Stability of SiN_x Prepared by Plasma-Enhanced Chemical Vapor Deposition at Low Temperature.

ABSTRACT: In this paper, the environmental stability of silicon nitride (SiNx) films deposited at 80 °C by plasma-enhanced chemical vapor deposition was studied systematically. X-ray photoelectron spectroscopy and Fourier transform infrared reflection were used to analyze the element content and atomic bond structure of the amorphous SiN_x films. Variation of mechanical and optical properties were also evaluated. It is found that SiN_x deposited at low temperature is easily oxidized, especially at elevated temperature and moisture. The hardness and elastic modulus did not change significantly with the increase of oxidation. The changes of the surface morphology, transmittance, and fracture extensibility are negligible. Finally, it is determined that SiN_x films deposited at low-temperature with proper processing parameters are suitable for thin-film encapsulation of flexible devices.

SUBMITTER: Zhang C

PROVIDER: S-EPMC8706910 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Direct synthesis of graphene on silicon oxide by low temperature plasma enhanced chemical vapor deposition.

Project description:Direct graphene growth on silicon with a native oxide using plasma enhanced chemical vapour deposition at low temperatures [550 °C-650 °C] is demonstrated for the first time. It is shown that the fine-tuning of a two-step synthesis with gas mixtures C2H2/H2 yields monolayer and few layer graphene films with a controllable domain size from 50 nm to more than 300 nm and the sheet resistance ranging from 8 k? sq-1 to less than 1.8 k? sq-1. Differences are understood in terms of the interaction of the plasma species - chiefly atomic H - with the deposited graphene and the native oxide layer. The proposed low temperature direct synthesis on an insulating substrate does not require any transfer processes and improves the compatibility with the current industrial processes.

| S-EPMC6130772 | biostudies-literature

Low-Temperature Direct Synthesis of Multilayered h-BN without Catalysts by Inductively Coupled Plasma-Enhanced Chemical Vapor Deposition.

Project description:Low-temperature direct synthesis of thick multilayered hexagonal-boron nitride (h-BN) on semiconducting and insulating substrates is required to produce high-performance electronic devices based on two-dimensional (2D) materials. In this study, multilayered h-BN with a thickness exceeding 5 nm was directly synthesized on quartz and Si at low temperatures, between 400 and 500 °C, by inductively coupled plasma-enhanced chemical vapor deposition using borazine as the precursor material. The quality and thickness of the h-BN crystals were investigated with respect to synthesis parameters, namely, temperature, radio frequency power, N2 flow rate, and H2 flow rate. Introducing N2 and H2 carrier gases critically affected the deposition rate, and increasing the carrier gas flow rate enhanced the h-BN crystal quality. The typical optical band gap of synthesized h-BN was approximately 5.8 eV, consistent with that of previous studies. The full width at half-maximum of the h-BN Raman peak was 32-33 cm-1, comparable to that of commercially available multilayered h-BN on Cu foil. These results are expected to facilitate the development of 2D materials for electronics applications.

| S-EPMC9933473 | biostudies-literature

Transferless Inverted Graphene/Silicon Heterostructures Prepared by Plasma-Enhanced Chemical Vapor Deposition of Amorphous Silicon on CVD Graphene.

Project description:The heterostructures of two-dimensional (2D) and three-dimensional (3D) materials represent one of the focal points of current nanotechnology research and development. From an application perspective, the possibility of a direct integration of active 2D layers with exceptional optoelectronic and mechanical properties into the existing semiconductor manufacturing processes is extremely appealing. However, for this purpose, 2D materials should ideally be grown directly on 3D substrates to avoid the transferring step, which induces damage and contamination of the 2D layer. Alternatively, when such an approach is difficult-as is the case of graphene on noncatalytic substrates such as Si-inverted structures can be created, where the 3D material is deposited onto the 2D substrate. In the present work, we investigated the possibility of using plasma-enhanced chemical vapor deposition (PECVD) to deposit amorphous hydrogenated Si (a-Si:H) onto graphene resting on a catalytic copper foil. The resulting stacks created at different Si deposition temperatures were investigated by the combination of Raman spectroscopy (to quantify the damage and to estimate the change in resistivity of graphene), temperature-dependent dark conductivity, and constant photocurrent measurements (to monitor the changes in the electronic properties of a-Si:H). The results indicate that the optimum is 100 C deposition temperature, where the graphene still retains most of its properties and the a-Si:H layer presents high-quality, device-ready characteristics.

| S-EPMC7153506 | biostudies-literature

Low-temperature synthesis of graphene on nickel foil by microwave plasma chemical vapor deposition.

Project description:Microwave plasma chemical vapor deposition (MPCVD) was employed to synthesize high quality centimeter scale graphene film at low temperatures. Monolayer graphene was obtained by varying the gas mixing ratio of hydrogen and methane to 80:1. Using advantages of MPCVD, the synthesis temperature was decreased from 750 °C down to 450 °C. Optical microscopy and Raman mapping images exhibited that a large area monolayer graphene was synthesized regardless of the temperatures. Since the overall transparency of 89% and low sheet resistances ranging from 590 to 1855 Ω∕sq of graphene films were achieved at considerably low synthesis temperatures, MPCVD can be adopted in manufacturing future large-area electronic devices based on graphene film.

| S-EPMC3144964 | biostudies-other

Backbone-Degradable Polymers Prepared by Chemical Vapor Deposition.

Project description:Polymers prepared by chemical vapor deposition (CVD) polymerization have found broad acceptance in research and industrial applications. However, their intrinsic lack of degradability has limited wider applicability in many areas, such as biomedical devices or regenerative medicine. Herein, we demonstrate, for the first time, a backbone-degradable polymer directly synthesized via CVD. The CVD co-polymerization of [2.2]para-cyclophanes with cyclic ketene acetals, specifically 5,6-benzo-2-methylene-1,3-dioxepane (BMDO), results in well-defined, hydrolytically degradable polymers, as confirmed by FTIR spectroscopy and ellipsometry. The degradation kinetics are dependent on the ratio of ketene acetals to [2.2]para-cyclophanes as well as the hydrophobicity of the films. These coatings address an unmet need in the biomedical polymer field, as they provide access to a wide range of reactive polymer coatings that combine interfacial multifunctionality with degradability.

| S-EPMC5749924 | biostudies-literature

Low Temperature Metal Free Growth of Graphene on Insulating Substrates by Plasma Assisted Chemical Vapor Deposition.

Project description:Direct growth of graphene films on dielectric substrates (quartz and silica) is reported, by means of remote electron cyclotron resonance plasma assisted chemical vapor deposition r-(ECR-CVD) at low temperature (650°C). Using a two step deposition process- nucleation and growth- by changing the partial pressure of the gas precursors at constant temperature, mostly monolayer continuous films, with grain sizes up to 500 nm are grown, exhibiting transmittance larger than 92% and sheet resistance as low as 900 ?·sq-1. The grain size and nucleation density of the resulting graphene sheets can be controlled varying the deposition time and pressure. In additon, first-principles DFT-based calculations have been carried out in order to rationalize the oxygen reduction in the quartz surface experimentally observed. This method is easily scalable and avoids damaging and expensive transfer steps of graphene films, improving compatibility with current fabrication technologies.

| S-EPMC5214927 | biostudies-literature

Nonthermal Plasma-Enhanced Chemical Vapor Deposition of Two-Dimensional Molybdenum Disulfide.

Project description:Molybdenum disulfide (MoS2) is being studied for a wide range of applications including lithium-ion batteries and hydrogen evolution reaction catalysts. In this paper, we present a single-step nonthermal plasma-enhanced chemical vapor deposition (PECVD) process for the production of two-dimensional MoS2. This method provides an alternative route to established CVD and plasma synthesis routes. The approach presented here synthesizes films in only a few minutes using elemental sulfur (S8) and molybdenum pentachloride (MoCl5) as precursors. Deposition utilizes a nonthermal inductively coupled plasma reactor and temperatures around 500 °C. Film growth characteristics and nucleation are studied as a function of precursor concentrations, argon flow rate, plasma power, and deposition time. Few-layer two-dimensional (MoS2) films were formed at low precursor concentrations. Films with nanoparticle-like features were formed when the precursor concentration was high. Noncontinuous nonstoichiometric films were found at low plasma power, while high plasma power led to continuous films with good stoichiometry. The vacancies and defects in these films may provide active sites for hydrogen evolution.

| S-EPMC7469405 | biostudies-literature

Novel Low-Temperature Chemical Vapor Deposition of Hydrothermal Delignified Wood for Hydrophobic Property.

Project description:As a hydrophilic material, wood is difficult to utilize for external applications due to the variable weather conditions. In this study, an efficient, facile, and low-cost method was developed to enhance the hydrophobicity of wood. By applying the low-temperature chemical vapor deposition (CVD) technology, the polydimethylsiloxane-coated wood (PDMS@wood) with hydrophobic surface was fabricated employing dichlorodimethylsilane as the CVD chemical resource. The result of water contact angle (i.e., 157.3°) revealed the hydrophobic behavior of the PDMS@wood. The microstructures of the wood samples were observed by scanning electron microscopy and energy dispersive X-ray spectroscopy (EDS) analysis verified PDMS successfully coated on wood surfaces. The chemical functional groups of the PDMS@wood were investigated by Fourier transform infrared (FT-IR) and Raman spectra. The thermogravimetric results indicated the enhanced thermal stability of the wood after PDMS coating. In addition, the stability test of PDMS@wood indicated that the hydrophobicity properties of the PDMS@wood samples were preserved after long-time storage (e.g., 30 days). The scratch test was carried out to examine the abrasion resistance of the hydrophobic coatings on PDMS@wood surface. It was suggested that low-temperature CVD process could be a successful approach for fabricating hydrophobic wood.

| S-EPMC7463729 | biostudies-literature

Polymer Encapsulation of an Amorphous Pharmaceutical by initiated Chemical Vapor Deposition for Enhanced Stability.

Project description:The usage of amorphous solids in practical applications, such as in medication, is commonly limited by the poor long-term stability of this state, because unwanted crystalline transitions occur. In this study, three different polymeric coatings are investigated for their ability to stabilize amorphous films of the model drug clotrimazole and to protect against thermally induced transitions. For this, drop cast films of clotrimazole are encapsulated by initiated chemical vapor deposition (iCVD), using perfluorodecyl acrylate (PFDA), hydroxyethyl methacrylate (HEMA), and methacrylic acid (MAA). The iCVD technique operates under solvent-free conditions at low temperatures, thus leaving the solid state of the encapsulated layer unaffected. Optical microscopy and X-ray diffraction data reveal that at ambient conditions of about 22 °C, any of these iCVD layers extends the lifetime of the amorphous state significantly. At higher temperatures (50 or 70 °C), the p-PFDA coating is unable to provide protection, while the p-HEMA and p-MAA strongly reduce the crystallization rate. Furthermore, p-HEMA and p-MAA selectively facilitate a preferential alignment of clotrimazole and, interestingly, even suppress crystallization upon a temporary, rapid temperature increase (3 °C/min, up to 150 °C). The results of this study demonstrate how a polymeric coating, synthesized directly on top of an amorphous phase, can act as a stabilizing agent against crystalline transitions, which makes this approach interesting for a variety of applications.

| S-EPMC4999961 | biostudies-literature

Insights into the Mechanism for Vertical Graphene Growth by Plasma-Enhanced Chemical Vapor Deposition.

Project description:Vertically oriented graphene (VG) has attracted attention for years, but the growth mechanism is still not fully revealed. The electric field may play a role, but the direct evidence and exactly what role it plays remains unclear. Here, we conduct a systematic study and find that in plasma-enhanced chemical vapor deposition, the VG growth preferably occurs at spots where the local field is stronger, for example, at GaN nanowire tips. On almost round-shaped nanoparticles, instead of being perpendicular to the substrate, the VG grows along the field direction, that is, perpendicular to the particles' local surfaces. Even more convincingly, the sheath field is screened to different degrees, and a direct correlation between the field strength and the VG growth is observed. Numerical calculation suggests that during the growth, the field helps accumulate charges on graphene, which eventually changes the cohesive graphene layers into separate three-dimensional VG flakes. Furthermore, the field helps attract charged precursors to places sticking out from the substrate and makes them even sharper and turn into VG. Finally, we demonstrate that the VG-covered nanoparticles are benign to human blood leukocytes and could be considered for drug delivery. Our research may serve as a starting point for further vertical two-dimensional material growth mechanism studies.

| S-EPMC8832395 | biostudies-literature