Room-temperature valence transition in a strain-tuned perovskite oxide.

ABSTRACT: Cobalt oxides have long been understood to display intriguing phenomena known as spin-state crossovers, where the cobalt ion spin changes vs. temperature, pressure, etc. A very different situation was recently uncovered in praseodymium-containing cobalt oxides, where a first-order coupled spin-state/structural/metal-insulator transition occurs, driven by a remarkable praseodymium valence transition. Such valence transitions, particularly when triggering spin-state and metal-insulator transitions, offer highly appealing functionality, but have thus far been confined to cryogenic temperatures in bulk materials (e.g., 90 K in Pr_1-xCa_xCoO₃). Here, we show that in thin films of the complex perovskite (Pr_1-yY_y)_1-xCa_xCoO_3-δ, heteroepitaxial strain tuning enables stabilization of valence-driven spin-state/structural/metal-insulator transitions to at least 291 K, i.e., around room temperature. The technological implications of this result are accompanied by fundamental prospects, as complete strain control of the electronic ground state is demonstrated, from ferromagnetic metal under tension to nonmagnetic insulator under compression, thereby exposing a potential novel quantum critical point.

SUBMITTER: Chaturvedi V

PROVIDER: S-EPMC9755214 | biostudies-literature | 2022 Dec

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Room-temperature valence transition in a strain-tuned perovskite oxide.

Chaturvedi Vipul V Ghosh Supriya S Gautreau Dominique D Postiglione William M WM Dewey John E JE Quarterman Patrick P Balakrishnan Purnima P PP Kirby Brian J BJ Zhou Hua H Cheng Huikai H Huon Amanda A Charlton Timothy T Fitzsimmons Michael R MR Korostynski Caroline C Jacobson Andrew A Figari Lucca L Barriocanal Javier Garcia JG Birol Turan T Mkhoyan K Andre KA Leighton Chris C

Nature communications 20221215 1

Cobalt oxides have long been understood to display intriguing phenomena known as spin-state crossovers, where the cobalt ion spin changes vs. temperature, pressure, etc. A very different situation was recently uncovered in praseodymium-containing cobalt oxides, where a first-order coupled spin-state/structural/metal-insulator transition occurs, driven by a remarkable praseodymium valence transition. Such valence transitions, particularly when triggering spin-state and metal-insulator transitions ...[more]

PMID: 36522321

Similar Datasets

Project description:A temperature induced valence phase transition from Yb3+ at higher temperatures to Yb2+ at lower temperatures was observed at T = 110(1) K for intermetallic YbPd2Al3. The title compound has been prepared from the elements in sealed tantalum ampoules. The structure was refined from single-crystal data and the title compound was found to crystallize in the hexagonal YNi2Al3 type structure with space group P6/mmm and lattice parameters of a = 929.56(7) and c = 420.16(3) pm (300 K data). Full ordering of the Pd and Al atoms within the [Pd2Al3] δ- polyanion was observed. Magnetic measurements revealed an anomaly in the dc susceptibility data and intermediate valent Yb at higher temperature, as observed from the effective magnetic moment. The proposed valence phase transition was also observed as a λ-type anomaly in heat capacity measurements (T = 108.4(1) K), however, no systematic shift of the λ-peak was observed in field dependent heat capacity measurements. An antiferromagnetic ordering at this temperature, however, could be excluded, based on field-dependent susceptibility measurements and magnetization isotherms. No dynamic phenomenon was observed in ac susceptibility measurements, excluding e.g. spin-glass behavior. Subsequent temperature dependent single-crystal and powder X-ray diffraction experiments indicated a steep increase in the length of the c axis around T = 110 K upon cooling. However, no structural phase transition was found via single-crystal diffraction experiments conducted at 90 K. The anomaly was also observed in other physical measurements of e.g. the electrical resistivity, indicating a clear change in the electronic structure of the material. X-ray photoelectron spectroscopy conducted at room temperature shows the presence of both, Yb2+ and Yb3+, underlining the mixed-valent state. Members of the solid solution Yb1-x Ca x Pd2Al3 (x = 0.33, 0.67, 1) were finally used to further study the charge ordering and the present temperature induced valence phase transition.

Dataset Information

Room-temperature valence transition in a strain-tuned perovskite oxide.

Publications

Room-temperature valence transition in a strain-tuned perovskite oxide.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets