219082 | biostudies-literature

Nanocomposite Electrospun Nanofiber Membranes for Environmental Remediation.

Project description:Rapid worldwide industrialization and population growth is going to lead to an extensive environmental pollution. Therefore, so many people are currently suffering from the water shortage induced by the respective pollution, as well as poor air quality and a huge fund is wasted in the world each year due to the relevant problems. Environmental remediation necessitates implementation of novel materials and technologies, which are cost and energy efficient. Nanomaterials, with their unique chemical and physical properties, are an optimum solution. Accordingly, there is a strong motivation in seeking nano-based approaches for alleviation of environmental problems in an energy efficient, thereby, inexpensive manner. Thanks to a high porosity and surface area presenting an extraordinary permeability (thereby an energy efficiency) and selectivity, respectively, nanofibrous membranes are a desirable candidate. Their functionality and applicability is even promoted when adopting a nanocomposite strategy. In this case, specific nanofillers, such as metal oxides, carbon nanotubes, precious metals, and smart biological agents, are incorporated either during electrospinning or in the post-processing. Moreover, to meet operational requirements, e.g., to enhance mechanical stability, decrease of pressure drop, etc., nanofibrous membranes are backed by a microfibrous non-woven forming a hybrid membrane. The novel generation of nanocomposite/hybrid nanofibrous membranes can perform extraordinarily well in environmental remediation and control. This reality justifies authoring of this review paper.

| S-EPMC5453108 | biostudies-other

Antibacterial Properties of Honey Nanocomposite Fibrous Meshes.

Project description:Natural substances are increasingly being developed for use in health-related applications. Honey has attracted significant interest, not only for its physical and chemical properties, but also for its antibacterial activity. For the first time, suspensions of Black Forest honeydew honey and manuka honey UMF 20+ were examined for their antibacterial properties against Escherichia coli and Staphylococcus epidermidis using flow cytometry. The inhibitory effect of honey on bacterial growth was evident at concentrations of 10, 20 and 30 v/v%. The minimum inhibitory effects of both honey types against each bacterium were also investigated and reported. Electrospray ionisation (ESI) mass spectrometry was performed on both Black Forest honeydew honey and manuka honey UMF 20+. Manuka honey had a gluconic concentration of 2519 mg/kg, whilst Black Forest honeydew honey had a concentration of 2195 mg/kg. Manuka honey demonstrated the strongest potency when compared to Black Forest honeydew honey; therefore, it was incorporated into nanofiber scaffolds using pressurised gyration and 10, 20 and 30 v/v% manuka honey-polycaprolactone solutions. Composite fibres were analysed for their morphology and topography using scanning electron microscopy. The average fibre diameter of the manuka honey-polycaprolactone scaffolds was found to range from 437 to 815 nm. The antibacterial activity of the 30 v/v% scaffolds was studied using S. epidermidis. Strong antibacterial activity was observed with a bacterial reduction rate of over 90%. The results show that honey composite fibres formed using pressurised gyration can be considered a natural therapeutic agent for various medicinal purposes, including wound-healing applications.

| S-EPMC9740266 | biostudies-literature

Co-axial fibrous scaffolds integrating with carbon fiber promote cardiac tissue regeneration post myocardial infarction.

Project description:Myocardium is an excitable tissue with electrical conductivity and mechanical strength. In this work, carbon fibers (CFs) and co-axial fibrous mesh were integrated which combined the high modulus and excellent electrical conductivity of CFs and the fibrous and porous structures of the electrospun fibers. The scaffold was fabricated by simply integrating coaxial electrospun fibers and carbon fibers through a freeze-drying procedure. It was shown that the integration of carbon fibers have the conductivity and Young's modulus of the fibrous mesh increased significantly, meanwhile, upregulated the expression of CX43, α-actinin, RhoA of the neonatal rat primary cardiomyocytes and primary human umbilical vein endothelial cells (HUVECs), and promoted the secretion of VEGF of HUVECs. Moreover, the cardiomyocytes grown on the scaffolds increased the ability of HUVECs migration. When implanted to the injury area post myocardial infraction, the scaffolds were able to effectively enhance the tissue regeneration and new vessel formation, which rescued the heart dysfunction induced by the myocardial infraction, evidenced by the results of echocardiography and histochemical analysis. In conclusion, the composite scaffolds could promote the myocardium regeneration and function's recovery by enhancing cardiomyocytes maturation and angiogenesis and establishing the crosstalk between the cardiomyocytes and the vascular endothelial cells.

| S-EPMC9465342 | biostudies-literature

Temperature-responsive biocompatible copolymers incorporating hyperbranched polyglycerols for adjustable functionality.

Project description:Temperature-triggered copolymers are proposed for a number of bio-applications but there is no ideal material platform, especially for injectable drug delivery. Options are needed for degradable biomaterials that not only respond to temperature but also easily accommodate linkage of active molecules. A first step toward realizing this goal is the design and synthesis of the novel materials reported herein. A multifunctional macromer, methacrylated hyperbranched polyglycerol (HPG-MA) with an average of one acrylate unit per copolymer, was synthesized and copolymerized with N-isopropylacrylamide (NIPAAm), hydroxyethyl methacrylate-polylactide (HEMAPLA) and acrylic acid (AAc). The potential to fully exploit the copolymers by modification of the multiple HPG hydroxyl groups will not be discussed here. Instead, this report focuses on the thermoresponsive, biocompatible, and degradation properties of the material. Poly(NIPAAm-co-HEMAPLA-co-AAc-co-HPG-MA) displayed increasing lower critical solution temperatures (LCST) as the HPG content increased over a range of macromer ratios. For the copolymer with the maximum HPG incorporation (17%), the LCST was ~30 °C. In addition, this sample showed no toxicity when human uterine fibroid cells were co-cultured with the copolymer for up to 72 h. This copolymer lost approximately 92% of its mass after 17 hours at 37 °C. Thus, the reported biomaterials offer attractive properties for the design of drug delivery systems where orthogonally triggered mechanisms of therapeutic release in relatively short time periods would be attractive.

| S-EPMC3208240 | biostudies-literature

Niobia Nanofiber-Reinforced Protective Niobium Oxide/Acrylate Nanocomposite Coatings.

Project description:In the present study, the corrosion resistance of a new niobium oxide/acrylate hybrid nanocomposite coating doped with niobia nanofibers is investigated. Nanofibers were initially synthesized from niobium(V) chloride precursor in a novel autoclave approach before fabricating the base coating from a two-step process involving the syntheses of acrylate resin via free radical polymerization and niobium oxide gel from niobium ethoxide via a sol-gel technique. Variants of the synthesized nanocomposite coating were incorporated with varying concentrations of niobia nanofibers before spin-coating on Q235 steel substrates to inhibit corrosive electrolytic ion percolation and further enhance corrosion resistance when treated with chloride-enriched corrosive media. The corrosion resistance of these nanocomposite coatings increased with nanofiber content up to an optimum concentration due to the corrosion-inhibiting and protective effects of niobium barrier layers within these coatings. The presence of the niobia nanofibers also promoted improved surface contact angle and toughened mechanical strengths.

| S-EPMC7711932 | biostudies-literature

Multiscale landscaping of droplet wettability on fibrous layers of facial masks.

Project description:Liquid mobility is ubiquitous in nature, with droplets emerging at all size scales, and artificial surfaces have been designed to mimic such mobility over the past few decades. Meanwhile, millimeter-sized droplets are frequently used for wettability characterization, even with facial mask applications, although these applications have a droplet-size target range that spans from millimeters to aerosols measuring less than a few micrometers. Unlike large droplets, microdroplets can interact sensitively with the fibers they contact with and are prone to evaporation. However, wetting behaviors at the single-microfiber level remain poorly understood. Herein, we characterized the wettability of fibrous layers, which revealed that a multiscale landscape of droplets ranged from the millimeter to the micrometer scale. The contact angle (CA) values of small droplets on pristine fibrous media showed sudden decrements, especially on a single microfiber, owing to the lack of air cushions for the tiny droplets. Moreover, droplets easily adhered to the pristine layer during droplet impact tests and then yielding widespread areas of contamination on the microfibers. To resolve this, we carved nanowalls on the pristine fibers by plasma etching, which effectively suppressed such wetting phenomena. Significantly, the resulting topographies of the microfibers managed the dynamic wettability of droplets at the multiscale, which reduced the probability of contamination with impact droplets and suppressed the wetting transition upon evaporation. These findings for the dynamic wettability of fibrous media will be useful in the fight against infectious droplets.

| S-EPMC9897442 | biostudies-literature

Electrospun Fibrous Nanocomposite Sensing Materials for Monitoring Biomarkers in Exhaled Breath.

Project description:Human-exhaled breath mainly contains water, oxygen, carbon dioxide, and endogenous gases closely related to human metabolism. The linear relationship between breath acetone and blood glucose concentration has been revealed when monitoring diabetes patients. Considerable attention has been directed toward developing a highly sensitive volatile organic compounds (VOCs) sensing material that can detect breath acetone. In this study, we propose a tungsten oxide/tin oxide/silver/poly (methyl methacrylate) (WO3/SnO2/Ag/PMMA) sensing material fabricated using the electrospinning technique. By monitoring the evolution of sensing materials' extinction spectra, low concentrations of acetone vapor can be detected. Moreover, the interfaces between SnO2 and WO3 nanocrystals construct n-n junctions, which generate more electron-hole pairs than those without such structure when the light strikes. This helps to improve the sensitivity of sensing materials when they are subjected to acetone surroundings. The established sensing materials (WO3/SnO2/Ag/PMMA) exhibit a sensing limit of 20 ppm for acetone vapor and show specificity for acetone even in ambient humidity.

| S-EPMC10143897 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data