Adsorption Behaviors of Cationic Methylene Blue and Anionic Reactive Blue 19 Dyes onto Nano-Carbon Adsorbent Carbonized from Small Precursors.

ABSTRACT: In this work, an innovative nano-carbon material (N-CM) adsorbent was reported for exploring its adsorption behaviors toward cationic methylene blue (MB) and anionic reactive blue 19 (RB19) pollutants. The proposed N-CM was synthesized by a one-step solvothermal treatment of citric acid and zinc gluconate small precursors. N-CM consists of nanosheets that have an advantageous specific surface area, large sp²/sp³ hybridized domains, and abundant nitrogen/oxygen-containing surface functional groups. The synergistic effects of these features are conducive to the MB and RB19 adsorption. Different from anionic RB19 adsorption (79.54 mg/g) by the cooperative π-π stacking and hydrogen bonding, cationic MB adsorbed onto N-CM mainly by the electrostatic attraction at the natural pH solution (> pH_pzc), with an adsorption capacity up to 118.98 mg/g. Interestingly, both MB and RB19 adsorption conformed to the pseudo-second order kinetic (R² ≥ 0.995) and Langmuir isothermal (R² ≥ 0.990) models, accompanied by similar maximum monolayer adsorption capacities of 120.77 and 116.01 mg/g, respectively. Their adsorption processes exhibited spontaneously endothermic characteristics. Moreover, N-CM showed superior selective capability toward MB in different mixed dye systems, with high removal efficiencies of 73-89%. These results demonstrate that the high-performance carbon adsorbent prepared from small precursors via low-temperature carbonization shows great potentials in wastewater treatment.

SUBMITTER: Liang C

PROVIDER: S-EPMC9182342 | biostudies-literature | 2022 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Adsorption Behaviors of Cationic Methylene Blue and Anionic Reactive Blue 19 Dyes onto Nano-Carbon Adsorbent Carbonized from Small Precursors.

Liang Caizhen C Shi Qingshan Q Feng Jin J Yao Junwei J Huang Hui H Xie Xiaobao X

Nanomaterials (Basel, Switzerland) 20220525 11

In this work, an innovative nano-carbon material (N-CM) adsorbent was reported for exploring its adsorption behaviors toward cationic methylene blue (MB) and anionic reactive blue 19 (RB19) pollutants. The proposed N-CM was synthesized by a one-step solvothermal treatment of citric acid and zinc gluconate small precursors. N-CM consists of nanosheets that have an advantageous specific surface area, large sp2/sp3 hybridized domains, and abundant nitrogen/oxygen-containing surface functional group ...[more]

PMID: 35683669

Similar Datasets

Project description:With increasing awareness of reduction of energy and CO2 footprint, more waste is considered recyclable for generating value-added products. Here we reported the negatively-valued iron mud, a waste from groundwater treatment plant, was successfully converted into magnetic adsorbent. Comparing with the conventional calcination method under the high temperature and pressure, the synthesis of the magnetic particles (MPs) by Fe2+/Fe3+ coprecipitation was conducted at environment-friendly condition using ascorbic acid (H2A) as reduction reagent and nitric acid (or acid wastewater) as leaching solution. The MPs with major component of Fe3O4 were synthesized at the molar ratio (called ratio subsequently) of H2A to Fe3+ of iron mud ≥ 0.1; while amorphous ferrihydrite phase was formed at the ratio ≤ 0.05, which were confirmed by vibrating sample magnetometer (VSM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). With the ratio increased, the crystalline size and the crystallization degree of MPs increased, and thus the Brunauer-Emmett-Teller (BET) surface and the cation-exchange capacity (CEC) decreased. MPs-3 prepared with H2A to Fe3+ ratio of 0.1 demonstrated the highest methylene blue (MB) adsorption of 87.3 mg/g and good magnetic response. The adsorption of MB onto MPs agreed well with the non-linear Langmuir isotherm model and the pseudo-second-order model. Pilot-scale experiment showed that 99% of MB was removed by adding 10 g/L of MPs-3. After five adsorption-desorption cycles, MPs-3 still showed 62% removal efficiency for MB adsorption. When nitric acid was replaced by acid wastewater from a propylene plant, the synthesized MPs-3w showed 3.7 emu/g of saturation magnetization (Ms) and 56.7 mg/g of MB adsorption capacity, 2.8 times of the widely used commercial adsorbent of granular active carbon (GAC). The major mechanism of MPs adsorption for MB was electrostatic attraction and cation exchange. This study synthesized a magnetic adsorbent from the negatively-valued iron mud waste by using an environment-friendly coprecipitation method, which had a potential for treatment of dye wastewater.

Dataset Information

Adsorption Behaviors of Cationic Methylene Blue and Anionic Reactive Blue 19 Dyes onto Nano-Carbon Adsorbent Carbonized from Small Precursors.

Publications

Adsorption Behaviors of Cationic Methylene Blue and Anionic Reactive Blue 19 Dyes onto Nano-Carbon Adsorbent Carbonized from Small Precursors.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets