Universal Preparation Strategy for Ultradurable Antibacterial Fabrics through Coating an Adhesive Nanosilver Glue

ABSTRACT: Microbiological protection textile materials played an important role in the battle against the epidemic. However, the traditional active antimicrobial treatment of textiles suffers from narrow textile applicability, low chemical stability, and poor washability. Here, a high-strength adhesive nanosilver glue was synthesized by introducing nontoxic water-soluble polyurethane glue as a protectant. The as-prepared nanosilver glue could adhere firmly to the fiber surfaces by forming a flexible polymer film and could encapsulate nanosilver inside the glue. The as-prepared nanosilver had a torispherical structure with diameter of ~22 nm, zeta potential of −42.7 mV, and good dispersibility in water, and it could be stored for one year. Further studies indicated that the nanosilver glue had wide applicability to the main fabric species, such as cotton and polyester fabric, surgical mask, latex paint, and wood paint. The antimicrobial cotton and polyester fabrics were prepared by a simple impregnation–padding–baking process. The corresponding antimicrobial activity was positively correlated with nanosilver content. The treated fabrics (500 mg/kg) exhibited ultrahigh washing resistance (maintained over 99% antibacterial rates for 100 times of standard washing) and wear resistance (99% antibacterial rates for 8000 times of standard wearing), equivalent breathability to untreated fabric, improved mechanical properties, and good flexibility, demonstrating a potential in cleanable and reusable microbiological protection textiles.

SUBMITTER: Feng J

PROVIDER: S-EPMC9323275 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Microbial colonization of urinary catheters remains a serious problem for medicine as it often leads to biofilm formation and infection. Among the approaches reported to deal with this problem, surfaces functionalization to render them with antimicrobial characteristics, comprises the most promising one. Most of these strategies, however, are designed to target bacterial biofilms, while fungal biofilms are much less taken into account. In real-life settings, fungi will be inevitably found in consortium with bacteria, especially in the field of biomaterials. The development of antifungal coating strategies to be combined with antibacterial approaches will be pivotal for the fight of biomaterial-associated infections. The main goal of the present study was, therefore, to engineer an effective strategy for the immobilization of liposomal amphotericin B (LAmB) on polydimethylsiloxane (PDMS) surfaces to prevent Candida albicans colonization. Immobilization was performed using a two-step mussel-inspired coating strategy, in which PDMS is first immersed in dopamine solution. Its polymerization results in the deposition of a thin adherent film, called polydopamine (pDA), which allowed the incorporation of LAmB, afterwards. Different concentrations of LAmB were screened in order to obtain a contact-killing surface with no release of LAmB. Surface characterization confirmed the polymerization of dopamine and further functionalization with LAmB yielded surfaces with less roughness and more hydrophilic features. The proposed coating strategy rendered the surfaces of PDMS with the ability to prevent the attachment of C. albicans and kill the adherent cells, without toxicity toward mammalian cells. Overall results showed that LAmB immobilization on a surface retained its antifungal activity and reduced toxicity, holding therefore a great potential to be applied for the design of urinary catheters. Since the sessile communities commonly found associated to these devices exhibit a polymicrobial nature, the next challenge will be to co-immobilize LAmB with antibacterial agents to prevent the establishment of catheter-associated urinary tract infections (CAUTI).

Dataset Information

Universal Preparation Strategy for Ultradurable Antibacterial Fabrics through Coating an Adhesive Nanosilver Glue

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets