Inverse Vulcanization of Norbornenylsilanes: Soluble Polymers with Controllable Molecular Properties via Siloxane Bonds.

ABSTRACT: The inverse vulcanization produces high sulfur content polymers from alkenes and elemental sulfur. Control over properties such as the molar mass or the solubility of polymers is not well established, and existing strategies lack predictability or require large variations of the composition. Systematic design principles are sought to allow for a targeted design of materials. Herein, we report on the inverse vulcanization of norbornenylsilanes (NBS), with a different number of hydrolysable groups at the silicon atom. Inverse vulcanization of mixtures of NBS followed by polycondensation yielded soluble high sulfur content copolymers (50 wt % S) with controllable weight average molar mass (M_W ), polydispersity (Đ), glass transition temperature (T_G ), or zero-shear viscosity (η₀ ). Polycondensation was conducted in the melt with HCl as a catalyst, abolishing the need for a solvent. Purification by precipitation afforded polymers with a greatly reduced amount of low molar mass species.

SUBMITTER: Scheiger JM

PROVIDER: S-EPMC9302686 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Chemically induced repair, adhesion, and recycling of polymers made by inverse vulcanization.

Project description:Inverse vulcanization is a copolymerization of elemental sulfur and alkenes that provides unique materials with high sulfur content (typically ?50% sulfur by mass). These polymers contain a dynamic and reactive polysulfide network that creates many opportunities for processing, assembly, and repair that are not possible with traditional plastics, rubbers and thermosets. In this study, we demonstrate that two surfaces of these sulfur polymers can be chemically joined at room temperature through a phosphine or amine-catalyzed exchange of the S-S bonds in the polymer. When the nucleophile is pyridine or triethylamine, we show that S-S metathesis only occurs at room temperature for a sulfur rank > 2-an important discovery for the design of polymers made by inverse vulcanization. This mechanistic understanding of the S-S metathesis was further supported with small molecule crossover experiments in addition to computational studies. Applications of this chemistry in latent adhesives, additive manufacturing, polymer repair, and recycling are also presented.

| S-EPMC7441575 | biostudies-literature

High sulfur content polymers: The effect of crosslinker structure on inverse vulcanization.

Project description:The discovery of inverse vulcanization has allowed polymers to be made using elemental sulfur as the major component. However, until now, there has been little discussion of why seemingly similar crosslinkers result in polymers with radically different properties. Combining synthesis, spectroscopy, and modeling, this study reveals the structure-property relationships of sulfur polymers and reports a new system using 5-ethylidene-2-norbornene as a crosslinker that can stabilize up to 90 wt % of elemental sulfur.

| S-EPMC6175008 | biostudies-literature

Catalytic inverse vulcanization.

Project description:The discovery of inverse vulcanization has allowed stable polymers to be made from elemental sulfur, an unwanted by-product of the petrochemicals industry. However, further development of both the chemistry and applications is handicapped by the restricted choice of cross-linkers and the elevated temperatures required for polymerisation. Here we report the catalysis of inverse vulcanization reactions. This catalytic method is effective for a wide range of crosslinkers reduces the required reaction temperature and reaction time, prevents harmful H2S production, increases yield, improves properties, and allows crosslinkers that would be otherwise unreactive to be used. Thus, inverse vulcanization becomes more widely applicable, efficient, eco-friendly and productive than the previous routes, not only broadening the fundamental chemistry itself, but also opening the door for the industrialization and broad application of these fascinating materials.

| S-EPMC6367372 | biostudies-literature

Scalable High Refractive Index polystyrene-sulfur nanocomposites via in situ inverse vulcanization.

Project description:In this work, we demostrate the preparation of low cost High Refractive Index polystyrene-sulfur nanocomposites in one step by combining inverse vulcanization and melt extrusion method. Poly(sulfur-1,3-diisopropenylbenzene) (PS-SD) copolymer nanoparticles (5 to 10 wt%) were generated in the polystyrene matrix via in situ inverse vulcanization reaction during extrusion process. Formation of SD copolymer was confirmed by FTIR and Raman spectroscopy. SEM and TEM further confirms the presence of homogeneously dispersed SD nanoparticles in the size range of 5 nm. Thermal and mechanical properties of these nanocomposites are comparable with the pristine polystyrene. The transparent nanocomposites exhibits High Refractive Index n = 1.673 at 402.9 nm and Abbe'y number ~ 30 at 10 wt% of sulfur loading. The nanocomposites can be easily processed into mold, films and thin films by melt processing as well as solution casting techniques. Moreover, this one step preparation method is scalable and can be extend to the other polymers.

| S-EPMC7483506 | biostudies-literature

Investigating the Antibacterial Properties of Inverse Vulcanized Sulfur Polymers.

Project description:More than 60 million tons of sulfur are produced as a byproduct of the petrochemical industry annually. Recently, the inverse vulcanization process has transformed this excess sulfur into functional polymers by stabilization with organic cross-linkers. These interesting new polymers have many potential applications covering diverse areas. However, there has been very little focus on the potential of these high-sulfur polymers for their antibacterial properties. These properties are examined here by exposing two common bacteria species, Escherichia coli (E. Coli) and Staphylococcus aureus (S. aureus), to two structurally different, inverse vulcanized sulfur polymers: sulfur-co-diisopropenyl benzene (S-DIB) and sulfur dicyclopentadiene (S-DCPD). We report the highest bacteria log reduction (>log 4.3) of adhered bacterial cells (S. aureus) to an inverse vulcanized sulfur polymer to date and investigate the potential pathways in which antibacterial activity may occur.

| S-EPMC7081397 | biostudies-literature

Inverse Vulcanization of Styrylethyltrimethoxysilane - Coated Surfaces, Particles and Crosslinked Materials.

Project description:Sulfur as a side product of natural gas and oil refining is an underused resource. Converting landfilled sulfur waste into materials merges the ecological imperative of resource efficiency with economic considerations. A strategy to convert sulfur into polymeric materials is the inverse vulcanization reaction of sulfur with alkenes. However, the formed materials are of limited applicability, since they need to be cured at high temperatures (> 130 °C) for multiple hours. Herein, the reaction of elemental sulfur with styrylethyltrimethoxysilane is reported. Marrying the inverse vulcanization and silane chemistry yielded high sulfur content polysilanes, which could be cured via room temperature polycondensation to obtain coated surfaces, particles, and crosslinked materials. The polycondensation was triggered by hydrolysis of poly(sulfur-r-styrylethyltrimethoxysilane) (poly(Sn-r- StyTMS) under mild conditions (HCl, pH 4). For the first time, an inverse vulcanization polymer could be conveniently coated and mildly cured via post-polycondensation. Silica microparticles coated with the high sulfur content polymer could improve their Hg2+ ion remediation capability.

| S-EPMC7589442 | biostudies-literature

Inverse Vulcanized Polymers with Shape Memory, Enhanced Mechanical Properties, and Vitrimer Behavior.

Project description:The invention of inverse vulcanization provides great opportunities for generating functional polymers directly from elemental sulfur, an industrial by-product. However, unsatisfactory mechanical properties have limited the scope for wider applications of these exciting materials. Here, we report an effective synthesis method that significantly improves mechanical properties of sulfur-polymers and allows control of performance. A linear pre-polymer containing hydroxyl functional group was produced, which could be stored at room temperature for long periods of time. This pre-polymer was then further crosslinked by difunctional isocyanate secondary crosslinker. By adjusting the molar ratio of crosslinking functional groups, the tensile strength was controlled, ranging from 0.14±0.01 MPa to 20.17±2.18 MPa, and strain was varied from 11.85±0.88 % to 51.20±5.75 %. Control of hardness, flexibility, solubility and function of the material were also demonstrated. We were able to produce materials with suitable combination of flexibility and strength, with excellent shape memory function. Combined with the unique dynamic property of S-S bonds, these polymer networks have an attractive, vitrimer-like ability for being reshaped and recycled, despite their crosslinked structures. This new synthesis method could open the door for wider applications of sustainable sulfur-polymers.

| S-EPMC7497146 | biostudies-literature

Conformable microneedle pH sensors via the integration of two different siloxane polymers for mapping peripheral artery disease.

Project description:[Figure: see text].

| S-EPMC8626065 | biostudies-literature

Antibacterial Activity of Inverse Vulcanized Polymers.

Project description:Inverse vulcanization is a bulk polymerization method for synthesizing high sulfur content polymers from elemental sulfur, a byproduct of the petrochemical industry, with vinylic comonomers. There is growing interest in polysulfides as novel antimicrobial agents due to the antimicrobial activity of natural polysulfides found in garlic and onions (Tsao et al. J. Antimicrob. Chemother. 2001, 47, 665-670). Herein, we report the antibacterial properties of several inverse vulcanized polymers against Gram-positive Staphylococcus aureus and Gram-negative Pseudomonas aeruginosa, two common causes of nosocomial infection and pathogens identified by the World Health Organization as priorities for antimicrobial development. High sulfur content polymers were synthesized with different divinyl comonomers and at different sulfur/comonomer ratios, to determine the effect of such variables on the antibacterial properties of the resulting materials. Furthermore, polymers were tested for their potential as antibacterial materials at different temperatures. It was found that the test temperature influenced the antibacterial efficacy of the polymers and could be related to the glass transition temperature of the polymer. These findings provide further understanding of the antibacterial properties of inverse vulcanized polymers and show that such polymers have the potential to be used as antibacterial surfaces.

| S-EPMC7614836 | biostudies-literature

Mechanochemical synthesis of inverse vulcanized polymers.

Project description:Inverse vulcanization, a sustainable platform, can transform sulfur, an industrial by-product, into polymers with broad promising applications such as heavy metal capture, electrochemistry and antimicrobials. However, the process usually requires high temperatures (≥159 °C), and the crosslinkers needed to stabilize the sulfur are therefore limited to high-boiling-point monomers only. Here, we report an alternative route for inverse vulcanization-mechanochemical synthesis, with advantages of mild conditions (room temperature), short reaction time (3 h), high atom economy, less H2S, and broader monomer range. Successful generation of polymers using crosslinkers ranging from aromatic, aliphatic to volatile, including renewable monomers, demonstrates this method is powerful and versatile. Compared with thermal synthesis, the mechanochemically synthesized products show enhanced mercury capture. The resulting polymers show thermal and light induced recycling. The speed, ease, versatility, safety, and green nature of this process offers a more potential future for inverse vulcanization, and enables further unexpected discoveries.

| S-EPMC9381570 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data