Interplay between Interfacial Energy, Contact Mechanics, and Capillary Forces in EGaIn Droplets.

ABSTRACT: Eutectic gallium-indium (EGaIn) is increasingly employed as an interfacial conductor material in molecular electronics and wearable healthcare devices owing to its ability to be shaped at room temperature, conductivity, and mechanical stability. Despite this emerging usage, the mechanical and physical mechanisms governing EGaIn interactions with surrounding objects─mainly regulated by surface tension and interfacial adhesion─remain poorly understood. Here, using depth-sensing nanoindentation (DSN) on pristine EGaIn/GaO_x surfaces, we uncover how changes in EGaIn/substrate interfacial energies regulate the adhesive and contact mechanic behaviors, notably the evolution of EGaIn capillary bridges with distinct capillary geometries and pressures. Varying the interfacial energy by subjecting EGaIn to different chemical environments and by functionalizing the tip with chemically distinct self-assembled monolayers (SAMs), we show that the adhesion forces between EGaIn and the solid substrate can be increased by up to 2 orders of magnitude, resulting in about a 60-fold increase in the elongation of capillary bridges. Our data reveal that by deploying molecular junctions with SAMs of different terminal groups, the trends of charge transport rates, the resistance of monolayers, and the contact interactions between EGaIn and monolayers from electrical characterizations are governed by the interfacial energies as well. This study provides a key understanding into the role of interfacial energy on geometrical characteristics of EGaIn capillary bridges, offering insights toward the fabrication of EGaIn junctions in a controlled fashion.

SUBMITTER: Amini S

PROVIDER: S-EPMC9227710 | biostudies-literature | 2022 Jun

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Interplay between Interfacial Energy, Contact Mechanics, and Capillary Forces in EGaIn Droplets.

Amini Shahrouz S Chen Xiaoping X Chua Jia Qing Isaiah JQI Tee Jinq Shi JS Nijhuis Christian A CA Miserez Ali A

ACS applied materials & interfaces 20220601 24

Eutectic gallium-indium (EGaIn) is increasingly employed as an interfacial conductor material in molecular electronics and wearable healthcare devices owing to its ability to be shaped at room temperature, conductivity, and mechanical stability. Despite this emerging usage, the mechanical and physical mechanisms governing EGaIn interactions with surrounding objects─mainly regulated by surface tension and interfacial adhesion─remain poorly understood. Here, using depth-sensing nanoindentation (DS ...[more]

PMID: 35649179

Similar Datasets

Project description:Corneal endothelial cell (CEC) loss occurs from tissue manipulation during anterior segment surgery and corneal transplantation as well as from contact with synthetic materials like intraocular lenses and tube shunts. While several studies have quantified CEC loss for specific surgical steps, the vulnerability of CECs to isolated, controllable and measurable mechanical forces has not been assessed previously. The purpose of this study was to develop an experimental testing platform where the susceptibility of CECs to controlled mechanical trauma could be measured. The corneal endothelial surfaces of freshly dissected porcine corneas were subjected to a range of indentation forces via a spherical stainless steel bead. A cell viability assay in combination with high-resolution fluorescence microscopy was used to visualize and quantify injured/dead CEC densities before and after mechanical loading. In specimens subjected to an indentation force of 9 mN, the mean ± SD peak contact pressure P0 was 18.64 ± 3.59 kPa (139.81 ± 26.93 mmHg) in the center of indentation and decreased radially outward. Injured/dead CEC densities were significantly greater (p ≤ 0.001) after mechanical indentation of 9 mN (167 ± 97 cells/mm2) compared to before indentation (39 ± 52 cells/mm2) and compared to the sham group (34 ± 31 cells/mm2). In specimens subjected to "contact only" - defined as an applied indentation force of 0.65 mN - the peak contact pressure P0 was 7.31 ± 1.5 kPa (54.83 ± 11.25 mmHg). In regions where the contact pressures was below 78% of P0 (<5.7 kPa or 42.75 mmHg), injured/dead CEC densities were within the range of CEC loss observed in the sham group, suggesting negligible cell death. These findings indicate that CECs are highly susceptible to mechanical trauma via indentation, supporting the established "no-touch" policy for ophthalmological procedures. While CECs can potentially remain viable below contact pressures of 5.7 kPa (42.75 mmHg), this low threshold suggests that prevention of indentation-associated CEC loss may be challenging.

Dataset Information

Interplay between Interfacial Energy, Contact Mechanics, and Capillary Forces in EGaIn Droplets.

Publications

Interplay between Interfacial Energy, Contact Mechanics, and Capillary Forces in EGaIn Droplets.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets