Influence of thickness and morphology of MoS₂ on the performance of counter electrodes in dye-sensitized solar cells.

ABSTRACT: Non-platinum electrodes for photoelectric devices are challenging and attractive to the scientific community. A thin film of molybdenum disulfide (MoS₂) was prepared on substrates coated with fluorine-doped tin oxide (FTO) to substitute the platinum counter electrode (CE) for dye-sensitized solar cells (DSSCs). Herein, we synthesized layered and honeycomb-like MoS₂ thin films via the cyclic voltammetry (CV) route. Thickness and morphology of the MoS₂ thin films were controlled via the concentration of precursor solution. The obtained results showed that MoS₂ thin films formed at a low precursor concentration had a layered morphology while a honeycomb-like MoS₂ thin film was formed at a high precursor concentration. Both types of MoS₂ thin film were composed of 1T and 2H structures and exhibited excellent electrocatalytic activity for the I₃ ^-/I^- redox couple. DSSCs assembled using these MoS₂ CEs showed a maximal power conversion efficiency of 7.33%. The short-circuit value reached 16.3 mA·cm^-2, which was higher than that of a conventional Pt/FTO CE (15.3 mA·cm^-2). This work reports for the first time the possibility to obtain a honeycomb-like MoS₂ thin film morphology by the CV method and investigates the effect of film structure on the electrocatalytic activity and photovoltaic performance of CEs for DSSC application.

SUBMITTER: Mai LTT

PROVIDER: S-EPMC9235830 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Transparent MoS2/PEDOT Composite Counter Electrodes for Bifacial Dye-Sensitized Solar Cells.

Project description:Dye-sensitized solar cells (DSSCs) are solar energy conversion devices with high efficiency and simple fabrication procedures. Developing transparent counter electrode (CE) materials for bifacial DSSCs can address the needs of window-type building-integrated photovoltaics (BIPVs). Herein, transparent organic-inorganic hybrid composite films of molybdenum disulfide and poly(3,4-ethylenedioxythiophene) (MoS2/PEDOT) are prepared to take full advantage of the conductivity and electrocatalytic ability of the two components. MoS2 is synthesized by hydrothermal method and spin-coated to form the MoS2 layer, and then PEDOT films are electrochemically polymerized on top of the MoS2 film to form the composite CEs. The DSSC with the optimized MoS2/PEDOT composite CE shows power conversion efficiency (PCE) of 7% under front illumination and 4.82% under back illumination. Compared with the DSSC made by the PEDOT CE and the Pt CE, the DSSC fabricated by the MoS2/PEDOT composite CE improves the PCE by 10.6% and 6.4% for front illumination, respectively. It proves that the transparent MoS2/PEDOT CE owes superior conductivity and catalytic properties, and it is an excellent candidate for bifacial DSSC in the application of BIPVs.

| S-EPMC7178793 | biostudies-literature

High-performance dye-sensitized solar cells using Ag-doped CoS counter electrodes.

Project description:CoS has been emerging as a promising Pt-free counter electrode (CE) material for dye-sensitized solar cells (DSSCs) due to its satisfactory electrocatalytic properties for redox reactions. However, its low electronic and ionic conductivities have limited its use in DSSCs. The doping of Ag with appropriate amount significantly improved the properties of CoS for application as a CE. Ag-doped CoS samples with various doping amounts were prepared by a facile one-step hydrothermal approach. There were very sharp changes of morphologies and particle sizes after doping different amounts of Ag. It is found that the DSSC fabricated with the 5% Ag-doped CoS CE achieved an impressive power-conversion efficiency (PCE) of 8.35% which was higher than that of the DSSC with a Pt CE (8.17%) by 2.2%, while the DSSC consisting of undoped CoS only exhibited a PCE of 6.93%. Such an enhanced PCE could be attributed to the significantly improved electrochemical activity and mixed conductivity resulting from the Ag dopant. Therefore, the excellent electrocatalytic activity, facile preparation and low material cost of the Ag-doped CoS electrode provide it with promising potential for large-scale production of new-generation DSSCs.

| S-EPMC9080620 | biostudies-literature

Biomass-Derived Nitrogen-Doped Carbon Aerogel Counter Electrodes for Dye Sensitized Solar Cells.

Project description:Dye sensitized solar cells have emerged as an attractive alternative to conventional solar cells due to their easy processing and the abundance and low cost of their materials. However, the counter electrode in these cells employs platinum which significantly impacts their cost. Here, we report biomass-derived, nitrogen-doped carbon aerogel as an effective alternative to conventional platinum-based counter electrodes for dye sensitized solar cells. A stable suspension of biomass-derived, nitrogen-doped carbon aerogel was prepared in DMF by using oleylamine as a binder. The nitrogen-doped carbon aerogel electrode was annealed at different temperatures, and its impact on photovoltaic performance is investigated. I-V measurements confirm that the annealing temperature substantially enhances the photovoltaic parameters of these devices; these enhancements are linked to the removal of the organic binders. Electrochemical impedance spectra of the counter electrodes confirm that removal of oleylamine in nitrogen-doped carbon aerogels reduces the series resistance of the resulting electrodes. The power conversion efficiency of the solar cells from optimized nitrogen-doped carbon aerogel exhibited comparable efficiency to that of a cell fabricated using a platinum-based counter electrode. This study demonstrates the potential of biomass-derived carbon aerogels as a cheap and sustainable replacement of platinum in DSSCs.

| S-EPMC6073752 | biostudies-literature

Large area growth of MoTe2 films as high performance counter electrodes for dye-sensitized solar cells.

Project description:A cost effective and efficient alternative counter electrode (CE) to replace commercially existing platinum (Pt)-based CEs for dye-sensitized solar cells (DSSCs) is necessary to make DSSCs competitive. Herein, we report the large-area growth of molybdenum telluride (MoTe2) thin films by sputtering-chemical vapor deposition (CVD) on conductive glass substrates for Pt-free CEs of DSSCs. Cyclic voltammetry (CV), Tafel curve analysis, and electrochemical impedance spectroscopy (EIS) results showed that the as-synthesized MoTe2 exhibited good electrocatalytic properties and a low charge transfer resistance at the electrolyte-electrode interface. The optimized MoTe2 CE revealed a high power conversion efficiency of 7.25% under a simulated solar illumination of 100 mW cm-2 (AM 1.5), which was comparable to the 8.15% observed for a DSSC with a Pt CE. The low cost and good electrocatalytic properties of MoTe2 thin films make them as an alternative CE for DSSCs.

| S-EPMC5758823 | biostudies-literature

Novel gamma-irradiated chitosan-doped reduced graphene-CuInS2 composites as counter electrodes for dye-sensitized solar cells.

Project description:To address the issues associated with traditional counter electrodes, a novel gamma-irradiated chitosan-doped reduced graphene-CuInS2 composite (Chi@RGO-CIS) was used as the counter electrode (CE). The system was fabricated following a simple hydrothermal method. The prepared Chi@RGO-CIS was characterized by various spectroscopic and microscopic techniques. The synergistic effect between chitosan, CuInS2, and reduced graphene oxide can help in producing a large surface area. It can also help in the generation of catalytic sites toward I-/I3-redox electrolytes. We used a composite (based on electrical considerations) to study the effect of the amount of graphene on the characteristics and photovoltaic efficiency of the Chi@RGO-CIS composites. The solar cell assembled with 1.5% Chi@RGO-CIS exhibited an efficiency of 12.21%. The efficiency was higher than that of a Pt-based device (9.96%) fabricated under the same conditions. Hence, Chi@RGO-CIS can be potentially used as the CE of dye-sensitized solar cells (DSSCs). It can be used as a substitute for Pt in DSSCs.

| S-EPMC9121354 | biostudies-literature

Designing Multifunctional Co and Fe Co-Doped MoS2 Nanocube Electrodes for Dye-Sensitized Solar Cells, Perovskite Solar Cells, and a Supercapacitor.

Project description:In the present study, three types of specific solid, core-shell, and hollow structured cobalt and iron co-doped MoS2 nanocubes (denoted as s-Co-Fe-MoS x , c-Co-Fe-MoS x , and h-Co-Fe-MoS x ) are controllably synthesized for the first time by regulating the reactant mass ratios. The prepared Co-Fe-MoS x nanocubes can function as a counter electrode in dye-sensitized and perovskite solar cells (DSCs and PSCs) and a working electrode in a supercapacitor. In the DSC system, the c-Co-Fe-MoS x nanocubes exhibit the maximum catalytic activity to the Co3+/2+ redox couple regeneration, and the device achieves a power conversion efficiency (PCE) of 8.69%, significantly higher than the devices using s-Co-Fe-MoS x (6.61%) and h-Co-Fe-MoS x (7.63%) counter electrodes. Similarly, all of the prepared Co-Fe-MoS x nanocubes show decent activity in PSCs and the device using the c-Co-Fe-MoS x counter electrode achieves the highest PCE of 6.88%. It is worth noting that, as the supercapacitor working electrode, the h-Co-Fe-MoS x exhibits a specific capacitance of 85.4 F g-1, significantly higher than the parallel values achieved by the s-Co-Fe-MoS x and c-Co-Fe-MoS x electrodes under identical conditions.

| S-EPMC8482514 | biostudies-literature

Photofabrication of Highly Transparent Platinum Counter Electrodes at Ambient Temperature for Bifacial Dye Sensitized Solar Cells.

Project description:Platinum (Pt) counter electrodes (CEs) have consistently shown excellent electrocatalytic performance and holds the record of the highest power conversion efficiency (PCE) for dye-sensitized solar cells (DSSCs). However, its use for large-scale production is limited either by high temperature required for thermal decomposition of its precursor or by wastage of the material leading to high cost or sophisticated equipment. Here, we report a novel photofabrication technique to fabricate highly transparent platinum counter electrodes by ultraviolet (UV) irradiation of platinic acid (H2PtCl6.6H2O) on rigid fluorine-doped tin oxide (FTO) and flexible indium-doped tin oxide (ITO) on polyethylene terephthalate (PET) substrates. The photofabrication technique is a facile and versatile method for the fabrication of Pt CEs for dye sensitized solar cells (DSSCs). The photofabricated Pt CEs were used to fabricate bifacial DSSCs with power conversion efficiencies (PCEs) attaining 7.29% for front illumination and 5.85% for rear illumination. The highest percentage ratio of the rear illumination efficiency to the front illumination efficiency (?R) of 85.92% was recorded while the least ?R is 77.91%.

| S-EPMC6110791 | biostudies-literature

Investigation of Coral-Like Cu2O Nano/Microstructures as Counter Electrodes for Dye-Sensitized Solar Cells.

Project description:In this study, a chemical oxidation method was employed to fabricate coral-like Cu2O nano/microstructures on Cu foils as counter electrodes (CEs) for dye-sensitized solar cells (DSSCs). The Cu2O nano/microstructures were prepared at various sintering temperatures (400, 500, 600 and 700 °C) to investigate the influences of the sintering temperature on the DSSC characteristics. First, the Cu foil substrates were immersed in an aqueous solution containing (NH4)2S2O8 and NaOH. After reacting at 25 °C for 30 min, the Cu substrates were converted to Cu(OH)2 nanostructures. Subsequently, the nanostructures were subjected to nitrogen sintering, leading to Cu(OH)2 being dehydrated into CuO, which was then deoxidized to form coral-like Cu2O nano/microstructures. The material properties of the Cu2O CEs were comprehensively determined using a scanning electron microscope, energy dispersive X-ray spectrometer, X-ray diffractometer, Raman spectrometer, X-ray photoelectron spectroscope, and cyclic voltameter. The Cu2O CEs sintered at various temperatures were used in DSSC devices and analyzed according to the current density-voltage characteristics, incident photon-to-current conversion efficiency, and electrochemical impedance characteristics. The Cu2O CEs sintered at 600 °C exhibited the optimal electrode properties and DSSC performance, yielding a power conversion efficiency of 3.62%. The Cu2O CEs fabricated on Cu foil were generally mechanically flexible and could therefore be applied to flexible DSSCs.

| S-EPMC5512654 | biostudies-other

Interface Engineered Binary Platinum Free Alloy-based Counter Electrodes with Improved Performance in Dye-Sensitized Solar Cells.

Project description:The high cost and platinum dissolution issues of counter electrodes (CEs) are two core problems for the development of dye-sensitized solar cells (DSSCs). In this work, different CEs based on binary alloy Ru81.09Co18.91, Ru80.55Se19.45 and Co20.85Se79.15 nanostructures for DSSCs were successfully synthesized and investigated by a facile and environmentally friendly approach. Here, we found that the Co20.85Se79.15 alloy CE-based device yields the higher photoelectric conversion efficiency of 7.08% compared with that (5.80%) of the DSSC using a pure Pt CE because of the larger number of active sites with improved charge transferability and reduced interface resistance by matching work function with the I3?/I? redox electrolyte. The inexpensive synthesis method, cost-effectiveness and superior catalytic activity of the Co20.85Se79.15 alloy may open up a new avenue for the development of CEs for DSSCs in the near future.

| S-EPMC7280534 | biostudies-literature

Low-Cost and Efficient Nickel Nitroprusside/Graphene Nanohybrid Electrocatalysts as Counter Electrodes for Dye-Sensitized Solar Cells.

Project description:Novel nickel nitroprusside (NNP) nanoparticles with incorporated graphene nanoplatelets (NNP/GnP) were used for the first time as a low-cost and effective counter electrode (CE) for dye-sensitized solar cells (DSSCs). NNP was synthesized at a low-temperature (25 °C) solution process with suitable purity and crystallinity with a size range from 5 to 10 nm, as confirmed by different spectroscopic and microscopic analyses. The incorporation of an optimized amount of GnP (0.2 wt%) into the NNP significantly improved the electrocatalytic behavior for the redox reaction of iodide (I-)/tri-iodide (I3-) by decreasing the charge-transfer resistance at the CE/electrolyte interface, lower than the NNP- and GnP-CEs, and comparable to the Pt-CE. The NNP/GnP nanohybrid CE when applied in DSSC exhibited a PCE of 6.13% (under one sun illumination conditions) with the Jsc, Voc, and FF of 14.22 mA/cm2, 0.628 V, and 68.68%, respectively, while the PCE of the reference Pt-CE-based DSSC was 6.37% (Jsc = 14.47 mA/cm2, Voc = 0.635 V, and FF = 69.20%). The low cost of the NNP/GnP hybrid CE with comparable photovoltaic performance to Pt-CE can be potentially exploited as a suitable replacement of Pt-CE in DSSCs.

| S-EPMC8585226 | biostudies-literature