Advantages of Fibrin Polymerization Method without the Use of Exogenous Thrombin for Vascular Tissue Engineering Applications.

ABSTRACT: Fibrin is widely used in vascular tissue engineering. Typically, fibrin polymerization is initiated by adding exogenous thrombin. In this study, we proposed a protocol for the preparation of completely autologous fibrin without the use of endogenous thrombin and compared the properties of the prepared fibrin matrix with that obtained by the traditional method. Fibrinogen was obtained by ethanol precipitation followed by fibrin polymerization by adding either exogenous thrombin and calcium chloride (ExThr), or only calcium chloride (EnThr). We examined the structure, mechanical properties, thrombogenicity, degradation rate and cytocompatibility of fibrin matrices. Factor XIII (FXIII) quantitative assay was performed by ELISA, and FXIII activity was assessed by SDS-PAGE detection of γ-γ cross-links. The results show that network structure of EnThr fibrin was characterized by thinner fibers. The EnThr fibrin matrices had higher strength, stiffness and resistance to proteolytic degradation compared to ExThr fibrin. EnThr fibrin matrices exhibited less thrombogenicity in vitro than ExThr, and retained high cytocompatibility. Thus, the proposed approach has several advantages over the traditional method, namely the fabrication of a completely autologous coating material that has better mechanical properties, higher resistance to proteolysis and lower thrombogenicity.

SUBMITTER: Matveeva VG

PROVIDER: S-EPMC9026760 | biostudies-literature | 2022 Mar

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Advantages of Fibrin Polymerization Method without the Use of Exogenous Thrombin for Vascular Tissue Engineering Applications.

Matveeva Vera G VG Senokosova Evgenia A EA Sevostianova Viktoriia V VV Khanova Mariam Yu MY Glushkova Tatiana V TV Akentieva Tatiana N TN Antonova Larisa V LV Barbarash Leonid S LS

Biomedicines 20220328 4

Fibrin is widely used in vascular tissue engineering. Typically, fibrin polymerization is initiated by adding exogenous thrombin. In this study, we proposed a protocol for the preparation of completely autologous fibrin without the use of endogenous thrombin and compared the properties of the prepared fibrin matrix with that obtained by the traditional method. Fibrinogen was obtained by ethanol precipitation followed by fibrin polymerization by adding either exogenous thrombin and calcium chlori ...[more]

PMID: 35453539

Similar Datasets

Project description:Myocardial infarction (MI) causes significant cell loss and damage to myocardium. Cell-based therapies for treatment of MI aim to remuscularize the resultant scar tissue, but the majority of transplanted cells do not survive or integrate with the host tissue. Scaffolds can improve cell retention following construct implantation, but often do little to enhance host-graft integration and/or show limited biodegradation. Fibrin is an ideal biomaterial for cardiac tissue engineering as it is a natural, biodegradable polymer that can induce neovascularization, promote cell attachment, and has tunable mechanical properties. Here we describe a novel, high-density microtemplated fibrin scaffold seeded with a tri-cell mixture of cardiomyocytes, endothelial cells (ECs), and fibroblasts to mimic native cardiac tissue in structure and cellular composition to improve cell retention and promote integration with the host tissue. Scaffolds were designed with uniform architecture of parallel 60 ?m microchannels surrounded by an interconnected microporous network of 27-?m-diameter pores and mechanical stiffness comparable to native cardiac tissues (70-90kPa). Scaffold degradation was controlled with the addition of Factor XIII (FXIII) and/or protease inhibitor (aprotinin). Unmodified scaffolds had a fast degradation profile both in vitro (19.9%±3.9% stiffness retention after 10 days) and in vivo. Scaffolds treated with FXIII showed an intermediate degradation profile in vitro (45.8%±5.9%), while scaffolds treated with aprotinin or both FXIII and aprotinin showed significantly slowed degradation in vitro (60.9%±5.2% and 76.4%±7.6%, respectively, p<0.05). Acellular aprotinin scaffold myocardial implants showed decreased collagen deposition after 7 days. Unmodified and aprotinin implants could not be located by 14 days, while 2 of 8 FXIII implants were found, but were significantly degraded. Constructs supported seeded cell survival and organization in vitro, promoting EC-lined lumen structure formation in construct channels and colocalization of viable ECs and cardiomyocytes. In addition, constructs promoted extracellular matrix deposition by seeded cells, as shown by collagen staining within construct channels and by significant increases in construct stiffness over 10 days in vitro (209%±32%, p<0.05). The data suggest our fibrin scaffolds are ideally designed to promote graft cell survival and organization, thus improving chances of promoting construct integration with the host tissue upon implantation.

Project description:ObjectiveAt sites of vascular injury, thrombin is an important mediator in thrombus growth and stability. Using microfluidic flow devices as well as patterned surfaces of collagen and tissue factor (TF), we sought to determine the role that fibrin plays in clot stability without interfering with the production of thrombin.Methods and resultsWe deployed an 8-channel microfluidic device to study coagulation during corn trypsin inhibitor-treated (XIIa-inhibited) whole blood perfusion over lipidated TF linked to a fibrillar collagen type 1 surface. Clot growth and embolization were measured at initial inlet venous (200 s(-1)) or arterial (1000 s(-1)) wall shear rates under constant flow rate or pressure relief mode in the presence or absence of Gly-Pro-Arg-Pro (GPRP) to block fibrin polymerization. Numerical calculations for each mode defined hemodynamic forces on the growing thrombi. In either mode at inlet venous flow, increasing amounts of TF on the surface led to a modest dose-dependent increase (up to 2-fold) in platelet deposition, but resulted in massive fibrin accumulation (>50-fold) only when exceeding a critical TF threshold. At a venous inlet flow, GPRP led to a slight 20% increase in platelet accumulation (P<0.01) in pressure relief mode with thrombi resisting ≈1500 s(-1) before full channel occlusion. GPRP-treated thrombi were unstable under constant flow rate, where shear forces caused embolization at a maximum shear rate of ≈2300 s(-1) (69 dynes/cm2). In constant flow rate mode, the nonocclusive platelet-fibrin deposits (no GPRP) withstood maximum shear rates of ≈29 000 s(-1) (870 dyne/cm2) at ≈95% of full channel occlusion. For arterial inlet shear rate, embolization was marked for either mode with GPRP present when shear forces reached 87 dynes/cm2 (≈2900 s(-1)). Under constant flow rate, platelet-fibrin deposits (no GPRP) withstood maximums of 2400 dynes/cm2 (80,000 s(-1)) at ≈90% of full channel occlusion prior to embolization.ConclusionsFibrin increased clot strength by 12- to 28-fold. Under pressure relief mode, ≈2-fold more fibrin was produced under venous flow (P<0.001). These studies define embolization criteria for clots formed with surface TF-triggered thrombin production (±fibrin) under venous and arterial flows.

Dataset Information

Advantages of Fibrin Polymerization Method without the Use of Exogenous Thrombin for Vascular Tissue Engineering Applications.

Publications

Advantages of Fibrin Polymerization Method without the Use of Exogenous Thrombin for Vascular Tissue Engineering Applications.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets