3D Printing of Nacre-Inspired Structures with Exceptional Mechanical and Flame-Retardant Properties.

ABSTRACT: Flame-retardant and thermal management structures have attracted great attention due to the requirement of high-temperature exposure in industrial, aerospace, and thermal power fields, but the development of protective fire-retardant structures with complex shapes to fit arbitrary surfaces is still challenging. Herein, we reported a rotation-blade casting-assisted 3D printing process to fabricate nacre-inspired structures with exceptional mechanical and flame-retardant properties, and the related fundamental mechanisms are studied. 3-(Trimethoxysilyl)propyl methacrylate (TMSPMA) modified boron nitride nanoplatelets (BNs) were aligned by rotation-blade casting during the 3D printing process to build the "brick and mortar" architecture. The 3D printed structures are more lightweight, while having higher fracture toughness than the natural nacre, which is attributed to the crack deflection, aligned BN (a-BNs) bridging, and pull-outs reinforced structures by the covalent bonding between TMSPMA grafted a-BNs and polymer matrix. Thermal conductivity is enhanced by 25.5 times compared with pure polymer and 5.8 times of anisotropy due to the interconnection of a-BNs. 3D printed heat-exchange structures with vertically aligned BNs in complex shapes were demonstrated for efficient thermal control of high-power light-emitting diodes. 3D printed helmet and armor with a-BNs show exceptional mechanical and fire-retardant properties, demonstrating integrated mechanical and thermal protection.

SUBMITTER: Yang Y

PROVIDER: S-EPMC8817185 | biostudies-literature | 2022

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

3D Printing of Nacre-Inspired Structures with Exceptional Mechanical and Flame-Retardant Properties.

Yang Yang Y Wang Ziyu Z He Qingqing Q Li Xiangjia X Lu Gengxi G Jiang Laiming L Zeng Yushun Y Bethers Brandon B Jin Jie J Lin Shuang S Xiao Siqi S Zhu Yizhen Y Wu Xianke X Xu Wenwu W Wang Qiming Q Chen Yong Y

Research (Washington, D.C.) 20220127

Flame-retardant and thermal management structures have attracted great attention due to the requirement of high-temperature exposure in industrial, aerospace, and thermal power fields, but the development of protective fire-retardant structures with complex shapes to fit arbitrary surfaces is still challenging. Herein, we reported a rotation-blade casting-assisted 3D printing process to fabricate nacre-inspired structures with exceptional mechanical and flame-retardant properties, and the relate ...[more]

PMID: 35169712

Similar Datasets

Project description:The effects of combining 0.1-5 wt % graphene nanoplatelet (GNP) and 3-30 wt % phosphorous flame retardant, 9,10- dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) as fillers in epoxy polymer on the mechanical, flame retardancy, and electrical properties of the epoxy nanocomposites was investigated. GNP was homogeneously dispersed into the epoxy matrix using a solvent-free three-roll milling process, while DOPO was incorporated into the epoxy resin by mechanical stirring at elevated temperature. The incorporation of DOPO reduced the crosslinking density of the epoxy resin. When using polyetheramine as a hardener, the structural rigidity effect of DOPO overshadowed the crosslinking effect and governed the flexural moduli of epoxy/DOPO resins. The flexural moduli of the nanocomposites were improved by adding GNP up to 5 wt % and DOPO up to 30 wt %, whereas the flexural strengths deteriorated when the GNP and DOPO loading were higher than 1 wt % and 10 wt %, respectively. Limited by the adverse effects on mechanical property, the loading combinations of GNP and DOPO within the range of 0-1 wt % and 0-10 wt %, respectively, in epoxy resin were further studied. Flame retardancy index (FRI), which depended on three parameters obtained from cone calorimetry, was considered to evaluate the flame retardancy of the epoxy composites. DOPO showed better performance than GNP as the flame retardant additive, while combining DOPO and GNP could further improve FRI to some extent. With the combination of 0.5 wt % GNP and 10 wt % DOPO, improvement in both mechanical properties and flame retardant efficiency of the nanocomposite was observed. Such a combination did not affect the electrical conductivity of the nanocomposites since the percolation threshold was at 1.6 wt % GNP. Our results enhance the understanding of the structure-property relationship of additive-filled epoxy resin composites and serve as a property constraining guidance for the composite manufacturing.

Dataset Information

3D Printing of Nacre-Inspired Structures with Exceptional Mechanical and Flame-Retardant Properties.

Publications

3D Printing of Nacre-Inspired Structures with Exceptional Mechanical and Flame-Retardant Properties.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets