Three-Layer PdO/CuWO₄/CuO System for Hydrogen Gas Sensing with Reduced Humidity Interference.

ABSTRACT: The growing hydrogen industry is stimulating an ongoing search for new materials not only for hydrogen production or storage but also for hydrogen sensing. These materials have to be sensitive to hydrogen, but additionally, their synthesis should be compatible with the microcircuit industry to enable seamless integration into various devices. In addition, the interference of air humidity remains an issue for hydrogen sensing materials. We approach these challenges using conventional reactive sputter deposition. Using three consequential processes, we synthesized multilayer structures. A basic two-layer system composed of a base layer of cupric oxide (CuO) overlayered with a nanostructured copper tungstate (CuWO₄) exhibits higher sensitivity than individual materials. This is explained by the formation of microscopic heterojunctions. The addition of a third layer of palladium oxide (PdO) in forms of thin film and particles resulted in a reduction in humidity interference. As a result, a sensing three-layer system working at 150 °C with an equalized response in dry/humid air was developed.

SUBMITTER: Kumar N

PROVIDER: S-EPMC8704960 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Improved NO<sub>2</sub> Gas Sensing Properties of Graphene Oxide Reduced by Two-beam-laser Interference.

Project description:We report on the fabrication of a NO2 gas sensor from room-temperature reduction of graphene oxide(GO) via two-beam-laser interference (TBLI). The method of TBLI gives the distribution of periodic dissociation energies for oxygen functional groups, which are capable to reduce the graphene oxide to hierarchical graphene nanostructures, which holds great promise for gaseous molecular adsorption. The fabricated reduced graphene oxide(RGO) sensor enhanced sensing response in NO2 and accelerated response/recovery rates. It is seen that, for 20 ppm NO2, the response (Ra/Rg) of the sensor based on RGO hierarchical nanostructures is 1.27, which is higher than that of GO (1.06) and thermal reduced RGO (1.04). The response time and recovery time of the sensor based on laser reduced RGO are 10 s and 7 s, which are much shorter than those of GO (34 s and 45 s), indicating that the sensing performances for NO2 sensor at room temperature have been enhanced by introduction of nanostructures. This mask-free and large-area approach to the production of hierarchical graphene micro-nanostructures, could lead to the implementation of future graphene-based sensors.

| S-EPMC5861053 | biostudies-literature

Tackling Humidity with Designer Ionic Liquid-Based Gas Sensing Soft Materials.

Project description:Relative humidity is simultaneously a sensing target and a contaminant in gas and volatile organic compound (VOC) sensing systems, where strategies to control humidity interference are required. An unmet challenge is the creation of gas-sensitive materials where the response to humidity is controlled by the material itself. Here, humidity effects are controlled through the design of gelatin formulations in ionic liquids without and with liquid crystals as electrical and optical sensors, respectively. In this design, the anions [DCA]- and [Cl]- of room temperature ionic liquids from the 1-butyl-3-methylimidazolium family tailor the response to humidity and, subsequently, sensing of VOCs in dry and humid conditions. Due to the combined effect of the materials formulations and sensing mechanisms, changing the anion from [DCA]- to the much more hygroscopic [Cl]- , leads to stronger electrical responses and much weaker optical responses to humidity. Thus, either humidity sensors or humidity-tolerant VOC sensors that do not require sample preconditioning or signal processing to correct humidity impact are obtained. With the wide spread of 3D- and 4D-printing and intelligent devices, the monitoring and tuning of humidity in sustainable biobased materials offers excellent opportunities in e-nose sensing arrays and wearable devices compatible with operation at room conditions.

| S-EPMC7613046 | biostudies-literature

Hydrogen gas sensing using aluminum doped ZnO metasurfaces.

Project description:Hydrogen (H2) sensing is crucial in a wide variety of areas, such as industrial, environmental, energy and biomedical applications. However, engineering a practical, reliable, fast, sensitive and cost-effective hydrogen sensor is a persistent challenge. Here we demonstrate hydrogen sensing using aluminum-doped zinc oxide (AZO) metasurfaces based on optical read-out. The proposed sensing system consists of highly ordered AZO nanotubes (hollow pillars) standing on a SiO2 layer deposited on a Si wafer. Upon exposure to hydrogen gas, the AZO nanotube system shows a wavelength shift in the minimum reflectance by ∼13 nm within 10 minutes for a hydrogen concentration of 4%. These AZO nanotubes can also sense the presence of a low concentration (0.7%) of hydrogen gas within 10 minutes. Their rapid response time even for a low concentration, the possibility of large sensing area fabrication with good precision, and high sensitivity at room temperature make these highly ordered nanotube structures a promising miniaturized H2 gas sensor.

| S-EPMC9417916 | biostudies-literature

Charge-transfer-based gas sensing using atomic-layer MoS2.

Project description:Two-dimensional (2D) molybdenum disulphide (MoS2) atomic layers have a strong potential to be used as 2D electronic sensor components. However, intrinsic synthesis challenges have made this task difficult. In addition, the detection mechanisms for gas molecules are not fully understood. Here, we report a high-performance gas sensor constructed using atomic-layered MoS2 synthesised by chemical vapour deposition (CVD). A highly sensitive and selective gas sensor based on the CVD-synthesised MoS2 was developed. In situ photoluminescence characterisation revealed the charge transfer mechanism between the gas molecules and MoS2, which was validated by theoretical calculations. First-principles density functional theory calculations indicated that NO2 and NH3 molecules have negative adsorption energies (i.e., the adsorption processes are exothermic). Thus, NO2 and NH3 molecules are likely to adsorb onto the surface of the MoS2. The in situ PL characterisation of the changes in the peaks corresponding to charged trions and neutral excitons via gas adsorption processes was used to elucidate the mechanisms of charge transfer between the MoS2 and the gas molecules.

| S-EPMC4307013 | biostudies-literature

Self-Assembled Monolayers Coated Porous SnO2 Film Gas Sensor with Reduced Humidity Influence.

Project description:Metal-oxide sensors, detect gas through the reaction of surface oxygen molecules with target gases, are promising for the detection of toxic pollutant gases, combustible gases, and organic vapors; however, their sensitivity, selectivity, and long-term stability limit practical applications. Porous structure for increasing surface area, adding catalyst, and altering the operation temperature are proposed for enhancing the sensitivity and selectivity. Although humidity can significantly affect the property and stability of the sensors, studies focusing on the long-term stability of gas sensors are scarce. To reduce the effects of humidity, 1H, 1H, 2H, 2H-perfluorooctyltriethoxysilane (PFOTS) was coated on a porous SnO2 film. The interconnected SnO2 nanowires improved the high surface area, and the PFOTS coating provided superhydrophobicity at water contact angle of 159°and perfect water vapor repellency inside E-SEM. The superhydrophobic porous morphology was maintained under relative humidity of 99% and operating temperature of 300 °C. The CO gas sensing of 5, 20, and 50 ppm were obtained with linearity at various humidity. Flame detection was also achieved with practical high humidity conditions. These results suggest the simple way for reliable sensing of nanostructured metal-oxide gas sensors with high sensitivity and long-term stability even in highly humid environments.

| S-EPMC7829704 | biostudies-literature

Fully Inkjet-Printed CuO Sensor on Flexible Polymer Substrate for Alcohol Vapours and Humidity Sensing at Room Temperature.

Project description:This work focuses on an inkjet-fabricated sensor based on copper oxide nanostructured particles on polymer flexible substrate for the sensing of alcohol vapours and humidity at room temperature. Nanoparticles were prepared by a microwave-assisted solvothermal sealed vessel synthesis method. The ink composition was developed on the basis of viscosity and surface tension optimization by the addition of polymeric steric surfactant and dispersant. The printing process was optimized with the help of non-dimensional criteria. Silver nanoink was used for the printing of an interdigitated pattern on a PET substrate which was overprinted by the copper oxide ink, thus obtaining a flexible flat sensor. Material design and all fabrication steps of the sensor respected the temperature limitation given by the thermal stability of the polymer substrate. Printed layers and motifs were characterized microscopically and by resistance measurement. The effectiveness of the prepared sensor was demonstrated and studied by measuring the response to saturated vapours at room temperature. The sensing layer showed the opposite resistance response to stimuli than expected for the well-known p-type sensing mechanism of CuO sensors operated at high temperatures. In addition to vapour sorption, condensation and desorption influencing electron, proton and ionic conductivity, manifestation of another mechanism was observed and an explanation suggested in terms of the electrochemical mechanism.

| S-EPMC6678509 | biostudies-literature

Laser-Tunable Printed ZnO Nanoparticles for Paper-Based UV Sensors with Reduced Humidity Interference.

Project description:Development of paper-based sensors that do not suffer with humidity interference is desirable for practical environmental applications. In this work, a laser processing method was reported to effectively modulate the cross-sensitivity to humidity of ZnO-based UV (Ultraviolet) sensors printed on paper substrate. The results reveal that the laser induced zinc oxide (ZnO) surface morphology contributes to the super-hydrophobicity of the printed ZnO nanoparticles, reducing humidity interference while enhancing UV sensitivity. Herein, this conducted research highlights for the first time that laser processing is an attractive choice that reduces the cross-sensitivity to water vapor in the UV sensing response of ZnO-based devices printed on paper, paving the way to low-cost and sophisticated paper-based sensors.

| S-EPMC7824355 | biostudies-literature

Effect of Humidity on Light-Activated NO and NO2 Gas Sensing by Hybrid Materials.

Project description:Air humidity is one of the main factors affecting the characteristics of semiconductor gas sensors, especially at low measurement temperatures. In this work we analyzed the influence of relative humidity on sensor properties of the hybrid materials based on the nanocrystalline SnO2 and In2O3 and Ru (II) heterocyclic complex and verified the possibility of using such materials for NO (0.25-4.0 ppm) and NO2 (0.05-1.0 ppm) detection in high humidity conditions (relative humidity (RH) = 20%, 40%, 65%, 90%) at room temperature during periodic blue (?max = 470 nm) illumination. To reveal the reasons for the different influence of humidity on the sensors' sensitivity when detecting NO and NO2, electron paramagnetic resonance (EPR) spectroscopy and di?use re?ectance infrared Fourier transform spectroscopy (DRIFTS) investigations were undertaken. It was established that the substitution of adsorbed oxygen by water molecules causes the decrease in sensor response to NO in humid air. The influence of humidity on the interaction of sensitive materials with NO2 is determined by the following factors: the increase in charge carrier's concentration, the decrease in the number of active sites capable of interacting with gases, and possible substitution of chemisorbed oxygen with NO2- groups.

| S-EPMC7279420 | biostudies-literature

Thermally reduced kaolin-graphene oxide nanocomposites for gas sensing.

Project description:Highly sensitive graphene-based gas sensors can be made using large-area single layer graphene, but the cost of large-area pure graphene is high, making the simpler reduced graphene oxide (rGO) an attractive alternative. To use rGO for gas sensing, however, require a high active surface area and slightly different approach is needed. Here, we report on a simple method to produce kaolin-graphene oxide (GO) nanocomposites and an application of this nanocomposite as a gas sensor. The nanocomposite was made by binding the GO flakes to kaolin with the help of 3-Aminopropyltriethoxysilane (APTES). The GO flakes in the nanocomposite were contacting neighboring GO flakes as observed by electron microscopy. After thermal annealing, the nanocomposite become conductive as showed by sheet resistance measurements. Based on the conductance changes of the nanocomposite films, electrical gas sensing devices were made for detecting NH3 and HNO3. These devices had a higher sensitivity than thermally annealed multilayer GO films. This kaolin-GO nanocomposite might be useful in applications that require a low-cost material with large conductive surface area including the demonstrated gas sensors.

| S-EPMC5378989 | biostudies-literature

CuO-Decorated ZnO Hierarchical Nanostructures as Efficient and Established Sensing Materials for H2S Gas Sensors.

Project description:Highly sensitive hydrogen sulfide (H2S) gas sensors were developed from CuO-decorated ZnO semiconducting hierarchical nanostructures. The ZnO hierarchical nanostructure was fabricated by an electrospinning method following hydrothermal and heat treatment. CuO decoration of ZnO hierarchical structures was carried out by a wet method. The H2S gas-sensing properties were examined at different working temperatures using various quantities of CuO as the variable. CuO decoration of the ZnO hierarchical structure was observed to promote sensitivity for H2S gas higher than 30 times at low working temperature (200 °C) compared with that in the nondecorated hierarchical structure. The sensing mechanism of the hybrid sensor structure is also discussed. The morphology and characteristics of the samples were examined by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV-vis absorption, photoluminescence (PL), and electrical measurements.

| S-EPMC4882619 | biostudies-literature