Influence of Mixed Imide Composition and Thermal Annealing on Ionic Liquid Uptake and Conductivity of Polyimide-Poly(ethylene glycol) Segmented Block Copolymer Membranes.

ABSTRACT: Understanding the impact of different bridging groups in the two-step polymerization of poly(ethylene glycol) (PEG)-incorporated polyimide (PI) materials is significant. It is known that the proton exchange membranes (PEMs) used in industry today can experience performance degradation under rising temperature conditions. Many efforts have been devoted to overcoming this problem by improving the physical and mechanical properties that extend the hygrothermal life of a PEM. This work examines the effect of oxygenated and fluorinated bridging anhydrides in the production of PI-PEG PEMs. It is shown that the dianhydride identity and the amount incorporated in the synthesis influences the properties of the segmented block copolymer (SBC) membranes, such as increased ionic liquid uptake (ILU), enhanced conductivity and higher Young's modulus favoring stiffness comparable to Nafion 115, an industrial standard. Investigations on the ionic conductivity of PI-PEG membranes were carried out to determine how thermal annealing would affect the material's performance as an ion-exchange membrane. By applying a thermal annealing process at 60 °C for one hour, the conductivities of synthesized segmented block copolymer membranes values were increased. The effect of thermal annealing on the mechanical properties was also shown for the undoped SBC via measuring the change in the Young's modulus. These higher ILU abilities and mechanical behavior changes are thought to arise from the interaction between PEG molecules and ethylammonium nitrate (EAN) ionic liquid (IL). In addition, higher interconnected routes provide a better ion-transfer environment within the membrane. It was found that the conductivity was increased by a factor of ten for undoped and a factor of two to seven for IL-doped membranes after thermal annealing.

SUBMITTER: Ciftcioglu GA

PROVIDER: S-EPMC8705581 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Proton exchange membranes (PEMs) suffer performance degradation under certain conditions-temperatures greater than 80 °C, relative humidity less than 50%, and water retention less than 22%. Novel materials are needed that have improved water retention, stability at higher temperatures, flexibility, conductivity, and the ability to function at low humidity. This work focuses on polyimide-poly(ethylene glycol) (PI-PEG) segmented block copolymer (SBC) membranes with high conductivity and mechanical strength. Membranes were prepared with one of two ionic liquids (ILs), either ethylammonium nitrate (EAN) or propylammonium nitrate (PAN), incorporated within the membrane structure to enhance the proton exchange capability. Ionic liquid uptake capacities were compared for two different temperatures, 25 and 60 °C. Then, conductivities were measured for a series of combinations of undoped or doped unannealed and undoped or doped annealed membranes. Stress and strain tests were performed for unannealed and thermally annealed undoped membranes. Later, these experiments were repeated for doped unannealed and thermally annealed. Mechanical and conductivity data were interpreted in the context of prior small angle X-ray scattering (SAXS) studies on similar materials. We have shown that varying the compositions of polyimide-poly(ethylene glycol) (PI-PEG) SBCs allowed the morphology in the system to be tuned. Since polyimides (PI) are made from the condensation of dianhydrides and diamines, this was accomplished using components having different functional groups. Dianhydrides having either fluorinated or oxygenated functional groups and diamines having either fluorinated or oxygenated diamines were used as well as mixtures of these species. Changing the morphology by creating macrophase separation elevated the IL uptake capacities, and in turn, increased their conductivities by a factor of three or more compared to Nafion 115. The stiffness of the membranes synthesized in this work was comparable to Nafion 115 and, thus, sufficient for practical applications.

Dataset Information

Influence of Mixed Imide Composition and Thermal Annealing on Ionic Liquid Uptake and Conductivity of Polyimide-Poly(ethylene glycol) Segmented Block Copolymer Membranes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets