Polyaniline inside the pores of high surface area mesoporous silicon as composite electrode material for supercapacitors.

ABSTRACT: Mesoporous silicon (mSi) obtained by the magnesiothermic reduction of mesoporous silica was used to deposit polyaniline (PANI) in its pores, the composite was tested for its charge storage application for high performance supercapacitor electrodes. The mesoporous silica as confirmed by Small Angle X-ray Scattering (SAXS) has a Brunauer-Emmett-Teller (BET) surface area of 724 m²g^-1 and mean pore size of 5 nm. After magnesiothermic reduction to mSi, the BET surface area is reduced to 348 m²g^-1 but the mesoporousity is retained with a mean pore size of 10 nm. The BET surface area of mesoporous silicon is among the highest for porous silicon prepared/reduced from silica. In situ polymerization of PANI inside the pores of mSi was achieved by controlling the polymerization conditions. As a supercapacitor electrode, the mSi-PANI composite exhibits better charge storage performance as compared to pure PANI and mesoporous silica-PANI composite electrodes. Enhanced electrochemical performance of the mSi-PANI composite is attributed to the high surface mesoporous morphology of mSi with a network structure containing abundant mesopores enwrapped by an electrochemically permeable polyaniline matrix.

SUBMITTER: Nawaz S

PROVIDER: S-EPMC9185315 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Preparation and Electrochemical Characterization of Mesoporous Polyaniline-Silica Nanocomposites as an Electrode Material for Pseudocapacitors.

Project description:Mesoporous polyaniline-silica nanocomposites with a full interpenetrating structure for pseudocapacitors were synthesized via the vapor phase approach. The morphology and structure of the nanocomposites were deeply investigated by scanning electron microscopy, infrared spectroscopy, X-ray diffraction, thermal gravimetric analysis and nitrogen adsorption-desorption tests. The results present that the mesoporous nanocomposites possess a uniform particle morphology and full interpenetrating structure, leading to a continuous conductive polyaniline network with a large specific surface area. The electrochemical performances of the nanocomposites were tested in a mixed solution of sulfuric acid and potassium iodide. With the merits of a large specific surface area and suitable pore size distribution, the nanocomposite showed a large specific capacitance (1702.68 farad (F)/g) due to its higher utilization of the active material. This amazing value is almost three-times larger than that of bulk polyaniline when the same mass of active material was used.

| S-EPMC5507039 | biostudies-other

Synthesis of polypyrrole/nitrogen-doped porous carbon matrix composite as the electrode material for supercapacitors.

Project description:Polypyrrole complex nitrogen-doped porous carbon matrix (PPy/N-PCM) was synthesized by a simple two-step method. Firstly, graphene oxide was prepared by the modified Hummers method. Secondly, Polypyrrole was compounded on the graphene oxide substrate, and the carbon matrix with a high specific surface area was obtained through high-temperature carbonization and KOH activation, and polypyrrole was used as a nitrogen source for the final nitrogen-doped composite material. The structure characterization of the carbon matrix and the final composite material shows that the carbon matrix surface has obvious porous structure, and the polypyrrole nanospheres grow uniformly on the porous carbon matrix surface. The electrochemical evaluation show that the prepared PPy/N-PCM has excellent supercapacitor performance, and its specific capacitance can reach 237.5 F g-1. When the current density reaches 10 A g-1, it has good cycle stability (the capacitance retention after 1000 charge and discharge is 88.53% of the initial capacitance value, which is better than pure PPy-60.76% and PPy/rGO-C-71.84%). The excellent capacitance performance, good-looking micro-morphology and simple synthesis method of the PPy/N-PCM provide the possibility for its commercialization.

| S-EPMC7505966 | biostudies-literature

In Situ Synthesis of a Polyaniline/ Fe-Ni Codoped Co3O4 Composite for the Electrode Material of Supercapacitors with Improved Cyclic Stability.

Project description:Conductive polymers have become a remarkable candidate for electrode materials of supercapacitors. Polyaniline (PANI) is the most promising contender for supercapacitors because of its easy method of synthesis, low cost, and higher choice in the improvement of energy storage applications. The main issue in the use of PANI in supercapacitors is its lower stability. In this work, PANI@Fe-Ni codoped Co3O4 (PANI@FNCO) nanocomposite has been prepared by in situ addition of 10 wt % FNCO as fillers in the PANI matrix. The nanocomposites were then characterized via scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy, thermogravimetric analysis, and differential scanning calorimetry to observe the morphology, crystal structure, functional groups, and thermal stability of samples, respectively. SEM results showed that FNCO was fairly dispersed in the PANI matrix, while XRD results showed a broad peak for nanocomposites because of the semicrystalline nature of polymers. The electrochemical properties of the samples were analyzed via cyclic voltammetry, galvanostatic charge and discharge, and electrochemical impedance spectroscopy. PANI@FNCO nanowires are found to overcome the shortcomings in electrochemical energy storage devices by exhibiting a higher value of specific capacitance of 1171 F g-1 and energy density of 144 W h kg-1 at a current density of 1 A g-1. Moreover, the FNCO nanowires also showed a cyclic charge/discharge stability of 84% for 2000 cycles.

| S-EPMC7818300 | biostudies-literature

Preparation of a MoS2/carbon nanotube composite as an electrode material for high-performance supercapacitors.

Project description:MoS2 and MoS2/carbon allotrope (MoS2/C) composites for use as anodes in supercapacitors were prepared via a facile hydrothermal method. In this study, we report the effects of various carbon-based materials (2D graphene nanosheet (GNS), 1D carbon nanotube (CNT), and 0D nano carbon (NC)) on the electrochemical performances. Among all nanocomposites studied, MoS2/CNT exhibited the best electrochemical performance. Specifically, the MoS2/CNT composite exhibits remarkable performances with a high specific capacitance of 402 F g-1 at a current density of 1 A g-1 and an outstanding cycling stability with 81.9% capacitance retention after 10 000 continuous charge-discharge cycles at a high current density of 1 A g-1, making it adaptive for high-performance supercapacitors. The superiority of MoS2/CNT was investigated by field emission scanning electron microscopy and transmission electron microscopy, which showed that MoS2 nanosheets were uniformly loaded into the three-dimensional interconnected network of nanotubes, providing an excellent three dimensional charge transfer network and electrolyte diffusion channels while effectively buffering the collapse and aggregation of active materials during charge-discharge processes. Overall, the MoS2/CNT nanocomposite synthesized by a simple hydrothermal process presents a new and promising candidate for high-performance anodes for supercapacitors.

| S-EPMC9085153 | biostudies-literature

Synthesis of mesoporous SnO2/NiO nanocomposite using modified sol-gel method and its electrochemical performance as electrode material for supercapacitors.

Project description:In this research work, SnO2, NiO and SnO2/NiO nanocomposites were synthesized at low temperature by modified sol-gel method using ultrasonication. Prepared samples were investigated for their properties employing various characterization techniques. X-ray diffraction (XRD) patterns confirmed the purity and phase of the samples as no secondary phase was detected. The average crystallite size of the nanocomposites was found to decrease from 19.24 to 4.53 nm with the increase in NiO concentration. It was confirmed from SEM micrographs that the material has mesoporous morphology. This mesoporous morphology resulted in the increase of the surface to mass ratio of the material, which in turn increases the specific capacitance of the material. The UV-Visible spectra showed the variation in the band gap of SnO2/NiO at different weight ratio ranging from 3.49 to 3.25 eV on increasing NiO concentration in the samples. These composites with different mass ratio of SnO2 and NiO were also characterized by FT-IR spectroscopy that showed shifting of the peaks centered at 545 cm-1 in the spectra for NiO/SnO2 nanocomposite. The analysis of the electrochemical performance of the material was done with the help of cyclic voltammetry and Galvanostatic charge-discharge. The specific capacitance of the synthesized samples with different concentration of SnO2 and NiO was analyzed at different scan rates of 5 to 100 mV/s. Interestingly, 7:1 mass ratio of NiO and SnO2 (SN7) nanocomposite exhibited a maximum specific capacitance of ~?464 F/g at a scan rate of 5 mV/s and good capacitance retention of 87.24% after 1,000 cycles. These excellent electrochemical properties suggest that the SnO2/NiO nanocomposite can be used for high energy density supercapacitor electrode material.

| S-EPMC7335181 | biostudies-literature

Fabrication of a vanadium nitride/N-doped carbon hollow nanosphere composite as an efficient electrode material for asymmetric supercapacitors.

Project description:Low-cost materials and facile processes to obtain novel electrode materials for assembling asymmetric supercapacitors (ASCs) are urgently needed. Herein, a vanadium nitride/nitrogen-doped carbon nanosphere (VN/NCS) composite composed of VN nanoparticles and N-doped carbon (NC) covering the surface of VN has been prepared by the nitridation of a V2O3/C nanocomposite. The hollow VN/NCS composite with a mesoporous structure and the dispersion of VN NPs in N-doped carbon result in a VN/NCS composite with good electrochemical behavior. Moreover, the N-doped carbon layer on the surface of VN effectively inhibits the oxidation of VN during cycling in an alkaline electrolyte. With the VN/NC composite utilized as a novel active electrode material for SCs, good rate capability, specific capacitance, and cycling stability are exhibited. Strikingly, using the VN/NCS composite as a negative electrode and its precursor, the V2O3/C composite, as a positive electrode, an asymmetric supercapacitor (ASC) device, with a good energy density of 19.8 W h kg-1 at 801 W kg-1 and a short charging time of 89 s, was assembled.

| S-EPMC9419796 | biostudies-literature

Hydrothermal synthesis of nanostructured graphene/polyaniline composites as high-capacitance electrode materials for supercapacitors.

Project description:As known to all, hydrothermal synthesis is a powerful technique for preparing inorganic and organic materials or composites with different architectures. In this reports, by controlling hydrothermal conditions, nanostructured polyaniline (PANi) in different morphologies were composited with graphene sheets (GNS) and used as electrode materials of supercapacitors. Specifically, ultrathin PANi layers with total thickness of 10-20 nm are uniformly composited with GNS by a two-step hydrothermal-assistant chemical oxidation polymerization process; while PANi nanofibers with diameter of 50~100 nm are obtained by a one-step direct hydrothermal process. Benefitting from the ultrathin layer and porous structure, the sheet-like GNS/PANi composites can deliver specific capacitances of 532.3 to 304.9 F/g at scan rates of 2 to 50 mV/s. And also, this active material showed very good stability with capacitance retention as high as ~99.6% at scan rate of 50 mV/s, indicating a great potential for using in supercapacitors. Furthermore, the effects of hydrothermal temperatures on the electrochemical performances were systematically studied and discussed.

| S-EPMC5349513 | biostudies-literature

Composite Mn-Co electrode materials for supercapacitors: why the precursor's morphology matters!

Project description:In the energy storage field, an electrode material must possess both good ionic and electronic conductivities to perform well, especially when high power is needed. In this context, the development of composite electrode materials combining an electrochemically active and good ionic conductor phase with an electronic conductor appears as a perfectly adapted approach to generate a synergetic effect and optimize the energy storage performance. In this work, three layered MnO2 phases with various morphologies (veils, nanoplatelets and microplatelets) were combined with electronic conductor cobalt oxyhydroxides with different platelet sizes (∼20 nm vs. 70 nm wide), to synthesize 6 different composites by exfoliation and restacking processes. The influence of precursors' morphology on the distribution of the Mn and Co objects within the composites was carefully investigated and correlated with the electrochemical performance of the final restacked material. Overall, the best performing restacked composite was obtained by combining MnO2 possessing a veil morphology with the smallest cobalt oxyhydroxide nanoplatelets, leading to the most homogeneous distribution of the Mn and Co objects at the nanoscale. More generally, the aim of this work is to understand how the size and morphology of the precursor building blocks influence their distribution homogeneity within the final composite and to find the most compatible building blocks to reach a homogeneous distribution at the nanoscale.

| S-EPMC9680945 | biostudies-literature

Ionic Liquid Directed Mesoporous Carbon Nanoflakes as an Effiencient Electrode material.

Project description:Supercapacitors are considered to be the most promising approach to meet the pressing requirements for energy storage devices. The electrode materials for supercapacitors have close relationship with their electrochemical properties and thus become the key point to improve their energy storage efficiency. Herein, by using poly (vinylidene fluoride-co-hexafluoropropylene) and ionic liquid as the dual templates, polyacrylonitrile as the carbon precursor, a flake-like carbon material was prepared by a direct carbonization method. In this method, poly (vinylidene fluoride-co-hexafluoropropylene) worked as the separator for the formation of isolated carbon flakes while aggregated ionic liquid worked as the pore template. The obtained carbon flakes exhibited a specific capacitance of 170 F/g at 0.1 A/g, a high energy density of 12.2 Wh/kg and a high power density of 5 kW/kg at the current of 10 A/g. It also maintained a high capacitance retention capability with almost no declination after 500 charge-discharge cycles. The ionic liquid directed method developed here also provided a new idea for the preparation of hierarchically porous carbon nanomaterials.

| S-EPMC4674753 | biostudies-literature

Controllable Preparation of Eucommia Wood-Derived Mesoporous Activated Carbon as Electrode Materials for Supercapacitors.

Project description:Activated carbons (ACs) for supercapacitors were synthesized from Eucommia ulmoides Oliver (EUO) wood by H3PO4 with systemic activation processes. The target structure of ACs could be prepared by adjusting the technological parameters. As the H3PO4 concentration was 25%, the mass ratio of feedstocks to activator was 1:4, the activation time was 6 h, and the activation temperature was 400 °C, the obtained AC revealed a high specific surface area (2033.87 m2·g-1) and well-developed mesoporous (the rate of mesoporous was 96.4%) with the best economic feasibility. Besides, it possessed excellent electrochemical performance: the maximum specific capacitance reached up to 252 F·g-1, the charging and discharging period was 3098.2 s at 0.2 A·g-1, and the retention rate of specific capacitance reached 92.3% after 10,000 cycles. This low temperature and convenience technology provide a valuable reference for synthesizing the EUO-based ACs, making high-value utilization on the EUO branches, and owning a broad application prospect in supercapacitors.

| S-EPMC9920536 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data