Preparation of ZnO-Incorporated Porous Carbon Nanofibers and Adsorption Performance Investigation on Methylene Blue.

ABSTRACT: To improve the adsorption performance of carbon materials, novel ZnO nanoparticle-incorporated porous carbon nanofibers (Zn@PCNFs) were prepared via an electrospinning technique. A facile one-step fabrication strategy was proposed to simultaneously complete the carbonization of a peroxided polyacrylonitrile framework, the activating treatment caused by ZnO reducing to Zn, and the pore generation caused by evaporation of reduced Zn with a low melting point. The influences of the pH, ion category, and concentration on methylene blue adsorption were investigated. The physical-chemical characterizations showed that ZnO was homogeneously distributed on the nanofibers and micropores were generated. The adsorption results revealed that an efficient adsorption was obtained within a large range of pH values through different adsorption models, which was accelerated by increasing the temperature. Therefore, the novel Zn@PCNFs are anticipated to be applied in the future as an effective dye waste adsorbent.

SUBMITTER: Nie D

PROVIDER: S-EPMC8771709 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Sawdust-Based Cellulose Nanocrystals Incorporated with ZnO Nanoparticles as Efficient Adsorption Media in the Removal of Methylene Blue Dye.

Project description:The continuous increase in the wastes generated from forestry, timber, and paper industries has engendered the need for their transformation into economically viable materials for the benefit of mankind. This study reports the preparation and application of sawdust-derived cellulose nanocrystals (CNC) incorporated with zinc oxide as a novel adsorbent for the removal of methylene blue (MB) from water. The CNC/ZnO nanocomposite was characterized using Fourier transform infrared, X-ray diffraction (XRD), and scanning electron microscopy. The amount of MB adsorbed was determined by a UV-vis spectrophotometer. The microscopic analysis revealed that the nanocomposite had a narrow particle size range and exhibited both spherical and rod-like morphologies. The XRD analysis of the nanocomposite showed characteristic high-intensity peaks in the range of 30-75° attributed to the presence of ZnO nanoparticles, which were responsible for the enhancement of the crystallinity of the nanocomposite. The results revealed a relationship between the MB removal efficiency and changes in solution pH, nanocomposite dosage, initial concentration, temperature, and reaction time. The adsorption equilibrium isotherm, measured in the temperature range of 25-45 °C and using a concentration of 20-100 mg/L, showed that the MB sorption followed the Langmuir isotherm with a maximum adsorption capacity of 64.93 mg/g. A pseudo-second-order kinetic model gave the best fit to the experimental data. Based on adsorption performance, the CNC/ZnO nanocomposite offers prospects for further research and application in amelioration of dye-containing effluent.

| S-EPMC7408268 | biostudies-literature

Studies on Kinetics, Isotherms, Thermodynamics and Adsorption Mechanism of Methylene Blue by N and S Co-Doped Porous Carbon Spheres.

Project description:Heteroatom-doped carbon is widely used in the fields of adsorbents, electrode materials and catalysts due to its excellent physicochemical properties. N and S co-doped porous carbon spheres (N,S-PCSs) were synthesized using glucose and L-cysteine as carbon and heteroatom sources using a combined hydrothermal and KOH activation process. The physicochemical structures and single-factor methylene blue (MB) adsorption properties of the N,S-PCSs were then studied. The optimized N,S-PCSs-1 possessed a perfect spherical morphology with a 2-8-μm diameter and a large specific area of 1769.41 m2 g-1, in which the N and S contents were 2.97 at% and 0.88 at%, respectively. In the single-factor adsorption experiment for MB, the MB adsorption rate increased with an increase in carbon dosage and MB initial concentration, and the adsorption reached equilibrium within 2-3 h. The pseudo-second-order kinetic model could excellently fit the experimental data with a high R2 (0.9999). The Langmuir isothermal adsorption equation fitted well with the experimental results with an R2 value of 0.9618, and the MB maximum adsorption quantity was 909.10 mg g-1. The adsorption of MB by N,S-PCSs-1 was a spontaneous, endothermic, and random process based on the thermodynamics analyses. The adsorption mechanism mainly involved Van der Waals force adsorption, π-π stacking, hydrogen bonds and Lewis acid-base interactions.

| S-EPMC8308386 | biostudies-literature

Citrus Pectin-Derived Carbon Microspheres with Superior Adsorption Ability for Methylene Blue.

Project description:In this study, citrus pectin-derived, green, and tunable carbon microspheres with superior adsorption capacity and high adsorption rate, as well as good reusability toward methylene blue adsorption, were prepared by a facile hydrothermal method without any hazardous chemicals. The materials hold great potential for the treatment of methylene blue wastewater.

| S-EPMC5535227 | biostudies-literature

Preparation and Characterization of Sodium Alginate-Based Oxidized Multi-Walled Carbon Nanotubes Hydrogel Nanocomposite and its Adsorption Behaviour for Methylene Blue Dye.

Project description:Herein, a sodium alginate/poly (acrylic acid)/oxidized-multi-walled carbon nanotubes hydrogel nanocomposite (SA/p(AAc)/o-MWCNTs HNC) was synthesized by in situ free-radical polymerization method. The synthesized SA/p(AAc)/o-MWCNTs HNC was used to remove methylene blue (MB) from aqueous solution. The synthesized HNC was confirmed by employing various characterization techniques. The SA/p(AAc)/o-MWCNTs HNC exhibited a maximum swelling capacity of 2265.4% at pH 8.0. The influence of vital parameters in the sorption process including the initial pH, adsorption dose, contact time and concentration were systematically examined on a batch mode. Subsequently, adsorption kinetics as well as isotherm models were applied to assess the nature and mechanism of the adsorption process. Adsorption kinetics were best described by pseudo-second-order model, while the Langmuir isotherm model governed the adsorption isotherm. The SA/p(AAc)/o-MWCNTs HNC exhibited a maximum adsorption capacity of 1596.0 mg/g at 25°C. This adsorbent showed excellent MB uptake and good regeneration ability.

| S-EPMC8009996 | biostudies-literature

Expermental investigation on adsorption of methylene blue dye from waste water using corncob cellulose-based hydrogel.

Project description:Hydrogel from corncob cellulose was synthesized in this investigation. The synthesized Hydrogel was characterized by SEM, XRD, and FTIR instruments. As the results indicate the synthesized hydrogel has required and important features, these suggest the suitability of hydrogel for the adsorption of methylene blue dye (MBD). Three important process variables (dosage, contact time, and initial concentration) with three levels were studied during the adsorption process at 30 °C and neutral pH. The efficiency of hydrogel for adsorption of MBD was determined in each experiment. The experimental results were statistically analyzed and interpreted. The maximum removal efficiency was achieved at 2.22 g/L of dosage, 80.36 min of contact time, and 74.54 mg/L of initial concentration. At this condition, 98.25% of MBD was achieved through experimental tests. Kinetics, isotherm, and thermodynamics studies were performed. Langmuir isotherm is more suitable to describe the adsorption process and the Pseudo second-order kinetic model fits this process. From the thermodynamics studies, all negative values of change in Gibbs free energy (ΔG°), and positive value of change in enthalpy (ΔH°), and change in entropy (ΔS°) indicate that the carried out experimental process is a spontaneous and endothermic. Moreover, the regeneration experiment for adsorbent was performed. The treatment of real textile industry waste water was conducted and the removal efficiency of hydrogel was 64.76%. This removal percentage reduction from sythetic aqueous solution is due to involvement of other pollutants in the real waste water. The synthesized hydrogel adsorbent is suitable up to the third cycle without significant loss in removal efficiency.

| S-EPMC11322434 | biostudies-literature

Efficient Adsorption of Methylene Blue by Porous Biochar Derived from Soybean Dreg Using a One-Pot Synthesis Method.

Project description:Soybean dreg is a by-product of soybean products production, with a large consumption in China. Low utilization value leads to random discarding, which is one of the important sources of urban pollution. In this work, porous biochar was synthesized using a one-pot method and potassium bicarbonate (KHCO3) with low-cost soybean dreg (SD) powder as the carbon precursor to investigating the adsorption of methylene blue (MB). The prepared samples were characterized with scanning electron microscopy (SEM), transmission electron microscopy (TEM), elemental analyzer (EA), Brunauer-Emmett-Teller (BET), X-ray diffractometer (XRD), Raman spectroscopy (Raman), Fourier transform infrared spectrometer (FTIR), and X-ray photoelectron spectroscopy (XPS). The obtained SDB-K-3 showed a high specific surface area of 1620 m2 g-1, a large pore volume of 0.7509 cm3 g-1, and an average pore diameter of 1.859 nm. The results indicated that the maximum adsorption capacity of SDB-K-3 to MB could reach 1273.51 mg g-1 at 318 K. The kinetic data were most consistent with the pseudo-second-order model and the adsorption behavior was more suitable for the Langmuir isotherm equation. This study demonstrated that the porous biochar adsorbent can be prepared from soybean dreg by high value utilization, and it could hold significant potential for dye wastewater treatment in the future.

| S-EPMC7865629 | biostudies-literature

Porous BiOBr/Bi2MoO6 Heterostructures for Highly Selective Adsorption of Methylene Blue.

Project description:Porous BiOBr/Bi2MoO6 (Br/Mo) heterostructures were designed and successfully fabricated, in which BiOBr nanoparticles were deposited on the surface of the secondary nanoplate of three-dimensional porous Bi2MoO6 architectures through a deposition-precipitation process. The as-prepared Br/Mo heterostructures were used as an adsorbent to remove methylene blue (MB) from aqueous solution. The batch adsorption results indicated that 50.0 wt % Br/Mo heterostructures show an enhanced adsorption capacity compared with pure Bi2MoO6 and BiOBr. The effects of initial solution, initial concentration, and contact time were systematically investigated. The optimum adsorbent amount and the pH value were determined to be 0.8 g L-1 and 2, respectively. Meanwhile, the experiments also revealed that porous Br/Mo heterostructures possess higher preferential adsorptivity for MB than that for methyl orange (MO-) and rhodamine B (RhB+). The dynamic experimental result indicated that the adsorption process conforms to the pseudo-second-order kinetic model. Weber's intraparticle diffusion model indicated that two steps took place during the adsorption process. Thermodynamic analysis results showed that the adsorption is a physisorption process, which conforms to the Langmuir isotherm model. Additionally, the possible adsorption mechanism was also investigated. The present study implied that Br/Mo heterostructures are promising candidates as adsorbents for MB removal. Therefore, fabrication of semiconductor-based heterostructures could be a strategy to design new efficient adsorbents for the removal of environmental pollutants.

| S-EPMC6640767 | biostudies-literature

Adsorption Behaviors of Cationic Methylene Blue and Anionic Reactive Blue 19 Dyes onto Nano-Carbon Adsorbent Carbonized from Small Precursors.

Project description:In this work, an innovative nano-carbon material (N-CM) adsorbent was reported for exploring its adsorption behaviors toward cationic methylene blue (MB) and anionic reactive blue 19 (RB19) pollutants. The proposed N-CM was synthesized by a one-step solvothermal treatment of citric acid and zinc gluconate small precursors. N-CM consists of nanosheets that have an advantageous specific surface area, large sp2/sp3 hybridized domains, and abundant nitrogen/oxygen-containing surface functional groups. The synergistic effects of these features are conducive to the MB and RB19 adsorption. Different from anionic RB19 adsorption (79.54 mg/g) by the cooperative π-π stacking and hydrogen bonding, cationic MB adsorbed onto N-CM mainly by the electrostatic attraction at the natural pH solution (> pHpzc), with an adsorption capacity up to 118.98 mg/g. Interestingly, both MB and RB19 adsorption conformed to the pseudo-second order kinetic (R2 ≥ 0.995) and Langmuir isothermal (R2 ≥ 0.990) models, accompanied by similar maximum monolayer adsorption capacities of 120.77 and 116.01 mg/g, respectively. Their adsorption processes exhibited spontaneously endothermic characteristics. Moreover, N-CM showed superior selective capability toward MB in different mixed dye systems, with high removal efficiencies of 73-89%. These results demonstrate that the high-performance carbon adsorbent prepared from small precursors via low-temperature carbonization shows great potentials in wastewater treatment.

| S-EPMC9182342 | biostudies-literature

Functionalized Attapulgite for the Adsorption of Methylene Blue: Synthesis, Characterization, and Adsorption Mechanism.

Project description:Attapulgite (denoted as APT, also called palygorskite) has been regarded as the green material in the "21st century world" and has attracted widespread attention due to its advantages of low cost, natural abundance, nontoxic nature, and environmental friendliness. However, the limited adsorption sites and surface charges of natural APT greatly hinder its application as an adsorbent in industrial fields. In this work, natural APT was modified with sodium humate (SA) via a facile one-step hydrothermal process to improve its adsorption capacity and systematically studied its ability to remove methylene blue (MB) from aqueous solutions. The effect of hydrothermal modification in the presence of SA on the microscopic structure, morphology, and physicochemical properties of APT was studied by field-emission scanning electron microscopy, Fourier transform infrared spectrometry, X-ray diffraction, and Brunauer-Emmett-Teller analyses. The adsorption properties of the modified APT toward MB were evaluated systematically. The results demonstrated that the modified APT has a high adsorption capacity of 227.27 mg/g and also shows a high removal rate up to 99.7% toward MB in a dye solution with an initial concentration of 150 mg/L, which was a 64.7% increase as compared to that of raw APT. The adsorption kinetics could be fitted to the pseudo-second-order model, while the adsorption isotherm could be well-described with the Langmuir model. It was concluded that electrostatic attraction, hydrogen-bonding interaction, and chemical association are the main driving force during the adsorption process.

| S-EPMC8340108 | biostudies-literature

Investigation into the Adsorption of Methylene Blue and Methyl Orange by UiO-66-NO2 Nanoparticles.

Project description:In this work, the adsorptive removal of methylene blue and methyl orange by UiO-66-NO2 nanoparticles was studied. The influence of pH on the adsorption capacity was assessed. The kinetics of the adsorption process were investigated and compared with pseudo-first-order, pseudo-second-order, Elovich, and intraparticle models. The kinetics of the adsorption fits moderately with the pseudo-first-order, but perfectly fits with pseudo-second-order models, and has a very good fit with the Elovich and intraparticle models. The adsorption isotherms were measured and compared with the Langmuir and Freundlich models. The adsorption capacity of methyl orange (MO) on UiO-66-NO2 nanoparticles (142.9 mg/g) was over three times higher than that of methylene blue (MB) on the nanoparticles (41.7 mg/g). The discrepancy between these capacities was attributed to the presence of the -NO2 functional group, which caused a strong negative mesomeric effect in the metal-organic framework structure.

| S-EPMC8216806 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data