Three-Color White Photoluminescence Emission Using Perovskite Nanoplatelets and Organic Emitter.

ABSTRACT: Three organic blue-light-emitting tetraphenylethylene (TPE) derivatives that exhibit aggregation-induced emission (AIE) were used as additives in the preparation of inorganic perovskite-structured green-light-emitting materials for three-color white-light emission. For these organic-inorganic light-emitting materials, two-color (blue and green) light-emitting films based on the CsPbBr₃ perovskite-structured green-light-emitting inorganic material were prepared. The three TPE derivatives were prepared by varying the number of bromide groups, and a distinct AIE effect was confirmed when the derivatives were dissolved in a water-tetrahydrofuran mixed solvent containing 90 vol% water. When 0.2 molar ratio of the 1,1,2,2-tetrakis(4-bromophenyl)ethylene (TeBrTPE) additive was mixed with nanocrystal-pinning toluene solvent, the green-light-emission photoluminescence quantum efficiency (PLQY) value at 535 nm was 47 times greater than that of the pure bulk CsPbBr₃ without additives and a blue emission at 475 nm was observed from the TeBrTPE itself. When a CBP:Ir(piq)₃ film was prepared on top of this layer, three PL peaks with maximum wavelength values of 470, 535, and 613 nm were confirmed. The film exhibited white-light emission with CIE color coordinates of (0.25, 0.36).

SUBMITTER: Kwon H

PROVIDER: S-EPMC9268134 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Achieving Tunable Cold/Warm White-Light Emission in a Single Perovskite Material with Near-Unity Photoluminescence Quantum Yield.

Project description:Single materials that exhibit efficient and stable white-light emission are highly desirable for lighting applications. This paper reports a novel zero-dimensional perovskite, Rb4CdCl6:Sn2+, Mn2+, which demonstrates exceptional white-light properties including adjustable correlated color temperature, high color rendering index of up to 85, and near-unity photoluminescence quantum yield of 99%. Using a co-doping strategy involving Sn2+ and Mn2+, cyan-orange dual-band emission with complementary spectral ranges is activated by the self-trapped excitons and d-d transitions of the Sn2+ and Mn2+ centers in the Rb4CdCl6 host, respectively. Intriguingly, although Mn2+ ions doped in Rb4CdCl6 are difficult to excite, efficient Mn2+ emission can be realized through an ultra-high-efficient energy transfer between Sn2+ and Mn2+ via the formation of adjacent exchange-coupled Sn-Mn pairs. Benefiting from this efficient Dexter energy transfer process, the dual emission shares the same optimal excitation wavelengths of the Sn2+ centers and suppresses the non-radiative vibration relaxation significantly. Moreover, the relative intensities of the dual-emission components can be modulated flexibly by adjusting the fraction of the Sn2+ ions to the Sn-Mn pairs. This co-doping approach involving short-range energy transfer represents a promising avenue for achieving high-quality white light within a single material.

| S-EPMC10471562 | biostudies-literature

A promising 1D Cd-based hybrid perovskite-type for white-light emission with high-color-rendering index.

Project description:A one dimensional (1D) perovskite-type (C6H7NBr)3[CdBr5] (abbreviated 4-BAPC) was synthesized by slow evaporation at room temperature (RT). 4-BAPC crystalizes in the monoclinic system with the space group P21/c. The 1D inorganic chains are formed by corner sharing CdBr6 octahedra. Thermal measurement shows that 4-BAPC is stable up to 190 °C. Optical characterization demonstrates that the grown crystal is an indirect bandgap material with a bandgap value of 3.93 eV, which is consistent with theoretical calculations. The electronic structure, calculated using density functional theory, reveals that the valence band originates from a combination of Br-4p orbitals and Cd-4d orbitals, whereas the conduction band originates from the Cd-5s orbitals. The photoluminescence spectroscopy shows that the obtained material exhibits a broad-band white light emission with extra-high CRI of 98 under λ exc = 380 nm. This emission is mainly resulting from the self-trapped exciton recombinations within the inorganic CdBr6 octahedron, and the fluorescence within the organic conjugated ammonium salt.

| S-EPMC9682491 | biostudies-literature

Emission and Color Tuning of Cyanostilbenes and White Light Emission.

