Effects of Process and Formulation Parameters on Submicron Polymeric Particles Produced by a Rapid Emulsion-Diffusion Method.

ABSTRACT: Emulsification-diffusion method is often used to produce polymeric nanoparticles. However, their numerous and/or lengthy steps make it difficult to use widely. Thus, a modified method using solvent blends (miscible/partially miscible in water, 25-100%) as the organic phases to overcome these disadvantages and its design space were investigated. To further simplify the process, no organic/aqueous phase saturation and no water addition after the emulsification step were performed. Biodegradable (PLGA) or pH-sensitive (Eudragit^® E100) nanoparticles were robustly produced using low/medium shear stirring adding dropwise the organic phase into the aqueous phase or vice versa. Several behaviors were also obtained: lowering the partially water-miscible solvent ratio relative to the organic phase or the poloxamer-407 concentration; or increasing the organic phase polarity or the polyvinyl alcohol concentration produced smaller particle sizes/polydispersity. Nanoparticle zeta potential increased as the water-miscible solvent ratio increased. Poloxamer-407 showed better performance to decrease the particle size (~50 nm) at low concentrations (≤1%, w/v) compared with polyvinyl alcohol at 1-5% (w/v), but higher concentrations produced bigger particles/polydispersity (≥600 nm). Most important, an inverse linear correlation to predict the particle size by determining the solubility parameter was found. A rapid method to broadly prepare nanoparticles using straightforward equipment is provided.

SUBMITTER: Dominguez-Delgado CL

PROVIDER: S-EPMC8780531 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The purpose of this work was to determine the effect of injection volume, formulation composition, and time on circumferential spread of particles, small molecules, and polymeric formulation excipients in the suprachoroidal space (SCS) after microneedle injection into New Zealand White rabbit eyes ex vivo and in vivo. Microneedle injections of 25-150 μL Hank's Balanced Salt Solution (HBSS) containing 0.2 μm red-fluorescent particles and a model small molecule (fluorescein) were performed in rabbit eyes ex vivo, and visualized via flat mount. Particles with diameters of 0.02-2 μm were co-injected into SCS in vivo with fluorescein or a polymeric formulation excipient: fluorescein isothiocyanate (FITC)-labeled Discovisc or FITC-labeled carboxymethyl cellulose (CMC). Fluorescent fundus images were acquired over time to determine area of particle, fluorescein, and polymeric formulation excipient spread, as well as their co-localization. We found that fluorescein covered a significantly larger area than co-injected particles when suspended in HBSS, and that this difference was present from 3 min post-injection onwards. We further showed that there was no difference in initial area covered by FITC-Discovisc and particles; the transport time (i.e., the time until the FITC-Discovisc and particle area began dissociating) was 2 d. There was also no difference in initial area covered by FITC-CMC and particles; the transport time in FITC-CMC was 4 d. We also found that particle size (20 nm-2 μm) had no effect on spreading area when delivered in HBSS or Discovisc. We conclude that (i) the area of particle spread in SCS during injection generally increased with increasing injection volume, was unaffected by particle size, and was significantly less than the area of fluorescein spread, (ii) particles suspended in low-viscosity HBSS formulation were entrapped in the SCS after injection, whereas fluorescein was not and (iii) particles co-injected with viscous polymeric formulation excipients co-localized near the site of injection in the SCS, continued to co-localize while spreading over larger areas for 2-4 days, and then no longer co-localized as the polymeric formulation excipients were cleared within 1-3 weeks and the particles remained largely in place. These data suggest that particles encounter greater barriers to flow in SCS compared to molecules and that co-localization of particles and polymeric formulation excipients allows spreading over larger areas of the SCS until the particles and excipients dissociate.

Dataset Information

Effects of Process and Formulation Parameters on Submicron Polymeric Particles Produced by a Rapid Emulsion-Diffusion Method.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets