Cobalt-Doped Carbon Nitride Frameworks Obtained from Calcined Aromatic Polyimines as Cathode Catalyst of Anion Exchange Membrane Fuel Cells.

ABSTRACT: Cobalt-doped carbon nitride frameworks (CoNC) were prepared from the calcination of Co-chelated aromatic polyimines (APIM) synthesized from stepwise polymerization of p-phenylene diamine (PDA) and o-phthalaldehyde (OPAl) via Schiff base reactions in the presence of cobalt (II) chloride. The Co-chelated APIM (Co-APIM) precursor converted to CoNC after calcination in two-step heating with the second step performed at 100 °C lower than the first one. The CoNCs demonstrated that its Co, N-co-doped carbonaceous framework contained both graphene and carbon nanotube, as characterized by X-ray diffraction pattern, Raman spectra, and TEM micropictures. CoNCs also revealed a significant ORR peak in the current-voltage polarization cycle and a higher O₂ reduction current than that of commercial Pt/C in a linear scanning voltage test in O₂-saturated KOH_(aq). The calculated e-transferred number even reaches 3.94 in KOH_(aq) for the CoNC1000A900 cathode catalyst, which has the highest BET surface area of 393.94 m² g^-1. Single cells of anion exchange membrane fuel cells (AEMFCs) are fabricated using different CoNCs as the cathode catalysts, and CoNC1000A900 demonstrates a peak power density of 374.3 compared to the 334.7 mW cm^-2 obtained from the single cell using Pt/C as the cathode catalyst.

SUBMITTER: Hsieh TH

PROVIDER: S-EPMC8779780 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Preparation and Application of Fe-N Co-Doped GNR@CNT Cathode Oxygen Reduction Reaction Catalyst in Microbial Fuel Cells.

Project description:Through one-step pyrolysis, non-noble-metal oxygen reduction reaction (ORR) electrocatalysts were constructed from ferric trichloride, melamine, and graphene nanoribbon@carbon nanotube (GNR@CNT), in which a portion of the multiwall carbon nanotube is unwrapped/unzipped radially, and thus graphene nanoribbon is exposed. In this study, Fe-N/GNR@CNT materials were used as an air-cathode electrocatalyst in microbial fuel cells (MFCs) for the first time. The Fe-N/C shows similar power generation ability to commercial Pt/C, and its electron transfer number is 3.57, indicating that the ORR process primarily occurs with 4-electron. Fe species, pyridinic-N, graphitic-N, and oxygen-containing groups existing in GNR@CNT frameworks are likely to endow the electrocatalysts with good ORR performance, suggesting that a GNR@CNT-based carbon supporter would be a good candidate for the non-precious metal catalyst to replace Pt-based precious metal.

| S-EPMC7912981 | biostudies-literature

Transition-Metal- and Nitrogen-Doped Carbide-Derived Carbon/Carbon Nanotube Composites as Cathode Catalysts for Anion-Exchange Membrane Fuel Cells.

Project description:Transition-metal- and nitrogen-codoped carbide-derived carbon/carbon nanotube composites (M-N-CDC/CNT) have been prepared, characterized, and used as cathode catalysts in anion-exchange membrane fuel cells (AEMFCs). As transition metals, cobalt, iron, and a combination of both have been investigated. Metal and nitrogen are doped through a simple high-temperature pyrolysis technique with 1,10-phenanthroline as the N precursor. The physicochemical characterization shows the success of metal and nitrogen doping as well as very similar morphologies and textural properties of all three composite materials. The initial assessment of the oxygen reduction reaction (ORR) activity, employing the rotating ring-disk electrode method, indicates that the M-N-CDC/CNT catalysts exhibit a very good electrocatalytic performance in alkaline media. We find that the formation of HO2 - species in the ORR catalysts depends on the specific metal composition (Co, Fe, or CoFe). All three materials show excellent stability with a negligible decline in their performance after 10000 consecutive potential cycles. The very good performance of the M-N-CDC/CNT catalyst materials is attributed to the presence of M-N x and pyridinic-N moieties as well as both micro- and mesoporous structures. Finally, the catalysts exhibit excellent performance in in situ tests in H2/O2 AEMFCs, with the CoFe-N-CDC/CNT reaching a current density close to 500 mA cm-2 at 0.75 V and a peak power density (P max) exceeding 1 W cm-2. Additional tests show that P max reaches 0.8 W cm-2 in an H2/CO2-free air system and that the CoFe-N-CDC/CNT material exhibits good stability under both AEMFC operating conditions.

| S-EPMC8744415 | biostudies-literature

Fe, N-Doped Metal Organic Framework Prepared by the Calcination of Iron Chelated Polyimines as the Cathode-Catalyst of Proton Exchange Membrane Fuel Cells.

Project description:Aromatic polyimine (PIM) was prepared through condensation polymerization between p-phenylene diamine and terephthalaldehyde via Schiff reactions. PIM can be physically crosslinked with ferrous ions into gel. The gel-composites, calcined at two consecutive stages, with temperatures ranging from 600 to 1000 °C, became Fe- and N-doped carbonaceous organic frameworks (FeNC), which demonstrated both graphene- and carbon nanotube-like morphologies and behaved as an electron-conducting medium. After the two-stage calcination, one at 1000 °C in N2 and the other at 900 °C in a mixture of N2 and NH3, an FeNC composite (FeNC-1000A900) was obtained, which demonstrated a significant O2 reduction peak in its current-voltage curve in the O2 atmosphere, and thus, qualified as a catalyst for the oxygen reduction reaction. It also produced a higher reduction current than that of commercial Pt/C in a linear scanning voltage test, and the calculated e-transferred number reached 3.85. The max. power density reached 400 mW·cm-2 for the single cell using FeNC-1000A900 as the cathode catalyst, which was superior to other FeNC catalysts that were calcined at lower temperatures. The FeNC demonstrated only 10% loss of the reduction current at 1600 rpm after 1000 redox cycles, as compared to be 25% loss for the commercial Pt/C catalyst in the durability test.

| S-EPMC8587573 | biostudies-literature

Cobalt-Containing Nanoporous Nitrogen-Doped Carbon Nanocuboids from Zeolite Imidazole Frameworks for Supercapacitors.

Project description:Pyrolyzing metal-organic frameworks (MOFs) typically yield composites consisting of metal/metal oxide nanoparticles finely dispersed on carbon matrices. The blend of pseudocapacitive metal oxides and conductive metals, as well as highly porous carbon networks, offer unique opportunities to obtain supercapacitor electrodes with mutually high capacitances and excellent rate capabilities. Herein, we demonstrate nitrogen-doped carbon nanocuboid arrays grown on carbon fibers and incorporating cobalt metal and cobalt metal oxides. This composite was synthesized via pyrolysis of a chemical bath deposited MOF, cobalt-containing zeolite imidazole framework (Co-ZIF). The active materials for charge storage are the cobalt oxide and nitrogen-doped carbon. Additionally, the Co metal and the nanoporous carbon network facilitated electron transport and the rich nanopores in each nanocuboid shortened ion diffusion distance. Benefited from these merits, our Co-ZIF-derived electrode delivered an areal capacitance of 1177 mF cm-2 and excellent cycling stability of ~94% capacitance retained after 20,000 continuous charge-discharge cycles. An asymmetric supercapacitor prototype having the Co-ZIF-derived hybrid material (positive electrode) and activated carbon (negative electrode) achieved a maximal volumetric energy density of 1.32 mWh cm-3 and the highest volumetric power density of 376 mW cm-3. This work highlights the promise of metal-metal oxide-carbon nanostructured composites as electrodes in electrochemical energy storage devices.

| S-EPMC6723694 | biostudies-literature

Zeolite Imidazolate Frameworks-67 Precursor to Fabricate a Highly Active Cobalt-Embedded N-Doped Porous Graphitized Carbon Catalyst for the Thermal Decomposition of Ammonium Perchlorate.

Project description:The more apparent specific heat release at a lower high-temperature decomposition (HTD) temperature of ammonium perchlorate (AP) poses a challenge for the development of highly active catalysts. In this work, a well-designed cobalt-embedded N-doped porous graphitized carbon (Co@NC) catalyst is obtained by high-temperature calcination of a zeolite imidazolate frameworks-67 precursor, in which the cobalt catalytic active center realizes effective nanoscale dispersion; meanwhile, the cobalt and N-doped porous graphitized carbon can release considerable heat after oxidation, and the cobalt oxides have an excellent catalytic effect on reducing the HTD temperature of AP. The catalytic activity of Co@NC was tested by a differential thermal analytical method. The results indicated that the HTD peak of AP was significantly decreased by 100.5 °C, the apparent activation energy of the HTD reaction of AP was reduced by 82.0 kJ mol-1, and the heat release compared with pure AP increased 2.9 times. On teh basis of these findings, Co@NC is expected to be one of the best candidate materials for AP thermal decomposition.

| S-EPMC8495879 | biostudies-literature

High catalytic activity and pollutants resistivity using Fe-AAPyr cathode catalyst for microbial fuel cell application.

Project description:For the first time, a new generation of innovative non-platinum group metal catalysts based on iron and aminoantipyrine as precursor (Fe-AAPyr) has been utilized in a membraneless single-chamber microbial fuel cell (SCMFC) running on wastewater. Fe-AAPyr was used as an oxygen reduction catalyst in a passive gas-diffusion cathode and implemented in SCMFC design. This catalyst demonstrated better performance than platinum (Pt) during screening in "clean" conditions (PBS), and no degradation in performance during the operation in wastewater. The maximum power density generated by the SCMFC with Fe-AAPyr was 167 ± 6 ?W cm(-2) and remained stable over 16 days, while SCMFC with Pt decreased to 113 ± 4 ?W cm(-2) by day 13, achieving similar values of an activated carbon based cathode. The presence of S(2-) and showed insignificant decrease of ORR activity for the Fe-AAPyr. The reported results clearly demonstrate that Fe-AAPyr can be utilized in MFCs under the harsh conditions of wastewater.

| S-EPMC4643260 | biostudies-literature

Carbon-doped SnS2 nanostructure as a high-efficiency solar fuel catalyst under visible light.

Project description:Photocatalytic formation of hydrocarbons using solar energy via artificial photosynthesis is a highly desirable renewable-energy source for replacing conventional fossil fuels. Using an L-cysteine-based hydrothermal process, here we synthesize a carbon-doped SnS2 (SnS2-C) metal dichalcogenide nanostructure, which exhibits a highly active and selective photocatalytic conversion of CO2 to hydrocarbons under visible-light. The interstitial carbon doping induced microstrain in the SnS2 lattice, resulting in different photophysical properties as compared with undoped SnS2. This SnS2-C photocatalyst significantly enhances the CO2 reduction activity under visible light, attaining a photochemical quantum efficiency of above 0.7%. The SnS2-C photocatalyst represents an important contribution towards high quantum efficiency artificial photosynthesis based on gas phase photocatalytic CO2 reduction under visible light, where the in situ carbon-doped SnS2 nanostructure improves the stability and the light harvesting and charge separation efficiency, and significantly enhances the photocatalytic activity.

| S-EPMC5766557 | biostudies-literature

Laccase Immobilization Strategies for Application as a Cathode Catalyst in Microbial Fuel Cells for Azo Dye Decolourization.

Project description:Enzymatic biocathodes have the potential to replace platinum as an expensive catalyst for the oxygen reduction reaction in microbial fuel cells (MFCs). However, enzymes are fragile and prone to loss of activity with time. This could be circumvented by using suitable immobilization techniques to maintain the activity and increase longevity of the enzyme. In the present study, laccase from Trametes versicolor was immobilized using three different approaches, i.e., crosslinking with electropolymerized polyaniline (PANI), entrapment in copper alginate beads (Cu-Alg), and encapsulation in Nafion micelles (Nafion), in the absence of redox mediators. These laccase systems were employed in cathode chambers of MFCs for decolourization of Acid orange 7 (AO7) dye. The biocatalyst in the anode chamber was Shewanella oneidensis MR-1 in each case. The enzyme in the immobilized states was compared with freely suspended enzyme with respect to dye decolourization at the cathode, enzyme activity retention, power production, and reusability. PANI laccase showed the highest stability and activity, producing a power density of 38 ± 1.7 mW m-2 compared to 25.6 ± 2.1 mW m-2 for Nafion laccase, 14.7 ± 1.04 mW m-2 for Cu-Alg laccase, and 28 ± 0.98 mW m-2 for the freely suspended enzyme. There was 81% enzyme activity retained after 1 cycle (5 days) for PANI laccase compared to 69% for Nafion and 61.5% activity for Cu-alginate laccase and 23.8% activity retention for the freely suspended laccase compared to initial activity. The dye decolourization was highest for freely suspended enzyme with over 85% decolourization whereas for PANI it was 75.6%, Nafion 73%, and 81% Cu-alginate systems, respectively. All the immobilized laccase systems were reusable for two more cycles. The current study explores the potential of laccase immobilized biocathode for dye decolourization in a microbial fuel cell.

| S-EPMC7847978 | biostudies-literature

A niobium and tantalum co-doped perovskite cathode for solid oxide fuel cells operating below 500?°C.

Project description:The slow activity of cathode materials is one of the most significant barriers to realizing the operation of solid oxide fuel cells below 500?°C. Here we report a niobium and tantalum co-substituted perovskite SrCo0.8Nb0.1Ta0.1O3-? as a cathode, which exhibits high electroactivity. This cathode has an area-specific polarization resistance as low as ?0.16 and ?0.68???cm2 in a symmetrical cell and peak power densities of 1.2 and 0.7?W?cm-2 in a Gd0.1Ce0.9O1.95-based anode-supported fuel cell at 500 and 450?°C, respectively. The high performance is attributed to an optimal balance of oxygen vacancies, ionic mobility and surface electron transfer as promoted by the synergistic effects of the niobium and tantalum. This work also points to an effective strategy in the design of cathodes for low-temperature solid oxide fuel cells.

| S-EPMC5216129 | biostudies-literature

Atomically dispersed cobalt catalyst anchored on nitrogen-doped carbon nanosheets for lithium-oxygen batteries.

Project description:Developing single-site catalysts featuring maximum atom utilization efficiency is urgently desired to improve oxidation-reduction efficiency and cycling capability of lithium-oxygen batteries. Here, we report a green method to synthesize isolated cobalt atoms embedded ultrathin nitrogen-rich carbon as a dual-catalyst for lithium-oxygen batteries. The achieved electrode with maximized exposed atomic active sites is beneficial for tailoring formation/decomposition mechanisms of uniformly distributed nano-sized lithium peroxide during oxygen reduction/evolution reactions due to abundant cobalt-nitrogen coordinate catalytic sites, thus demonstrating greatly enhanced redox kinetics and efficiently ameliorated over-potentials. Critically, theoretical simulations disclose that rich cobalt-nitrogen moieties as the driving force centers can drastically enhance the intrinsic affinity of intermediate species and thus fundamentally tune the evolution mechanism of the size and distribution of final lithium peroxide. In the lithium-oxygen battery, the electrode affords remarkably decreased charge/discharge polarization (0.40 V) and long-term cyclability (260 cycles at 400 mA g-1).

| S-EPMC7101366 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data