Project description:White-light-emitting diodes are energy efficiency replacement of conventional lighting sources. Herein, we report the luminescent behavior of three simple cyanostilbenes with triphenylamine-donating groups bearing different electron-withdrawing groups (phenyl, pyridyl, and p-nitrophenyl) in a common donor (D)-π-acceptor (A) α-cyanostilbene construct along with their thermal and electrochemical properties. The density functional theory (DFT) studies reveal that aggregation-induced emission characteristic feature of the D-π-A dyes is inversely proportional to the intramolecular charge transfer (ICT) effect, that is, phenyl-and pyridyl-substituted compounds show characteristic aggregation-induced emission in water, whereas the ICT effect is dominant for the nitro derivative. The extent of ICT and the solvatochromic emission shifts, from blue to red, depend on the strength of the electron-withdrawing group. White luminescence and tunable emission colors are obtained by careful admixtures of these cyanostilbenes bearing triphenylamines. The results rationalized through DFT and time-dependent DFT calculations follow a consistent trend with the energy levels measured from the electrochemical and optical studies. Thermogravimetric analysis and differential scanning calorimetry studies showed excellent thermal stability of the compounds. The scanning electron microscopy and dynamic light scattering measurements were performed to reveal the formation of aggregates. This strategy involving synthetically simple and structurally similar molecules with different emission properties has potential applications in the fabrication of multicolor and white-light-emitting materials.

| S-EPMC6643655 | biostudies-literature

Photoluminescence and Stoichiometry Correlation in Nanocrystalline EuO x Thin Films: Tunable Color Emission.

Project description:The development of broadband and ultracompact optoelectronic devices relies on the possibility of fabricating bright and tunable emitters at the nanoscale. Here, we show emission from EuO x (1 ? x < 1.4) thin films on silicon formed by nanocrystals with average sizes in the range of 5 nm. The photoluminescence emission of the nano-EuO x films is tunable as a function of the oxygen concentration changing from a green broadband Eu2+-related emission to a narrow red Eu3+-related emission. To reach these results has been instrumental through the use of a new methodology specially designed to achieve high-quality europium oxide films whose compositional properties are controlled by the growth base pressure and preserved thanks to a chemically stable and transparent cover layer of Al2O3. Our findings confirm the outstanding potential of nanostructured EuO x films as "one-compound" optical elements with tunable emission properties for their implementation in integrated silicon-based devices.

| S-EPMC7370298 | biostudies-literature

Controlling light emission from semiconductor nanoplatelets using surface chemistry.

Project description:Semiconductor nanoplatelets are atomically flat nanocrystals which emit light with high spectral purity at wavelengths controlled by their thickness. Despite their technological potential, efforts to further sharpen the emission lines of nanoplatelets have generally failed for unknown reasons. Here, we demonstrate theoretically that the linewidth is controlled by surface chemistry-specifically, inhomogeneities in the ligand layer on the nanoplatelet surface lead to a spatially fluctuating potential that localizes excitons. This localization leads to increased scattering and optical broadening. Importantly, localization also reduces the rate of radiative emission. Our model explains the observed linewidth and predicts that a more uniform ligand layer will sharpen the lines and increase the emission rates. These findings demonstrate that light emission from nanoplatelets can be controlled by optimizing their surface chemistry, an important advantage for their eventual use in optical technologies.

| S-EPMC11374790 | biostudies-literature

Spontaneous Self-Assembly of Cesium Lead Halide Perovskite Nanoplatelets into Cuboid Crystals with High Intensity Blue Emission.

Project description:Colloidal all-inorganic perovskite nanocrystals have gained significant attention as a promising material for both fundamental and applied research due to their excellent emission properties. However, reported photoluminescence quantum yields (PL QYs) of blue-emitting perovskite nanocrystals are rather low, mostly due to the fact that the high energy excitons for such wide bandgap materials are easily captured by interband traps, and then decay nonradiatively. In this work, it is demonstrated how to tackle this issue, performing self-assembly of 2D perovskite nanoplatelets into larger size (≈50 nm × 50 nm × 20 nm) cuboid crystals. In these structures, 2D nanoplatelets being isolated from each other within the cuboidal scaffold by organic ligands constitute multiple quantum wells, where exciton localization on potential disorder sites helps them to bypass nonradiative channels present in other platelets. As a result, the cuboid crystals show an extremely high PL QY of 91% of the emission band centered at 480 nm. Moreover, using the same synthetic method, mixed-anion CsPb(Br/Cl)3 cuboid crystals with blue emission peaks ranging from 452 to 470 nm, and still high PL QYs in the range of 72-83% are produced.

| S-EPMC6662087 | biostudies-literature

Green Photoluminescence of Perovskite CsPb(Br1-x I x )3 Nanocrystals for Wide Color Gamut Displays.

Project description:All-inorganic mixed-halide CsPb(Br1-x I x )3 perovskite nanocrystals (NCs) are excellent candidates for green-emitting phosphors in wide color gamut displays; however, a detailed investigation of their photoluminescence (PL) properties based on the halide composition has been missing. In this work, we report a fundamental investigation of the changes in the PL properties of CsPb(Br1-x I x )3 NCs. The PL color of the NCs, which were prepared by a hot-injection method, changed from green to red with increasing iodide composition (x). Almost ideal green emission close to the chromaticity coordinates of the green vertex of the BT.2020 standard was achieved by appropriately substituting iodide ions for bromide ions in monohalide CsPbBr3 NCs. However, the PL peak width of the mix-halide NCs at x ∼ 0.5 was 0.127 eV, which was broader than the 0.105 eV peak width of the monohalide CsPbBr3 NCs. This phenomenon should be due to the compositional inhomogeneity among the individual CsPb(Br1-x I x )3 NCs. On the other hand, the PL quantum yield (PLQY) for the monohalide CsPbBr3 NCs decreased from 70 to 25% as x increased to 0.5. This result may be attributed to lattice distortion by the difference in the ionic radii of bromide and iodide. Improvements in the compositional inhomogeneity and lattice distortion would enhance the color purity of the green emission and the PLQY, respectively, of the CsPb(Br1-x I x )3 NCs.

| S-EPMC6751700 | biostudies-literature

Quantum-dot and organic hybrid tandem light-emitting diodes with multi-functionality of full-color-tunability and white-light-emission.

Project description:Realizing of full-color quantum-dot LED display remains a challenge because of the poor stability of the blue quantum-dot and the immature inkjet-printing color patterning technology. Here, we develop a multifunctional tandem LED by stacking a yellow quantum-dot LED with a blue organic LED using an indium-zinc oxide intermediate connecting electrode. Under parallel connection and alternate-current driving, the tandem LED is full-color-tunable, which can emit red, green and blue primary colors as well as arbitrary colors that cover a 63% National Television System Committee color triangle. Under series connection and direct current driving, the tandem LED can emit efficient white light with a high brightness of 107000?cd?m-2 and a maximum external quantum efficiency up to 26.02%. The demonstrated hybrid tandem LED, with multi-functionality of full-color-tunability and white light-emission, could find potential applications in both full-color-display and solid-state-lighting.

| S-EPMC7272409 | biostudies-literature

Halogen-Bond-Assisted Photoluminescence Modulation in Carbazole-Based Emitter.

Project description:Halogen bonding between a carbazole-based, pyridine-substituted organic semiconductor and a common halogen-bond donor (pentafluoroiodobenzene) yields efficient halogen-bond-driven fluorescence modulation in solution. Steady-state, time-resolved emission and absorption spectroscopy as well as density functional theory studies demonstrate that the fluorescence modulation arises from halogen-bond-induced intramolecular charge transfer. Fluorescence modulation offers a range of possibilities both in solution and in the solid state, for instance providing a potential pathway for the design of tunable luminescent materials for light-emitting devices.

| S-EPMC6158238 | biostudies-literature

Overcoming the exciton binding energy in two-dimensional perovskite nanoplatelets by attachment of conjugated organic chromophores.

Project description:In this work we demonstrate a novel approach to achieve efficient charge separation in dimensionally and dielectrically confined two-dimensional perovskite materials. Two-dimensional perovskites generally exhibit large exciton binding energies that limit their application in optoelectronic devices that require charge separation such as solar cells, photo-detectors and in photo-catalysis. Here, we show that by incorporating a strongly electron accepting moiety, perylene diimide organic chromophores, on the surface of the two-dimensional perovskite nanoplatelets it is possible to achieve efficient formation of mobile free charge carriers. These free charge carriers are generated with ten times higher yield and lifetimes of tens of microseconds, which is two orders of magnitude longer than without the peryline diimide acceptor. This opens a novel synergistic approach, where the inorganic perovskite layers are combined with functional organic chromophores in the same material to tune the properties for specific applications.

| S-EPMC7171160 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data