Fabrication and Characterization of Nanostructured Rock Wool as a Novel Material for Efficient Water-Splitting Application.

ABSTRACT: Rock wool (RW) nanostructures of various sizes and morphologies were prepared using a combination of ball-mill and hydrothermal techniques, followed by an annealing process. Different tools were used to explore the morphologies, structures, chemical compositions and optical characteristics of the samples. The effect of initial particle size on the characteristics and photoelectrochemical performance of RW samples generated hydrothermally was investigated. As the starting particle size of ball-milled natural RW rises, the crystallite size of hydrothermally formed samples drops from 70.1 to 31.7 nm. Starting with larger ball-milled particle sizes, the nanoparticles consolidate and seamlessly combine to form a continuous surface with scattered spherical nanopores. Water splitting was used to generate photoelectrochemical hydrogen using the samples as photocatalysts. The number of hydrogen moles and conversion efficiencies were determined using amperometry and voltammetry experiments. When the monochromatic wavelength of light was increased from 307 to 460 nm for the manufactured RW_>0.3 photocatalyst, the photocurrent density values decreased from 0.25 to 0.20 mA/mg. At 307 nm and +1 V, the value of the incoming photon-to-current efficiency was ~9.77%. Due to the stimulation of the H⁺ ion rate under the temperature impact, the J_ph value increased by a factor of 5 when the temperature rose from 40 to 75 °C. As a result of this research, for the first time, a low-cost photoelectrochemical catalytic material is highlighted for effective hydrogen production from water splitting.

SUBMITTER: El-Gharbawy SA

PROVIDER: S-EPMC9267974 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Coconut-Water-Mediated Carbonaceous Electrode: A Promising Eco-Friendly Material for Bifunctional Water Splitting Application.

Project description:The organic and eco-friendly materials are extended to prevail over the worldwide energy crisis where bio-inspired carbonaceous electrode materials are being prepared from biogenic items and wastes. Here, coconut water is sprayed over three-dimensional (3D) nickel foam for obtaining a carbonaceous electrode material, i.e., C@Ni-F. The as-prepared C@Ni-F electrode has been used for structural elucidation and morphology evolution studies. Field emission scanning electron microscopy analysis confirms the vertically grown nanosheets of the C@Ni-F electrode, which is further employed in the oxygen evolution reaction (OER) and hydrogen evolution reaction (HER), where excellent OER and HER performances with small overpotentials of 219 and 122 mV and with stumpy Tafel slopes, i.e., 27 and 53 mV dec-1, are respectively obtained, suggesting a bifunctional potential of the sprayed electrode material. Moreover, sustainable bifunctional performance of C@Ni-F proves considerable chemical stability and moderate mechanical robustness against long-term operation, suggesting that, in addition to being a healthy drink to mankind, coconut water can also be used for water splitting applications.

| S-EPMC8154170 | biostudies-literature

Nanostructured Nickel Nitride with Reduced Graphene Oxide Composite Bifunctional Electrocatalysts for an Efficient Water-Urea Splitting.

Project description:A three-dimensional nickel nitride with reduced graphene oxide composite on nickel foam (s-X, where s represents Ni3N/rGO@NF and the annealing temperature X can be 320, 350, or 380) electrode has been fabricated through a facile method. We demonstrate that s-350 has excellent urea oxidation reaction (UOR) activity, with a demanded potential of 1.342 V to reach 10 mA/cm2 and bears high hydrogen evolution reaction (HER) activity. It provides a low overpotential of 124 mV at 10 mA/cm2, which enables the successful construction of its two-electrode alkaline electrolyzer (s-350||s-350) for water-urea splitting. It merely requires a voltage of 1.518 V to obtain 100 mA/cm2 and is 0.145 V lower than that of pure water splitting. This noble metal-free bifunctional electrode is regarded as an inexpensive and effective water-urea electrolysis assisted hydrogen production technology, which is commercially viable.

| S-EPMC6915570 | biostudies-literature

Facile fabrication of an efficient BiVO4 thin film electrode for water splitting under visible light irradiation.

Project description:An efficient BiVO(4) thin film electrode for overall water splitting was prepared by dipping an F-doped SnO(2) (FTO) substrate electrode in an aqueous nitric acid solution of Bi(NO(3))(3) and NH(4)VO(3), and subsequently calcining it. X-ray diffraction of the BiVO(4) thin film revealed that a photocatalytically active phase of scheelite-monoclinic BiVO(4) was obtained. Scanning electron microscopy images showed that the surface of an FTO substrate was uniformly coated with the BiVO(4) film with 300-400 nm of the thickness. The BiVO(4) thin film electrode gave an excellent anodic photocurrent with 73% of an IPCE at 420 nm at 1.0 V vs. Ag/AgCl. Modification with CoO on the BiVO(4) electrode improved the photoelectrochemical property. A photoelectrochemical cell consisting of the BiVO(4) thin film electrode with and without CoO, and a Pt counter electrode was constructed for water splitting under visible light irradiation and simulated sunlight irradiation. Photocurrent due to water splitting to form H(2) and O(2) was confirmed with applying an external bias smaller than 1.23 V that is a theoretical voltage for electrolysis of water. Water splitting without applying external bias under visible light irradiation was demonstrated using a SrTiO(3)Rh photocathode and the BiVO(4) photoanode.

| S-EPMC3406872 | biostudies-other

Application of wool keratin: an anti-ultraviolet wall material in spray drying.

Project description:Low-molecular-weight keratin (LMWK) obtained from wool was employed as a wall material for the spray drying encapsulation of fish oil. Microcapsules with different LMWK contents were prepared, and their anti-ultraviolet performance and other features were studied. The results showed that LMWK was able to improve the encapsulation efficiency of fish oil because of its good emulsifying properties. When the LMWK content was increased from 0 to 10, 30 and 50%, the shelf life of the microcapsules under ultraviolet irradiation increased from 48 to 96 h, 144 h and 168 h, respectively. The strongest absorption efficiency of LMWK is shown in the UVc band. The chemical structure of LMWK did not change during an ultraviolet accelerating ageing test.

| S-EPMC8405791 | biostudies-literature

Controlled fabrication of Sn/TiO2 nanorods for photoelectrochemical water splitting.

Project description:In this work, we investigate the controlled fabrication of Sn-doped TiO2 nanorods (Sn/TiO2 NRs) for photoelectrochemical water splitting. Sn is incorporated into the rutile TiO2 nanorods with Sn/Ti molar ratios ranging from 0% to 3% by a simple solvothermal synthesis method. The obtained Sn/TiO2 NRs are single crystalline with a rutile structure. The concentration of Sn in the final nanorods can be well controlled by adjusting the molar ratio of the precursors. Photoelectrochemical experiments are conducted to explore the photocatalytic activity of Sn/TiO2 NRs with different doping levels. Under the illumination of solar simulator with the light intensity of 100 mW/cm2, our measurements reveal that the photocurrent increases with increasing doping level and reaches the maximum value of 1.01 mA/cm2 at -0.4 V versus Ag/AgCl, which corresponds to up to about 50% enhancement compared with the pristine TiO2 NRs. The Mott-Schottky plots indicate that incorporation of Sn into TiO2 nanorod can significantly increase the charge carrier density, leading to enhanced conductivity of the nanorod. Furthermore, we demonstrate that Sn/TiO2 NRs can be a promising candidate for photoanode in photoelectrochemical water splitting because of their excellent chemical stability.

| S-EPMC4228341 | biostudies-literature

Nanostructured Hybrid-Material Transparent Surface with Antireflection Properties and a Facile Fabrication Process.

Project description:Highly transparent optical surfaces with antireflection (AR) properties have the potential to increase the performance of a wide range of applications, such as windows for photovoltaic cells, photodetectors, and display screens among others. Biomimetic structures inspired by the moth-eye have attracted much attention as they can offer superior AR properties, which can generate broadband, omnidirectional optical transmission, and water-repellent self-cleaning behavior. However, many biomimetic surfaces suffer from time-consuming and complex processing, for example, electron beam and nanoimprint lithography, and/or sub-optimal mechanical reliability. In this paper, we introduce a hybrid material approach-nanostructured polyimide on a substrate-for demonstrating a surface with significant AR and hydrophobic properties together with low scattering (haze) and high mechanical resistance. As an example of applications, we demonstrate an indium tin oxide transparent conductive substrate with a large AR effect and optical transmission associated to the nanostructured polyimide coating. The proposed design and method based on conventional spin-coating and lithography-free metal dewetting have the potential to be a low-cost processing path of nanostructured AR transparent substrates.

| S-EPMC6882085 | biostudies-literature

Template-Free Nanostructured Fluorine-Doped Tin Oxide Scaffolds for Photoelectrochemical Water Splitting.

Project description:The synthesis and characterization of highly stable and conductive F:SnO2 (FTO) nanopyramid arrays are investigated, and their use as scaffolds for water splitting is demonstrated. Current densities during the oxygen evolution reaction with a NiFeOx catalyst at 2 V vs reversible hydrogen electrode were increased 5-fold when substituting commercial FTO (TEC 15) by nanostructured FTO scaffolds. In addition, thin α-Fe2O3 films (∼50 nm thick) were employed as a proof of concept to show the effect of our nanostructured scaffolds during photoelectrochemical water splitting. Double-layer capacitance measurements showed a drastic increase of the relative electrochemically active surface area for the nanostructured samples, in agreement with the observed photocurrent enhancement, whereas UV-vis spectroscopy indicates full absorption of visible light at wavelengths below 600 nm.

| S-EPMC6790916 | biostudies-literature

Flexible Electrode Based on PES/GO Mixed Matrix Woven Membrane for Efficient Photoelectrochemical Water Splitting Application.

Project description:We introduced, for the first time, a membrane composed of nanostructured self-polyether sulphone (PES) filled with graphene oxide (GO) applied to photoelectrochemical (PEC) water splitting. This membrane was fabricated through the phase inversion method. A variety of characteristics analysis of GO and its composite with PES including FTIR, XRD, SEM, and optical properties was studied. Its morphology was completely modified from macro voids for bare PES into uniform layers with a random distribution of GO structure which facilitated the movement of electrons between these layers for hydrogen production. The composite membrane photocathode brought a distinct photocurrent generation (5.7 mA/cm2 at 1.6 V vs. RHE). The optimized GO ratio in the membrane was investigated to be PG2 (0.008 wt.% GO). The conversion efficiencies of PEC were assessed for this membrane. Its incident photon-to-current efficiency (IPCE) was calculated to be 14.4% at λ = 390 nm beside the applied bias photon-to-current conversion efficiency (ABPE) that was estimated to be 7.1% at -0.4 V vs. RHE. The stability of the PG2 membrane after six cycles was attributed to high thermal and mechanical stability and excellent ionic conductivity. The number of hydrogen moles was calculated quantitively to be 0.7 mmol h-1 cm-2. Finally, we designed an effective cost membrane with high performance for hydrogen generation.

| S-EPMC10384634 | biostudies-literature

A molecular tandem cell for efficient solar water splitting.

Project description:Artificial photosynthesis provides a way to store solar energy in chemical bonds. Achieving water splitting without an applied external potential bias provides the key to artificial photosynthetic devices. We describe here a tandem photoelectrochemical cell design that combines a dye-sensitized photoelectrosynthesis cell (DSPEC) and an organic solar cell (OSC) in a photoanode for water oxidation. When combined with a Pt electrode for H2 evolution, the electrode becomes part of a combined electrochemical cell for water splitting, 2H2O ? O2 + 2H2, by increasing the voltage of the photoanode sufficiently to drive bias-free reduction of H+ to H2 The combined electrode gave a 1.5% solar conversion efficiency for water splitting with no external applied bias, providing a mimic for the tandem cell configuration of PSII in natural photosynthesis. The electrode provided sustained water splitting in the molecular photoelectrode with sustained photocurrent densities of 1.24 mA/cm2 for 1 h under 1-sun illumination with no applied bias.

| S-EPMC7306789 | biostudies-literature

Amorphization activated ruthenium-tellurium nanorods for efficient water splitting.

Project description:Pursuing active and durable water splitting electrocatalysts is of vital significance for solving the sluggish kinetics of the oxygen evolution reaction (OER) process in energy supply. Herein, theoretical calculations identify that the local distortion-strain effect in amorphous RuTe2 system abnormally sensitizes the Te-pπ coupling capability and enhances the electron-transfer of Ru-sites, in which the excellent inter-orbital p-d transfers determine strong electronic activities for boosting OER performance. Thus, a robust electrocatalyst based on amorphous RuTe2 porous nanorods (PNRs) is successfully fabricated. In the acidic water splitting, a-RuTe2 PNRs exhibit a superior performance, which only require a cell voltage of 1.52 V to reach a current density of 10 mA cm-2. Detailed investigations show that the high density of defects combine with oxygen atoms to form RuOxHy species, which are conducive to the OER. This work offers valuable insights for constructing robust electrocatalysts based on theoretical calculations guided by rational design and amorphous materials.

| S-EPMC6908605 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data