Controllable synthesis of raspberry-like PS-SiO₂ nanocomposite particles via Pickering emulsion polymerization.

ABSTRACT: This paper presents a simple and controllable method for the synthesis of monodisperse nanometer-sized organic-inorganic raspberry-like polystyrene (PS)-SiO₂ nanocomposite particles (NCPs) via Pickering emulsion polymerization, by simply using a silane coupling agent, 3-(trimethoxysilyl)propyl methacrylate (MPS), as an auxiliary monomer and controlling its hydrolysis/condensation processes and amount. In this method, when MPS was stirred in acidic water with styrene (St) for a period of time, and then a basic silica solution added, raspberry-like PS-SiO₂ NCPs were directly obtained after the polymerization. The whole process needs neither surface treatment for the silica particles nor additional surfactants or stabilizers. We propose that a silica-stabilized Pickering emulsion is formed through Si-OH reaction between the hydrolysis/condensation products of MPS distributed on the St droplets surface and the silica particles.

SUBMITTER: Zhang X

PROVIDER: S-EPMC9077750 | biostudies-literature | 2018 Jan

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Controllable synthesis of raspberry-like PS-SiO2 nanocomposite particles via Pickering emulsion polymerization.

Zhang Xiaotian X Sun Yangyi Y Mao Yijing Y Chen Kunlin K Cao Zhihai Z Qi Dongming D

RSC advances 20180122 7

This paper presents a simple and controllable method for the synthesis of monodisperse nanometer-sized organic-inorganic raspberry-like polystyrene (PS)-SiO2 nanocomposite particles (NCPs) via Pickering emulsion polymerization, by simply using a silane coupling agent, 3-(trimethoxysilyl)propyl methacrylate (MPS), as an auxiliary monomer and controlling its hydrolysis/condensation processes and amount. In this method, when MPS was stirred in acidic water with styrene (St) for a ...[more]

PMID: 35542926

Similar Datasets

Project description:Incorporating unmodified silica nanoparticles onto polymer latexes to fabricate aqueous polymer dispersions without relying on electrostatic attraction during the Pickering emulsion polymerization process still faces challenges. For negatively charged silica nanoparticles to successfully adsorb onto polymer latexes, particularly in an anionic initiator emulsion polymerization system, they have remained elusive without the use of auxiliary monomers and cationic initiators. This study investigates various experimental parameters, such as emulsion polymerization temperature, monomer solubility, salt concentration, and cation type, to elucidate the factors influencing the adsorption of unmodified silica nanoparticles in Pickering emulsion polymerization. While poly(methyl methacrylate) (PMMA)/SiO2 hybrid latexes can be obtained under pH conditions of 5-6 and at temperatures of 65 °C or below, the loading rate of silica nanoparticles decreases as the reaction temperature increases, resulting in bare PMMA latexes without silica nanoparticle adsorption at temperatures exceeding 70 °C. Introducing styrene (St) into the monomer mixture with methyl methacrylate in a ratio of up to 10 wt % leads to a gradual decrease in silica nanoparticle loading rate, from 27.3 to 8.2 wt %, attributed to the low solubility of St in water. Furthermore, the presence of sodium ions (Na+) is found to be crucial for silica nanoparticle adsorption onto PMMA latexes, as the sodium ions have a stabilizing effect on both the silica nanoparticles and the silica nanoparticle-armored latexes. These findings highlight the complex nature of Pickering emulsion polymerization in the presence of unmodified silica nanoparticles, demonstrating that the loading rate of silica nanoparticles onto polymer latexes is influenced by various factors. These insights pave the way for developing aqueous polymer dispersions with high silica nanoparticle loading rates onto polymer latexes, which is a desirable trait in the coating industry.

Dataset Information

Controllable synthesis of raspberry-like PS-SiO₂ nanocomposite particles via Pickering emulsion polymerization.

Publications

Controllable synthesis of raspberry-like PS-SiO<sub>2</sub> nanocomposite particles <i>via</i> Pickering emulsion polymerization.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets