Pearson's Principle-Inspired Robust 2D Amorphous Ni-Fe-Co Ternary Hydroxides on Carbon Textile for High-Performance Electrocatalytic Water Splitting.

ABSTRACT: Layered double hydroxide (LDH) is widely used in electrocatalytic water splitting due to its good structural tunability, high intrinsic activity, and mild synthesis conditions, especially for flexible fiber-based catalysts. However, the poor stability of the interface between LDH and flexible carbon textile prepared by hydrothermal and electrodeposition methods greatly affects its active area and cyclic stability during deformation. Here, we report a salt-template-assisted method for the growth of two-dimensional (2D) amorphous ternary LDH based on dip-rolling technology. The robust and high-dimensional structure constructed by salt-template and fiber could achieve a carbon textile-based water splitting catalyst with high loading, strong catalytic activity, and good stability. The prepared 2D NiFeCo-LDH/CF electrode showed overpotentials of 220 mV and 151 mV in oxygen evolution and hydrogen evolution reactions, respectively, and simultaneously had no significant performance decrease after 100 consecutive bendings. This work provides a new strategy for efficiently designing robust, high-performance LDH on flexible fibers, which may have great potential in commercial applications.

SUBMITTER: Hu R

PROVIDER: S-EPMC9316908 | biostudies-literature | 2022 Jul

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Pearson's Principle-Inspired Robust 2D Amorphous Ni-Fe-Co Ternary Hydroxides on Carbon Textile for High-Performance Electrocatalytic Water Splitting.

Hu Rong R Jiang Huiyu H Xian Jinglin J Mi Shiyun S Wei Liyun L Fang Guangyu G Guo Jiayue J Xu Siqi S Liu Ziyang Z Jin Huanyu H Yu Huimin H Wan Jun J

Nanomaterials (Basel, Switzerland) 20220714 14

Layered double hydroxide (LDH) is widely used in electrocatalytic water splitting due to its good structural tunability, high intrinsic activity, and mild synthesis conditions, especially for flexible fiber-based catalysts. However, the poor stability of the interface between LDH and flexible carbon textile prepared by hydrothermal and electrodeposition methods greatly affects its active area and cyclic stability during deformation. Here, we report a salt-template-assisted method for the growth ...[more]

PMID: 35889644

Similar Datasets

Project description:High valence multi transition metal hydroxides are greatly enriched with OER redox active sites due to strong synergy of heteroatomic nuclei. The efficiency of these redox active sites could be efficiently improved by coupling with highly conductive substrate. The advanced three-dimensional (3D) architecture and hydrophilic terminal functionalities of MXene (MX) considerably enhance the maximum utilization rate of anchored redox active sites by triggering the direct growth of these at MX substrate. Here-in, the freeze-dried 3D network of crumpled Vanadium-Carbide (V2C) MX sheets regulates the crystallization of in-situ grown NiFeCr multi transition metal hydroxides on MX scaffold through co-precipitation process. The XPS results suggest a synergistic chemical interaction of 3D MX scaffold with NiFeCr that modifies the electronic structure of the composite ensuring reduced charge transfer resistance. Besides, as found in FESEM morphological investigation, the well-dispersed NiFeCr multi-transition metal hydroxides are immobilized on open pores like structure of V2C-MX facilitate thoroughly accessible active sites. As a result, the NiFeCr@3D V2C-MX composite has shown an excellent electrocatalytic activity with an overpotential of 410 mV at a current density of 200 mA cm-2, Tafel slope of 100 mV dec in 1M KOH. Besides, the significant interaction between metallic centers and MXene support prevent detachment or agglomeration of active centers providing maximum interaction with the electrolytic ions, quick ionic OH- transportation, speedy and stable electron transfer channels thus ensure the long-term stability of NV-5MX during 53 h continuous operation of OER. Furthermore, we have utilized a more accurate value of half-cell standard reduction potential of the Hg/HgO electrode in the Nernst equation to represent all test voltages and to determine the overpotential values. In essence, this study features a facile approach for the confined growth of multi transition metal hydroxides in the presence of morphologically unique 3D crumpled V2C MXene architectures. Consequently, the increased OER reaction kinetics and improved stability of the synthesized composites are potentially due to synergistic interplay between well dispersed active sites and the conductive substrate.

Project description:The security of future energy, hydrogen, is subject to designing high-performance, stable, and low-cost electrocatalysts for hydrogen and oxygen evolution reactions (HERs and OERs), for the realization of efficient overall water splitting. Two-dimensional (2D) metal-organic frameworks (MOFs) introduce a large family of materials with versatile chemical and structural features for a variety of applications, such as supercapacitors, gas storage, and water splitting. Herein, a series of nanocomposites based on NCM/Ni-BDC@NF (N=Ni, C=Co, M:F=Fe, C=Cu, and Z=Zn, BDC: benzene dicarboxylic acid, NF: nickel foam) were directly developed on NF using a facile yet scalable solvothermal method. After coupling, the electronic structure of metallic atoms was well-modulated. Based on the XPS results, for the NCF/Ni-BDC, cationic atoms shifted to higher oxidation states, favorable for the OER. Conversely, for the NCZ/Ni-BDC and NCC/Ni-BDC nanocomposites, cationic atoms shifted to lower oxidation states, advantageous for the HER. The as-prepared NCF/Ni-BDC demonstrated prominent OER performance, requiring only 1.35 and 1.68 V versus a reversible hydrogen electrode to afford 10 and 50 mA cm-2 current densities, respectively. On the cathodic side, NCZ/Ni-BDC exhibited the best HER activity with an overpotential of 170 and 350 mV to generate 10 and 50 mA cm-2, respectively, under 1.0 M KOH medium. In a two-electrode alkaline electrolyzer, the assembled NCZ/Ni-BDC (cathode) ∥ NCF/Ni-BDC (anode) couple demanded a cell voltage of only 1.58 V to produce 10 mA cm-2. The stability of NCF/Ni-BDC toward OER was also exemplary, experiencing a continuous operation at 10, 20, and 50 mA cm-2 for nearly 45 h. Surprisingly, the overpotential after OER stability at 50 mA cm-2 dropped drastically from 450 to 200 mV. Finally, the faradaic efficiencies for the overall water splitting revealed the respective values of 100 and 85% for the H2 and O2 production at a constant current density of 20 mA cm-2.

Dataset Information

Pearson's Principle-Inspired Robust 2D Amorphous Ni-Fe-Co Ternary Hydroxides on Carbon Textile for High-Performance Electrocatalytic Water Splitting.

Publications

Pearson's Principle-Inspired Robust 2D Amorphous Ni-Fe-Co Ternary Hydroxides on Carbon Textile for High-Performance Electrocatalytic Water Splitting.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets