Ferrocene-functionalized polyheteroacenes for the use as cathode active material in rechargeable batteries.

ABSTRACT: Herein we report the synthesis and characterization of new conjugated polymers bearing redox-active pendant groups for applications as cathode active materials in secondary batteries. The polymers comprise a ferrocene moiety immobilized at a poly(cyclopenta[2,1-b:3,4-b']dithiophene) (pCPDT, P1) or a poly(dithieno[3,2-b:2',3'-d]pyrrole) (pDTP, P2) backbone via an ester or an amide linker. Electrochemical and oxidative chemical polymerizations were performed in order to investigate the redox behaviour of the obtained polymers P1 and P2 and to synthesize materials on gram-scale for battery tests, respectively. During galvanostatic cycling in a typical battery environment, both polymers showed high reversible capacities of 90% and 87% of their theoretical capacity and excellent capacity retentions of 84% and 97% over 50 cycles.

SUBMITTER: Schwartz PO

PROVIDER: S-EPMC9079884 | biostudies-literature | 2018 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Ferrocene-functionalized polyheteroacenes for the use as cathode active material in rechargeable batteries.

Schwartz Pierre-Olivier PO Förtsch Sebastian S Mena-Osteritz Elena E Weirather-Köstner Dagmar D Wachtler Mario M Bäuerle Peter P

RSC advances 20180417 26

Herein we report the synthesis and characterization of new conjugated polymers bearing redox-active pendant groups for applications as cathode active materials in secondary batteries. The polymers comprise a ferrocene moiety immobilized at a poly(cyclopenta[2,1-b:3,4-b']dithiophene) (pCPDT, P1) or a poly(dithieno[3,2-b:2',3'-d]pyrrole) (pDTP, P2) backbone via an ester or an amide linker. Electrochemical and oxidative chemical polymerizations were performed in o ...[more]

PMID: 35540730

Similar Datasets

Synthesis of manganese-based complex as cathode material for aqueous rechargeable batteries.

Project description:A low-cost and eco-friendly system based on a manganese-based complex cathode and zinc anode was demonstrated. The cathode is able to reversibly (de-)insert Zn2+ ions, providing a high capacity of 248 mA h g-1 at 0.1 A g-1. Ex situ TEM and XRD were utilized to determine the electrochemical mechanism of this high capacity cathode. Moreover, the contribution of pre-added Mn2+ in electrolyte to the capacity was revealed, and nearly 18.9% of the capacity is ascribed to the contribution of pre-added Mn2+. With the help of additive, this aqueous rechargeable battery shows outstanding electrochemical property. Its cycling performance is good with 6% capacity loss after 2000 cycles at 4.0 A g-1, highlighting it as a promising system for aqueous rechargeable battery applications.

| S-EPMC9080094 | biostudies-literature

Coulombic self-ordering upon charging a large-capacity layered cathode material for rechargeable batteries.

Project description:Lithium- and sodium-rich layered transition-metal oxides have recently been attracting significant interest because of their large capacity achieved by additional oxygen-redox reactions. However, layered transition-metal oxides exhibit structural degradation such as cation migration, layer exfoliation or cracks upon deep charge, which is a major obstacle to achieve higher energy-density batteries. Here we demonstrate a self-repairing phenomenon of stacking faults upon desodiation from an oxygen-redox layered oxide Na2RuO3, realizing much better reversibility of the electrode reaction. The phase transformations upon charging A2MO3 (A: alkali metal) can be dominated by three-dimensional Coulombic attractive interactions driven by the existence of ordered alkali-metal vacancies, leading to counterintuitive self-repairing of stacking faults and progressive ordering upon charging. The cooperatively ordered vacancy in lithium-/sodium-rich layered transition-metal oxides is shown to play an essential role, not only in generating the electro-active nonbonding 2p orbital of neighbouring oxygen but also in stabilizing the phase transformation for highly reversible oxygen-redox reactions.

| S-EPMC6522540 | biostudies-literature

Heteroaromatic organic compound with conjugated multi-carbonyl as cathode material for rechargeable lithium batteries.

Project description:The heteroaromatic organic compound, N,N'-diphenyl-1,4,5,8-naphthalenetetra- carboxylic diimide (DP-NTCDI-250) as the cathode material of lithium batteries is prepared through a simple one-pot N-acylation reaction of 1,4,5,8-naphthalenetetra-carboxylic dianhydride (NTCDA) with phenylamine (PA) in DMF solution followed by heat treatment in 250 °C. The as prepared sample is characterized by the combination of elemental analysis, NMR, FT-IR, TGA, XRD, SEM and TEM. The electrochemical measurements show that DP-NTCDI-250 can deliver an initial discharge capacity of 170 mAh g(-1) at the current density of 25 mA g(-1). The capacity of 119 mAh g(-1) can be retained after 100 cycles. Even at the high current density of 500 mA g(-1), its capacity still reaches 105 mAh g(-1), indicating its high rate capability. Therefore, the as-prepared DP-NTCDI-250 could be a promising candidate as low cost cathode materials for lithium batteries.

| S-EPMC4827395 | biostudies-literature

New O3-Type Layer-Structured Na0.80[Fe0.40Co0.40Ti0.20]O2 Cathode Material for Rechargeable Sodium-Ion Batteries.

Project description:Herein, we formulated a new O3-type layered Na0.80[Fe0.40Co0.40Ti0.20]O2 (NFCTO) cathode material for sodium-ion batteries (SIBs) using a double-substitution concept of Co in the parent NaFe0.5Co0.5O2, having the general formula Na1-x[Fe0.5-x/2Co0.5-x/2M4+x]O2 (M4+ = tetravalent ions). The NFCTO electrode delivers a first discharge capacity of 108 mAhg-1 with 80% discharge capacity retention after 50 cycles. Notably, the first charge-discharge profile shows asymmetric yet reversible redox reactions. Such asymmetric redox reactions and electrochemical properties of the NFCTO electrode were correlated with the phase transition behavior and charge compensation reaction using synchrotron-based in situ XRD and ex situ X-ray absorption spectroscopy. This study provides an exciting opportunity to explore the interplay between the rich chemistry of Na1-x[Fe0.5-x/2Co0.5-x/2M4+x]O2 and sodium storage properties, which may lead to the development of new cathode materials for SIBs.

| S-EPMC8124707 | biostudies-literature

Vanadium Pentoxide-Based Composite Synthesized Using Microwave Water Plasma for Cathode Material in Rechargeable Magnesium Batteries.

Project description:Multivalent cation rechargeable batteries are expected to perform well as high-capacity storage devices. Rechargeable magnesium batteries have an advantage in terms of resource utilization and safety. Here, we report on sulfur-doped vanadium pentoxide (S-V₂O₅) as a potential material for the cathodes of such a battery; S-V₂O₅ showed a specific capacity of 300 mAh·g-1. S-V₂O₅ was prepared by a method using a low-temperature plasma generated by carbon felt and a 2.45 GHz microwave generator. This study investigates the ability of S-V₂O₅ to achieve high capacity when added to metal oxide. The highest recorded capacity (420 mAh·g-1) was reached with MnO₂ added to composite SMn-V₂O₅, which has a higher proportion of included sulfur than found in S-V₂O₅. Results from transmission electron microscopy, energy-dispersive X-ray spectroscopy, Micro-Raman spectroscopy, and X-ray photoelectron spectroscopy show that the bulk of the SMn-V₂O₅ was the orthorhombic V₂O₅ structure; the surface was a xerogel-like V₂O₅ and a solid solution of MnO₂ and sulfur.

| S-EPMC5452843 | biostudies-other

Design of Organic Cathode Material Based on Quinone and Pyrazine Motifs for Rechargeable Lithium and Zinc Batteries.

Project description:Despite the rapid expansion of the organic cathode materials field, we still face a shortage of materials obtained through simple synthesis that have stable cycling and high energy density. Herein, we report a two-step synthesis of a small organic molecule from commercially available precursors that can be used as a cathode material. Oxidized tetraquinoxalinecatechol (OTQC) was derived from tetraquinoxalinecatechol (TQC) by the introduction of additional quinone redox-active centers into the structure. The modification increased the voltage and capacity of the material. The OTQC delivers a high specific capacity of 327 mAh g-1 with an average voltage of 2.63 V vs Li/Li+ in the Li-ion battery. That corresponds to an energy density of 860 Wh kg-1 on the OTQC material level. Furthermore, the material demonstrated excellent cycling stability, having a capacity retention of 82% after 400 cycles. Similarly, the OTQC demonstrates increased average voltage and specific capacity in comparison with TQC in aqueous Zn-organic battery, reaching the specific capacity of 326 mAh g-1 with an average voltage of 0.86 V vs Zn/Zn2+. Apart from good electrochemical performance, this work provides an additional in-depth analysis of the redox mechanism and degradation mechanism related to capacity fading.

| S-EPMC10995900 | biostudies-literature

Exploration of Li-Organic Batteries Using Hexaphyrin as an Active Cathode Material.

Project description:Lithium-collaborating organic batteries (Li-[28]hexs) were investigated with [28]hexaphyrin(1.1.1.1.1.1) as an active electrode material. Each hexaphyrin of [28]Hex cathode ideally involved four electrons per unit cycle and performed a typical charge/discharge processes of Li-organic battery. Li-[28]Hex batteries set with fast charging rates showed reasonably stable charge and discharge performances over 200 cycles even though it caused incomplete (2~3 electrons) charge/discharge cycles due to failing the complete charging process. UV absorption changes of [28]hexaphyrin in CH2Cl2 were supplementary for the electrochemical oxidation, which performed a conversion from [28]hexaphyrin to [26]hexaphyrin.

| S-EPMC6651293 | biostudies-literature

Nitridation effect on lithium iron phosphate cathode for rechargeable batteries.

Project description:A novel oxynitride Li0.94FePO3.84N0.16 with olivine structure (space group Pnma, no. 62) has been synthesized by heating a parent LiFePO4 precursor obtained by citrate chemistry in flowing ammonia at 650 °C. The polycrystalline sample has been characterized by X-ray and neutron powder diffraction (NPD), elemental and thermal analysis, scanning electron microscopy (SEM) and electrochemical measurements. Based on the existing contrast between the scattering lengths of the N and O species, a Rietveld refinement of the structure from NPD data revealed that N preferentially occupies the O2 positions, as likely required to fulfil the bonding power of N ions. The refined crystallographic formula implies an oxidation state of 2.2+ for Fe cations. The differential thermal analysis, in still air, shows a strong exothermic peak at 520-540 °C due to the combustion of C contents, which are embedding the olivine particles, as observed by SEM. The electrochemical measurements suggest a better performance for the nitrided sample relative to the unnitrided LiFePO4 material, as far as capacity and cyclability are concerned. A bond-valence energy landscape study reveals a decrease in the percolation activation energy of about 6% upon nitridation, concomitant with the better electrochemical properties of the oxynitride compound. Additionally, ceramic samples prepared under NH3 flow could be obtained as pure and well-crystallized olivine phases at milder temperatures (650 °C) than those usually described in literature.

| S-EPMC8979366 | biostudies-literature

Enhanced charge transport properties of an LFP/C/graphite composite as a cathode material for aqueous rechargeable lithium batteries.

Project description:Electrodes that offer quick ion transport, a large surface area, and excellent electrical conductivity support high performance aqueous rechargeable lithium batteries. LiFePO4 (LFP) nanoparticles have been successfully coated with carbon by a chemical sol-gel route, and assembled on graphite by an ultrasonication method to acquire LFP/C/graphite. This LFP/C/graphite composite exhibits exceptional electrochemical performance at various current densities (1C to 20C). LFP/C/graphite delivers better capacity that is higher than that of LFP/C particles and high stability after 60 cycles at a current density of 1C for aqueous rechargeable lithium batteries as a cathode material. The graphite serves as a good volume buffer in improving the lithium performance of LFP/C/graphite during the charge/discharge process. The LFP/C/graphite composite shows high rate capability at 20C that returned to the initial capacity at 1C after 25 cycles with coulombic efficiency of 97%. Therefore, this effort presents a super low-cost route to fabricate high performance cathode materials in aqueous rechargeable lithium batteries and other energy storage appliances.

| S-EPMC10445526 | biostudies-literature

Binder-Free V2O5 Cathode for High Energy Density Rechargeable Aluminum-Ion Batteries.

Project description:Nowadays, research on electrochemical storage systems moves into the direction of post-lithium-ion batteries, such as aluminum-ion batteries, and the exploration of suitable materials for such batteries. Vanadium pentoxide (V2O5) is one of the most promising host materials for the intercalation of multivalent ions. Here, we report on the fabrication of a binder-free and self-supporting V2O5 micrometer-thick paper-like electrode material and its use as the cathode for rechargeable aluminum-ion batteries. The electrical conductivity of the cathode was significantly improved by a novel in-situ and self-limiting copper migration approach into the V2O5 structure. This process takes advantage of the dissolution of Cu by the ionic liquid-based electrolyte, as well as the presence of two different accommodation sites in the nanostructured V2O5 available for aluminum-ions and the migrated Cu. Furthermore, the advanced nanostructured cathode delivered a specific discharge capacity of up to ~170 mAh g-1 and the reversible intercalation of Al3+ for more than 500 cycles with a high Coulomb efficiency reaching nearly 100%. The binder-free concept results in an energy density of 74 Wh kg-1, which shows improved energy density in comparison to the so far published V2O5-based cathodes. Our results provide valuable insights for the future design and development of novel binder-free and self-supporting electrodes for rechargeable multivalent metal-ion batteries associating a high energy density, cycling stability, safety and low cost.

| S-EPMC7075190 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data