Epitaxial Growth of Diamond-Shaped Au_1/2Ag_1/2CN Nanocrystals on Graphene.

ABSTRACT: Epitaxial synthesis of inorganic nanomaterials on pristine 2D materials is of interest in the development of nanostructured devices and nanocomposite materials, but is quite difficult because pristine surfaces of 2D materials are chemically inert. Previous studies found a few exceptions including AuCN, AgCN, CuCN, and Cu_0.5Au_0.5CN, which can be preferentially synthesized and epitaxially aligned onto various 2D materials. Here, we discover that Au_1/2Ag_1/2CN forms diamond-shaped nanocrystals epitaxially grown on pristine graphene surfaces. The nanocrystals synthesized by a simple drop-casting method are crystallographically aligned to lattice structures of the underlying graphene. Our experimental investigations on 3D structures and the synthesis conditions of the nanocrystals imply that the rhombic 2D geometries originate from different growth rates depending on orientations along and perpendicular to 1D molecular chains of Au_1/2Ag_1/2CN. We also perform in situ TEM observations showing that Au_1/2Ag_1/2CN nanocrystals are decomposed to Au and Ag alloy nanocrystals under electron beam irradiation. Our experimental results provide an additional example of 1D cyanide chain families that form ordered nanocrystals epitaxially aligned on 2D materials, and reveal basic physical characteristics of this rarely investigated nanomaterial.

SUBMITTER: Park C

PROVIDER: S-EPMC8706316 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Growth of Epitaxial Oxide Thin Films on Graphene.

Project description:The transfer process of graphene onto the surface of oxide substrates is well known. However, for many devices, we require high quality oxide thin films on the surface of graphene. This step is not understood. It is not clear why the oxide should adopt the epitaxy of the underlying oxide layer when it is deposited on graphene where there is no lattice match. To date there has been no explanation or suggestion of mechanisms which clarify this step. Here we show a mechanism, supported by first principles simulation and structural characterisation results, for the growth of oxide thin films on graphene. We describe the growth of epitaxial SrTiO3 (STO) thin films on a graphene and show that local defects in the graphene layer (e.g. grain boundaries) act as bridge-pillar spots that enable the epitaxial growth of STO thin films on the surface of the graphene layer. This study, and in particular the suggestion of a mechanism for epitaxial growth of oxides on graphene, offers new directions to exploit the development of oxide/graphene multilayer structures and devices.

| S-EPMC4981861 | biostudies-literature

TAO-DFT Study on the Electronic Properties of Diamond-Shaped Graphene Nanoflakes.

Project description:At the nanoscale, it has been rather troublesome to properly explore the properties associated with electronic systems exhibiting a radical nature using traditional electronic structure methods. Graphene nanoflakes, which are graphene nanostructures of different shapes and sizes, are typical examples. Recently, TAO-DFT (i.e., thermally-assisted-occupation density functional theory) has been formulated to tackle such challenging problems. As a result, we adopt TAO-DFT to explore the electronic properties associated with diamond-shaped graphene nanoflakes with n = 2-15 benzenoid rings fused together at each side, designated as n-pyrenes (as they could be expanded from pyrene). For all the n values considered, n-pyrenes are ground-state singlets. With increasing the size of n-pyrene, the singlet-triplet energy gap, vertical ionization potential, and fundamental gap monotonically decrease, while the vertical electron affinity and symmetrized von Neumann entropy (which is a quantitative measure of radical nature) monotonically increase. When n increases, there is a smooth transition from the nonradical character of the smaller n-pyrenes to the increasing polyradical nature of the larger n-pyrenes. Furthermore, the latter is shown to be related to the increasing concentration of active orbitals on the zigzag edges of the larger n-pyrenes.

| S-EPMC7353095 | biostudies-literature

Epitaxial growth of ?-stacked perfluoropentacene on graphene-coated quartz.

Project description:Chemical-vapor-deposited large-area graphene is employed as the coating of transparent substrates for the growth of the prototypical organic n-type semiconductor perfluoropentacene (PFP). The graphene coating is found to cause face-on growth of PFP in a yet unknown substrate-mediated polymorph, which is solved by combining grazing-incidence X-ray diffraction with theoretical structure modeling. In contrast to the otherwise common herringbone arrangement of PFP in single crystals and "standing" films, we report a ?-stacked arrangement of coplanar molecules in "flat-lying" films, which exhibit an exceedingly low ?-stacking distance of only 3.07 Å, giving rise to significant electronic band dispersion along the ?-stacking direction, as evidenced by ultraviolet photoelectron spectroscopy. Our study underlines the high potential of graphene for use as a transparent electrode in (opto-)electronic applications, where optimized vertical transport through flat-lying conjugated organic molecules is desired.

| S-EPMC3558021 | biostudies-literature

Flower-shaped domains and wrinkles in trilayer epitaxial graphene on silicon carbide.

Project description:Trilayer graphene is of particular interest to the 2D materials community because of its unique tunable electronic structure. However, to date, there is a lack of fundamental understanding of the properties of epitaxial trilayer graphene on silicon carbide. Here, following successful synthesis of large-area uniform trilayer graphene, atomic force microscopy (AFM) showed that the trilayer graphene on 6H-SiC(0001) was uniform over a large scale. Additionally, distinct defects, identified as flower-shaped domains and isolated wrinkle structures, were observed randomly on the surface using scanning tunneling microscopy and spectroscopy (STM/STS). These carbon nanostructures formed during growth, has different structural and electronic properties when compared with the adjacent flat regions of the graphene. Finally, using low temperature STM/STS at 4K, we found that the isolated wrinkles showed an irreversible rotational motion between two 60° configurations at different densities of states.

| S-EPMC3920218 | biostudies-other

Epitaxial diamond-hexagonal silicon nano-ribbon growth on (001) silicon.

Project description:Silicon crystallizes in the diamond-cubic phase and shows only a weak emission at 1.1 eV. Diamond-hexagonal silicon however has an indirect bandgap at 1.5 eV and has therefore potential for application in opto-electronic devices. Here we discuss a method based on advanced silicon device processing to form diamond-hexagonal silicon nano-ribbons. With an appropriate temperature anneal applied to densify the oxide fillings between silicon fins, the lateral outward stress exerted on fins sandwiched between wide and narrow oxide windows can result in a phase transition from diamond-cubic to diamond-hexagonal Si at the base of these fins. The diamond-hexagonal slabs are generally 5-8 nm thick and can extend over the full width and length of the fins, i.e. have a nano-ribbon shape along the fins. Although hexagonal silicon is a metastable phase, once formed it is found being stable during subsequent high temperature treatments even during process steps up to 1050?ºC.

| S-EPMC4523848 | biostudies-other

Large-area epitaxial growth of curvature-stabilized ABC trilayer graphene.

Project description:The properties of van der Waals (vdW) materials often vary dramatically with the atomic stacking order between layers, but this order can be difficult to control. Trilayer graphene (TLG) stacks in either a semimetallic ABA or a semiconducting ABC configuration with a gate-tunable band gap, but the latter has only been produced by exfoliation. Here we present a chemical vapor deposition approach to TLG growth that yields greatly enhanced fraction and size of ABC domains. The key insight is that substrate curvature can stabilize ABC domains. Controllable ABC yields ~59% were achieved by tailoring substrate curvature levels. ABC fractions remained high after transfer to device substrates, as confirmed by transport measurements revealing the expected tunable ABC band gap. Substrate topography engineering provides a path to large-scale synthesis of epitaxial ABC-TLG and other vdW materials.

| S-EPMC6987307 | biostudies-literature

Surface Structure of Aerobically Oxidized Diamond Nanocrystals.

Project description:We investigate the aerobic oxidation of high-pressure, high-temperature nanodiamonds (5-50 nm dimensions) using a combination of carbon and oxygen K-edge X-ray absorption, wavelength-dependent X-ray photoelectron, and vibrational spectroscopies. Oxidation at 575 °C for 2 h eliminates graphitic carbon contamination (>98%) and produces nanocrystals with hydroxyl functionalized surfaces as well as a minor component (<5%) of carboxylic anhydrides. The low graphitic carbon content and the high crystallinity of HPHT are evident from Raman spectra acquired using visible wavelength excitation (?excit = 633 nm) as well as carbon K-edge X-ray absorption spectra where the signature of a core-hole exciton is observed. Both spectroscopic features are similar to those of chemical vapor deposited (CVD) diamond but differ significantly from the spectra of detonation nanodiamond. The importance of these findings to the functionalization of nanodiamond surfaces for biological labeling applications is discussed.

| S-EPMC4242000 | biostudies-literature

Diamond-Graphene Composite Nanostructures.

Project description:The search for new nanostructural topologies composed of elemental carbon is driven by technological opportunities as well as the need to understand the structure and evolution of carbon materials formed by planetary shock impact events and in laboratory syntheses. We describe two new families of diamond-graphene (diaphite) phases constructed from layered and bonded sp3 and sp2 nanostructural units and provide a framework for classifying the members of this new class of materials. The nanocomposite structures are identified within both natural impact diamonds and laboratory-shocked samples and possess diffraction features that have previously been assigned to lonsdaleite and postgraphite phases. The diaphite nanocomposites represent a new class of high-performance carbon materials that are predicted to combine the superhard qualities of diamond with high fracture toughness and ductility enabled by the graphitic units and the atomically defined interfaces between the sp3- and sp2-bonded nanodomains.

| S-EPMC7227005 | biostudies-literature

CdSe Ring- and Tribulus-Shaped Nanocrystals: Controlled Synthesis, Growth Mechanism, and Photoluminescence Properties.

Project description:With air-stable and generic reagents, CdSe nanocrystals with tunable morphologies were prepared by controlling the temperature in the solution reaction route. Thereinto, the lower reaction temperature facilitates the anisotropic growth of crystals to obtain high-yield CdSe ring- and tribulus-shaped nanocrystals with many branches on their surfaces. The photoluminescence properties are sensitive to the nature of particle and its surface. The products synthesized at room temperature, whose surfaces have many branches, show higher blue shift and narrower emission linewidths (FWHM) of photoluminescence than that of samples prepared at higher temperature, whose surfaces have no branches. Microstructural studies revealed that the products formed through self-assembly of primary crystallites. Nanorings formed through the nonlinear attachment of primary crystallites, and the branches on the surfaces grew by linear attachment at room temperature. And the structure of tribulus-shaped nanoparticle was realized via two steps of aggregation, i.e., random and linear oriented aggregation. Along with the elevation of temperature, the branches on nanocrystal surfaces shortened gradually because of the weakened linear attachment. ELECTRONIC SUPPLEMENTARY MATERIAL: The online version of this article (doi:10.1007/s11671-009-9265-2) contains supplementary material, which is available to authorized users.

| S-EPMC2894197 | biostudies-literature

A Diamond/Graphene/Diamond Electrode for Waste Water Treatment.

Project description:Boron-doped diamond (BDD) thin film electrodes have great application potential in water treatment. However, the high electrode energy consumption due to high resistance directly limits the application range of existing BDD electrodes. In this paper, the BDD/graphene/BDD (DGD) sandwich structure electrode was prepared, which effectively improved the conductivity of the electrode. Meanwhile, the sandwich electrode can effectively avoid the degradation of electrode performance caused by the large amount of non-diamond carbon introduced by heavy doping, such as the reduction of the electrochemical window and the decrease of physical and chemical stability. The microstructure and composition of the film were characterized by scanning electron microscope (SEM), atomic force microscopy (AFM), Raman spectroscopy, and transmission electron microscopy (TEM). Then, the degradation performance of citric acid (CA), catechol, and tetracycline hydrochloride (TCH) by DGD electrodes was systematically studied by total organic carbon (TOC) and Energy consumption per unit TOC removal (ECTOC). Compared with the single BDD electrode, the new DGD electrode improves the mobility of the electrode and reduces the mass transfer resistance by 1/3, showing better water treatment performance. In the process of dealing with Citric acid, the step current of the DGD electrode was 1.35 times that of the BDD electrode, and the energy utilization ratio of the DGD electrode was 2.4 times that of the BDD electrode. The energy consumption per unit TOC removal (ECTOC) of the DGD electrode was lower than that of BDD, especially Catechol, which was reduced to 66.9% of BDD. The DGD sandwich electrode, as a new electrode material, has good electrochemical degradation performance and can be used for high-efficiency electrocatalytic degradation of organic pollutants.

| S-EPMC10707964 | biostudies-literature