Enhanced osseointegration of dental implants with reduced graphene oxide coating.

ABSTRACT:

Background

The implants of pure titanium (Ti) and its alloys can lead to implant failure because of their poor interaction with bone-associated cells during bone regeneration. Surface modification over implants has achieved successful implants for enhanced osseointegration. Herein, we report a robust strategy to implement bioactive surface modification for implant interface enabled by the combinatorial system of reduced graphene oxide (rGO)-coated sandblasted, large-grit, and acid-etched (SLA) Ti to impart benefits to the implant.

Methods

We prepared SLA Ti (ST) implants with different surface modifications [i.e., rGO and recombinant human bone morphogenetic protein-2 (rhBMP-2)] and investigated their dental tissue regenerating ability in animal models. We performed comparative studies in surface property, in vitro cellular behaviors, and in vivo osseointegration activity among different groups, including ST (control), rhBMP-2-immobilized ST (BI-ST), rhBMP-2-treated ST (BT-ST), and rGO-coated ST (R-ST).

Results

Spectroscopic, diffractometric, and microscopic analyses confirmed that rGO was coated well around the surfaces of Ti discs (for cell study) and implant fixtures (for animal study). Furthermore, in vitro and in vivo studies revealed that the R-ST group showed significantly better effects in cell attachment and proliferation, alkaline phosphatase activity, matrix mineralization, expression of osteogenesis-related genes and protein, and osseointegration than the control (ST), BI-ST, and BT-ST groups.

Conclusion

Hence, we suggest that the rGO-coated Ti can be a promising candidate for the application to dental or even orthopedic implants due to its ability to accelerate the healing rate with the high potential of osseointegration.

SUBMITTER: Shin YC

PROVIDER: S-EPMC8935794 | biostudies-literature | 2022 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Enhanced osseointegration of dental implants with reduced graphene oxide coating.

Shin Yong Cheol YC Bae Ji-Hyeon JH Lee Jong Ho JH Raja Iruthayapandi Selestin IS Kang Moon Sung MS Kim Bongju B Hong Suck Won SW Huh Jung-Bo JB Han Dong-Wook DW

Biomaterials research 20220321 1

<h4>Background</h4>The implants of pure titanium (Ti) and its alloys can lead to implant failure because of their poor interaction with bone-associated cells during bone regeneration. Surface modification over implants has achieved successful implants for enhanced osseointegration. Herein, we report a robust strategy to implement bioactive surface modification for implant interface enabled by the combinatorial system of reduced graphene oxide (rGO)-coated sandblasted, large-grit, and acid-etched ...[more]

PMID: 35313996

Similar Datasets

Project description:Spatiotemporal implant-bone biomechanics and mechanoadaptive strains in peri-implant tissue are poorly understood. Physical and chemical characteristics of an implant-bone complex (IBC) were correlated in three-dimensional space (along the length and around a dental implant) to gather insights into time related integration of the implant with the cortical portion of a jaw bone in a rat. Rats (N = 9) were divided into three experimental groups with three rats per time point; 3-, 11-, and 24-day. All rats were fed crumbled hard pellets mixed with water (soft-food diet) for the first 3 days followed by a hard-food diet with intact hard-food pellets (groups of 11- and 24-day only). Biomechanics of the IBCs harvested from rats at each time point was evaluated by performing mechanical testing in situ in tandem with X-ray imaging. The effect of physical association (contact area) of a loaded implant with adapting peri-implant tissue, and resulting strain within was mapped by using digital volume correlation (DVC) technique. The IBC stiffness at respective time points was correlated with mechanical strain in peri-implant tissue. Results illustrated that IBC stiffness at 11-day was lower than that observed at 3-day. However, at 24-day, IBC stiffness recovered to that which was observed at 3-day. Correlative microscopy and spectroscopy illustrated that the lower IBC stiffness was constituted by softer and less mineralized peri-implant tissue that contained varying expressions of osteoconductive elements. Lower IBC stiffness observed at 11-day was constituted by less mineralized peri-implant tissue with osteoconductive elements that included phosphorus (P) which was co-localized with higher expression of zinc (Zn), and lower expression of calcium (Ca). Higher IBC stiffness at 24-day was constituted by mineralized peri-implant tissue with higher expressions of osteoconductive elements including Ca and P, and lower expressions of Zn. These spatiotemporal correlative maps of peri-implant tissue architecture, heterogeneous distribution of mineral density, and elemental colocalization underscore mechanoadaptive physicochemical properties of peri-implant tissue that facilitate functional osseointegration of an implant. These results provided insights into 1) plausible "prescription" of mechanical loads as an osteoinductive "therapeutic dose" to encourage osteoconductive elements in the peri-implant tissue that would facilitate functional osseointegration of the implant; 2) a "critical temporal window" between 3 and 11 days, and perhaps it is this acute phase during which key candidate regenerative molecules can be harnessed to accelerate osseointegration of an implant under load.

Project description:Currently, selective laser melting (SLM) has been thriving in implant dentistry for on-demand fabricating dental implants. Based on the coarse microtopography of SLM titanium surfaces, constructing nanostructure to form the hierarchical micro-nano topography is effective in enhancing osseointegration. Given that current nanomodification techniques of SLM implants, such as anodization and hydrothermal treatment, are facing the inadequacy in costly specific apparatus and reagents, there has been no recognized nanomodified SLM dental implants. The present study aimed to construct hierarchical micro-nano topography on self-made SLM dental implants by a simple and safe inorganic chemical oxidation, and to evaluate its contribution on osteoblastic cells bioactivity and osseointegration. The surface chemical and physical parameters were characterized by FE-SEM, EDS, profilometer, AFM, and contact angle meter. The alteration on bioactivity of MG-63 human osteoblastic cells were detected by qRT-PCR. Then the osseointegration was assessed by implanting implants on the femur condyle of New Zealand Rabbits. The hierarchical micro-nano topography was constituted by the microrough surface of SLM implants and nanoneedles (diameter: 20∼50 nm, height: 150∼250 nm), after nanomodifying SLM implants in 30% hydrogen peroxide and 30% hydrochloride acid (volume ratio 1:2.5) at room temperature for 36 h. Low chemical impurities content and high hydrophilicity were observed in the nanomodified group. Cell experiments on the nanomodified group showed higher expression of mitophagy related gene (PINK1, PARKIN, LC3B, and LAMP1) at 5 days and higher expression of osteogenesis related gene (Runx2 and OCN) at 14 days. In the early stage of bone formation, the nanomodified SLM implants demonstrated higher bone-to-implant contact. Intriguingly, the initial bone-to-implant contact of nanomodified SLM implants consisted of more mineralized bone with less immature osteoid. After the cessation of bone formation, the bone-to-implant contact of nanomodified SLM implants was equal to untreated SLM implants and marketable TixOs implants. The overall findings indicated that the inorganic chemical oxidized hierarchical micro-nano topography could enhance the bioactivity of osteoblastic cells, and consequently promote the peri-implant bone formation and mineralization of SLM dental implants. This study sheds some light on improvements in additive manufactured dental implants.

Dataset Information

Enhanced osseointegration of dental implants with reduced graphene oxide coating.

Background

Methods

Results

Conclusion

Publications

Enhanced osseointegration of dental implants with reduced graphene oxide coating.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets