The Preparation and Wear Behaviors of Phenol-Formaldehyde Resin/BN Composite Coatings.

ABSTRACT: Phenolic-matrix composites possess excellent synergistic effects on mechanical and tribological properties and can be used in the aerospace, medical, and automobile industries. In this work, a series of phenol-formaldehyde resin/hexagonal boron nitride nanocomposites (PF/BNs) were in situ synthesized using an easy method. PF/BN coatings (PF/BNCs) on 316L steels were prepared through a spin-casting method. The wear behaviors of these PF/BNCs were investigated by dry sliding with steel balls. The percentage of BN, the thickness of the coating, and the heat treatment temperature affected the coefficients of friction (COFs) and wear rates of these coatings. After heat treatment at 100 °C, the tribological properties of the PF/BNCs were remarkably improved, which might be attributed to both the transformation of carbon on the worn surfaces from C-O/C=O into C=N, carbide, and other chemical bonds and the cross-linking of the prepolymers.

SUBMITTER: Zang C

PROVIDER: S-EPMC9572075 | biostudies-literature | 2022 Oct

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

The Preparation and Wear Behaviors of Phenol-Formaldehyde Resin/BN Composite Coatings.

Zang Chao C Xing Yaping Y Yang Tingting T Teng Qi Q Zhen Jinming J Zhang Ran R Jia Zhengfeng Z Han Weifang W

Polymers 20221009 19

Phenolic-matrix composites possess excellent synergistic effects on mechanical and tribological properties and can be used in the aerospace, medical, and automobile industries. In this work, a series of phenol-formaldehyde resin/hexagonal boron nitride nanocomposites (PF/BNs) were in situ synthesized using an easy method. PF/BN coatings (PF/BNCs) on 316L steels were prepared through a spin-casting method. The wear behaviors of these PF/BNCs were investigated by dry sliding with steel balls. The ...[more]

PMID: 36236185

Similar Datasets

Project description:This work involves the synthesis of hybrid oligomers based on the epoxy methacrylate resin. The EA resin was obtained by the modification of industrial-grade bisphenol A-based epoxy resin and methacrylic acid has been synthesized in order to develop multifunctional resins comprising both epoxide group and reactive, terminal unsaturation. Owing to the presence of both epoxy and double carbon-carbon pendant groups, the reaction product exhibits photocrosslinking via two distinct mechanisms: (i) cationic ring-opening polymerization and (ii) free radical polymerization. Monitoring of EA synthesis reactions over time using PAVs, MAAC and NV parameters, and the FT-IR method reveals that esterification reactions proceed faster at the start, exhibiting over 40% of conversion within the initial 60 min, which can be associated with a relatively high concentration of reactive sites and low viscosity of the reaction mixture at the initial reaction stage. With the further increase in the reaction time, the reaction rate tends to decrease. The control of the EA synthesis process can guide how to adjust reactions to obtain EAs with desired characteristics. Based on obtained values, one can state that the optimum synthesis time of about 4-5 h should be adopted to prepare EAs having both epoxy groups and unsaturated double bonds. The structure of the obtained EA was confirmed by FT-IR and NMR methods, as well as the determination of partial acid value and epoxy equivalent. Samples at various stages of synthesis were cured with UV radiation in order to study the kinetics of the process according to cationic and radical polymerization determined via photo-differential scanning calorimetry (photo-DSC) and real-time infrared spectroscopy (RT-IR) and then the properties of the cured coatings were tested. It turned out that the cationic polymerization was slower with a lower conversion of the photoreactive groups, as compared to the radical polymerization. All the obtained EA coatings were characterized by good properties of cured coatings and can be successfully used in the coating-forming sector.

Dataset Information

The Preparation and Wear Behaviors of Phenol-Formaldehyde Resin/BN Composite Coatings.

Publications

The Preparation and Wear Behaviors of Phenol-Formaldehyde Resin/BN Composite Coatings.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets