Biodegradable and Reusable Cellulose-Based Nanofiber Membrane Preparation for Mask Filter by Electrospinning.

ABSTRACT: Environmentally friendly face masks with high filtration efficiency are in urgent need to fight against the COVID-19 pandemic, as well as other airborne viruses, bacteria and particulate matters. In this study, coaxial electrospinning was employed to fabricate a lithium chloride enhanced cellulose acetate/thermoplastic polyurethanes (CA/TPU-LiCl) face mask nanofiber filtration membrane, which was biodegradable and reusable. The analysis results show that the CA/TPU-LiCl membrane had an excellent filtration performance: when the filtration efficiency reached 99.8%, the pressure drop was only 52 Pa. The membrane also had an outstanding reusability. The filtration performance maintained at 98.2% after 10 test cycles, and an alcohol immersion disinfection treatment showed no effect on its filtration performance. In summary, the CA/TPU-LiCl nanofiber membrane made in this work is a promising biodegradable and reusable filtration material with a wide range of potential applications, including high-performance face mask.

SUBMITTER: Wang J

PROVIDER: S-EPMC8777847 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Biodegradable and high-performance multiscale structured nanofiber membrane as mask filter media via poly(lactic acid) electrospinning.

Project description:The usage of single-use face masks (SFMs) has increased since the outbreak of the coronavirus pandemic. However, non-degradability and mismanagement of SFMs have raised serious environmental concerns. Moreover, both melt-blown and nanofiber-based mask filters inevitably suffer from poor filtration performance, like a continuous decrease in the removal efficiency for particulate matter (PM) and weak breathability. Herein, we report a new method to create biodegradable and reusable fibrous mask filters. The filter consists of a true nanoscale bio-based poly(lactic acid) (PLA) fiber (an average size of 37 ± 4 nm) that is fabricated via electrospinning of an extremely dilute solution. Furthermore, we designed a multiscale structure with integrated features, such as low basis weight (0.91 g m-2), small pore size (0.73 μm), and high porosity (91.72%), formed by electrospinning deposition of true nanoscale fibers on large pore of 3D scaffold nanofiber membranes. The resultant mask filter exhibited a high filtration efficiency (PM0.3-99.996%) and low pressure drop (104 Pa) superior to the commercial N95 filter. Importantly, this filter has a durable filtering efficiency for PM and natural biodegradability based on PLA. Therefore, this study offers an innovative strategy for the preparation of PLA nanofibers and provides a new design for high-performance nanofiber filters.

| S-EPMC8559669 | biostudies-literature

Biodegradable, Efficient, and Breathable Multi-Use Face Mask Filter.

Project description:The demand for face masks is increasing exponentially due to the coronavirus pandemic and issues associated with airborne particulate matter (PM). However, both conventional electrostatic- and nanosieve-based mask filters are single-use and are not degradable or recyclable, which creates serious waste problems. In addition, the former loses function under humid conditions, while the latter operates with a significant air-pressure drop and suffers from relatively fast pore blockage. Herein, a biodegradable, moisture-resistant, highly breathable, and high-performance fibrous mask filter is developed. Briefly, two biodegradable microfiber and nanofiber mats are integrated into a Janus membrane filter and then coated by cationically charged chitosan nanowhiskers. This filter is as efficient as the commercial N95 filter and removes 98.3% of 2.5 µm PM. The nanofiber physically sieves fine PM and the microfiber provides a low pressure differential of 59 Pa, which is comfortable for human breathing. In contrast to the dramatic performance decline of the commercial N95 filter when exposed to moisture, this filter exhibits negligible performance loss and is therefore multi-usable because the permanent dipoles of the chitosan adsorb ultrafine PM (e.g., nitrogen and sulfur oxides). Importantly, this filter completely decomposes within 4 weeks in composting soil.

| S-EPMC7967051 | biostudies-literature

Multifunctional filter membrane for face mask using bacterial cellulose for highly efficient particulate matter removal.

Project description:AbstractParticulate matter (PM) pollution and SARS-CoV-2 (COVID-19) have brought severe threats to public health. High level of PM serves as a carrier of COVID-19 which is a global pandemic. This study fabricated filter membrane for face mask using bacterial cellulose and fingerroot extract (BC-FT) via immersion technique. The surface area, pore volume and pore size of BC were analyzed by Brunauer-Emmett-Teller. The physiochemical properties of the membrane were analyzed by scanning electron microscopy, Fourier transform infrared spectroscopy and X-ray diffractometer. The crystallinity decreased from 63.7% in pure BC to 52.4% in BC-FT filter membrane. Young's modulus increased from 1277.02 MPa in pure BC to 2251.17 MPa in BC-FT filter membrane. The filter membrane showed excellent PM 0.1 removal efficiency of 99.83% and antimicrobial activity against Staphylococcus aureus and Escherichia coli. The fabricated membrane is excellent to prevent inhalation of PM2.5 and COVID-19 respiratory droplet.Graphic abstractSupplementary informationThe online version contains supplementary material available at 10.1007/s10570-022-04641-3.

| S-EPMC9167669 | biostudies-literature

Biodegradable nanofiber-based piezoelectric transducer.

Project description:Piezoelectric materials, a type of "smart" material that generates electricity while deforming and vice versa, have been used extensively for many important implantable medical devices such as sensors, transducers, and actuators. However, commonly utilized piezoelectric materials are either toxic or nondegradable. Thus, implanted devices employing these materials raise a significant concern in terms of safety issues and often require an invasive removal surgery, which can damage directly interfaced tissues/organs. Here, we present a strategy for materials processing, device assembly, and electronic integration to 1) create biodegradable and biocompatible piezoelectric PLLA [poly(l-lactic acid)] nanofibers with a highly controllable, efficient, and stable piezoelectric performance, and 2) demonstrate device applications of this nanomaterial, including a highly sensitive biodegradable pressure sensor for monitoring vital physiological pressures and a biodegradable ultrasonic transducer for blood-brain barrier opening that can be used to facilitate the delivery of drugs into the brain. These significant applications, which have not been achieved so far by conventional piezoelectric materials and bulk piezoelectric PLLA, demonstrate the PLLA nanofibers as a powerful material platform that offers a profound impact on various medical fields including drug delivery, tissue engineering, and implanted medical devices.

| S-EPMC6955346 | biostudies-literature

Preparation and Characteristics of Polyethylene Oxide/Curdlan Nanofiber Films by Electrospinning for Biomedical Applications.

Project description:In this study, polyethylene oxide (PEO) and curdlan solutions were used to prepare PEO/curdlan nanofiber films by electrospinning using deionized water as the solvent. In the electrospinning process, PEO was used as the base material, and its concentration was fixed at 6.0 wt.%. Moreover, the concentration of curdlan gum varied from 1.0 to 5.0 wt.%. For the electrospinning conditions, various operating voltages (12-24 kV), working distances (12-20 cm) and feeding rates of polymer solution (5-50 μL/min) were also modified. Based on the experimental results, the optimum concentration for the curdlan gum was 2.0 wt.%. Additionally, the most suitable operating voltage, working distance and feeding rate for the electrospinning process were 19 kV, 20 cm and 9 μL/min, respectively, which can help to prepare relatively thinner PEO/curdlan nanofibers with higher mesh porosity and without the formation of beaded nanofibers. Finally, the PEO/curdlan nanofiber instant films containing 5.0 wt.% quercetin inclusion complex were used to perform wetting and disintegration processes. It was found that the instant film can be dissolved significantly on the low-moisture wet wipe. On the other hand, when the instant film touched water, it can be disintegrated very quickly within 5 s, and the quercetin inclusion complex was dissolved in water efficiently. Furthermore, when the instant film encountered the water vapor at 50 °C, it almost completely disintegrated after immersion for 30 min. The results indicate that the electrospun PEO/curdlan nanofiber film is highly feasible for biomedical applications consisting of instant masks and quick-release wound dressings, even in the water vapor environment.

| S-EPMC10220793 | biostudies-literature

Biomimetic, Highly Reusable and Hydrophobic Graphene/Polyvinyl Alcohol/Cellulose Nanofiber Aerogels as Oil-Removing Absorbents.

Project description:Aerogels have great potential in oil absorption applications; however, many reported aerogels have the drawbacks of a low oil-recovery rate and poor mechanical properties, which limit their application. In this study, highly reusable graphene oxide (GO)/TEMPO-oxidized cellulose nanofiber (TOCN)/polyvinyl alcohol (PVA) aerogels with excellent mechanical properties and with an architecture similar to that of Thalia dealbata stems were fabricated through a three-step process of bidirectional-freezing, freeze-drying, and chemical vapor deposition (CVD) modification. After CVD modification, the modified GTPA (MGTPA) accorded hydrophobicity. The synergistic effects of the three components and the unique biomimetic structure conferred biomimetic-MGTPA (b-MGTPA) with excellent compressible properties. As an adsorbent, b-MGTPA showed a high adsorption capacity (75-151 g/g) for various types of organic solvents. In addition, its high compressibility enables b-MGTPA to have fast and highly efficient recovery of absorbed oil through simple mechanical squeezing and it possesses excellent reusable stability (the oil recovery rate and oil retention rate reached 80% and 91.5%, respectively, after 10 repeated absorption-compression cycles).

| S-EPMC8951047 | biostudies-literature

Structure and Properties of Biodegradable PLLA/ZnO Composite Membrane Produced via Electrospinning.

Project description:These days, composite materials based on polymers and inorganic nanoparticles (NPs) are widely used in optoelectronics and biomedicine. In this work, composite membranes of polylactic acid and ZnO NPs containing 5-40 wt.% of the latter NPs were produced by means of electrospinning. For the first time, polymer material loaded with up to 40 wt.% of ZnO NPs (produced via laser ablation in air and having non-modified surface) was used to prepare fiber-based composite membranes. The morphology, phase composition, mechanical, spectral and antibacterial properties of the membranes were tested by a set of analytical techniques including SEM, XRD, FTIR, UV-vis, and photoluminescence spectroscopy. Antibacterial activity of the materials was evaluated following standard procedures (ISO 20743:2013) and using S. aureus and E. coli bacteria. It is shown that incorporation of 5-10 wt.% of NPs led to improved mechanical properties of the composite membranes, while further increase of ZnO content up to 20 wt.% and above resulted in their noticeable deterioration. At the same time, the antibacterial properties of ZnO-rich membranes were more pronounced, which is explained by a larger number of surface-exposed ZnO NPs, in addition to those embedded into the bulk of fiber material.

| S-EPMC7792573 | biostudies-literature

Preparation of Network-Structured Carbon Nanofiber Mats Based on PAN Blends Using Electrospinning and Hot-Pressing Methods for Supercapacitor Applications.

Project description:In this work, we prepared network-structured carbon nanofibers using polyacrylonitrile blends (PAN150 and PAN85) with different molecular weights (150,000 and 85,000 g mol-1) as precursors through electrospinning/hot-pressing methods and stabilization/carbonization processes. The obtained PAN150/PAN85 polymer nanofibers (PNFs; PNF-73, PNF-64 and PNF-55) with different weight ratios of 70/30, 60/40 and 50/50 (w/w) provided good mechanical and electrochemical properties due to the formation of physically bonded network structures between the blended PAN nanofibers during the hot-processing/stabilization processes. The resulting carbonized PNFs (cPNFs; cPNF-73, cPNF-64, and cPNF-55) were utilized as anode materials for supercapacitor applications. cPNF-73 exhibited a good specific capacitance of 689 F g-1 at 1 A g-1 in a three-electrode set-up compared to cPNF-64 (588 F g-1 at 1 A g-1) and cPNF-55 (343 F g-1 at 1 A g-1). In addition, an asymmetric hybrid cPNF-73//NiCo2O4 supercapacitor device also showed a good specific capacitance of 428 F g-1 at 1 A g-1 compared to cPNF-64 (400 F g-1 at 1 A g-1) and cPNF-55 (315 F g-1 at 1 A g-1). The cPNF-73-based device showed a good energy density of 1.74 W h kg-1 (0.38 W kg-1) as well as an excellent cyclic stability (83%) even after 2000 continuous charge-discharge cycles at a current density of 2 A g-1.

| S-EPMC8467548 | biostudies-literature

Photocatalytic Nanowires-Based Air Filter: Towards Reusable Protective Masks.

Project description:In the last couple decades, several viral outbreaks resulting in epidemics and pandemics with thousands of human causalities have been witnessed. The current Covid-19 outbreak represents an unprecedented crisis. In stopping the virus' spread, it is fundamental to have personal protective equipment and disinfected surfaces. Here, the development of a TiO2 nanowires (TiO2NWs) based filter is reported, which it is believed will work extremely well for personal protective equipment (PPE), as well as for a new generation of air conditioners and air purifiers. Its efficiency relies on the photocatalytic generation of high levels of reactive oxygen species (ROS) upon UV illumination, and on a particularly high dielectric constant of TiO2, which is of paramount importance for enhanced wettability by the water droplets carrying the germs. The filter pore sizes can be tuned by processing TiO2NWs into filter paper. The kilogram-scale production capability of TiO2NWs gives credibility to its massive application potentials.

| S-EPMC7435547 | biostudies-literature

Poly(aspartic acid) Electrospun Nanofiber Hydrogel Membrane-Based Reusable Colorimetric Sensor for Cu(II) and Fe(III) Detection.

Project description:Electrospun nanofiber membrane (ENM) with huge specific surface area is an ideal solid substrate for sensors. However, only a few ENMs are developed into colorimetric sensors and it is even more challenging to fabricate multiple-ion-responsive ENM-based colorimetric sensor. In this study, benefiting from the excellent metal ion adsorption ability of poly(aspartic acid) (PASP) and high specific surface area of nanofibers, a reusable colorimetric sensor utilizing PASP electrospun nanofiber hydrogel membrane (ENHM) was designed to detect Cu2+ and Fe3+ in aqueous solution with simple filtration. The sensor based on PASP-ENHM exhibited high sensitivity and selectivity, and colorimetric responses for Cu2+ and Fe3+ detection could be observed by the naked eye. Upon exposure to Cu2+ aqueous solution, the color of the sensor changed from white to blue with a naked eye detection limit of 0.3 mg/L, while it turned from white to yellow with a detection limit of 0.1 mg/L for Fe3+ detection. Furthermore, this sensor was reusable after metal ion extraction by the desorption process.

| S-EPMC6740173 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data