Relationship between Thoroughbred workloads in racing and the fatigue life of equine subchondral bone.

ABSTRACT: Fatigue life (FL) is the number of cycles of load sustained by a material before failure, and is dependent on the load magnitude. For athletes, 'cycles' translates to number of strides, with load proportional to speed. To improve previous investigations estimating workload from distance, we used speed (m/s, x) per stride collected using 5 Hz GPS/800 Hz accelerometer sensors as a proxy for limb load to investigate factors associated with FL in a Thoroughbred race start model over 25,234 race starts, using a combination of mathematical and regression modelling. Fore-limb vertical force (NKg^-1) was estimated using a published equation: Vertical force = 2.778 + 2.1376x - 0.0535x². Joint load (σ) was estimated based on the vertical force, scaled according to the maximum speed and defined experimental loads for the expected variation in load distribution across a joint surface (54-90 MPa). Percentage FL (%FL) was estimated using a published equation for cycles to failure (N_f) summed across each race start: N_f = 10^{(σ-134.2)/-14.1.} Multivariable mixed-effects linear regression models were generated on %FL, adjusting for horse-level clustering, presented as coefficients; 95%CI. Scaled to the highest joint load, individual starts accrued a mean of 9.34%FL (sd. 1.64). Older age (coef. 0.03; 0.002-0.04), longer race-distances (non-linear power transformed), and firmer track surfaces (ref. Heavy 10: Good 3 coef. 2.37; 2.26-2.48) were associated with greater %FL, and males accrued less than females (p < 0.01). Most variables associated with %FL are reported risk factors for injury. Monitoring strides in racehorses may therefore allow identification of horses at risk, enabling early detection of injury.

SUBMITTER: Morrice-West AV

PROVIDER: S-EPMC9262984 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Fatigue-induced subchondral bone (SCB) injury is common in racehorses. Understanding how subchondral microstructure and microdamage influence mechanical properties is important for developing injury prevention strategies. Mechanical properties of the disto-palmar third metacarpal condyle (MCIII) correlate poorly with microstructure, and it is unknown whether the properties of other sites within the metacarpophalangeal (fetlock) joint are similarly complex. We aimed to investigate the mechanical and structural properties of equine SCB from specimens with minimal evidence of macroscopic disease. Three sites within the metacarpophalangeal joint were examined: the disto-palmar MCIII, disto-dorsal MCIII, and proximal sesamoid bone. Two regions of interest within the SCB were compared, a 2 mm superficial and an underlying 2 mm deep layer. Cartilage-bone specimens underwent micro-computed tomography, then cyclic compression for 100 cycles at 2 Hz. Disto-dorsal MCIII specimens were loaded to 30 MPa (n = 10), while disto-palmar MCIII (n = 10) and proximal sesamoid (n = 10) specimens were loaded to 40 MPa. Digital image correlation determined local strains. Specimens were stained with lead-uranyl acetate for volumetric microdamage quantification. The dorsal MCIII SCB had lower bone volume fraction (BVTV), bone mineral density (BMD), and stiffness compared to the palmar MCIII and sesamoid bone (p < 0.05). Superficial SCB had higher BVTV and lower BMD than deeper SCB (p < 0.05), except at the palmar MCIII site where there was no difference in BVTV between depths (p = 0.419). At all sites, the deep bone was stiffer (p < 0.001), although the superficial to deep gradient was smaller in the dorsal MCIII. Hysteresis (energy loss) was greater superficially in palmar MCIII and sesamoid (p < 0.001), but not dorsal MCIII specimens (p = 0.118). The stiffness increased with cyclic loading in total cartilage-bone specimens (p < 0.001), but not in superficial and deep layers of the bone, whereas hysteresis decreased with the cycle for all sites and layers (p < 0.001). Superficial equine SCB is uniformly less stiff than deeper bone despite non-uniform differences in bone density and damage levels. The more compliant superficial layer has an important role in energy dissipation, but whether this is a specific adaptation or a result of microdamage accumulation is not clear.

Dataset Information

Relationship between Thoroughbred workloads in racing and the fatigue life of equine subchondral bone.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets